• 한국세라믹학회지
• /
• 제52권6호
• /
• pp.473-478
• /
• 2015

Green bodies of earthenware tile were prepared from a mixture of earthenware tile powder and SiC as forming agents by applying a conventional process. Granule powder for tile samples was prepared using the spray drying method with commercial earthenware raw material with a quantity of SiC of 0.3 wt%. The applied pressure was $250kg{\cdot}f/m^2$ and the firing temperature was $1050-1200^{\circ}C$. The effects of the SiC particle size and sintering temperature on the open porosity and total porosity were investigated and the correlative mechanism was also discussed. While total porosity was not significantly changed by decreasing the SiC particle size, the open porosity showed a gradual decrease, which represents an increase of the closed porosity. As the sintering temperature increased, coarsening was made among the pores due to excessive oxidation. The volume shrinkage and bending strength were demonstrated for the sintered tile samples. The sintered bulk density was also measured to determine the weight reduction value.

• 한국세라믹학회지
• /
• 제54권2호
• /
• pp.114-120
• /
• 2017

In underdeveloped countries, many people suffer from water shortage due to the absence of water supply service. Although water purifiers have provided support in such situations, it is not easy to maintain water filters without a continuous supply of consumable filters. To obtain a sustainable drinking water source, appropriate technology of water treatment is necessary. Herein, a low cost water purification system was developed using natural raw materials. A non-electric water treatment system was developed using filtration through an Onggi filter, which is a type of Korean traditional earthenware with a microporous surface. The porosity and flux of the prepared Onggi filter were 29.06% and 31.63 LMH, respectively. After purification of water with total dissolved solids of 10.4 mg/L and turbidity of 100 NTU, the total dissolved solids and turbidity of the water treated using the Onggi filter decreased by 12% and 99.8%, respectively.

• 보존과학회지
• /
• 제37권5호
• /
• pp.545-556
• /
• 2021

본 연구에서는 정선 아우라지 유적에서 출토된 신석기시대 및 청동기시대 토기 총 11점을 대상으로 재료학적 특성을 연구하였다. 불석결과, 청동기시대 조기 토기의 염기성 및 산성 성분은 신석기시대 토기와 청동기시대 전기 토기의 중간 영역에서 분포하였지만, 각 제작시기에 따른 큰 차이는 확인되지 않았다. 이미 연구되었던 강원지역 출토 토기와 비교해본 결과, 정선 아우라지 출토 토기는 영동지역 출토 토기보다 산성 성분이 적은 경향성을 보였으며, 염기성 성분은 출토유적에 따라 차이가 있었다. 희토류 원소 분포 패턴에서는 분석대상 토기 모두 유사한 패턴 결과를 나타내어 태토원료의 모암이 동일기원임을 확인하였으며, 기 연구되었던 타 유적 토기 태토와의 비교를 통하여 정선 아우라지 출토 토기 태토의 특성을 확인하였다. 미세구조 불석결과 분석대상 토기는 대체로 점토입자 및 공극의 분포가 불규칙하며, 기질이 느슨하여 치밀한 소성이 이루어지지 못했다. 신석기시대 토기에서는 부정형 공극이 많이 확인되었으며, 점토기질과 함께 장석을 포함한 알루미노 규산염의 배열이 관찰된 반면, 청동기시대 전기 토기의 공극은 미정질 입자와 입방체 결정 등으로 채워진 부분이 다수 확인되었다. 정선 아우라지 출토 토기 태토의 주된 광물상은 제작시기와는 별개로 각 토기의 특성에 따른 광물 조성이 검출되기도 했지만, 전체적으로 유사한 조성을 나타내었다. 따라서 토기의 소성온도에는 큰 차이가 없었던 것으로 확인되며, 약 750~850℃ 범위에서 저온소성된 것으로 추정된다.