• Journal of the Korean Electrochemical Society
• /
• v.9 no.1
• /
• pp.34-39
• /
• 2006

Electrochemical properties of Cu foil current collector with a $Li_{0.5}La_{0.5}TiO_3$ Cu a Si thin film deposited by r.f sputtering as an anode for Li free battery were evaluated. The Cu foil current collectors were lied in and out of plasma during sputtering process. The X-ray diffraction results indicated that the as-deposited Si and $Li_{0.5}La_{0.5}TiO_3$ thin films in and out of plasma did not show any crystalline difference. The $Li_{0.5}La_{0.5}TiO_3$ film in plasma and Si film out of plasma showed better cyclability since crystalline $Li_{0.5}La_{0.5}TiO_3$ has much higher ionic conductivity and crystalline Si film is much sensitive far volume change during charge-discharge process. These results suggested that the deposition of amorphous Si on Cu foil current collector is much better for fabrication of Li free battery and it can be useful for the unique battery with a cycling number constraint of below 10.

• Journal of the Korean Electrochemical Society
• /
• v.15 no.4
• /
• pp.230-235
• /
• 2012

Polymer electrolytes consisted of $BF_3LiMA$ and 300 (PEGMA300) or 1100 (PEGMA1100) g $mol^{-1}$ of PEGMA were prepared and the electrochemical properties were characterized. Interestingly, the AC-impedance measurement shows $1.22{\times}10^{-5}S\;cm^{-1}$ of room temperature ionic conductivity from PEGMA1100 based solid polymer electrolytes while $8.54{\times}10^{-7}S\;cm^{-1}$ was observed in PEGMA300 based liquid polymer electrolytes. The more suitable coordination between lithium ion and ethylene oxide (EO) unit might be the reason of higher ionic conductivity which can be possible in PEGMA1100 based electrolytes since it has 23 EO units in monomer. The lithium ion transference number was found to be 0.6 due to the side reactions between $BF_3$ and lithium metal expecially for longer time but 0.9 was observed within 3000 seconds of measuring time which is strong evidence of a single-ion conductor.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.3
• /
• pp.203-218
• /
• 2009

The development of lithium-ion battery (LIB) technologies and their application in the field of large-scale power sources, such as electric vehicles (EVs), hybrid EVs, and plug-in EVs require enhanced reliability and superior safety. The main components of LIBs should withstand to the inevitable heating of batteries during high current flow. Carbonate solvents that contribute to the dissociation of lithium salts are volatile and potentially combustible and can lead to the thermal runaway of batteries at any abuse conditions. Recently, an interest in nonflammable materials is greatly growing as a means for improving battery safety. In this review paper, novel approaches are described for designing highly safe electrolytes in detail. Non-flammability of liquid electrolytes and battery safety can be achieved by replacing flammable organic solvents with thermally resistive materials such as flame-retardants, fluorinated organic solvents, and ionic liquids.

• Journal of the Korean Electrochemical Society
• /
• v.12 no.4
• /
• pp.342-348
• /
• 2009

Zn/Air secondary batteries are high energy density type and environment-friendly. Also, they have safer properties than batteries of other type by low manufacturing cost and using the electrolyte solution. But, they have a weak concerning large output discharge. Oxygen evolution reaction(OER) and oxgen reduction reaction(ORR) in aqueous solution make a result of a decrease of cell efficiency and life span. Therefore, to minimize the voltage drop from between OCV and charge/discharge voltage is key point. The problem should be solved through developing catalysts of high efficiency. In this study, we synthesized $Pr_{1-x}(Sr,\;Ca)_x\;CoO_3$ powders by citric method and then measured physical characteristics of each powder by XRD, SEM, TGA etc. We examined its electrochemical properties by the cathodic polarization, anodic polarization and cyclic voltammogram. We achieved results that new catalysts showed better performances than existing $La_{1-x}Sr_xCoO_3$, $La_{1-x}Ca_xCoO_3$, ect. catalysts prepared in our lab.

