• Korean Journal of Materials Research
• /
• v.9 no.6
• /
• pp.577-582
• /
• 1999

In order to make the electroconductive $Si_3N_4$-TiN composities, the Si-Ti(N) compacts were nitrided at $1450^{\circ}C$ for 20hours, and then they were post-sintered by a gas-pressure-sintering technique at 1TEX>$1950^{\circ}C$ for 3.5 hours. As starting powders, commercial si powder of about $10\mu\textrm{m}$, two types of Ti powders of 100 and 325 mesh, and fine-sized TiN of $2.5\mu\textrm{m}$ powders were used. In the $Si_3N_4$-TiN sintered bodies used Ti powders, the relative density and fracture strength and electrical conductivity are low due to the existence of large amounts of coarse pores. However, in the $Si_3N_4$-TiN composite used TiN powder, the fracture toughness, fracture strength and electrical resistivity were $5.0MPa{\cdot}m^{1/2}$, 624MPa and $1400{\omega}cm$, respectively. The dispersion of TiN particles in the composite inhibited the growth of $Si_3N_4$ in the shape of rod and made strong strain field contrasts at the $Si_3N_4$-TiNinterfaces. It was recognized that microstructural control is required to improve the electrical conductivity and mechanical properties of $Si_3N_4$-TiN composites by dispersing TiN particles homogeneously.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.381-384
• /
• 2001

The $\beta$-SiC+ZrB$_2$ and $\beta$-SiC+TiB$_2$ceramic electroconductive composites were pressureless-sintered and annealed by adding l2wt% A1$_2$ $O_3$+Y$_2$ $O_3$(6 : 4wt%) powder as a function of sintering temperature. The relative density showed highest value of 84.92% of the theoretical density for SiC-TiB$_2$ at 190$0^{\circ}C$ sintering temperature. The phase analysis of the composites by XRD revealed of $\alpha$-SiC(6H), TiB$_2$, $Al_{5}$Y$_2$ $O_{12}$ and $\beta$-SiC(15R). Flexural strength showed the highest of 230 MPa for SiC-ZrB$_2$ composites sintered at 190$0^{\circ}C$. The vicker's hardness increased with increasing sintering temperature and showed the highest for SiC-ZrB$_2$ composites sintered at 190$0^{\circ}C$. Owing to YAG, the fracture toughness showed the highest of 6.50 MPa . m$^{1}$2/ for SiC-ZrB$_2$ composites at 190$0^{\circ}C$. The electrical resistivity was measured by the Rauw method from $25^{\circ}C$ to $700^{\circ}C$. The electrical resistivity of the composites showed the PTCR(Positive Temperature Coefficient Resistivity).).

• Proceedings of the KIEE Conference
• /
• 1998.11c
• /
• pp.853-855
• /
• 1998

The electrical resistivity and mechanical properties of the hot-pressed and annealed ${\beta}$-SiC+39vol.%$ZrB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of $Al_{2}O_{3}+Y_{2}O_{3}$(6:4wt%). In this microstructures. no reactions were observed between $\beta$-SiC and $ZrB_2$, and the relative density is over 97.6% of the theoretical density. Phase analysis of composites by XRD revealed mostly of a $\alpha$-SiC(6H, 4H), $ZrB_2$ and weakly $\beta$-SiC(15R) phase. The fracture toughness decreased with increased $Al_{2}O_{3}+Y_{2}O_{3}$ contents and showed the highest for composite added with 4wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives. The electrical resistivity increased with increased $Al_{2}O_{3}+Y_{2}O_{3}$ contents because of the increasing tendency of pore formation according to amount of liquid forming additives $Al_{2}O_{3}+Y_{2}O_{3}$. The electrical resistivity of composites is all positive temperature coefficient resistance(PTCR) against temperature up to $700^{\circ}C$.

