• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.10a
• /
• pp.47-52
• /
• 2000

F.R.P specimens were made by mixture CM(chopped mat) 450-104 matrix & RC(roving clothes)570-100 Roving, the mixture ratio Resin: hardener (92:8) for tensile test. It was also made of plates by hand lay-up method and was been cured for 24 hours and then was cut tensile specimens in accordance with ASTM D638 Type 3. Knowing exact behavior of bonded area's stress and strain when the tensile test was going on, the test specimens were made of 2 plies laminae of F.R.P in each for supporting cut part in middle of specimen length. And in middle part also were covered of F.R.P plies of 1/2, 2/3 length of specimen in each as well. Also we consider shear stress in adhered area. This study reveals that as plys length is more longer, rupture stress grows remarkably larger.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.19 no.6
• /
• pp.439-447
• /
• 1999

One of the problems for practical use of fiber-reinforced plastics is the performance degradation by fatigue damage in the joints. The study is to develop a nondestructive technique for real-time evaluation of adhesively bonded composite-metal joints. From the prior study we confirmed that the bonding strength can be estimated from the correlation between the qualify of bonded parts and AUP's. We obtained a curve showing the correlation between the degree of fatigue damage and AUP's calculated from signals acquired during fatigue loading of single-lap and double-lap joints of CFRP and Al6061. The curve is an analogy to the one showing stiffness reduction ($E/E_o$) of polymer matrix composites by fatigue damage. From those facts, it is plausible to predict the degree of fatigue damage in real-time. Amplitude and AUP2 appeared to be optimal parameters to provide more reliable results for single-lap joints whereas Amplitude and AUP2 did for double-lap joints. It is recommended to select optimal parameters for different geometries in the application for real structures.

• International Journal of Korean Welding Society
• /
• v.4 no.1
• /
• pp.53-60
• /
• 2004

Adhesive-bonded joints are widely used in the industry. Recently, applications of adhesive bonding joints have been increased extensively in automobile and aircraft industry. The strength of adhesive joints is influenced by the surface roughness, adhesive shape, stress distribution, and etc. However, the magnitude of the influence has not yet been clarified because of the complexity of the phenomena. In this study, as the fundamental research of adhesive bonding joints, the effects of adhesive shape and loading speed on bonding strength properties and durability of aluminum to polycarbonate single-lap joints were studied. To evaluate the effect of adhesive shape, several modified shapes were used, and loading speeds were varied from 0.05 to 5mm/min. As a result, the load distribution showed a brittle fracture tendency. The trigonal edged single lap and bevelled lap joints showed the higher strength than the plain single lap, trigonal single lap, joggle lap and double lap joints in same adhesive area. The fractures of trigonal single lap and trigonal edged single lap joints that had the higher strength level were shown as the mixture type of the cohesive and interfacial-failure, mostly joggle lap joints that had the lower strength level were shown as the adhesive-failure.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.34 no.3
• /
• pp.44-50
• /
• 2006

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.6
• /
• pp.783-790
• /
• 2004

Adhesive-bonded joints are widely used in the industry. Recently, applications of adhesive bonding joints have been increased extensively in automobile and aircraft industry. The strength of adhesive joints is influenced by the surface roughness, adhesive shape, stress distribution, and etc. However, the magnitude of the influence has not yet been clarified because of the complexity of the phenomena. In this study, as the fundamental research of adhesive bonding joints, the effects of adhesive shape and loading speed on bonding strength properties and durability of aluminum to polycarbonate single-lap joints were studied. To evaluate the effect of adhesive shape, several modified shapes were used, and loading speeds were varied from 0.05 to 5 mm/min. As a result, the load-displacement distribution was shown a brittle fracture tendency. The trigonal edged single lap and bevelled lap joints showed the higher strength than the plain single lap, trigonal single lap, joggle lap and double lap joints in same adhesive area. The fractures of trigonal single lap and trigonal edged single lap joints that had the higher strength level were shown as the mixture type of the cohesive and interfacial-failure, mostly joggle lap joints that had the lower strength level were shown as the adhesive-failure.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.15 no.2
• /
• pp.357-363
• /
• 1995

