• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.68-70
• /
• 2006

For the aluminum material of the thick-thickness more than 100mm Penetration depth Electron beam welding is effectively applicable with a characteristic of high energy intensity. But Al 6061 alloy has high crack sensitivity due to minor alloys, which are silicon, magnesium, copper etc. With a sample block of 135mm thickness EBW test was performed in vertical position. As tensile strength has $210{\sim}220N/mm^2$ with weld area broken. Bend test shows low ductility with fracture of partly specimens. Chemical contents of alloys show no difference between weld and base metal. Defect in middle weld area figures out typical hot crack due to low melting materials. Micro structure of weld area has some difference compare to HAZ and base metal. As a result of EBW test for Al 6061 alloy, it shows that weld defect could be occurred even though establishing of optimum weld parameter condition.

• Journal of Welding and Joining
• /
• v.31 no.6
• /
• pp.50-57
• /
• 2013

Characterization of microstructures and cryogenic mechanical properties of electro beam (EB) welds between cast and forged Inconel 718 superalloys has been investigated. Optimal EBW condition was found in the beam current range of 36~39 mA with the constant travel speed of 12 mm/s and arc voltage of 120 kV for 10 mm-thick specimens. Electron beam current lower than 25 mA caused to occur the liquation microfissuring in cast-side heat affected zone (HAZ) of EB welds. The HAZ liquation microfissure was found on the liquated grain boundaries with resolidified ${\gamma}/Laves$ and ${\gamma}/NbC$ eutectic constituents. EBW produced welds showing a fine dendritic structure with relatively discrete Laves phase due to fast cooling rate. After post weld aging treatment, blocky Laves phase and formation of ${\gamma}^{\prime}+{\gamma}^{{\prime}{\prime}}$ strengtheners were observed. Presence of primary strengthener and coarse Laves particles in PWHT weld may cause to reduce micro-plastic zone ahead of a crack, leading to a significant decrease in Charpy impact toughness at $-196^{\circ}C$. Fracture initiation and propagation induced by Charpy impact testing were discussed in terms of the dislocation structures ahead of crack arisen from the fractured Laves phase.

• Proceedings of the KWS Conference
• /
• 1995.10a
• /
• pp.180-186
• /
• 1995

• Proceedings of the KWS Conference
• /
• 1997.10a
• /
• pp.142-144
• /
• 1997

• Proceedings of the KWS Conference
• /
• 1992.10a
• /
• pp.55-58
• /
• 1992

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.8
• /
• pp.138-148
• /
• 1999

Thermal deformations of tension mask under localized heating are analyzed using finite element method and electron beam landing shifts are predicted by the analysis results. In CRT, electron beam landing shifts due to thermal deformations of the tension mask make the color purity of screen worse. In order to get the final results of thermal deformations, firstly the tension processes of the mask and following welding processes between the tensional mask and rail must be analyzed sequentially. And then, nonlinear transient thermo-elastic finite element analysis is performed on every part inside CRT including tension mask, wherein thermal radiation is a main heat transfer mechanism. Because the tension mask has numerous slits, the effective thermal conductivity and effective and effective elastic modulus is calculated, and the tension mask is modeled as a shell without slits. From the displacement results of tension mask, electron beam landing shifts is calculated directly. Experiments are performed to confirm our analysis results. Temperature distributions and beam landing shifts of tension mask are measured and the results are in good agreement with those of analyses.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.43-46
• /
• 2010

As the nuclear power plant has been constructed continuously for several decades in Korea, the welding technology for components manufacturing and installation has been improved largely. Standardization for weld test and qualification was also established systematically according to the concerned code. The welding for the main components requires the high reliability to keep the constant quality level, which means the repeatability of weld quality. Therefore the weld process qualified by thorough test and evaluation is able to be applied for manufacturing. Narrow gap SAW and GTAW process are usually applied for girth seam welding of pressure vessel like Reactor vessel, steam generator, and etc. For the surface cladding with stainless steel and Inconel material, strip welding process is mainly used. Inside cladding of nozzles is additionally applied with Hot wire GTAW and semi-auto welding process. Especially the weld joint having elliptical weld line on curved surface needs a specialized weld system which is automatically rotating with adjusting position of the head torch. The small sized pipe, tube, and internal parts of reactor vessel requests precise weld processes like an automatic GTAW and electron beam welding. Welding of dissimilar materials including Inconel690 material has high possibility of weld defects like a lack of fusion, various types of crack. To avoid these kinds of problem, optimum weld parameters and sequence should be set up through the many tests. As the life extension of nuclear power plant is general trend, weld technologies having higher reliability is required gradually. More development of specialized welding systems, weld part analysis and evaluation, and life prediction for main components should be taken into a consideration extensively.

• Journal of Advanced Marine Engineering and Technology
• /
• v.21 no.2
• /
• pp.157-165
• /
• 1997

The strength level of welded joint in room temperature and elevated temperature up to $600^{\circ}C$ was investigated in 250 and 300 grade 18% Ni maraging steel sheet welded with electron beam. The results obtained in this study are as follows; 1. Optimum welding heat input was 600J/cm in 1.0mm thickness and the room temperature tensile strength, joint efficiency of welded joint treated with optimum aging condition were found to be about 166kg/$mm^2$, 95% in 250 grade, 189kg/$mm^2$, 92% in 300 grade maraging steel sheet, respectively. 2. Tensile strength of welded joint in room temperature increased slightly by aging after repeated solution heat treatment, but the fracture mode showed a shear. 3. Joint efficiency at a temperature between $540^{\circ}C$and $600^{\circ}C$ found to be about 72% to 55%, but the joint efficiency exceeded about 90% below $300^{\circ}C$. 4. The fracture occurred in most weld metal, and the fracture surface showed a shallow dimple.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.11 no.4
• /
• pp.76-82
• /
• 2008

Alloy 718 nozzle component was manufactured by hot forging and electron beam welding process. In this process, 718 billets produced in domestic company were used and evaluated. Before performing industrial scale hot forging, small size hot compression tests were carried out under various process conditions and then microstructural evaluations were analyzed. Using the results, FEM simulations were performed in order to optimize the hot working process. After hot working, forged work-pieces were machined and welded by electron beam. Final nozzle components were heat treated and their microstructure and mechanical properties were investigated.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.555-555
• /
• 2008