• Journal of the Korean institute of surface engineering
• /
• v.31 no.6
• /
• pp.325-333
• /
• 1998

A duplex surface treatment process of simultaneous aluminizing-chromizing process followed by plasma nitriding was performed on AISI HI3 steel and STS 403 steel. The properties of these duplex-treated steels were investigated and were compared with those of steels treated by single process of either simultaneous aluminizing-chromizing or plasma nilriding, in terms of microstructure, microhardness and high temperature wear resistance. Sim~dtaneous alumizing-chromizing process was done using a 2-step coating cycle and plasma nitriding process was done at $530^{\circ}C$ for 1.5 hour. AISI HI3 steel and STS 403 steel showed a FeA1 compound layer of approximately 350$\mu\textrm{m}$ thickness on the surface after simultaneous diffusion coating and nitrided layer of approximately 70-80$\mu\textrm{m}$ formed after the subsequent plasma nitriding process. The microhardness was improved much more by the duplex surface heatment than only by plasma nitriding. In addition the duplex treated specimens showed an improved high temperature wear resistance.

• Journal of the Korean Society for Heat Treatment
• /
• v.15 no.2
• /
• pp.57-64
• /
• 2002

The 22%Cr-5%Ni-3%Mo duplex and 18%Cr-8%Ni austenitic stainless steels have been nitrogen permeated under the $1Kg/cm^2$ nitrogen gas atmosphere at the temperature range of $1050^{\circ}C{\sim}1150^{\circ}C$. The nitrogen-permeated duplex and austenitic stainless steels showed the gradual decrease in hardness with increasing depth below surface. The duplex stainless steel showed nitrogen pearlite at the outmost surface and austenite single phase in the center after nitrogen permeation treatment, while the obvious microstructural change was not observed for the nitrogen-permeated austenitic stainless steel. After solution annealing the nitrogen-permeated stainless steels(NPSA treatment) at $1200^{\circ}C$ for 10 hours, the hardness of the duplex and austenitic stainless steels was constant through the 2 mm thickness of the specimen, and the ${\alpha}+{\gamma}$ phase of duplex stainless steel changed to austenite single phase. Tensile strengths and elongations of the NPSA-treated duplex stainless steel remarkably increased compared to those of solution annealed (SA) duplex stainless steel due to the solution strengthening effect of nitrogen and the phase change from a mixture of ferrite and austenite to austenite single phase, while the NP-treated austenitic stainless steel displayed the lowest value in elongation due to inhomogeneous deformation by the hardness difference between surface and interior.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.3
• /
• pp.183-189
• /
• 2005

The effects of duplex-treatment of plasma carburization and CrN coating onto Ti-6Al-4V alloy on its creep properties were investigated by means of a constant stress creep tester. Applying duplex-treatment, specimens having an inner carburized layer of about $150{\mu}m$ in depth and outer CrN layer of about $7.5{\mu}m$ in thickness were prepared. The hardness of duplex-treatment surface was about 1,960 VHN. It also appeared that the duplex-treatment improved the roughness of the surface significantly; $Ra=0.045{\mu}m$ for treated alloy while $Ra=0.321{\mu}m$ for untreated alloy. The steady-state creep behaviors were investigated in a temperature range of $510{\sim}550^{\circ}C$ ($0.42{\sim}0.44T_m$) under an applied stress range of 200~275 MPa. The stress exponent, n, was derived assuming the power law creep behavior. The surface treatment showed a decrease in a value from 9.32 (untreated) to 8.79 (treated). Also the activation energy obtained from an Arrhenius plot increased from 238 to 257 kJ/mol.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.6
• /
• pp.306-311
• /
• 2020

In this work, diamond-like carbon (DLC) films are coated onto plasma nitrided AISI 4140 steel by DC-pulsed PECVD. One problem of DLC films is their very poor adhesion on steel substrates. The purpose of the nitriding was to enhance adhesion between the substrate and the DLC films. The white layer formation is avoided. Plasma nitriding increased adhesion from 8 N for DLC coating to 25 N for duplex coating. Duplex plasma nitriding/DLC coating was proven to be more effective in improving the adhesion. The purpose of the bond layer was to enhance adhesion between the substrate and the DLC films.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.6
• /
• pp.234-240
• /
• 2005

In this study, ion nitriding of a EHA pump part made of AISI 4340 steel was performed under different applied power conditions to study the relationship between dimensional changes of specimens and the type of applied power source. Microstructures and micohardness distribution at different processing conditions were also examined. Duplex surface treatment of ion nitriding with the optimum process conditions to produce the minimum dimensional variation in a EHA pump part and a TiN thin film coating by unbalanced magnetron sputtering was performed and the specimens with a duplex surface treatment were subjected to a high speed wear test to evaluate the wear performance of EHA hydraulic pump parts with various surface treatment conditions. Results indicated that uniform and continuous surface layer with a minimum dimensional variation could be obtained by ion nitriding with bipolar mode power source and much enhanced wear characteristics with a duplex surface treatment could be obtained, compared with results from ion nitriding or single-layerd TiN coating specimens.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.5
• /
• pp.221-226
• /
• 2014

