• Transactions of Materials Processing
• /
• v.9 no.2
• /
• pp.193-202
• /
• 2000

The influence of rolling draughts on the formation of through-thickness textures in aluminum 5000X sheet was investigated by X-ray texture measurements and microstructure observations. In order to intensify the deformation inhomogeneities, cold rolling was performed without lubrication. Applying a large draught gave rise to the formation of the shear texture at the surface, whereas a normal plane strain testure formed at the surface after deformation with a small draught. The orientation density along the $\beta$-fiber orientations which developed in the center layer of the rolled specimen was also dependent on the strain gradients in a roll gap. Upon annealing, the deformed substructure of sample surfaces was transformed into a fine grained recrystallized microsturcture through extended recovery reaction. However, coarse grains developed after the discontinuous recrystallization which gave rise to the development of the Cube-texture.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.11
• /
• pp.1844-1853
• /
• 2001

In the present investigation, it was attempted to design the rolling pass schedule fur a clean steel of 0.1C-1.5Mn-0.25Si with the objective of the austenite grain refinement. As the method of approach, a coupled mathematical modeling technique was proposed which consists of a recrystallization model and a flow stress modes. The validity of the coupled model was examined through comparison with results of continuous and discontinuous compression tests at various temperatures, strains and strain rates. The coupled model was incorporated with the finite element method to set up a systematic design methodology far the rolling path schedule for austenite grain refinement. Two path schedules were obtained and discussed in the paper with regard to rolling path time, average grain size, grain size deviation in thickness, etc.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.05a
• /
• pp.53-56
• /
• 2003

The disappearance of continuous yielding and the formation of an extended region in engineering stress-strain curves at tempering temperatures of 673-873K is closely related to the reduction of mobile dislocations during tempering and dynamic recovery during tensile deformation. In addition, the occurrence of discontinuous yielding at tempering temperature above 923K would be attributed to the formation of new strain-free polygonal ferrite grain.

• Transactions of Materials Processing
• /
• v.12 no.8
• /
• pp.744-749
• /
• 2003

The effect of tempering temperatures on microstructures and mechanical properties was studied in a low carbon steel. The disappearance of continuous yielding and the formation of an extended region in engineering stress-strain curves at tempering temperatures ranging from 673 to 873K was caused by the reduction of mobile dislocations during tempering and dynamic recovery during tensile deformation. In addition, the occurrence of discontinuous yielding in the sample treated at the tempering temperatures above 923K was attributed to the formation of new strain-free polygonal ferrite grain.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.05a
• /
• pp.176-179
• /
• 2001

A simple cold pressing procedure which allows shear deformations on sheet metals is proposed by designing dies with grooves and applied to aluminum 3003 sheets. shear deformation led to the formation of preferred orientation along <100>//RD, and the effect of initial tortures on the formation of shear textures was also studied Rectangular shaped dislocation cells formed in the deformed microstructure and boundaries of dislocation cells gradually rounded with the increased plastic strain. Upon subsequent annealing textures inherited deformation textures. Recrystallized grains consisted of a large number of fully recovered subgrains with well defined boundaries which persisted even after annealing at a higher temperature.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.172-175
• /
• 2006

Effects of deformation at austenite non-recrystallization region and cooling rate on the microstructure and mechanical properties of low carbon (0.06 wt. %) high strength low alloy steels have been investigated. Average grain size decreased and polygonal ferrite transformation promoted with increasing deformation amount due to increase of ferrite nucleation site. As cooling rate increased, the major microstructure changed from polygonal ferrite to acicular ferrite and the fraction of M/A constituents gradually increased. Discontinuous yielding occurred in highly deformed specimen due to the formation of polygonal ferrite. However, small grain size of highly deformed specimen caused lower ductile-to-brittle transition temperature than slightly deformed specimen.

• Korean Journal of Materials Research
• /
• v.24 no.11
• /
• pp.585-590
• /
• 2014

Microstructural evolution in the thickness direction of an oxygen free copper processed by accumulative rollbonding (ARB) is investigated by electron back scatter diffraction (EBSD) measurement. For the ARB, two copper alloy sheets 1 mm thick, 30 mm wide and 300 mm long are first degreased and wire-brushed for sound bonding. The sheets are then stacked and roll-bonded by about 50% reduction rolling without lubrication at an ambient temperature. The bonded sheet is then cut to the two pieces of the same dimensions and the same procedure was repeated on the sheets up to eight cycles. The specimen after 1 cycle showed inhomogeneous microstructure in the thickness direction so that the grains near the surface were finer than those near the center. This inhomogeneity decreased with an increasing number of ARB cycles, and the grain sizes of the specimens after 3 cycles were almost identical. In addition, the aspect ratio of the grains decreased with an increasing number of ARB cycles due to the subdivision of the grains by shear deformation. The fraction of grains with high angle grain boundaries also increased with continuing process of the ARB so that it was higher than that of the low angle grain boundaries in specimens after 3 cycles. A discontinuous dynamic recrystallization occurred partially in specimens after 5 cycles.