• Proceedings of the KIEE Conference
• /
• 2001.07c
• /
• pp.1436-1438
• /
• 2001

The $\beta$-SiC + $ZrB_2$ ceramic electroconductive composites were pressureless-sintered and annealed by adding 12wt% $Al_2O_3$ + $Y_2O_3$ (6 : 4wt%) powder as a function of sintering temperature. The relative density showed the highest value of 81.1% at 1900$^{\circ}C$ sintering temperature. The phase analysis of the composites by XRD revealed of $\alpha$-SiC(6H), $TiB_2$, $Al_5Y_2O_{12}$ and $\beta$-SiC(15R). Flexural strength showed the highest value of 230 MPa for composites sintered at 1900$^{\circ}C$. The vicker's hardness and the fracture toughness showed the highest value of increased with increasing sintering temperature and showed the highest of 9.88 GPa and 6.05 $MPa{\cdot}m^{1/2}$ at 1900$^{\circ}C$. The electrical resistivity was measured by the Pauw method from 25$^{\circ}C$ to 700$^{\circ}C$. The electrical resistivity of the composites showed the PTCR (Positive Temperature Coefficient Resistivity).

• Proceedings of the KIEE Conference
• /
• 1997.11a
• /
• pp.311-313
• /
• 1997

The effects of porosity on the pressureless sintered $\beta$-SiC-$ZrB_2$ composites with $Al_2O_3$ additions(4, 8, 12wt.%) under argon atmosphere were investigated. Relative density of $\beta$-SiC-$ZrB_2$ composites were decreased with the $Al_2O_3$ content. The relative density and fracture toughness of $\beta$-SiC-$ZrB_2$ with 4wt% $Al_2O_3$ are 93.2%, $1.323MPa{\cdot}m^{1/2}$ respectively. The Vicker's hardness and flexural strength of $\beta$-SiC-$ZrB_2$ with 12wt.% $Al_2O_3$ are 0.492GPa, 261MPa respectively. Fracture toughness of $\beta$-SiC-$ZrB_2$ composites are directly proportional to relative density.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.5
• /
• pp.242-242
• /
• 2004

The composites were fabricated 61 vol.%α-α-SiC and 39vol.% WC powders with the liquid forming additives of 12wt% Al₂O₃＋Y₂O₃ by pressureless annealing at 1700, 1800, 1900℃ for 4 hours. The result of phase analysis of composites by XRD revealed α-SiC(2H), WC, and YAG($Al_5Y_3O_{12}$) crystal phase. The relative density, the flexural strength, fracture toughness and Young′s modulus showed respectively the highest value of 99.4%, 375.76㎫, 5.79㎫ㆍ$m^{\frac{1}{2}}$, and 106.43㎬ for composite by pressureless annealing temperature 1900℃ at room temperature. The electrical resistivity showed the lowest value of 1.47×$10^{-3}$/Ω·㎝ for composite by pressureless annealing temperature 1900℃ at 25℃. The electrical resistivity of the α-SiC-WC composites was all positive temperature cofficient resistance (PTCR) in the temperature ranges from 25℃ to 500℃.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.5
• /
• pp.241-247
• /
• 2004

The composites were fabricated 61 vol.%$\alpha$-$\alpha$-SiC and 39vol.% WC powders with the liquid forming additives of 12wt% $Al_2$O$_3$＋Y$_2$O$_3$ by pressureless annealing at 1700, 1800, 190$0^{\circ}C$ for 4 hours. The result of phase analysis of composites by XRD revealed $\alpha$-SiC(2H), WC, and YAG(Al$_{5}$ Y$_3$O$_{12}$ ) crystal phase. The relative density, the flexural strength, fracture toughness and Young's modulus showed respectively the highest value of 99.4%, 375.76㎫, 5.79㎫ㆍm$\frac{1}{2}$, and 106.43㎬ for composite by pressureless annealing temperature 190$0^{\circ}C$ at room temperature. The electrical resistivity showed the lowest value of 1.47${\times}$10$^{-3}$ $\Omega$$.$cm for composite by pressureless annealing temperature 190$0^{\circ}C$ at $25^{\circ}C$. The electrical resistivity of the $\alpha$-SiC-WC composites was all positive temperature cofficient resistance (PTCR) in the temperature ranges from $25^{\circ}C$ to 50$0^{\circ}C$.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.50 no.5
• /
• pp.221-225
• /
• 2001

