• Macromolecular Research
• /
• v.14 no.5
• /
• pp.552-558
• /
• 2006

Biodegradable nanofibrous poly(L-lactic acid) (PLLA) scaffold was prepared by an electrospinning process for use in tissue regeneration. The nanofiber scaffold was treated with oxygen plasma and then simultaneously in situ grafted with hydrophilic acrylic acid (AA) to obtain PLLA-g-PAA. The fiber diameter, pore size, and porosity of the electrospun nanofibrous PLLA scaffold were estimated as $250\sim750nm,\;\sim30{\mu}m$, and 95%, respectively. The ultimate tensile strength was 1.7 MPa and the percent elongation at break was 120%. Although the physical and mechanical properties of the PLLA-g-PAA scaffold were comparable to those of the PLLA control, a significantly lower contact angle and significantly higher ratio of oxygen to carbon were notable on the PLLA-g-PAA surface. After the fibroblasts were cultured for up to 6 days, cell adhesion and proliferation were much improved on the nanofibrous PLLA-g-PAA scaffold than on either PLLA film or unmodified nanofibrous PLLA scaffold. The present work demonstrated that the applications of plasma treatment and hydrophilic AA grafting were effective to modify the surface of electrospun nanofibrous polymer scaffolds and that the altered surface characteristics significantly improved cell adhesion and proliferation.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.04a
• /
• pp.165-168
• /
• 2003

Nylon was the first commercialized synthetic fiber. It is a polyamide, derived from a diamine and dicarboxylic acid. The nylon fiber has outstanding durability and excellent physical properties such as stiffness, wear and abrasion resistance, friction coefficient and chemical resistance. Due to these properties of nylon 66, nano-sized fibers are produced by electrospinning method in this study. During the past years the nylon 66 fibers have been prepared by conventional melt spining. (omitted)

• Carbon letters
• /
• v.12 no.2
• /
• pp.70-80
• /
• 2011

Two pitches with different average molecular structures were electrospun and compared in terms of the properties of their fibers after oxidative stabilization, carbonization, and activation. The precursor with a higher molecular weight and greater content of aliphatic groups (Pitch A) resulted in better solubility and spinnability compared to that with a lower molecular weight and lower aliphatic group content (Pitch B). The electrical conductivity of the carbon fiber web from Pitch A of 67 S/cm was higher than that from Pitch B of 52 S/cm. The carbon fiber web based on Pitch A was activated more readily with lower activation energy, resulting in a higher specific surface area compared to the carbon fiber based on Pitch B (Pitch A, 2053 $m^2/g$; Pitch B, 1374 $m^2/g$).

• Carbon letters
• /
• v.23
• /
• pp.17-21
• /
• 2017

Polyurethane (PU) nanofibers containing graphene oxide (GO) and Ag doped functionalized reduced graphene oxide (Ag-RGO) were successfully prepared via the electrospinning technique. The uniform distribution of GO sheets along with Ag nanoparticle in the nanofibers was investigated by scanning electron microscopy and the elemental mapping technique. X-ray diffraction and thermal gravimetric analysis verified the presence of GO and Ag in the bicomposite nanofibrous mats. Antibacterial tests against Escherichia coli demonstrated that the addition of GO and Ag-RGO to the PU nanofiber greatly enhanced bactericidal efficiency. Overall, these features of the synthesized nanofibers make them a promising candidate material in the biomedical field for applications such as tissue engineering, wound healing, and drug delivery systems.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.24 no.2
• /
• pp.160-165
• /
• 2015

The 14k, 45k, and 70k Mw PCL have different crystallization temperatures and therefore have slightly different characteristics affecting the fiber diameter. To observe these behaviors, the fiber was produced at every step of $10^{\circ}C$ for each molecular weights and the diameter was measured. Moreover, the fiber was fabricated over the cooled ground plate to observe the change in fiber diameter in comparison to the normal ground plate. In case of molecular Mw 14k PCL, the diameter increased as the temperature increased. For Mw 45k PCL, the fiber diameter decreased as the temperature increased. As of Mw 70k PCL, the fiber diameter decreased with increasing temperature as well. When the experiment was conducted over the cooled collector plate, the data did not change significantly from the previous lexperiments.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10b
• /
• pp.275-276
• /
• 2003

