• Journal of Power System Engineering
• /
• v.4 no.2
• /
• pp.31-39
• /
• 2000

Relationships between the plating condition and the plating rate of the deposition film for the electroless plating of Co-Cu-P alloy were discussed in this report. The result obtained from this experiment were summarized as follow ; The optimum bath composition was consisted of 0.8 ppm thiourea as a stabilizing agent. Composition of the deposit was found to be uniform after two hours of electroless plating. Plating rates of nickel-catalytic surface and zincate-catalytic surface were found to be very closely equal, but the plating time of nickel-catalytic surface took longer than that of the zincated-catalytic surface.

• Journal of Power System Engineering
• /
• v.8 no.3
• /
• pp.36-43
• /
• 2004

The effect of bath composition, plating condition and plating rate on the magnetic property of electroless Co-Cu-P deposits were investigated. With increasing $CuCl_2$ concentration in the bath, plating rate increased, while the Br value of deposit decreased sharply. Deposited surface were inferiority by the increase pH above 10.5, bath temperature higher than $80^{\circ}C$. Plating reaction had been ceased by the increase of pH above 11, bath temperature higher than $90^{\circ}C$ and under $40^{\circ}C$. The Br value of deposit was uniform with various concentration of complexing agent(sodium citrate) in the bath. The Br value of deposit was almost equal to that found by the addition of stabilizer (thiourea) and accelerator(NaF). The Br value of deposit was uniform in plating time(20min) and heat treatment temperature(below $200^{\circ}C$), and were confirmed to have adequate bath stability for practical use.

• Resources Recycling
• /
• v.14 no.4 s.66
• /
• pp.34-40
• /
• 2005

Reusing of electroless Co-Cu-P waste solution was investigated in the respect of plating time, plating rate, solution composition and deposit. Plating time of cobalt-catalytic surface took longer than that of zincated-catalytic surface. It was possible to reuse the waste solution by mixing $50\%$ fresh solution at batch type. Plating time of initial solution at continuous type took longer 7.5 times over than that of batch type. Plating time of $50\%$ waste solution additive at continuous type took longer 2.5 times over than that of batch type. Component change of cobalt-topper for electroless deposition was greatly affected by deposit inferiority and rapid decrease in plating rate.

• Korean Journal of Materials Research
• /
• v.23 no.11
• /
• pp.661-665
• /
• 2013

We investigated the characteristics of electroless plated Cu films on screen printed Ag/Anodized Al substrate. Cu plating was attempted using neutral electroless plating processes to minimize damage of the anodized Al substrate; this method used sodium hypophosphite instead of formaldehyde as a reducing agent. The basic electroless solution consisted of $CuSO_4{\cdot}5H_2O$ as the main metal source, $NaH_2PO_2{\cdot}H_2O$ as the reducing agent, $C_6H_5Na_3O_7{\cdot}2H_2O$ and $NH_4Cl$ as the complex agents, and $NiSO_4{\cdot}6H_2O$ as the catalyser for the oxidation of the reducing agent, dissolved in deionized water. The pH of the Cu plating solutions was adjusted using $NH_4OH$. According to the variation of pH in the range of 6.5~8, the electroless plated Cu films were coated on screen printed Ag pattern/anodized Al/Al at $70^{\circ}C$. We investigated the surface morphology change of the Cu films using FE-SEM (Field Emission Scanning Electron Microscopy). The chemical composition of the Cu film was determined using XPS (X-ray Photoelectron Spectroscopy). The crystal structures of the Cu films were investigated using XRD (X-ray Diffraction). Using electroless plating at pH 7, the structures of the plated Cu-rich films were typical fcc-Cu; however, a slight Ni component was co-deposited. Finally, we found that the formation of Cu film plated selectively on PCB without any lithography is possible using a neutral electroless plating process.

• Journal of the Korean Ceramic Society
• /
• v.52 no.4
• /
• pp.264-268
• /
• 2015

Cu films were plated in an eco-friendly electroless bath (No-Formaldehyde) on Ni/screen printed Ag pattern/PET substrate. For electroless Cu plating, we used sodium-phosphinate ($NaH_2PO_2{\cdot}H_2O$) as reducing agent instead of Formaldehyde. All processes were carried out in electroless solution of pH 7 to minimize damage to the PET substrate. According to the increase of sodium-phosphinate, the deposition rate, the granule size, and rms roughness of the electroless Cu film increased and the Ni content also increased. The electroless Cu films plated using 0.280 M and 0.575 M solutions of sodium-phosphinate were made with Cu of 94 at.% and 82 at.%, respectively, with Ni and a small amount P. All electroless Cu plated films had typical FCC crystal structures, although the amount of co-deposited Ni changed according to the variation of the sodium-phosphinate contents. From these results, we concluded that a formation of higher purity Cu film without surface damage to the PET is possible by use of sodium-phosphinate at pH 7.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.1
• /
• pp.54-61
• /
• 2016

Screen printing of commercially available Ag paste is the most widely used method for the front side metallization of Si solar cells. However, the metallization using Ag paste is expensive and needs high temperature annealing for reliable contact. Among many metallization schemes, Ni/Cu/Sn plating is one of the most promising methods due to low contact resistance and mass production, resulting in high efficiency and low production cost. Ni layer serves as a barrier which would prevent copper atoms from diffusion into the silicon substrate. However, Ni based schemes by electroless deposition usually have low thermal stability, and require high annealing process due to phosphorus content in the Ni based films. These problems can be resolved by adding W element in Ni-based film. In this study, Ni-W-P alloys were formed by electroless plating and properties of it such as sheet resistance, resistivity, specific contact resistivity, crystallinity, and morphology were investigated before and after annealing process by means of transmission line method (TLM), 4-point probe, X-ray diffraction (XRD), and Scanning Electron Microscopy (SEM).

