• Korean Journal of Materials Research
• /
• v.19 no.4
• /
• pp.198-202
• /
• 2009

For use in ultrasonic actuators, we investigated the structural and piezoelectric properties of $(1\;-\;x)Pb(Zr_{0.515}Ti_{0.485})O_3$ - $xPb(Sb_{1/2}Nb_{1/2})O_3$ + 0.5 wt% $MnO_2$ [(1 - x)PZT - xPSN + $MnO_2$] ceramics with a variation of x (x = 0.02, 0.04, 0.06, 0.08). All the ceramics, which were sintered at $1250^{\circ}C$ for 2 h, showed a typical perovskite structure, implying that they were well synthesized. A homogeneous micro structure was also developed for the specimens, and their average grain size was slightly decreased to $1.3{\mu}m$ by increasing x to 0.8. Moreover, a second phase with a pyrochlore structure appeared when x was above 0.06, which resulted in the deterioration of their piezoelectric properties. However, the 0.96PZT-0.04PSN+$MnO_2$ ceramics, which corresponds with a morphotropic phase boundary (MPB) composition in the (1 - x)PZT - xPSN + $MnO_2$ system, exhibited good piezoelectric properties: a piezoelectric constant ($d_{33}$) of 325 pC/N, an electromechanical coupling factor ($k_p$) of 70.8%, and a mechanical quality factor ($Q_m$) of 1779. The specimens with a relatively high curie temperature ($T_c$) of $305^{\circ}C$ also showed a significantly high dielectric constant (${\varepsilon}_r$) value of 1109. Therefore, the 0.96PZT - 0.04PSN + $MnO_2$ ceramics are suitable for use in ultrasonic vibrators.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.1
• /
• pp.1-7
• /
• 2021

This study investigated the structural, dielectric, ferroelectric, and strain properties of (0.98-x)Bi1/2Na1/2TiO3-0.02BiFeO3-xSrTiO3 (BNT-BF-100xST, x＝0.20, 0.22, 0.24, 0.26, and 0.28). All samples were successfully synthesized using the conventional solid-state reaction method and sintered at 1,175℃ for 2 h. The average grain size of the BNT-BF-100x ceramics decreased with increasing ST content. Furthermore, we observed that the ferroelectric- relaxor transition temperature (TF-R) decreased with increasing ST content, which eventually vanished in the BNT-BF-24ST ceramics. The results indicated that a ferroelectric to relaxor phase transition could be induced by ST modification. Consequently, a large electromechanical strain of 633 pm/V at 4 kV/mm was observed for the BNT-BF-26ST ceramics. These results imply that our materials have the competitive advantage of larger strain under lower operating field conditions compared with other BNT-based lead-free piezoelectric ceramics. We expect that BNT-BF-ST lead-free piezoelectric ceramics are promising candidates as a novel ternary BNT-based system and can find potential applications in actuators.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.4
• /
• pp.626-633
• /
• 1998

For the fabrication of low temperature cofirable glass/ceramic with high dielectric constant, crystallizing glass [$SiO_2-TiO_2-RO (RO:BaO, CaO:SrO)$] was formed. The glass/ceramic composites were made by mixing this glass and alumina ceramic as filler, and its characteristics was investigated. With this glass compositon, it was possible to fabricate the glass which could be crystallized under $900^{\circ}C$. And it was found that the crystallizing temperature was changed in accordance with the composition of RO in glass. By adding $Bi_2O_3$ as flux, using $Al_2O_3$ as filler and sintering at $860^{\circ}C$, low temperature cofirable glass/ceramic with high dielectric constant was fabricated. The density of that composites was 3.96 g/$\textrm{cm}^3$, dielectric constant was 17 and Q. f was 600.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.6
• /
• pp.478-484
• /
• 2000

The structural changes and the microwave dielectric properties of $Ba_{1-x}$/A$_{x}$/(Mg$_{1}$3//Nb$_{2}$3/)O$_3$(A=Sr, Ca=x0, 0.2, 0.4, 0.6, 0.8, 1.0) were investigated. The densities of samples are gradually decreased with increasing x(BMN=6.1, SMN=5.22 and CMN=4.26 g/m$^3$)The crystal structure of BMN was untilting of oxygen octahedral. The structural changes of BSMN showed the antiphase tilting at x>0.4, and those of BCMN showed the antiphase tilting at 0.20.8. The variation of dielectric constant with Sr was small(BMN=32, SMN=30) However the variation with Ca was large the highest value was 42 at Ca=0.2(CMN=25) The maximum quality factor was 68,000 GHz at Sr=0.2 and the minimum quality factor was 3,000 GHz at Ca=0.2 (BMN=35,000, SMN=20,000 and CMN=23,000 GHz) The temperature coefficients of resonant frequency of BSMN were about 2 times larger than those of BCMN in all composition.ion.

• Korean Journal of Materials Research
• /
• v.5 no.1
• /
• pp.36-41
• /
• 1995

Dielectric properties were investigated at Mn doped $(Pb_{1-x}Ca_{x})ZrO_{3}$ with x=0.38 in microwavefrequencies. Both the density and Q values of sintered ceramics increased with increasing calciningtemperature. In the sample sintered at $1300^{\circ}C$ for 2 hrs, the deped Mn ions completely solubled in $(Pb,Ca)ZrO_{3}$ phase until 0.5wt% and the grain size was independent of doping amount. It was observed thathigh dielectric constant of 90 - 100 and high quality factor of 1300 at 4 GHz for O.l5wt% Mn doped$(Pb_{0.62}Ca_{0.38})ZrO_{3}$. The Mn" and Mn" worked as acceptors in $(Pb,Ca)ZrO_{3}$ which created the oxygen vacancies and affected the increment of the Q values. However, the excess Mn doping more than 0.5wt% resulted in decreasing Q values.decreasing Q values.

