• Journal of the Korean GEO-environmental Society
• /
• v.13 no.12
• /
• pp.17-25
• /
• 2012

In this study, dielectrical constant of the ground was measured using TDR method and correlated with water contents and density of ground. In order to evaluate the applicability as a cavity exploration, model experiments were carried out to analyze the effects of cavity size on the dielectrical constant. Test result indicated that dielectrical constant of the ground tended to linearly increase with the increase in water contents and density, which can be represented in a certain relational expression. Also, the dielectrical constant of ground varied sensitively with the cavity size of ground. The results conclude that the dielectrical constant, water contents and density of the ground proved to have a correlation among them, and the dielectrical constant is expected to be a basic data on cavity exploration.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.34 no.8
• /
• pp.323-330
• /
• 1985

Dielectric loss tangent and ac dielectric strength of GFRP (Glass Fiber Reinforced Plastics, G-10)was investigated as parameters of mechanical and thermal stresses, in order to study the basic dielectrical characteristics of composite insulating materials. The dielectric loss tangent was increased and the ac dielectric strength was decreased with increase in the mechanical stresses beyond the mechanical yield point on account of fiber-matrix debonding, but the dielectric constant was not varied sigificantly. the dielectric strength of G-10 was about 2 MV/cm and the dielectric constant was about 4.8.

• Proceedings of the KIEE Conference
• /
• 1991.11a
• /
• pp.316-320
• /
• 1991

The dielectric properties of the ZnO varistor fabricated by the method of 3-composition seed grain was studied. In this paper, we present the C-V charateristic for the specimen. The dielectric constant and disppation which changed with additives may be explained on the basis of the deplation layer; the presence of deplation layer has been inferred by donor and state density obtained from the $1/C^2$ vs. V.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.5
• /
• pp.397-404
• /
• 2001

This study describes the effect of γ-ray irradiation on the properties of insulation materials for low voltage cables in a nuclear power plant. The radiation effects were characterized by measuring OIT, FTIR, electrical properties of the irradiated specimens. As a result, they showed the decrease of OIT and the increase of chemical structural defects with the increase of γ-ray amount. Also, the electrical properties such as dielectrical constant, tan $\delta$ and current were changed by aging. These changes may come from the increase of chemical structural defects by $\delta$-ray irradiation.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.158-162
• /
• 1997

In this paper, the electrical and dielectrical properties were investigated in Pb(Zr,Ti)O$_3$-Pb(Mn,Nb)O$_3$ ceramics which are manufactured with the substitution of Ba in site Pb. In older to increase the del and Kp , Ba was substitued to site Pb from 0 to 0.1 by 0.02 mol%. As the Ba substitution is increased, dielectric constant is increased and electricmachanical coupling factor showed the maximum value at Ba 0.06mol% and the mechanical qualify factor is decreased and the tetragonality and the grain size are decreased as the Ba substitution.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.288-291
• /
• 2002

An alkoxide-based sol-gel method was used to fabricate $(Pb_{x},Sr_{1-x})$TiO3 (PST) thin films on a Pt/Ti/SiO2/Si substrate, and the dielectric properties of the PST thin films were investigated as a function of the Pb/Sr composition for use in tunable microwave device applications. The dielectric properties of the PST films were strongly dependent on the Pb/Sr ratio. The dielectric constant and dielectric loss of the PST films increased with increasing Pb content, and the figure of merit (FOM) reached a maximum value of 27.5 at a Pb/Sr ratio of 4:6. The tunability increased with increasing Pb content. The dielectric constant, loss factor, and tunability of PST (50/50) thin films were 404, 0.023, and 51.73%, respectively. From the result, the PST films with good dielectric properties are useful candidates for tunable microwave device.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.123-130
• /
• 1997

In this study, (Sr.Pb.Ca)TiO3-Bi2O3.3TiO2(SPCT) systems were investigated to develop a new material which has a high dielectric constant, a low dielectric loss and a small TCC(Temperature Coefficient of Capa-citance), and are suitable for high voltage applications as a function of the additions of Bi2O3.3TiO2 from 5 mol.% to 9 mol.%. The result obtained from our investigation showed that up to 6 mol.% Bi2O3.3TiO ad-dition the dielectric constant increased and it deteriorated at higher concentrations with increasing amount of the acicular grains. As a result of some dopants (SiO2, Nb2O3, MnO2) addition to SPCT, the specimens with MnO2 showed good dielectric properties. The dielectric constant decreased, but the TCC was improved with the addition of MnO2 from 0.15 wt.% to 0.45 wt. %.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.48 no.7
• /
• pp.514-520
• /
• 1999

