• Journal of Mechanical Science and Technology
• /
• 제14권10호
• /
• pp.1021-1027
• /
• 2000

In this study, fatigue tests were performed to examine the effects of micro drill hole on fatigue limit of as cast and austempered ductile cast iron (ADI) using the rotary bending fatigue tester. As results, micro drill holes ($diameter{\leq}0.4mm$) did not influence the fatigue limit of ADI, compared to annealed ductile cast iron; the critical defect size of crack initiation, in ADI was larger than as cast. If the ${\sqrt{area}}$ of micro drill hole and graphite nodule in ADI are comparable, crack initiates at the graphite nodule. When the ruggedness developes through austempering treatment process, microstructure on crack initiation at micro drill hole is tougher than that of as cast ductile cast iron.

• Journal of Advanced Marine Engineering and Technology
• /
• 제23권3호
• /
• pp.284-291
• /
• 1999

Recently the ductile cast iron is being used successfully to the parts for processing machinery vessels and gear etc. This study is mainly concerned with the heat treatment for the specimens of crank shaft which are made of ductile cast iron. The results obtained are summarized as follows. Comparing the mechanical properties of the specimens for the normalized ductile cast irons the specimen heat treated at $550^{\circ}C$ was the best for crank shaft of air-compressor. After austenizing at $910^{\circ}C$ it was observed that the higher the reheating temperature is the less tensile strength and the hardness became which was supposedly attributed to the fact that the amount of pearlite. Austenite matrix was reduced by reheating after normalizing and that as the reheating tem-perature went up the pearlite generated was less and the distance between the pearlites were widened at last made pearlite globular. In the comparsison of crank shaft for air compressor made of ductile cast iron with that made by forged steel the crank shaft made of ductile cast iron was superior in economical terms. And ductile cast iron could be practically enough if only the elonga-tion which was inferior mechanical property to forged steel could be reinforced by increasing the diameter of crank pin when designing the crank shaft.

• 한국주조공학회지
• /
• 제28권6호
• /
• pp.273-281
• /
• 2008

Effects of alloying elements on the mechanical properties of hardened and austempered 3.60wt%C - 2.50wt%C ductile cast iron were investigated. Strength and hardness were increased and ductility was decreased as the amount of alloying element increased. The increasing effect of copper addition on the strength was the most pronounced. The strength and hardness were greatly increased and ductility was decreased by hardening. The effect of alloying element on the mechanical properties of the hardened ductile cast iron was not so pronounced due to the high contents of C and Si. The strength and hardness of austempered ductile cast iron were greatly increased, meanwhile the difference of strength from that of hardened one was not so big. The ductility of the former was higher than that of the latter. The strength and ductility of austempered ductile cast iron with 0.25%Mn were the maximum of all Mn added ones. The maximum strength of that was obtained with the addition of 0.80wt%Cu or 2.00wt%Ni along with this amount of Mn added.

• 한국주조공학회지
• /
• 제27권1호
• /
• pp.24-30
• /
• 2007

The effects of C, Si and RE additions on the tendency of chill formation of ductile cast iron obtained from metal mold casting were investigated. In case of metal mold cast, the ductile cast iron with 2.5%Si had pearlitic matrix, and specimens with 2.9%Si had bull's eye type regardless of C contents. As-cast specimen with a large amount of fine graphites could be obtained by adding 0.2% RE. Normalizing process was necessary to remove carbide and form a large amount of spheroidal graphites for the as-cast specimens. Good mechanical properties could be obtained by heat-treatment of as-cast specimens with pearlitic matrix. Normalizing the specimens with RE caused the reduction in mechanical properties.

• Smart Structures and Systems
• /
• 제7권4호
• /
• pp.241-262
• /
• 2011

Cast iron pipe has been used as a water distribution technology in North America since the early nineteenth century. The first cast iron pipes were made of grey cast iron which was succeeded by ductile iron as a pipe material in the 1940s. These different iron alloys have significantly different microstructures which give rise to distinct mechanical properties. Insight into the non-destructive structural condition assessment of aging pipes can be advantageous in developing mitigation strategies for pipe failures. This paper examines the relationship between the small-strain and large-strain properties of exhumed cast iron water pipes. Nondestructive and destructive testing programs were performed on eight pipes varying in age from 40 to 130 years. The experimental program included microstructure evaluation and ultrasonic, tensile, and flexural testing. New applications of frequency domain analysis techniques including Fourier and wavelet transforms of ultrasonic pulse velocity measurements are presented. A low correlation between wave propagation and large-strain measurements was observed. However, the wave velocities were consistently different between ductile and grey cast iron pipes (14% to 18% difference); the ductile iron pipes showed the smaller variation in wave velocities. Thus, the variation of elastic properties for ductile iron was not enough to define a linear correlation because all the measurements were practically concentrated in single cluster of points. The cross-sectional areas of the specimens tested varied as a result of minor manufacturing defects and levels of corrosion. These variations affect the large strain testing results; but, surface defects have limited effect on wave velocities and may also contribute to the low correlations observed. Lamb waves are typically not considered in the evaluation of ultrasonic pulse velocity. However, Lamb waves were found to contribute significantly to the frequency content of the ultrasonic signals possibly resulting in the poor correlations observed. Therefore, correlations between wave velocities and large strain properties obtained using specimens manufactured in the laboratory must be used with caution in the condition assessment of aged water pipes especially for grey cast iron pipes.

