• Polymer(Korea)
• /
• v.35 no.3
• /
• pp.244-248
• /
• 2011

Poly(2,6-dimethyl-1,4-phenylene ether) (PPE) was synthesized by oxidative polymerization using various Cu(I)-amine catalyst system. The effects of catalyst/monomer ratio, different amine ligand, and the content of 2,4,6-trimethylphenol (TMP) additive on the polymer yield and molecular weight were investigated by using gel permeation chromatography. The catalytic activity of various Cu-amine systems on the 2,S-dimethylphenol (DMP) polymerization was monitored and compared each other through oxygen-uptake experiment. In addition, the effect of catalyst removal using aqueous EDTA on the thermal stability of the prepared polymer was elucidated by thermogravimetric analysis.

• Nuclear Engineering and Technology
• /
• v.55 no.6
• /
• pp.2256-2262
• /
• 2023

The electrochemical corrosion behaviors of SA106 Grade B (SA106B) carbon steel in H₂SO₄4-N₂H₄ and H₂SO₄-N₂H₄-CuSO₄ solutions at 95 ℃ have been investigated with the addition of commercial corrosion inhibitors (CI#30 and No. 570S), to determine the stability of SA106B in the hydrazine-based reductive metal ion decontamination (HyBRID) process. The potentiodynamic polarization experiment revealed that the corrosion inhibitors were capable of lowering the corrosion rate of SA106B in H₂SO₄-N₂H₄ solution. It was found that the corrosion inhibitors induced formation of fixed surface layer on the carbon steel upon the corrosion. This corrosion inhibition performance was reduced in the presence of CuSO₄ in the solution owing to the chemical reactions between organic compounds in the corrosion inhibitors and CuSO₄. CI#30 showed a better corrosion inhibition effect in the H₂SO₄-N₂H₄-CuSO₄ solution. Although the corrosion inhibitors can provide better stability to SA106B in the HyBRID solution, their application should be carefully considered because it may result in reduced decontamination performance and increased secondary waste generation.

• Korean Journal of Materials Research
• /
• v.8 no.5
• /
• pp.394-398
• /
• 1998

We have studied the effect of Ag additions on the microstructure and the related mechanical and supercon¬ducting properties of $ YBa_{2}$$Cu_{3}$$O_{7-\delta}$ (YBCO) superconductors. A 5-15 vol.% of Ag was added to YBCO in the forms of Ag and $AgNO_{3}$, powder and the resultant microstructural evolution was evaluated. It was observed that the strength and fracture toughness of YBCO increased with increasing Ag content. These improvements in strength and fracture toughness are believed to be due to the strengthening mechanisms caused by the presence of Ag. In addition, YBCO-Ag composite superconductors showed higher values of strength and fracture toughness when Ag was added in the form of AgNO, than those of which was added Ag. The higher mechanical properties of YBCO- Ag resulting from $AgNO_{3}$, addition are probably due to the microstructure of more finely and uniformly distributed Ag particles. The addition of Ag also showed slightly improved critical current density of YBCO superconductors.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.2
• /
• pp.70-76
• /
• 2014

$Zn_2TiO_4$, using an anatase form of $TiO_2$ on zinc crystalline glaze, was shown as effective nuclear agent. Thus the effects on glaze were studied with synthesized $Zn_2TiO_4$ at low temperature. First, the chromophore elements were employed in synthesized $Zn_2TiO_4$ then add them in the zinc crystalline glaze. Crystal creation and development of color by $Zn_2TiO_4$ addition on the zinc crystalline glaze were more effective. Addition of $Zn_2TiO_4$, which is developed in low range temperature, is effected as zinc crystalline nuclear in the willemite glaze. When 5 wt% of synthesized $Zn_2TiO_4$ was added to the willemite glaze, nuclear creation increases and steadily retains. Therefore addition of respectively doped $Zn_2TiO_4$ with CoO, NiO, and CuO would increase doped effects in the glaze, various color willemite crystal were obtained.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.232-235
• /
• 1999

In this paper, We described the effect of $MoO_3$ Addition and firing temperature on the microwave dielectric properties of $BiNb0_4$ ceramics. The specimens prepared by conventional mixed method was addicted by 0 - 0.03 wt% $MoO_3$ and fired at 860 - $950^{\circ}$ for 3hr. Density increased when $MoO_3$ is below O.Olwt% but decreased when over O.Olwt%. $BiNb0_4$ ceramics addicted with CuO 0.03wt % and $MoO_3$ 0.01 wt% showed microwave dielectric properties, Dielectric constant 37.5, Quality factor[Qx$f_0$]5500, Temperature coefficient of resonance frequency 15ppm/$^{\circ}$