Ferroelectric PZT(30/70)/PZT(70/30) heterolayered thin films were fabricated by spin-coating method on the $Pt/Ti/SiO_2Si$ substrate alternately using(30/70) and PZT(70/30) alkoxide solutions prepared by sol-coating method. The coating and heating procedure was repeated six times to form PZT heterolayered films, and thickness of the film obtained by one-times drying/sintering process was about 40-50 nm. All PZT heterolayered films, showed dense and homogeneous structure without the presence of rosette sturctrue. The relative dielectric constant, remanent polarization and leakage current density of PZT heterolayered films were superior to those of single composition PZT(30/70) and PZT(70/30) films, and those values for the PZT-6 film were 975, $21 \muC/cm^2\; and\; 8\times10^{-9}\; A/cm^2$, respectively. And the PZT-6 heterolayered film showed fairly good fatigue characteristics of remanent polarization and coercive field after application of $10^8$ switching cycles.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.10
• /
• pp.796-801
• /
• 2001

Ferroelectric 0.05PZN-xPZT(90/10)-(0.95-x)PZT(10/90) (x=0.65, 0.85) specimens were fabricated by the solid-state reaction method, and especially PZT(90/10) and PZT(10/90) powders were derived by the sol-gel method. All specimens showed a uniform ferroelectric grain without the presence of the pyrocholre phase. Average grain size increased with an increased in sintering temperature, the values for the x=0.65 and x=0.85 specimens sintered at 125$0^{\circ}C$ were 14.4$\mu$m and 9.8$\mu$m, respectively. The dielectric constant and dielectric loss of the x=0.65 specimen sintered at 125$0^{\circ}C$ were 1247. 2.06%, respectively. The coercive field and the remanent polarization of x=0.65 and x=0.85 specimens sintered at 125$0^{\circ}C$ were 8.5kV/cm, 13$\mu$C/$\textrm{cm}^2$ and 17.2kV/cm, 28 $\mu$C/$\textrm{cm}^2$, respectively. The pyroelectric coefficient of the x=0.65 and x=0.85 specimens sintered at 125$0^{\circ}C$ were 5.64$\times$10$^{-8}$ C/$\textrm{cm}^2$K and 2.76$\times$10$^{-8}$ C/$\textrm{cm}^2$K, respectively.

• Proceedings of the KIEE Conference
• /
• 1988.07a
• /
• pp.799-801
• /
• 1988

This paper was studied on the effects of Ca-La-Nb substitution and Zr/Ti ratio variation to Pb(Zr, Ti)$O_3$ system on structural, electrical, optical and sound level characteristics in order to develope the piezoelectric and electrooptic ceramic devices. Also the specimens were prepared by the two stage sintering technique. The molecular formular was X($CaO{\cdot}1/4La_{2}O_{3}{\cdot}1/4Nb_{2}O_{5}){\cdot}(1-X)Pb(Zr_{Y}Ti_{1-Y})O_{3}$(x=100X, y=100Y), and the variation of x was $6{\sim}12$, y was 60${\sim}$49 and second stage sintering time was 20${\sim}$40 hours. The experimental results obtained from this study are as follows : 1. The density was decreased, the grain size was increased according to increase of Ca-La-Nb substitution. 2. The crystal structure was rhombohedral in composition 6/60/40, and the crystal structure was tetragonal and cubic according to increase of Ca-La-Nb substitution. 3. The Ca substitution of PZT system enhanced the sintering property. The Pb site vacancy resulting from the substitution of La-Nb increased the dielectrical constant, the piezoelectric charge constant, the dielectric loss and decreased the coercive field. 4. The resistivity of PZT system which has the P type conduction mechanism increased according to substitution of La-Nb because of the substituent acting as donor. 5. The PZT ceramics varied from ferroelectric substance according to increase of Ca-La-Nb substituent. The coercive field and saturation remanent polarization decreased, and at last straight line according to increase of La-Nb substitution. 6. The amount of Ca-La-Nb substitution to improve the light transmittance of speciment was 10 mol%, the Zr/Ti ratio was 49/51, and the second stage sintering time was 40 hours. 7. According to Ca-La-Nb substitution, the specimens was to be transparent. The 7.5/51/49 specimen was suitable for transparent sound vibrator because it had 58% light transmittance (thick 0.2[mm], wave length 700[mm]) and 48% electromechanical coupling factor.