• 산업기술연구
• /
• 제24권A호
• /
• pp.3-8
• /
• 2004

This study was performed to investigate the effect of two step austenitized treatment on the mechanical properties and fracture characteristic of the ductile cast iron and austempered ductile cast iron(ADI). The obtained results of this study were as follows. The matrix structures of specimens were changed differently by austenitizing heat treatment. Microstructure of austempered ductile cast iron obtained by two step austenitized treatment was bainitic ferrite and retained austenite. With two step austenitized treatment, vield strength, tensile strength and hardness decreased, while the elongation increased.

• 한국주조공학회지
• /
• 제32권2호
• /
• pp.81-85
• /
• 2012

The effects of section size and melt holding time on the mechanical properties and microstructure of high silicon ductile cast iron were investigated. The strength, elongation and hardness of the test specimen with smaller cross-section were higher than those with larger one. The nodule count and volume fraction of pearlite of the former were higher than those of the latter. The mechanical properties decreased with increased melt holding time before pouring. Nodularity and nodule count decreased and the volume fraction of pearlite rather slightly increased with it.

• 한국주조공학회지
• /
• 제29권2호
• /
• pp.86-94
• /
• 2009

The effect of austenitizing temperature and time on the processing window of 3.60wt%C - 2.50wt%Si - 0.80wt%Cu ductile cast iron and that of the amount of copper added were investigated. The second stage reaction at 400oC was retarded with increased austenitizing temperature. The widest processing window was obtained at the lower austempering temperature with the increased time at the same austenitizing temperature. The width of the widest processing window was decreased with the increase of time at the same austenitizing temperature. The width of processing window was increased with the increased amount of copper added.

• 한국주조공학회지
• /
• 제43권6호
• /
• pp.279-285
• /
• 2023

본 연구에서는 임계간 온도 범위에서 열처리한 구상흑연주철의 열처리 온도에 따른 물성 예측을 위해, 인장강도 450 MPa 급 구상흑연주철을 다양한 온도에서 열처리한 후 공냉하여 물성 예측에 필요한 미세조직을 분석하고 브리넬 경도를 측정하였다. 임계간 온도 구간에서 열처리 온도가 증가할수록 구상흑연주철 내 페라이트 분율은 감소함과 동시에 펄라이트 분율은 증가하였으나, 흑연 구상화율 및 구상흑연입수는 주방상태에서 측정된 값과 유사하였다. 열처리한 구상흑연주철의 브리넬 경도는 열처리 온도가 증가할수록 점점 증가하였다. 측정된 합금 조성 및 각 안정상의 분율, 그리고 문헌에 알려진 구상흑연주철의 브리넬 경도 예측 모델을 활용하여 열처리 온도 별 구상흑연주철의 경도 값을 계산해 본 결과, 측정값과 매우 유사한 값을 얻을 수 있었다. 또한 열역학 계산을 통해 예측된 상분율을 활용하여 정확한 경도 예측이 가능할지 확인해보기 위해, 열처리 온도 별로 구상흑연주철 내 흑연, 페라이트 및 오스테나이트의 부피를 계산한 후, 이를 면적으로 변환하여 동일한 구상흑연주철의 경도 예측 모델에 적용하였다. 이렇게 열역학 계산과 경도 예측 모델을 동시에 활용하여 계산된 구상흑연주철의 경도 값은 실제 측정한 브리넬 경도 대비 최대 27의 오차 범위 내에서 유사한 값을 나타내었다.

• 한국주조공학회지
• /
• 제10권4호
• /
• pp.299-308
• /
• 1990

Ductile cast iron has a good ductility and ductility and toughness than those of gray cast iron, because the shape of graphite is spheroidal. It has been reported that the strengthening and toughening of the ductile cast iron was resulted from the good modification of various matrix structures obtained by the heat treatment or addition of alloying elements. This study aims to investigate the effect of various special heat treatment(Cyclic Heat Treatment, Intermediate Heat Treatment, Step Quenching), austempering and alloying element(Ni) on the strength and toughness of ductile cast iron. The results obtained from this study are summarized as follows. 1) With addition of Ni, the amount of pearlite or bainite were increased and the morphologies of pearlite or bainite became finer by special heat treatments. 2) As the Ni added and not added ductile cast iron were treated by austenitizing at $900^{\circ}C$ and $840^{\circ}C$, in the latter the austenite was mostly formed in the vicinity of eutectic cell boundary, but in the former on the whole matrix. 3) In cyclic heat treatment, the volume fraction of pearlite was increased and the shape of pearlite was fined with increase of the number of cycle. 4) The shape of pearlite was mostly bar type in the intermediate heat treatment, but spheroidal type in step quenching. 5) The mechanical properties of ductile cast iron containing 1.5%Ni austempered at $400^{\circ}C$ for 25min. after austenitizing at $900^{\circ}C$ for 15min. were a good value of hardness 105(HRB), impact energy 12.5(kg.m), tensile strength 112($kg/mm^2$) and elongation 6.8(%).