The effect of $Al_2O_3+Y_2O_3$ additives on fracture toughness of ${\beta}-SiC-TiB_2$ composites by hot-pressed sintering was investigated. The ${\beta}-SiC-TiB_2$ ceramic composites were hot-press sintered and pressureless-annealed by adding 16, 20, 24 wt% ${\beta}-SiC-TiB_2$(6:4 wt%) powder as a liquid forming additives at low temperature(1800 $^{\circ}C$) for 4 h. Phase analysis of composites by XRD revealed mostly of ${\alpha}$-SiC(6H), $TiB_2$, and YAG($Al_5Y_3O_{12}$). The relative density was over 95-88 % of the theoretical density, and the porosity increased with increasing $Al_2O_3+Y_2O_3$ contents because of the increasing tendency of pore formation. The fracture toughness showed the highest value of 5.88 MPa${\cdot}m^{1/2}$ for composites added with 20 wt% $Al_2O_3+Y_2O_3$ additives at room temperature. The electrical resistivity showed the lowest value of $5.22{\times}10^{-4}\;{\Omega}\;{\cdot}\;cm$ for composite added with 20 wt% $Al_2O_3+Y_2O_3$ additives at room temperature, and was all positive temperature coefficeint resistance(PTCR) against temperature up to 900 $^{\circ}C$.

• Proceedings of the KIEE Conference
• /
• 2007.11a
• /
• pp.124-125
• /
• 2007

The composites were fabricated $\beta$-SiC and $TiB_2$ powders with the liquid forming additives of 8, 12, 16[wt%] $Al_2O_3+Y_2O_3$ as a sintering aid by pressureless annealing at $1,650[^{\circ}C]$ for 4 hours. Reactions between SiC and transition metal $TiB_2$ were not observed in the microstructure and the phase analysis of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. The relative density, the flexural strength, the Young's modulus and the Vicker's hardness showed the highest value of 82.29[%], 189.5[MPa], 54.60 [GPa] and 2.84[GPa] for SiC-$TiB_2$ composites added with 16[wt%] $Al_2O_3+Y_2O_3$ additives at room temperature. The relative density of SiC-$TiB_2$ composites was lowered due to gaseous products of the result of reaction between SiC and $Al_2O_3+Y_2O_3$. The electrical resistivity showed the lowest value of 0.012[${\Omega}{\cdot}cm$] for 16[wt%] at 25[$^{\circ}C$]. The electrical resistivity was all negative temperature coefficient resistance (NTCR) in the temperature ranges from 25[$^{\circ}C$] to 700[$^{\circ}C$].

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.2
• /
• pp.92-97
• /
• 1999

The mechanical and electrical properties of the hot-pressed and annealed $\beta-Sic$+39vol.%$ZrB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of $Al_2O_3+Y_2O_3(6:4wt%)$. In this microstructures, no reactions and elongated $\alpha$-SiC grains with equiaxed $ZrB_2$, gains were observed between $\beta-SiC$ and $ZrB_2$, and the relative density was over 97.6% of the theoretical density. Phase analysis of the composites by XRD revealedmostly of $\alpha$-SiC(6H, 4H), $ZrB_2$, and weakly $\beta-SiC$(15R) phase. The fracture toughness decreased with increasing $Al_2O_3+Y_2O_3$ contents and showed the highest of $6.37MPa.m^{\fraction ane-half}$ for composite added with 4wt% $Al_2O_3+Y_2O_3$ additives at room temperature. The electrical resistivity increased with increasing $Al_2O_3+Y_2O_3$contents and showed the lowest of $1.51\times10^{-4}\Omega.cm$ for composite added with $Al_2O_3+Y_2O_3$ additives at $25^{\circ}C$. This reason is the increasing tendency of pore formation according to amount of liquid forming additives $Al_2O_3+Y_2O_3$. The electrical resistivity of the composites was all positive temperature coefficient resistance(PTCR) against temperature up to $700^{\circ}C$.