• Journal of the Korean Ceramic Society
• /
• v.45 no.11
• /
• pp.707-712
• /
• 2008

Plasma resistant nanocrystalline $Y_2O_3$ films were deposited on alumina substrates through the electron-beam PVD technique. Increasing substrate temperature to $600^{\circ}C$ resulted in the textured microstructures with significantly enhanced adhesion force of the coating to the substrate. During the exposure to fluorine plasma, erosion rate of the coated specimen was higher than that of a sintered yttria specimen, but significantly lower than that of a single crystalline alumina. Considering the adhesion and erosion behaviors observed in the coated specimen prepared at $600^{\circ}C$, the deposition technique appears effective in reducing contamination particles generated from the ceramic parts in the plasma environment.

• Proceedings of the Korea Society for Energy Engineering kosee Conference
• /
• 2006.05a
• /
• pp.350-356
• /
• 2006

• Journal of the Korean institute of surface engineering
• /
• v.46 no.6
• /
• pp.258-263
• /
• 2013

4 mol% Yttria-stabilized zirconia (4YSZ) coatings are fabricated by Air Plasma Spray (APS) and Electron Beam Physical Vapor Deposition (EB-PVD) with top coating of thermal barrier coating (TBC). NiCrAlY based bond coat is prepared as 150 ${\mu}m$ thickness by conventional APS (Air Plasma Spray) method on the NiCrCoAl alloy substrate before deposition of top coating. Each 4YSZ top coating shows different tribological behaviors based on the inherent layer structures. 4YSZ by APS which has splat-stacked structure shows lower friction coefficient but higher wear rate than 4YSZ by EB-PVD which has columnar structure. For 4YSZ by APS, such results are expected due to the sliding wear accompanied with local delamination of splats.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.10a
• /
• pp.136-137
• /
• 2003

In this study, in order to fabricate sintered dental implant, the effects of HA, Ti and TiN on corrosion and biocompatibility, cell toxicity, osseointegration of electroless Cu-plated and sintered stainless steel implant were investigated using various characteristics. The effects of Ti/TiN/HA coating on the interface activation and surface characteristics of sintered stainless steels(SSS) by electron-beam physical vapor deposition(EB-PVD) method have been studied. Stainless steel compacts containing 2, 4, and 10 wt%Cu were prepared by electroless Cu-plating method which results in the increased homogenization in alloying powder. The specimens were coated with HA, Ti and TiN with few $\mu\textrm{m}$ thickness respectively by EB-PVD method. The microstructures and phase analysis were conducted by using SEM. Biocompatibility were investigated in experimental dog. The corrosion behaviors were investigated using potentiosat in 0.9% NaCl solution and corrosion surface was observed using SEM and XPS.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.1
• /
• pp.39-48
• /
• 2001

Fe-Cr-Al alloy has been studied for application in automobile muffler materials due to good corrosion and oxidation resistance. In order to develop the automobile muffler materials, corrosion behaviors of electron beam physical vapor deposition (EB-PVD) coated surface of muffler matericls of muffler materials were investigated using potentiostat. For 0.1M NaCl solution, corrosion potential and pitting potential of Fe-20Cr-10Al was higher than that of Fe-5Cr- 10Al samples. Especially, in the case of Ti and Nb coated samples, pitting potential increased remarkably compared with non-coated samples. For 0.1M $CaCl_2$ solution, Ti-coated Fe-20Cr-10Al showed remarkably improved pitting corrosion resistance in comparison with non-coated Fe-20Cr-10Al and Fe-5Cr-10Al. The number and size of pits were decreased in the case of Ti coated samples in the 0.1M NaCl and 0.1M $CaCl_2$ solution.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.210.2-210
• /
• 2003

• Journal of the Korean Ceramic Society
• /
• v.42 no.1
• /
• pp.43-49
• /
• 2005

YSZ layer containing nano-sized particles has been deposited on the commercial A1203 substrate by Electron Beam Physical Vapor Deposition (EB-PVD). The role of coating rnjcrostructures of YSZ to indentation damage is studied. The different coating microsouctures are prepared by varying the substrate temperatures from $600^{circ}C$ to $800^{circ}C$ during the deposition. Microhardness test and Hertzian indentation are conducted on the $YSZ/Al_{2}O_{3}$ layered systems. The damage and flilure behaviors have been investigated according to the effect of microstructures and indentation loads. With increasing the substrate temperature during EB-PVD, the overall grain sizes are coarser and more faceted, which microsoucture ultimately influences on the indentation behavior, thus, YSZ/Al_{2}O_{3}$ layered system prepared at the substrate temperature of $800^{circ}C$ shows relatively higher damage tolerance.

• Journal of the Korean Ceramic Society
• /
• v.53 no.1
• /
• pp.81-86
• /
• 2016

The effect of substrate rotation speed on the phase forming behavior and microstructural variation of 8 wt% yttria ($Y_2O_3$) stabilized $ZrO_2$ (8YSZ) coatings as a thermal barrier coating has been investigated. 8YSZ coatings with $100{\sim}200{\mu}m$ thickness were deposited by electron beam-physical vapor deposition onto a super alloy (Ni-Cr-Co-Al) substrate with a bond coating (NiCo-CrAlY). The width of the columnar grains of the 8YSZ coatings increased with increasing substrate rotation speed from 1 to 30 rpm at a substrate temperature range of $900{\sim}950^{\circ}C$. In spite of the different growth behaviors of coatings with different substrate rotation speeds, the phases of each coating were not changed remarkably. Even after post heat treatments with various conditions of the coated specimens fabricated at 20 rpm, only a change of color was noticeable, without any remarkable change in the phase or microstructure.

• Journal of Powder Materials
• /
• v.20 no.6
• /
• pp.460-466
• /
• 2013

4 mol% Yttria-stabilized zirconia (4YSZ) coatings with $200{\mu}m$ thick are fabricated by Electron Beam Physical Vapor Deposition (EB-PVD) for thermal barrier coating (TBC). $150{\mu}m$ of NiCrAlY based bond coat is prepared by conventional APS (Air Plasma Spray) method on the NiCrCoAl alloy substrate before deposition of top coating. 4 mol% YSZ top coating shows typical tetragonal phase and columnar structure due to vapor phase deposition process. The adhesion strength of coating is measured about 40 MPa. There is no delamination or cracking of coatings after thermal cyclic fatigue and shock test at $850^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.45 no.9
• /
• pp.549-555
• /
• 2008

The thermal barrier coating must withstand erosion when subjected to flowing gas and should also maintain good stability and mechanical properties while it must also protect the turbine component from high temperature, hot corrosion, creep, and oxidation during operation. In this study we investigated the influence of subsurface layer, $Al_2O_3$ or NiCrCoAIY bond coat layer, on the indentation damage behavior of YSZ thermal barrier coating layers deposited by electron beam physical vapor deposition (EB-PVD). The bond coat is deposited using different process such as air plasma spray (APS) or spray of high velocity oxygen fuel (HVOF) and the thickness is varied. Hertzian indentation technique is used to induce micro damages on the coated layer. The stress-strain behaviors are characterized by results of the indentation tests.