Electrostatic spinning or electrospinning has been recently paid attention to prepare ultrafine fiber mats which are composed of diameters in a range of submicrons to nanoscale size[l]. Due to small diameters and porous structure, electrosun fibers have a high specific surface area and expected to use for broad applications, such as filters, membranes, wound dressing materials, artificial blood vessels. a nonwoven fabric, a reiforcement of nanocomposites[2,3], etc. (omitted)

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10b
• /
• pp.134-137
• /
• 2003

탄소섬유나 활성탄소섬유(activated carbon fiber, ACF)는 일반적으로 출발물질에 따라 polyacrylonitrile(PAN)계, 아크릴(acryl)계, 피치(pitch)계, 페놀(phenol)계 등으로 분류할 수 있다. 보통 습식, 용융 혹은 용융분사(melt-blown) 방사 방법에 의해 섬유 형태로 형성한 다음 산화성 가스 분위기에서 불융화 과정을 거쳐 열에 대한 안정성을 부여하여 불활성 분위기에서 탄소화하여 탄소섬유를 제조하거나, 수증기나 이산화 탄소와 같은 산화성 분위기에서 활성화하여 활성탄소섬유를 제조한다. (중략)

• Proceedings of the Polymer Society of Korea Conference
• /
• 2006.10a
• /
• pp.299-299
• /
• 2006

Polydioxanone nanofibers for TEM observation can be produced. To collect parallelly aligned nanofibers can crystallize them partially. The SAED pattern of nanofibers drawn and/or heat-treated shows a well-developed fiber pattern, and in the patterns we can observe crystalline reflections up to third layer line.

• Membrane Journal
• /
• v.20 no.1
• /
• pp.40-46
• /
• 2010

In this study, we manufactured the membrane using the polyethersulfone (PES) of fiber by using the electrospinning method. The polymer electrolyte membrane for fuel cells was manufactured by impregnating Nafion solution to the porous PES membrane. We confirmed that electrospun PES membrane has higher thermal stability than Nafion 212 membrane by thermogravimetric analysis. Impregnated Nafion in the pores of the electrospun PES membrane was characterized by scanning electron microscopy. The AC impedance data shows the hydrogen ionic conductivity of $10^{-2}$ S/cm below $100^{\circ}C$. Nafion impregnated PES membrane shows the maximum performance at $90^{\circ}C$ showing current density of 389 mA/$cm^2$ at 0.6 V, while Nafion 212 membrane shows maximum at $75^{\circ}C$.

• Fibers and Polymers
• /
• v.6 no.2
• /
• pp.121-126
• /
• 2005

Semicrystalline poly(ethylene terephthalate) (cPET)/amorphous poly(ethylene terephthalate) with isophthalic acid (aPET) blends with 100/0, 75/25, 50/50, 25/75, and 0/100 by weight ratios were dissolved in a mixture of trifluoroacetic acid (TFA)/methylene chloride (MC) (50/50, v/v) and electrospun via the electrospinning technique. Solution properties such as solution viscosity, surface tension and electric conductivity were determined. The solution viscosity slightly decreased as aPET content increased, while there was no difference in surface tension with respect to aPET composition. The characteristics of the electro spun cPET/aPET blend nonwovens were investigated in terms of their morphology, pore size and gas permeability. All these measurements were carried out before and after heat treatment for various blend weight ratios. The average diameter of the fibers decreased with increasing aPET composition due to the decrease in viscosity. Also, the morphology of the electrospun cPET/aPET blend nonwovens was changed by heat treatment. The pore size and pore size distribution varied greatly from a few nanometers to a few microns. The gas permeability after heat treatment was lower than that before heat treatment because of the change of the morphology.