• Textile Coloration and Finishing
• /
• v.15 no.3
• /
• pp.154-160
• /
• 2003

Polypropylene nonwoven fabrics were grafted with acrylic acid by a preirradiation method by using electron beam accelerator. The effect of irradiation dose, storage time, concentration of acrylic acid, reaction temperature, reaction time and Mohr's salt concentration on the degree of grafting were investigated in detail. The grafted Polypropylene nonwoven fabrics were characterized using IR spectroscopy and SEM. The results showed that the degree of grafting increased with increasing absorbed dose and the Mohr's salt in the acrylic acid solution promoted grafting efficiency.

• Nuclear Engineering and Technology
• /
• v.52 no.2
• /
• pp.373-380
• /
• 2020

This study was carried out to convert the hydrophobic characteristics of PVDF to hydrophilic. Poly(-vinylidene fluorine) (PVDF) was grafted by electron beam irradiation and sulfonated. The grafting degree of modified PVDF increased with the monomer concentration, but not the conversion degree. From the results of FTIR and XPS, it was shown that the amount of converted sulfur increased with the grafting degree. The radiation-induced graft polymerization led to decrease fluorine from 35.7% to 21.3%. Meanwhile, the oxygen and sulfur content increased up to 8.1% and 3.2%. The pore size of modified membranes was shrunken and the roughness sharply decreased after irradiation. The ion exchange capacity and contact angle were investigated to show the characteristics of PVDF. The enhanced ion exchange capacity and lower contact angle of modified PVDF showed that the hydrophilicity played a role in determining membrane fouling. Electron beam irradiation successfully modified the hydrophobic characteristics of PVDF to hydrophilic.

• Nuclear Engineering and Technology
• /
• v.15 no.1
• /
• pp.1-10
• /
• 1983

By controlling both the means of grafting and the cast-solution components, no degradation and dimensional change of radiation-induced graft polymerization were found. The electric resistance of styrene-cellulose acetate grafts increases with increasing styrene content, while those for the hydrophilic monomers show no marked effect. In comparison with the grafted cellulose acetate membrane by simultaneous irradiation method, the appearance of the grafted membrane by post-polymerization method was not markedly changed irrespective of the percent of grafting and radiation dose of electron beam or ${\gamma}$-ray. The combination of crosslinking agents such as divinyl benzene (OB) or trimethyl propane triacrylate (TMPT) in the VP:St:BPO system leads to gradual increase of the percent of grafting. The activation energy for grafting of St:VP:BPO solution onto cellulose acetate membrane was determined to be about 21.8 Kcal/mole over the range of 55$^{\circ}$-8$0^{\circ}C$. The initial rate of grafting (in %/hr) is proportional to the power 0.76 for dose intensities.

• Journal of Environmental Science International
• /
• v.23 no.8
• /
• pp.1419-1428
• /
• 2014

Electron beam-induced grafting polymerization was employed to prepare Acrylic acid-grafted bacterial cellulose (BC-g-AAc). BC-g-AAc as an adsorbent was applied to remove heavy metals (e.g., As, Pb, and Cd). This study examined followings; morphological change of surface, adsorptive behavior of BC-g-AAc, and interpretation of adsorptive kinetics. Specific surface areas of BC and BC-g-AAc were $0.9527m^2g^{-1}$ for BC and $0.2272m^2g^{-1}$ for BC-g-AAc, respectively as measured by BET nitrogen adsorption, revealing the morphological change of the surface of BC-g-AAc. Batch adsorption test was performed to investigate adsorptive behavior of BC-g-AAc in aqueous solution. The amounts of Pb and Cd adsorbed on BC-g-AAc were $69mg\;g^{-1}$ and $56mg\;g^{-1}$, respectively. However, As was not adsorbed on BC-g-AAc due to its neutral nature. Both the Benaissa model and the Kurniawan model were applied in the study to interpret adsorptive kinetics. From the value of correction coefficient ($R^2$), adsorptive kinetics of Pb and Cd were subjected to Kurniawan model referred to pseudo-second-order. Taken together, the results of this study show that BC-g-AAc has potential as a heavy metal (eg., Pb, Cd)-adsorbent made of an environmentally friendly material.

• Composites Research
• /
• v.32 no.6
• /
• pp.335-341
• /
• 2019

In this study, an acrylic acid (AAc) was grafted on a polypropylene (PP) nonwoven fabric using electron beam irradiation. Electron beam grafting was carried out under various conditions to produce AAc grafted PP (PP-g-AAc) nonwoven fabric having a grafting yield of about 50% at radiation dose of 100 kGy and a monomer concentration of 60%. The physical and chemical properties of PP-g-AAc nonwoven fabric were evaluated by SEM, ATR-FTIR, thermal analysis and tensile strength. The morphology of PP and PP-g-AAc nonwoven fabric confirmed by SEM showed no significant change, and it was judged that AAc was introduced into PP nonwoven fabric from ATR-FTIR. PP-g-AAc nonwoven fabric showed an increase in tensile strength and a decrease in tensile strain compared to PP nonwoven fabric. However, since change of value is not significant, it is considered that there is no significant influence on the physical characterization. Adsorption experiments of PP-g-AAc nonwoven fabric on various ions showed selective adsorption behavior for lead ion. In conclusion, the electron beam radiation-induced PP-g-AAc nonwoven fabric is expected to be applied as an effective adsorbent for the adsorption of lead ions.