• Journal of Korean Academic Society of Home Health Care Nursing
• /
• v.8 no.2
• /
• pp.121-134
• /
• 2001

The purpose of this study were to analyze the home care services and to evaluate the client's satisfaction with the home care services provided by home care service center in the C hospital. The data were collected by reviewing charts of 128 home care clients who were receiving home care services at C hospital from October 1997 to September 2000. The subjects for satisfaction of home care service were 20 clients from July 10 to September 30, 2000. The tool for measurement of present condition of home care service was developed by the researchers. The satisfactions of the home care services were measured by using the instrument developed by Im(997). The data were analyzed by using the SPSS/PC+. The results of this study were as followings : 1. Majority of the subjects was female(61.7%). The average of age was 63.5 years. The service has been used mostly by the elderly 60 years of age or older(71.1%). The economic level of most of subjects was in middle class(94.5%). 2. Majority of the subject had a cancer(55.4%), following stroke(25.0%). The average duration of disease for the subjects was 31 months. The average time of hospitalization for the subjects was 3.3 times. The duration of hospitalization was 10$\sim$30 days(26.6%), 30$\sim$60 days(23.4%) and above of the 210 days(9.4%). 3. Most of the subjects used his/her doctor (47.7%), as a consultant, following his/her nurse (28.1%), other patients or their family (21.9%). Most of reasons for a consultation were supportive management(Infusion or medication, 60.94%), following tube management(L-tube or T-tube, 25%), Foley catheter management (15.63%) etc. 4. 28 types of nursing diagnoses were used by the home care service. The nursing diagnosis altered nutrition: less than body requirement were used mostly by the home care service, following risk for infection, impaired skin integrity, impaired swallowing, ineffective airway clearance altered comfort: pain, impaired physical mobility. By the human-response pattern, exchanging(63.2%), moving(7.5%), feeling(10.4%), knowing(5.2%), communicating (2.6%), relating(0.5%) perceiving(0.4%) and choosing(0.3%). There were 42 nursing intervention types were performed by the home care service. By the NIC(nursing intervention classification. McCloskey. Bulech. 1996). physiologic: complex (30.3%) was the most, safety(28.3%), behavioral(20.0%), physiologic: basic(10.8%) and health system(1.7%). Observation or assessment was the most nursing intervention performed by the home care service. following IV infusion. vital sign observation. infusion management and fluid-electrolyte balance management. 5. The level of client's satisfaction with provided home care services showed considerably high(2.67/ 3).

• Korean Chemical Engineering Research
• /
• v.52 no.3
• /
• pp.279-288
• /
• 2014

Nuclear energy is expected to meet the growing energy demand while avoiding CO2 emission. However, the problem of accumulating spent fuel from current nuclear power plants which is mainly composed of uranium oxides should be addressed. One of the most practical solutions is to reduce the spent oxide fuel and recycle it. Next-generation fuel cycles demand innovative features such as a reduction of the environmental load, improved safety, efficient recycling of resources, and feasible economics. Pyroprocessing based on molten salt electrolysis is one of the key technologies for reducing the amount of spent nuclear fuel and destroying toxic waste products, such as the long-life fission products. The oxide reduction process based on the electrochemical reduction in a LiCl-$Li_2O$ electrolyte has been developed for the volume reduction of PWR (Pressurized Water Reactor) spent fuels and for providing metal feeds for the electrorefining process. To speed up the electrochemical reduction process, the influences of the feed form for the cathode and the type of anode shroud on the reduction rate were investigated.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.3
• /
• pp.125-130
• /
• 2002

An attempt was made for the application of porous reticular metal to a heat dissipation material in semiconductor process. For this aim, the electrodeposition of Fe/Ni alloy on the porous reticular Cu has been performed to minimize the thermal expansion mismatch between Cu skeleton and electronic chip. Preliminary tests for the electrodeposition of Fe/Ni alloy layer were conducted by using standard Hull Cell to examine the effect of current density on the composition of alloy layer. It seemed that mass transfer affected significantly the composition of Fe/Ni layer due to anomalous codeposition in the electrodeposition of Fe/Ni alloy. A paddle type stirring bath, which was employed to control the mass transfer of electrolyte in the work, was found to allow the electrodeposition Fe/Ni with a precise composition. result showed that the thermal expansion of Fe/Ni alloy layer was much lower than that of pure copper. From the tests of heat dissipation by using the apparatus designed in the work the heat dissipation material fabricated in the work showed the excellent heat dissipation capacity, namely, more than two times as compared to that of pure copper plate.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.3
• /
• pp.153-158
• /
• 2002

