• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.667-670
• /
• 2005

This study is concerned with application of SWP-2H with performance which could be improved compressive strength, crack control of high strength concrete ranged from 35MPa to 70MPa. Expermental data showed that initial. behavior of SWP-2H added concrete had a similar tendency that of non-added concrete. As well crack resulted from autogeneous and drying shrinkage and compressive strength were well controled or elevated by application of SWP-2H.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.11a
• /
• pp.1-4
• /
• 2007

Because reinforced concrete structures were being high more and more in recent year, concrete was being demanded high performance of high strength and high fluidity. But various characteristics must be confirmed besides guarantee of demand strength in ultra-high strength concrete. In ultra-high strength concrete, autogenous shrinkage and drying shrinkage grow big because of a low water cement ratio and much quantity of binder. So dangerousness of crack generation grow big in early ages. And ultra-high strength concrete is influenced by use materials more than ordinary strength concrete. In this study we were examined mix design, atuogenous shrinkage and pumpability of ultra-high strength concrete to apply on the ground.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.581-584
• /
• 2008

In this study, it is willing to present that fundamental data for proposing quantitatively shrinkage cracking evaluation method such as plat-ring type restrained test method. To examine suitable size of specimen of plat-ring type restrained test method, Evaluated concrete about restrained shrinkage crack properties of numerical analysis of 3D solid element using the MIDAS program, drying shrinkage deformation, restrained shrinkage stress, crack area and crack point with inside ring diameter of specimen in 100mm, 150mm, 200mm and high of Specimen in 30mm, 50mm after curing in condition of constant temperature and usual habit of temperature 20${\pm}$3$^{\circ}$C, humidity 60${\pm}$5%. As a result, it was available about suitable estimation with inside ring diameter of specimen in more than 150mm and high of Specimen in 50mm. Hereafter, it is considered that the study concerning environmental condition and mixing factor in plat-ring type restrained test method is need.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.1
• /
• pp.136-143
• /
• 2006

In this study, recently it is urgently required that demolition waste concrete has to be recycled on the construction because urban development is accelerated and redevelopment project is rapidly expanded, production quantity of construction and demolition waste concrete is being increased. As a results of drying shrinkage test under restrained and unrestrained condition, although workability and mechanical properites of concrete using HQRS were similar to that of concrete using natural sand, there were a great difference in deformation characteristic of dry shrinkage according to replacement ratio of HQRS. And, it makes sure that use of HQRS instead of partial nature sand was effective because drying shrinkage of concrete using 30 volume percentage of HQRS was smaller than that using only natural sand. Therefore, it is the objective of this study to provide the fundamental data about the re-application as an analysis of the drying shrinkage characteristics of concrete using HQRS and it is able to creta a high value-added by using HQRS.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.6
• /
• pp.561-569
• /
• 2016

Concrete is cheap, easy to deal with, and the quality is satisfactory. Also, it is one of the easiest materials to get because chemical composition of cement is similar to chemical composition of surface. On the other hand, it is so vulnerable to transform because of weak binding capacity and low binding energy that it produces cracks. Cracks decline durability, usability, safety of structures and damage exterior. In order to decline drying shrinkage crack, this study used shrinkage reducing typed Superplasticizer, which is combination of and water-reducing agent for convenience, different with existing study using AE agent, water-reducing agent, shrinkage reducing agent,. Considering SRS field application possibility, this study planned to mix concrete and mortar generally used in ready-mixed concrete company and did basic experiment depending on a change of SRS content ratio and admixture. Based on the experiment result. It is judged that SRS admixture 2% is proper ratio when Given the intensity and length change. Also mass combination will conduct follow-up studies.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.5
• /
• pp.457-464
• /
• 2015

The alternative material for cement has been attracting attention in construction projects. Especially, the alkali activated slag(hereafter, AAS) concrete is able to use for a structural vertical member because of 40MPa of compressive strength, However, the research about time-dependent deformation such as creep which is important to strength member is insufficient. Therefore, in this study, experiments were performed with respect to time-dependent deformation including the drying shrinkage and creep deformation of AAS concrete. The creep deformed ratio of AAS concrete was more than OPC concrete by approximately 4.3% and the dry shrinkage deformation of AAS concrete was more than OPC concrete by approximately 69%. The large amount of sodium silicate, alkali activator, is added causing temperature crack than promoted drying and drying creep which is confirmed by water ration test and SEM.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.251-257
• /
• 2018