A low temperature plasma nitrocarburizng was implemented on the duplex stainless steel to achieve the enhancement of surface hardness without degradation of its corrosion resistance. Attempts were made to investigate the influence of Pulse frequency and Duty factor of pulsed power in a high Pulse frequency regime on the surface characteristics of the hardened layer. The hardened layer (S-phase) was formed on all of the treated surfaces. Surface hardness reached up to 1300 $HV_{0.1}$ which is about 4.6 times higher than that of the untreated material (280 $HV_{0.1}$). The thickness of the hardened layer tends to increase lightly with the higher Pulse frequency and the higher Duty factor. The corrosion resistance of nitrocarburized duplex stainless steel was almost similar to that of the untreated material. Both the Pulse frequency and the Duty factor do not have a significant influence on the corrosion property of plasma treated duplex stainless steel.

• Journal of the Korean institute of surface engineering
• /
• v.31 no.6
• /
• pp.334-344
• /
• 1998

Yew coating pmccss t.o form a surface layer ol CrN phasc on mild steel (A81 1020!, AlSI Hi3, 1Cr-0.5Mo steel (ASTM A213 and Nickrl-base superalloy (Inconel 718) was developed. Surlaces of various alloys t,n.ateii by chromizing for the formation ol Cr diffusion layer was subsequently trcaled by plasma nitriding in order t.o form the hard CrS coating layer on the surfaces. This duplex plasma surface tri-atments of chromizing and plasma nitriding have induced a lormation of a duplex-lrcated surfacr hyer of approximat~ls 70-80 $\mu\textrm{m}$thickncss with a iargcly improved microiiardnrss up to approxiniateW 1500Hv(50gf). The main cause for the lage improvment in the surface hardncss is altribilted to [.he fact that CrN and $Fe_xN$ phases are created successfully by ccliromizins and plasma nilriding treatment. High tenipera1,urc wear resislance of the duplex-treated mild steel and HI3 steels at $600^{\circ}C$ was examined. Comparing the duplex-treated specimens with the specimens treated only by chromizing, the rcsults shovmi that, thc wear volume of the duplex-treated mild skcl and 1113 stcel aSt.er a wear test, at $600^{\circ}C$ were reduced hy a Iactor of 8 and 3, respectively. Characteristics of the CrS phase by duplrx treatment were compared with $CrN_x$,/TEX> film by ion plating and the wear behaviors of CrN film lormed by two different nroccsses arc nea.riy identical.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.1
• /
• pp.14-20
• /
• 2013

Duplex stainless steel, which is a kind of stainless steel with a mixed microstructure of about equal proportions of austenite and ferrite, is generally known as a unique material with excellent corrosion resistance and high strength. However, toughness, strength, and corrosion resistance of the steel could be reduced due to precipitation of topologically closed packed phases such as sigma phase during cooling. In case of large forged products, they have strong possibility that ${\sigma}$-phase precipitates due to difference of cooling rate between surface and inner of the products. Investigation on sigma phase precipitation behavior of duplex stainless steel with change of cooling rate was carried out in this study. Forged SAF 2205 duplex stainless steel was used as specimens to examine the cooling rate effect. Dissolution behavior of sigma phase was also discussed through resolution test of duplex stainless steel containing lots of sigma phase. Experimental results revealed that impact energy was very sensitive to precipitation of small amount sigma phase. However, sigma phase could be removed by short term resolution treatment and impact resistance of the duplex stainless steel was restored.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.291-292
• /
• 2015

Duplex Stainless Steel의 Plasma Nitriding 처리 시 가스량과 처리온도가 표면 특성에 미치는 영향을 조사하였다. $N_2$함량 및 처리 온도가 각각 10%에서 25%로 $400^{\circ}C$에서 $430^{\circ}C$로 증가함에 따라서 질소가 과고용된 S-phase의 두께 및 표면 경도가 증가하였으나, 내부 식성은 $Cr_2N$ 및 $(Fe,Cr)_4N$이 석출하여 감소하였다. 질소를 10%로 고정하고 $CH_4$함량을 증가시키면 1%일 때 S-phase의 두께가 최대가 되며 그이후로 감소하였다. 처리온도 $400^{\circ}C$일 때 질소함량이 10%, $CH_4$ 함량이 5%일 경우 내식성이 모재보다 증가하였다.

• Journal of the Korean institute of surface engineering
• /
• v.39 no.1
• /
• pp.1-8
• /
• 2006

In this study, effect of sputtering after plasma nitriding and before PVD coating on the microstucture, microhardness, surface roughness and the adhesion strength of CrN thin films were investigated. Experimental results showed that this sputtering process not only removed surface compound layer which formed during a plasma nitriding process but also induced an alteration of the surface of plasma nitrided substrate in terms of microhardness distribution and surface roughness, which in turn affected the adhesion strength of PVD coatings. After sputtering, microhardness distribution showed general decrease and the surface roughness became increased slightly. The critical shear stress measured from the scratch test on the CrN coatings showed an approximately twice increase in the binding strength through the sputtering prior to the coating and this could be attributed to a complete removal of compound layer from the plasma nitrided surface and to an increase in the surface roughness after sputtering.