• Journal of the Korean Ceramic Society
• /
• v.39 no.6
• /
• pp.582-588
• /
• 2002

IrO$_2$-RuO$_2$ films were deposited on plasma sprayed TiO$_2$ buffer layer above Ti metal by sol-gel and dip-coating method. Organic vehicle (ethyl cellulose and $\alpha$-terpineol) and glass frit were added to improve adherence of the coatings. Taguchi method and L$_{18}$ (2$^1$$\times$3$^{7}$ ) orthogonal arrays were evalvated in terms of current density to determine the optimal combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed conditions were as fellows: ethyl cellulose (100 cp), drying temperature and time (17$0^{\circ}C$,20 min), heat treatment temperature and time (75$0^{\circ}C$,10 min), the weight ratio of IrO$_2$-RuO/powders to glass frit (99:5), final heat treatment time (120 min) and flow rate of air (5 sccm), respectively. ANOVA analysis suggested that the influence of the factors within $\alpha$= 0.1 was significant with a 90% confidence level.

• Korean Chemical Engineering Research
• /
• v.50 no.3
• /
• pp.562-566
• /
• 2012

A novel design of tubular segmented-in-series(SIS) solid oxide fuel cell (SOFC) sub module was presented in this paper. The tubular ceramic support was fabricated by the extrusion technique. The NiO-YSZ anode and the yttria-stabilized zirconia (YSZ) electrolyte were deposited onto the ceramic support by dip coating method. After sintering at $1350^{\circ}C$ for 5 h, a dense and crack-free YSZ film was successfully fabricated. Also, the multi-layered cathode composed of LSM-YSZ composite, LSM and LSCF were coated onto the sintered ceramic support by dip coating method and sintered at $1150^{\circ}C$. The performance of the tubular SIS SOFC cell and sub module electrically connected by the Ag-glass interconnect was measured and analysed with different fuel flow and operating temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.332-332
• /
• 2010

We have successfully demonstrated the inkjet printing method to create $Al_2O_3$ films withouWe have successfully demonstrated the inkjet printing method to create $Al_2O_3$ films without a high temperature sintering process. In order to remove the coffee ring effect in the ink drop, we have introduced a co-solvent system in order to create Marangoni flow in the ink drop, which leads to the dense packing of ceramic powders on the substrate during inkjet process. The packing density of the Inkjet-printed $Al_2O_3$ films is around 60% (max. 70%) which is very high compared to the value obtained from the same material films by other conventional methods such as film casting, dip coating process, etc. The voids inside the films (which are around 40% of the entire film volume) are filled with the polymer resin (Cyanate ester) by the infiltration process. This resin infiltration is also implemented by the inkjet printing process right after the Ah03 film ink-jetting process. The microstructures of the printed $Al_2O_3$ films are investigated by Scanning Electron Microscope (SEM) to understand the degree of packing density in the printed films. The inkjet-printed $Al_2O_3$ films have been characterized to investigate its thickness and roughness. Quality factor of the printed $Al_2O_3$ film is also measured to be over 300 at 1MHz.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.1
• /
• pp.56-62
• /
• 2021

In this study, we created a DBD plasma device and a MnO2 catalyst mesh filter for evaluating ozone reduction of devices via the catalyst method. The DBD plasma device was manufactured by applying Ag paste to soda lime glass via the screen-printing method. The MnO2 catalyst mesh filter was manufactured by mixing MnO2 powder with binder with a 10% difference in concentration from 10% to 50% and then applying it using the dip-coating method. Finally, we sintered a MnO2 catalyst mesh filter in an electric furnace. We evaluated the characteristics of ozone generation according to the Ar gas flow of DBD plasma devices, the opening ratio, and ozone reduction performance of the MnO2 catalyst filters. Ozone reduction performance was approximately 20.4% at MnO2 10 wt%, 37.8% at MnO2 30 wt% and 50% at MnO2 50 wt%.