There are various quality deteriorations of concrete such as plastic, drying shrinkage due to abrupt moisture evaporation, slump loss and cold joint under hot weather condition. To protect from above deteriorations, several kinds of modified bubble sheets have been applied to secure heat insulation performance. But, there is not enough application cases of bubble sheets at job site under hot weather condition. The objective of the paper is to investigate the temperature profile and crack occurrence of the concrete covered with five different kinds of surface curing sheets, which is placed under hot weather condition. Single layer transparent bubble sheet, white colored bubble sheet, aluminum metalizing bubble sheet and PE film are adopted for surface curing sheets. Test results indicated that application of aluminum metalizing bubble sheet had most favorable effect on the reduction of on temperature rise and on the crack reduction of concrete. But due to larger reflection of light by aluminum, it brings about visual pollution to the workers. Hence, the application of white colored bubble sheet can be the most desirable alternative to protect the concrete from hot weather in the field.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.11a
• /
• pp.5-8
• /
• 2006

This study investigates the field application, Songdo the # 1st WORLD, on zero-crack construction of the fundamental mass concrete using double bubble sheets and applying low heat mixture. Experimental results of hydration heat analysis showed that crack modulus of concrete incorporating 20% of blast furnace slag cement was 1.0 in 120 hours, representing 50% probability of crack occurrence, thus requiring additional measures. As for a curing method, a specimen insulating two layers of vinyl chloride+double bubble sheets exhibited only $16.5^{\circ}C$ difference between upper and lower sections, and it also showed favorable workability as well as competitive economic side. Therefore it was determined to use it for curing method in this field. For the curing results of practical field, using 2 layers of vinyl chloride+double bubble sheets and applying low heat mixture on the fundamental mass concrete in 3A residential building exhibited less than only $15^{\circ}C$ difference between surface and center section of that in 5 days elapse and less than $20^{\circ}C$ in 9 days. This means that the crack by hydration heat was prevented, and other fields structures also resisted the plastic shrinkage by insulating the vinyl, sinking crack by second temping, even drying shrinkage by the mixture of low unit water. Therefore the crack on the placement has not been found so far, since the construction was started before 6 month.

• International Journal of Concrete Structures and Materials
• /
• v.7 no.1
• /
• pp.79-93
• /
• 2013

One of the biggest problems affecting bridges is the transverse cracking and deterioration of concrete bridge decks. The causes of early age cracking are primarily attributed to plastic shrinkage, temperature effects, autogenous shrinkage, and drying shrinkage. The cracks can be influenced by material characteristics, casting sequence, formwork, climate conditions, geometry, and time dependent factors. The cracking of bridge decks not only creates unsightly aesthetic condition but also greatly reduces durability. It leads to a loss of functionality, loss of stiffness, and ultimately loss of structural safety. This investigation consists of field, laboratory, and analytical phases. The experimental and field testing investigate the early age transverse cracking of bridge decks and evaluate the use of sealant materials. The research identifies suitable materials, for crack sealing, with an ability to span cracks of various widths and to achieve performance criteria such as penetration depth, bond strength, and elongation. This paper also analytically examines the effect of a wide range of parameters on the development of cracking such as the number of spans, the span length, girder spacing, deck thickness, concrete compressive strength, dead load, hydration, temperature, shrinkage, and creep. The importance of each parameter is identified and then evaluated. Also, the AASHTO Standard Specification limits liveload deflections to L/800 for ordinary bridges and L/1000 for bridges in urban areas that are subject to pedestrian use. The deflection is found to be an important parameter to affect cracking. A set of recommendations to limit the transverse deck cracks in bridge decks is also presented.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.493-496
• /
• 2008

The risk of transverse cracking in concrete decks of composite bridges is affected by many factors related to the bridge design, materials, and construction. Among others, the thermal and shrinkage stresses are the most important factors that affect the transverse cracking in early-age concrete decks. The thermal stress at the concrete deck is mainly affected by both ambient temperature and solar radiation. The shrinkage stress at the general strength concrete deck is mainly affected by drying shrinkage and the high strength concrete deck is mainly affected by autogeneous shrinkage. Three-dimensional finite element models of composite bridges were made to investigate the stress due to thermal and shrinkage stress.