• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.162-167
• /
• 2004

The low velocity impact characteristics of composite laminate curved beams are investigated to increase damage tolerance and reduce the deflection. Drop weight impact tests of the composite curved beam were performed with respect to pre-load, then the damage after impact was measured by macrography. Also, finite element analyses were performed using ABAQUS to investigate the stress state of composite curved beam with respect to pre-load and impact. From the investigation, it was found that pre-load of the composite curved beams had much influence on impact damage of the curved beam, which showed good agreement with the experiment results.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.04a
• /
• pp.71-75
• /
• 2005

For the damage tolerance improvement of conventional laminated composites, stitching process have been utilized for providing through-thickness reinforcements. 2D preforms were stacked with S-2 glass plain weave and S-2 glass MWK (Multi-axial Warp Knit) L type. 3D preforms were fabricated using the stitching process. All composite samples were fabricated by RTM (Resin Transfer Molding) process. To examine the damage resistance performance the low speed drop weight impact test has been carried out. For the assessment of damage after the impact loading, specimens were examined by scanning image. CAI (Compressive After Impact) tests were also conducted to evaluate residual compressive strength. Compared with 2D composites, the damage area of 3D composites was reduced by 20-30% and the CAI strength showed 5-10% improvement.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.04a
• /
• pp.235-239
• /
• 2005

In this research, we investigated the frequency characteristic of low-velocity impact induced damage signals on graphite/epoxy composite laminates using high-speed fiber Bragg grating(FBG) sensor system. Appling the FBG sensors to damage assessment, we need to study the response of FBG sensors as the damage signals of the different incident angles because FBG shows different directional sensitivity. In order to discriminate an impact induced damage signal from that of undamaged case, drop impacts with different energies were applied to the composite panel with different incident angle to the FBG sensor. Finally, detected impact signals were compared using frequency distributions of wavelet detail components in order to find distinctive signal characteristics of composites delamination.

• Journal of Aerospace System Engineering
• /
• v.3 no.1
• /
• pp.12-16
• /
• 2009

The laminated sequence and thickness of a composite structure is an important design parameter which affect the strength and impact damage. In this study, it was investigated the residual strength of carbon fiber laminate after impact damage by the experimental investigation. The tensile strength test and compressive strength test were used to find the mechanical properties, previously. Impact test was performed using low-velocity drop-weight test equipment. The impact damages were finally assessed by the compressive strength test. The investigation results revealed the residual strength of the damaged specimens due to the impact damage.

• Advanced Composite Materials
• /
• v.18 no.2
• /
• pp.121-134
• /
• 2009

The present study investigated, both experimentally and numerically, the improvement of low-velocity impact damage resistance of carbon fiber reinforced plastic (CFRP) laminates due to through-the-thickness stitching. First, we conducted drop-weight impact tests for stitched and unstitched laminates. The results of damage inspection confirmed that stitching did improve the impact damage resistance, and revealed that the improvement effect became greater as the impact energy increased. Moreover, the stitching affected the through-the-thickness damage distribution. Next, we performed FEM analysis and calculated the energy release rate of the delamination crack using the virtual crack closure technique (VCCT). The numerical results revealed that the stitching affected the through-the-thickness damage distribution because the stitch threads had a marked effect on decreasing both the modes I and II energy release rate around the bottom of the laminate. Comparison of the results for models that contained delaminations of various sizes revealed that the energy release rate became lower as delamination size increased; therefore the stitching improved the impact resistance more effectively when the impact energy was higher.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.1 s.232
• /
• pp.81-87
• /
• 2005

A fracture of hand held device, such as radio, TV and CD-RW drive, mainly occurs due to drop situation. For CD-RW drive, the need of high reading/writing speed in conjunction with low price accelerates the fracture of the device. Computer simulation can reduce the period of development and enhance impact characteristic of device. In this study, the detailed finite element model of CD-RW drive was developed to predict the damage under drop conditions. Material property for shock absorbing damper was obtained from tensile test of raw material. A MOONEY-RIVLIN type rubber in LS-DYNA was used as the material model of damper. To assess the reliability of the developed model, drop test at 200G-2msec and 150G-10msec condition was conducted and acceleration at pick-up was compared.