The effects of leveler on the copper trench filling were investigated during damascene plating process. To investigate the trench filling effect with the addition of a leveler, a cross-section images of the electroplated trenches with the width of$0.37{\mu}m,\;and\;0.18{\mu}m$ were observed by field emission scanning electron microscope (FE-SEM). Polyethylene glycol(PEG), 3-mercapto-1-propanesulfonic acid and Janus Green B were used as a carrier, an accelerator and a leveler. $0.37{\mu}m$ trenches were superfilled without voids, but there was voids formation in $0.18{\mu}m$ trenches when the leveler was not added into the electrolyte. On the other hand $0.18{\mu}m$ trenches were superfilled without voids with the addition of the leveler due to the reduction growth rate of copper at protrusions and edges, which yield smooth final deposit surface. The leverer effect becomes more significant as the width of trenches becomes smaller when trenches are filed.

• Journal of the Korean Electrochemical Society
• /
• v.4 no.1
• /
• pp.6-9
• /
• 2001

[ $SiO_2$ ] effect on the electrochemical properties of polymeric gel electrolytes(PGEs) reinforced with glass fiber cloth(GFC) was investigated . PGEs were composed of polyacrylronitrile(PAN), poly(vinylidenefluoride-co-hexafluoropropylene) (P(VdF-co-HFP)), $LiClO_4$ and three kind of plasticizer(ethylene carbonate, dietyl carbonate, propylene carbonate). $SiO_2$ was added to PGEs in the weight fraction of 10, 20, $30\%$ respectively. PGEs containing $SiO_2$ showed conductivity of over $10^{-3}S/cm\;at\;23^{\circ}C$ and electrochemical stability window to 4.8V. In the impedance spectra of the cells, which were constructed by lithium metals as electrodes, interfacial resistance increased due to growth of passivation layer during storage time and remarkable difference was not observed with content of $SiO_2$. In the impedance spectra of the lithium ion polymer batteries consisted of $LiClO_2$ and mesophase pitch-based carbon fiber(MCF), ohmic cell resistance of $SiO_2-free$ PGE was changed continuously with number of cycle, but those of $SiO_2-dispersed$ PGEs were not. Discharge capacity of the PGE containing $20wt\%\;SiO_2$ showed 132 mAh/g at 0.2C rate and $85\%$ of discharge capacity was retained at 2C rate.

• Journal of the Korean Electrochemical Society
• /
• v.2 no.2
• /
• pp.88-92
• /
• 1999

The apparent density. self-separation of the electrode composite from current collector in the electrolyte solution and specific resistance of electronic conduction of the electrode composite were examined by the variation of content of conductive material such as graphitic and black carbons in $LiCoO_2$ composite electrode for lithium ion battery. Increasing the content of conductive material, the apparent density of Lico02 composite electrode was decreased and that of $LiCoO_2$ in composite electrode was only rapidly decreased compared to that of composite. $LiCoO_2$ composite electrodes containing more than 4.1 weight percent of super s black as a conductive material were seU-separated by the immersion into 1 mol/I $LiPF_6$ in propylene carbonate and diethyl carbonate (1:1 volume ratio). Specific resistances related to the electronic conduction of composite electrode were decreased by the increasing the content i)f conductive material. Specific resistance of the composite electrode including $2\~3\%w/w$ of super s black as conductive material was similar to that of $12\%w/w$ of Lonza KS6. In the range of this study, super s black as conductive material is better than Lonza KS6 on battery capacity because of apparent density of $LiCoO_2$ in electrode composite including super s black is higher than that of Lonza KS6.