• Corrosion Science and Technology
• /
• v.13 no.1
• /
• pp.28-35
• /
• 2014

Recently, the fuel oil of diesel engines of marine ships has been increasingly changed to heavy oil of low quality as the oil price is getting higher and higher. Therefore, the spiral gear attached at the motor of the oil purifier which plays an important role to purify the heavy oil is also easy to expose at severe environmental condition due to the purification of the heavy oil in higher temperature. Thus, the material of the spiral gear requires a better mechanical strength, wear and corrosion resistance. In this study, the heat treatment(tempering) with various holding time at temperature of $500^{\circ}C$ was carried out to the alloy of Cu-7Al-2.5Si as centrifugal casting, and the properties of both hardness and corrosion resistance with and without heat treatment were investigated with observation of the microstructure and with electrochemical methods, such as measurement of corrosion potential, cathodic and anodic polarization curves, cyclic voltammogram, and a.c. impedance. in natural seawater solution. The ${\alpha}$, ${\beta}^{\prime}$ and ${\gamma}_2$ phases were observed in the material in spite of no heat treatment due to quenching effect of a spin mold. However, their phases, that is, ${\beta}^{\prime}$ and ${\gamma}_2$ phases decreased gradually with increasing the holding time at a constant temperature of $500^{\circ}C$. The hardness more or less decreased with heat treatment, however its corrosion resistance was improved with the heat treatment. Furthermore, the longer holding time, the better corrosion resistance. In addition, when the holding time was 48hrs, its corrosion current density showed the lowest value. The pattern of corroded surface was nearly similar to that of the pitting corrosion, and this morphology was greatly observed in the case of no heat treatment. It is considered that ${\gamma}_2$ phase at the grain boundary was corroded preferentially as an anode. However, the pattern of general corrosion exhibited increasingly due to decreasing the ${\gamma}_2$ phase with heat treatment. Consequently, it is suggested that the corrosion resistance of Cu-7Al-2.5Si alloy can be improved with the heat treatment as a holding time for 48 hrs at $500^{\circ}C$.

• Journal of Korea Foundry Society
• /
• v.28 no.6
• /
• pp.273-281
• /
• 2008

Effects of alloying elements on the mechanical properties of hardened and austempered 3.60wt%C - 2.50wt%C ductile cast iron were investigated. Strength and hardness were increased and ductility was decreased as the amount of alloying element increased. The increasing effect of copper addition on the strength was the most pronounced. The strength and hardness were greatly increased and ductility was decreased by hardening. The effect of alloying element on the mechanical properties of the hardened ductile cast iron was not so pronounced due to the high contents of C and Si. The strength and hardness of austempered ductile cast iron were greatly increased, meanwhile the difference of strength from that of hardened one was not so big. The ductility of the former was higher than that of the latter. The strength and ductility of austempered ductile cast iron with 0.25%Mn were the maximum of all Mn added ones. The maximum strength of that was obtained with the addition of 0.80wt%Cu or 2.00wt%Ni along with this amount of Mn added.

• Journal of Microbiology and Biotechnology
• /
• v.6 no.2
• /
• pp.103-109
• /
• 1996

Mn(II)+succinate decreased the carotenoid formation of the yeast Phaffia rhodozyma, probably by scavenging $O_2$. When duroquinone (DQ), an internal and external $O_2$ generator, was added to medium, P. rhodozyma produced more amount of carotenoids. The increased carotenoid production was destroyed by oxygen radical (OR) scavengers, ascorbate+Cu(II) and dimethylsulfoxide. When sub-lethal concentrations of $H_2O_2$ , an external OR source, and antimycin, an internal OR inducer, were used, the effect of $H_2O_2$ on carotenoid formation and composition was less significant than that of antimycin. Addition of superoxide dismutase, an external OR remover, rescued cells from death caused by the high concentration of DO. In this condition, the yeast culture showed an increase in carotenoid content. Addition of DQ into P. rhodozyma culture in the stationary phase did not increase carotenoid production. Therefore, carotenoid formation was stimulated by internal ORs in the growing yeast. It was probably due to release of catabolite repression on carotenogenesis in the yeast. Aeration was important for carotenoid production but was not as effective as the internal OR producer, DQ.

• Textile Coloration and Finishing
• /
• v.13 no.5
• /
• pp.10-10
• /
• 2001

The Purpose of this study was to investigate spectrophotometric characteristics of Korean knotweed extracts. The properties were evaluated by it′s extracting solvent, effect of metallic ion, variations of pH values and effect of light exposure. The results were as following; The highest absorbance was found in methanol extract of Korean knotweed, while the lowest absorbance was carbon tetrachloride extract. The UV-vis. spectra of Korean knotweed colors in several solvents showed hypsochromic shift of n-π/sup ＊/ transition with the polarity of solvent. Absorbance and peak of UV-vis. spectra of Korean knotweed colors became lower and broader by addition of metallic ion. The light stability in irradiation with xenon ]amp of the color solution with Cu were higher than those of Al and Fe. The UV-vis. spectra of Korean knotweed extracts in various pH values showed bathochromic shift under alkaline condition, and their peaks disappeared after 5 hours exposure.

• Textile Coloration and Finishing
• /
• v.13 no.5
• /
• pp.298-305
• /
• 2001

The Purpose of this study was to investigate spectrophotometric characteristics of Korean knotweed extracts. The properties were evaluated by it's extracting solvent, effect of metallic ion, variations of pH values and effect of light exposure. The results were as following; The highest absorbance was found in methanol extract of Korean knotweed, while the lowest absorbance was carbon tetrachloride extract. The UV-vis. spectra of Korean knotweed colors in several solvents showed hypsochromic shift of $n->\pi^*$ transition with the polarity of solvent. Absorbance and peak of UV-vis. spectra of Korean knotweed colors became lower and broader by addition of metallic ion. The light stability in irradiation with xenon ]amp of the color solution with Cu were higher than those of Al and Fe. The UV-vis. spectra of Korean knotweed extracts in various pH values showed bathochromic shift under alkaline condition, and their Peaks disappeared after 5 hours exposure.