• International Journal of Ocean System Engineering
• /
• v.2 no.2
• /
• pp.92-96
• /
• 2012

This study presents a rockfall impact analysis of a typical roadway. Dynamic finite element analyses using ANSYS AUTODYN are conducted to determine the effect of the drop heights (5 m, 10 m) on the damage to a roadway model. The Rockfall is modeled as a spherical shape with a weight of 400 kg, and each drop height is converted to a corresponding impact velocity to save computational time. The roadway model is comprised of an asphalt layer, base layer, sub-base layer, and sub-grade layer. In this paper, the asphalt is modeled using a linear elastic model. The base layer, sub-base layer, and sub-grade layer are modeled using a Mohr-Coulomb model. From the analyses, the effects of the drop height on the damages and stresses are examined and discussed.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.171-174
• /
• 2004

In order to improve the damage tolerance of the conventional laminated composites, three­dimensional fiber structures incorporated with stitching yams have been utilized in this study. From the newly developed process termed as TAPIS(TApe Placement Incorporated with Stitching), carbon/epoxy composites have been fabricated. Two-dimensional composites with the same stacking sequence as 3D counterparts have also been fabricated for the property comparison. To examine the damage resistance performance the low speed drop weight impact test has been adopted. For the assessment of damage after the impact loading, specimens were subjected to C-scan nondestructive inspection compression after impact(CAI) were also conducted to evaluate residual compressive strength. Although the damage area of 3D composites was greatly reduced$(30-40\%)$ compared with that of 2D composites, the CAI strength did not show drastic improvement.

• Advanced Composite Materials
• /
• v.16 no.1
• /
• pp.45-61
• /
• 2007

This paper describes a damage accumulation mechanism in cross-ply CFRP laminates $[0_2/90_2]_{2S}$ subjected to out-of-plane loading. Drop-weight impact and static indentation tests were carried out, and induced damage was observed by ultrasonic C-scan and an optical microscope. Both tests gave essentially the same results for damage modes, sizes, and load-deformation history. First, a crack occurred in the bottom $0^{\circ}$ layer accompanying some delamination along the crack caused by bending stress. Then, transverse cracks occurred in the middle $90^{\circ}$ layer with decreasing contact force between the specimen and the indenter. Measured local strains near the impact point showed that the stress state changed from a bending dominant state to an in-plane tensile dominant state. A cohesive interface element was used to simulate the propagation of multiple delaminations and transverse cracks under static indentation. Two types of analytical models are considered, one with multiple delaminations and the other with both multiple delaminations and transverse cracks. The damage obtained for the model with only multiple delaminations was quite different from that obtained from the experiment. However, the results obtained from the model with both delaminations and transverse cracks well explain the characteristics of the damage obtained in the experiment. The existence of the transverse cracks is essential to form the characteristic impact damage.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.3
• /
• pp.440-449
• /
• 2003

Residual strength of fiber metal laminates after impact was studied. 3/4 lay up FML was fabricated using 4 ply prepreg, 2 ply aluminum sheets, and 1 ply steel sheet. Quasi isotropic ([0/45/90/-45]s) and orthotropic ([0/90/0/90]s) FRP were also fabricated to compare with FML. Impact test were conducted by using instrumented drop weight impact machine (Dynatup, Model 8250). Penetration load and absorbed energy of FML were superior to those of FRPs. Tensile tests were conducted to evaluate the residual strength after impact. Strength degradation of FML was less than that of FRP. This means that the damage tolerance of FML is excellent than that of FRP. Residual strength of each specimen was predicted by using Whitney and Nuismer(WN) Model. Impact damage area is assumed as a circular notch in WN model. Damage width is defined as the average of back face and top face damage width of each specimen. Average stress and point stress criterions were used to calculate the characteristic length. It is supposing that a characteristic length is a constant. The distribution of characteristic length shows that the assumption is reasonable. Prediction was well matched with experiment under both stress criterions.