• 센서학회지
• /
• 제23권4호
• /
• pp.224-228
• /
• 2014

The electrocaloric effect of 9/65/35 PLZT thin film fabricated by the sol-gel method, which has not been studied yet, was investigated for its structural, electrical properties as well as temperature change property. The relaxor ferroelectric property of 9/65/35 PLZT thin film was confirmed by examining its dielectric and electrical properties. The relaxor property can cause a more pronounced electrocaloric effect (ECE) in a wider temperature range than normal ferroelectric film. To avoid errors caused by using an indirect measurement method, the leakage current generated by increasing temperatures was minimized by using the optimal maximum electric field ($350kVcm^{-1}$) in the thin film. The largest temperature change ${\delta}T$ (0.23 K) and the electrocaloric strength ${\xi}$ (0.68 mkcm/kV), calculated by equations were obtained. The maximum field change ${\delta}E$ ($191kVcm^{-1}$) was in the vicinity of the curie temperature ($200^{\circ}C$).

• 한국전기전자재료학회논문지
• /
• 제28권6호
• /
• pp.375-378
• /
• 2015

In this study, in order to develop the composition ceramics with the excellent electrocaloric properties, $(Pb_{0.88}La_{0.08})(Zr_{0.65}Ti_{0.35})O_3$ ceramics were fabricated by the conventional solid-state method. Electrocaloric effects of $(Pb_{0.88}La_{0.08})(Zr_{0.65}Ti_{0.35})O_3$ ferroelectric ceramics were investigated and discussed using the characteristics of P-E hysteresis loops at wide temperature range from room temperature to $220^{\circ}C$. The temperature change ${\Delta}T$ due to the electrocaloric effect was calculated by Maxwell's relations, and reached the maximum of ~0.19 at $190^{\circ}C$ under applied electric field of 30 kV/cm.

• 한국전기전자재료학회논문지
• /
• 제30권4호
• /
• pp.223-228
• /
• 2017

In this study, in order to develop composition ceramics for refrigeration device application at a temperature of less than $90^{\circ}C$, a $Ba(Ti_{1-x}Zr_x)O_3$ composition was fabricated using a conventional solid-state method. Electrocaloric properties of these ceramics were investigated using the characteristics of P-E hysteresis loops in a wide temperature range from room temperature to $150^{\circ}C$. The Curie temperature of $Ba(Ti_{1-x}Zr_x)O_3$ ceramics decreased with the increase of x. The maximum value of ${\Delta}T=0.07^{\circ}C$ in an ambient temperature of $85^{\circ}C$ under 30 kV/cm appeared when x = 0.125. It was concluded that the composition (x = 0.125) ceramics can be used for refrigeration device applications.

• 한국전기전자재료학회논문지
• /
• 제28권10호
• /
• pp.615-619
• /
• 2015

In this study, in order to develop the composition ceramics with the excellent electrocaloric properties, 8/65/35 PLZT ceramics were fabricated by the conventional solid-state method with the addition of $Bi_2O_3$, CuO, $Li_2CO_3$ and the variation of sintering temperature from $930^{\circ}C$ to $990^{\circ}C$. The XRD pattern of all specimens indicated general perovskite structure and the rhombohedral phase were observed. Curie temperature ($T_c$) of all specimens was observed in the vicinity of about $190^{\circ}C$. Density, coercive field and remnant polarization of the specimen sintered at $950^{\circ}C$ was $7.55g/cm^3$, 8.895 kV/cm, $11.22{\mu}C/cm^2$, respectively. EC effect of PLZT ceramics was measured by indirect method and the temperature change ${\Delta}T$ due to the electrocaloric effect was calculated by Maxwell's relations. ${\Delta}T$ of ceramic sintered at $950^{\circ}C$ was $0.21^{\circ}C$ under application of 40 kV/cm at $190^{\circ}C$.

• 한국전기전자재료학회논문지
• /
• 제29권3호
• /
• pp.164-167
• /
• 2016

In this study, in order to develop relaxor ferroelectric ceramics for refrigeration device application with large electrocaloric effect, PLZT(8/65/35) composition was fabricated using conventional solid-state method. The Curi temperature of this composition PLZT ceramics was $230^{\circ}C$, and the P-E hysteresis loops of the PLZT ceramics as a fuction of temperature became slim by degrees with higher temperatures. The maximum value of ${\Delta}T$ of $0.243^{\circ}C$ in ambient temperature of $215^{\circ}C$ with 30 kV/cm was appeared. It is considered that PLZT ceramics possess the possibility of refrigeration device application.