• Korean Chemical Engineering Research
• /
• v.45 no.6
• /
• pp.633-637
• /
• 2007

Electroless plating of Co-alloy thin films as capping layers for Cu interconnection has been investigated using alkali-free precursors such as $(NH_4)_2Co(SO_4)_2{\cdot}6H_2O$, $(NH_4)_2WO_4$, $(NH_4)H_2PO_4$, etc. The characteristics of the Co-alloy thin films were discussed by analyses of the effects of pH, Co-precursor concentration, and deposition temperature on the thickness and surface morphology of the films. The thickness of the Co-alloy thin films increased with increasing pH, Co-precursor concentration, and deposition temperature, similarly to the results of electroless plating of Co-alloy thin films using alkali-containing chemicals. The SEM images of the surface of the Co-alloy thin films showed that the proper ranges of pH and deposition temperature were 8.5~9.5 and $75{\sim}85^{\circ}C$, respectively. This work found a feasibility that Co-alloy thin films as capping layers for Cu interconnection could be electroless plated using alkali-free chemicals.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.132-132
• /
• 2013

본 연구는 R/F-PCB(Rigid/Flexible Printed circuit Board)의 Cu Pattern에 최종 표면처리 방법으로 사용되는 ENIG(Electroless Ni/Immersion Gold) 공정을 대체하여 ECIG(Electroless Co/Immersion Gold)공정을 적용하고자 하는 것으로 무전해 니켈 도금의 장점인 고경도, 내마모성, 납땜성, 내식성을 가지면서 니켈 도금의 취약점인 연성을 개선한 도금액을 개발하고자 하였다. 개발된 도금액을 이용하여 Cu Pattern에 도금할 경우 일반 무전해 니켈 도금에서 나타나는 불량 원인 중 하나인 Space 부분에 도금이 되는 현상이 현저히 감소하였으며, 연성 또한 향상됨을 관찰할 수 있었다.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.3
• /
• pp.27-33
• /
• 2008

With increasing use of portable appliances such as PDA and cellular phone, changing environment of applications requires higher solder joint reliability. The ENIG (Electroless Nickel Immersion Gold) process has been widely used for fine pitch SMT (Surface Mount Technology) and BGA (Ball Grid Array) packaged devices due to its benefits including excellent solderability, high uniformity and substantial legibility throughout the packaging process. Its brittle fracture of solder, however, has received increasingly attentions. It was Down that fracture brittleness is mainly related with black pad resulting from galvanic nickel corrosion and P-enriched layer formation between the IMC (Intermetallic Compounds) and electroless nickel layer. Theoretically, smooth electroless Ni layer was blown to have a advantages in minimizing the black pad phenomenon by uniform solution exchange during immersion gold plating. Nevertheless, how to control the surface morphology of electroless Ni layer has been hardly blown. This study investigates an effect of surface morphology of Cu underlayer on surface morphology of electroless Ni layer. To obtain various kinds of surface morphology of Cu layer, two types of Cu etching chemical and a number of Cu etching treatment were applied.

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.3
• /
• pp.63-71
• /
• 2022

In this study, the interfacial reaction and drop impact reliability of Sn-Ag-Cu (SAC) solder and electroless nickel autocatalytic gold (ENAG) were studied. In addition, the solder joint properties with the ENAG surface finish was compared with electroless nickel immersion gold (ENIG) and electroless nickel electroless palladium immersion gold (ENEPIG). The IMC thickness of SAC/ENAG and SAC/ENEPIG were 1.15 and 1.12 ㎛, respectively, which were similar each other. The IMC thickness of the SAC/ENIG was 2.99 ㎛, which was about two times higher than that of SAC/ENAG. Moreover, it was found that the IMC thickness of the solder joint was affected by the metal turnover (MTO) condition of the electroless Ni(P) plating solution, and it was found that the IMC thickness increased when the MTO increased from 0 to 3. The shear strength of SAC/ENEPIG was the highest, followed by SAC/ENAG and SAC/ENIG. It was found that when the MTO increased, the shear strength was lowered. In terms of brittle fracture, SAC/ENEPIG was the lowest among the three joints, followed by SAC/ENAG and SAC/ENIG. Likewise, it was found that as MTO increased, brittle fracture increased. In the drop impact test, it was confirmed that the 0 MTO condition had a higher average number of failures than the 3 MTO condition, and the average number of failures was also higher in the order of SAC/ENEIG, SAC/ENAG, and SAC/ENIG. As a result of observing the fracture surface after the drop impact, it was found that the fracture was between the IMC and the Ni(P) layer.