• Journal of Powder Materials
• /
• v.11 no.5
• /
• pp.383-390
• /
• 2004

In order to investigate behavior of abnormal expansion of the iron-copper compacts, we compared the dilatometric curves of the compacts which mixed the copper powder to the iron powder with those of compacts which mixed the copper powder to the iron-copper alloy powder. The dilatometric curves were obtained below the sintering conditions, which heated up to 115$0^{\circ}C$ by a heating rate of 1$0^{\circ}C$/min, held for 60min at 115$0^{\circ}C$ and cooled down at a rate of 2$0^{\circ}C$/min to room temperature. The dilatometric curves of the compacts showed the different expansion behavior at temperatures above the copper melting point in spite of same chemical composition. All of the compacts of former case showed large expansion, but all of the compacts in latter case showed large contraction. The microstructures of sintered compacts also showed the different progress in alloying of the copper into the iron powder. Namely we could observe the segregation at alloy part of copper into iron powder in case of the sintered compacts, which mixed the copper powder to the iron powder, but could not observe the segregation in compacts which mixed the copper powder to the iron-copper alloy powder. But the penetration of liquid copper into the interstices between solid particles was occurred at both cases. Therefore, the showing of the different dimensional changes in the compacts in spite of same chemical composition is due to more the alloying of copper into iron powder than the penetration of liquid copper into the interstices between solid particles.

• The Korean Journal of Ceramics
• /
• v.5 no.4
• /
• pp.414-418
• /
• 1999

The synthesis of polycrystalline $Al_2TiO_5$ ceramics with low thermal expansion by fusion in an electric arc furnance was investigated. The thermal expansion curves of $Al_2TiO_5$ ceramics were lowered because of microcracks caused by the strong thermal expansion anisotropy of the crystal axes and were accompanied by hysteresis curves. These phenomena are explained by the opening and closing of microcracks. The difference in microcracking temperatures of dilatometric cooling curves in the range of 400~$620^{\circ}C$ is caused by the difference in sintering temperature, grain size and stabilization status.

• Journal of the Korean Ceramic Society
• /
• v.27 no.2
• /
• pp.288-296
• /
• 1990

Parent glasses for the experiments were prepared to be ratio of Li2O : Al2O3 : SiO2=4.5 : 25 : 70.5 as basic components, and TiO2 and ZrO2 in the mixing ratio of 1 : 1 were added as the nucleating agents, whose contents were increased in each sample. DTA, XRD, SEM, IR were observed, and thermal expansion and transmissivities were measured for the crystallized samples under the controlled heat-treatments. The transformation temperatures and the dilatometric softening temperatures in thermal expansion curves, and also the exothermic peaks in differential thermo-analytical curves were shifted to lower temperature. The crystal phase deposited through the heat-treatment was identified as ${\beta}$-quartz solid solution with XRD and IR analysis. The crystalline phases in oopactified samples were ${\beta}$-spodumene coexiting with ${\beta}$-quartz solid solution. The samples having more than 3% nucleating agents were transparent. The crystallized grain sizes were ranged 0.05 to 0.1$\mu\textrm{m}$. The crystallized transparent samples were exceeded 85% in the transmissivity.

• Journal of Powder Materials
• /
• v.7 no.2
• /
• pp.93-101
• /
• 2000

In order to clarify the enhanced sintering behavior of nanostructured(NS) W-Cu powder prepared by mechaincal alloying, the sintering behavior during heating stage was analysed by a dilatometry with various heating rates. The sintering of NS W-Cu powders was characterized by the densification of two stages, having two peaks in shrinkage rate curves. The temperature at which the first peak appear was much lower than Cu melting point, and dependent on heating rate. On the basis of the shrinkage rate curves and the microstructural observation, the coupling effect of nanocrystalline W-grain growth and the liquid-like behavior of Cu phase was suggested as a possible mechanism for the enhanced sintering of NS W-Cu powder in the state.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.812-813
• /
• 2006

Dimensional change of compact made from (Fe-Cu) prealloyed powder and copper powder compared to that of compact made from iron-copper elemental powder. The compact made from the prealloyed powder with a copper content of 7.18mass% which is nearly equal to its solution limit and copper powder showed only the large contraction in spite of penetration of liquid copper into grain boundary of the prealloyed powder. But the compact made from iron-copper elemental powder showed the large expansion in spite of same chemical composition with former case.