• Journal of Ceramic Processing Research
• /
• 제21권6호
• /
• pp.725-730
• /
• 2020

This study investigated the structural and electrical properties of thin K(Ta_0.6Nb_0.4)O₃ films for their applicability to electrocaloric devices. Both of the sol-gel and spin coating methods were used to fabricate thin films. Those sintered at 650 ℃ showed a KTN phase with pyrochlore of K₂Ta₂O₆, but those sintered at 750 ℃ showed pure polycrystalline phase without a pyrochlore phase. The lattice constants observed were a= 3.990nm. The dielectric constant rapidly decreased due to decrease in polarization of space charge approximately at an applied frequency of 10 kHz. The dielectric constant and loss at 30 ℃ of the thin films sintered at 750 ℃ were 3,617 and 0.264. The dielectric constant of the specimen sintered at 750 ℃ decreased to about -8.27 %/V according to the applied DC field. The remanent polarization and coercive field at 36 ℃ of the specimen sintered at 750 ℃ were 20.0 µC/cm² and 122.6 kV/cm. When the electric field of 247 kV/cm was applied to the specimen sintered at 750 ℃, the highest electrocaloric property of 3.02 ℃ was obtained.

• Journal of Ceramic Processing Research
• /
• 제22권2호
• /
• pp.214-220
• /
• 2021

Heterolayered potassium tantalate niobate(KTN(70/30)/KTN(30/70)) thin films on Pt/Ti/SiO2/Si substrates prepared by the sol-gel process and spin coating method. When sintered at 700 ℃ or higher, the X-ray diffraction intensities of the perovskite phase were greatly increased, and it was observed as the main phase of the KTN heterolayered thin film. As the sintering temperature increased from 650 ℃ to 800 ℃, the average grain size increased from 146nm to 380 nm, and the average thickness of the KTN films coated six times was about 394-441 nm. Dielectric constant and dielectric loss of the KTN film sintered at 750 ℃ and room temperature showed good properties of about 2850 and 0.573, respectively, and all films exhibited the typical dielectric relaxation characteristics. The phase transition temperature of KTN thin film was around 12-13 ℃. Remanent polarization and the coercive field of KTN film sintered at 750 ℃ showed excellent properties of 23.98 μC/cm2 and 35.41 kV/cm, respectively. Adiabatic temperature changes (ΔT) and electrocaloric strength of the KTN films sintered at 750 ℃ at 60 ℃ were 2.67℃ and 0.012 KcmkV-1, respectively.

• 한국전기전자재료학회논문지
• /
• 제33권6호
• /
• pp.465-470
• /
• 2020

Heterolayered K(Ta,Nb)O₃/Pb(Zr,Ti)O₃ thin films on Pt/Ti/SiO₂/Si substrates were prepared by a sol-gel process and spin-coating method. The structural and electrical properties were measured to investigate the possibility of application as an electrocaloric effect device. All specimens exhibited dense and uniform cross-sectional structures without pores, and the average thickness of the specimen coated six times was approximately 394 nm. Curie temperatures were observed at 5℃ or less in type-I and 10℃ in type-II specimens, respectively. Type-II specimens coated 6 times showed a relative dielectric constant of 758 and remanent polarization of 9.71 μC/㎠ at room temperature. The maximum electrocaloric effect occurred between 20 and 25℃, slightly higher than their Curie temperature, and the electrocaloric property (ΔT) of the type-II specimens coated 6 times was approximately 1.2℃ at room temperature.

• 한국전기전자재료학회논문지
• /
• 제26권11호
• /
• pp.801-805
• /
• 2013

In this study, electrocaloric effects of Pb-free $(Ba_{0.85}Ca_{0.15})(Ti_{0.92}Zr_{0.08})O_3$ ferroelectric ceramics were investigated and discussed using the characteristics of P-E hysteresis loops at wide temperature range from room temperature to $140^{\circ}C$. The remnant polarization $P_r$ and coercive field $E_c$ were decreased with increasing temperature. The temperature change ${\Delta}T$ by the electrcaloric effect was calculated by Maxwell's relations, and reached the maximum of ~0.15 at $120^{\circ}C$ under applied electric field of 30 kV/cm.

• Journal of Ceramic Processing Research
• /
• 제20권6호
• /
• pp.603-608
• /
• 2019

In this study, the multilayered thin films of (Ba,Sr)TiO3/K(Ta,Nb)O3 were fabricated by the sol-gel and spin coating methods, and their structural and electrical properties were investigated. The specimen showed polycrystalline X-ray diffraction (XRD) characteristics with a tetragonal structure. The average grain size and film thickness for one coating were about 30~40nm and 60nm, respectively. The phase transition temperature of specimen was lower than 10 ℃. The dielectric constant and loss at 20 ℃ of the specimen coated six times were 1,231 and 0.69, respectively. The rate of change in dielectric constant at an applied direct current (DC) voltage of the six times coated thin films was 17.3%/V. The electrocaloric effect was the highest around the temperature at which the remanent polarization rapidly changed. When an electric field of 660kV/cm was applied to the triply coated thin films, the highest electrocaloric property of 4.41 ℃ was observed.