Disbond size of adhesively bonded single lap and double lap joints CFRP composite specimens has been evaluated using acousto-ultrasonic(AU) technique. Frequency spectra for all specimens were obtained by measuring peak amplitude of the stress wave propagated through the bond-lines. By analyzing these frequency spectra, peak amplitude was found to be proportional to fractional bonding area and to be maxima at the fundamental and the third order higher harmonic frequencies of specimen thickness mode. The disbond size can be evaluated quantitatively and this technique can be applied to real structures if the reference specimens are prepared in advancve.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.10
• /
• pp.923-930
• /
• 2003

We jointed Bi(Pb)-Sr-Ca-Cu-O multifilament tapes and evaluated their electrical and mechanical properties. In order to improve connectivity of multifilaments, one or two single-filament tape was inserted between two multifilament tapes. The critical current ratio(CCR) and n-value of the jointed tapes were evaluated as a function of uniaxial pressure. It was observed that critical current ratio and n-value were 24.8-29.0% and 2.5-2.8 for MM lap-jointed tape. On the other hand, the corresponding values were improved to 24.7-53.9% and 3.1-4.2 for MSM jointed tape, and 63.4-76.0% and 3.4-5.1 for double MS:vr lap-jointed tape, respectively. The highest electrical properties of double MSM lap-jointed tape are considered to be owing to the presence of single core, causing better interconnections of multifilaments between the two tapes. The mechanical property of jointed tape was evaluated and correlated to the microstructural evolution. The strength of jointed tapes was 44-64% less than that of the unjoined tape. The strain tolerance of jointed tape was also reduced compared to that of the unjoined tape. These lower mechanical properties of jointed tape are probably due to the induced nonuniform microstructure such as the existence of cracks and Ag-intrusion in the joined region.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.1
• /
• pp.85-92
• /
• 2018

In order to use glued built up timber beam as a structural member for post and beam construction, it must be possible to manufacture long-span lumber. In this study, the researchers conducted a performance evaluation for longitudinal bonding of lumber (cross-section $89{\times}120mm$) made from larch. The specimens were prepared in six different forms using the longitudinal bonding method. The bonding strength of these specimens was tested through tensile strength tests and bending strength tests. The tensile strength test result of the longitudinally bonded parts was better than that of the double lap specimens. And, the tensile strength value of the scarf specimen was better than that of the hooked scarf specimen. The tensile strength of the GFRP (Glass Fiber Reinforced Plastic) rod insertion bonding specimen was 3.6 MPa, which was the highest. As for the bending strength test result of the longitudinally bonded part, the average MOR (modulus of rupture) of the specimen where a GFRP rod was inserted and bonded measured 29 MPa, while the specimens of other bonded parts showed a MOR no more than 11 MPa. Toughness destruction was observed in specimens where a GFRP rod was insertion-bonded. The rest of the specimens showed brittle destruction. The average MOR strength of the Rod + Lap specimen was 30.5 MPa, which was the highest among all longitudinally bonded specimens. The bending strength of the Rod + Lap specimens showed an effective strength that was 66% of that of the control group which were not longitudinally bonded.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.78-82
• /
• 2004

The co-cured joint has been widely used in joining process of composite structures due to its simple and easy manufacturing process. In this paper, the effect of stacking sequence of the carbon epoxy prepreg, bonding length and thickness of the aluminum plate on the static tensile load capability of the co-cured aluminum-composite double lap joint were experimentally investigated. From experimental results, the optimum EA ratios with respect to stacking sequence and bonding length of the co-cured joint were obtained, which may be useful for the joining of hybrid structures.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.11a
• /
• pp.57-60
• /
• 2005

Composite-to-aluminum joins were tested to get failure loads and modes for three types of joins; adhesive bonding, bolt fastening, and adhesive-bolt hybrid joining. Film type adhesive FM73 and paste type adhesive Cytec EA9394S were used for aluminum and composite bonding to make a double-lap joint. A digital microscope camcorder was used to monitor the failure initiation and propagation. It was found that the hybrid joining is an effective method to strengthen the joint when the mechanical fastening is stronger than the bonding as in the case of using the paste type adhesive. On the contrary, when the strength of the bolted joint is lower than the strength of the bonded joint as in the joint with the film type adhesive, the bolt joining contribute little to the hybrid joint strength.