• The Korean Journal of Ceramics
• /
• v.3 no.4
• /
• pp.274-278
• /
• 1997

(Ba, Sr) TiO$_3$(BST) thin films were prepared on RuO$_2$/Si substrates by rf magnetron sputtering and annealing was followed at temperatures ranging from 550 to 80$0^{\circ}C$ in $N_2$or $O_2$atmosphere. The effects of annealing conditions on the properties of BST film deposited on RuO$_2$bottom electrodes were investigated. It was found that the crystallinity. surface roughness, and grain size of BST films vary with the annealing temperature but they are not dependent upon the annealing atmosphere. The flat region in the current-voltage (I-V) curves of BST capacitors shortened with increasing annealing temperature under both atmospheres. This is believed to be due to the lowering of potential barrier caused by unstable interface and the increase of charge The shortening of the flat region by $O_2$annealing was more severe than that by $N_2$-annealing. As a result, there was no flat region when the films were annealed at 700 and 80$0^{\circ}C$ in $O_2$atmosphere. The dielectric properties of BST films were improved by annealing in either atmosphere. however, a degradation with frequency was observed when the films were annealed at relatively high temperature under $O_2$atmosphere.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.2
• /
• pp.152-164
• /
• 1995

$xPb(Fe_{1/2}Nb_{1/2})O_3 - (1 - x)Pb(Mg_{1/3}Nb_{2/3})O_3$ powders were synthesized by the molten salt synthesis method using the NaC!- KCI flux with 1 : 1 molar ratio, and their powders and dielectric properties were investigated. The synthesized powders showed less agglomerated shape with the average particle size of less than $2 \mu\textrm{m}$. The composition $x0.3Pb(Fe_{1/2}Nb_{1/2})O_3-0.7Pb(Mg_{1/3}Nb_{2/3})O_3$ could be sintered at $1000{\times}C$ and its dielectric constnat was over 11, 000.

• Journal of the Korean Ceramic Society
• /
• v.38 no.3
• /
• pp.280-286
• /
• 2001

10 이하의 저유전율을 갖는 (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x=0.1~0.9) 세라믹스의 미세구조와 고주파 유전특성을 조사하였다. (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x=0.1~0.9) 세라믹스는 정방정(tetragonal) 구조를 가진다. 0.1BaWO$_4$-0.9Mg$_2$SiO$_4$세라믹스는 BaWO$_4$와 $Mg_2$SiO$_4$의 상들이 공존하는 혼합상을 보였으며, $Mg_2$SiO$_4$가 이차사으로 형성된 것이 관찰되었다. 120$0^{\circ}C$~140$0^{\circ}C$에서 2시간 동안 소결된 (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x=0.1~0.9) 세라믹스는 $\varepsilon$$_{r}$=6.37~8.21, Q.f=15000~99422 그리고 $ au$$_{f}$=73.9~48.9 ppm/$^{\circ}C$의 고주파 유전특성을 가졌다. $\tau$$_{f}$를 보정하기 위해, CaTiO$_3$(1,5 wt%)가 (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x$\geq$0.9) 세라믹스에 첨가되었다. 135$0^{\circ}C$에서 2시간 동안 소결된 0.1BaWO$_4$-0.9Mg$_2$SiO$_4$+CaTiO$_3$(5 wt%) 세라믹스는 $\varepsilon$$_{r}$=7.3, Q.f=30532 그리고 $\tau$$_{f}$=-30 ppm/$^{\circ}C$의 고주파 유전특성을 얻었다. 얻었다.

• Journal of the Korean Chemical Society
• /
• v.40 no.9
• /
• pp.607-614
• /
• 1996

The structural changes and dielectric properties of Pb1-x(Na1/2La1/2)x(Mg1/3Nb2/3)O3 compounds substituted by 0∼50 mol.% of Na+/La3+ mixed ions were investigated by X-ray diffraction method, IR and Raman spectroscopy, and LCR meter. The amount of perovskite phase increased with the increases of Na+/La3+ substituents and sintering temperatures. Although the superlattice lines due to 1:1 ordering were not detected by X-ray diffraction method, it was found, from the Raman spectroscopy and the increase of diffuseness coefficient, that the ordering behavior was related to the decrease of A site ion size. Dielectric properties in Pb1-x(Na1/2La1/2)x(Mg1/3Nb2/3)O3 were affected by the amount of perovskite phase, grain size, and density. The phase transitions were broadened and phase transition temperatures were lowered by the increase of Na+/La3+ ions.

• Korean Journal of Materials Research
• /
• v.15 no.12
• /
• pp.756-759
• /
• 2005

A lead free piezoelectric material, bismuth sodium barium titanate $(Bi_{0.5}Na_{0.5})_{0.94}Ba_{0.06}TiO_3$ (BNBT), was considered as an environment-friendly alternatives for the current PZT system. A perovskite BNBT was synthesized by conventional bulk ceramic processing technique. In order to improve piezoelectric properties, $La_2O_3$ as a dopant was incorporated into the BNBT system up to 0.025 moi, ana the effects on subsequent the piezoelectric ana dielectric properties were systematically investigated. With increasing $La_2O_3$ contents, the equilibrium grain shape was remarkably evidenced and sintered density was increased. Piezoelectric and dielectric properties were s]town to have maximum values at the $La_2O_3$ contents of 0.02 mol. $La^{3+}$ ions seemed to act as a softener in the BNBT system and to enhance dielectric and piezoelectric properties in this study.