• Design & Manufacturing
• /
• v.2 no.4
• /
• pp.32-36
• /
• 2008

Roll forming process for the bumper beam of high strength steel is developed by an experimental method. The size of the bumper beam is reduced to 1/1.8 to save development time and cost. The developed forming rolls are installed in the small three-stage roll forming machine and roll forming experiments are carried out. It is found that the experimental method using small forming machine is effective in developing roll forming process for the bumper beam of high strength steel.

• Journal of Biosystems Engineering
• /
• v.35 no.5
• /
• pp.336-342
• /
• 2010

This study was performed to develop extrusion pelletizer for pelletizing the compost waste food. The effect of water content on the shape of pellet, the relationship between diameter of pellet and of extrusion hole and the relationship between extrusion force and die angle were investigated. Considering the stable shape of compost pellet and the operation efficiency of pelletizer, the water content of 2~4% was considered as the best condition. And the compost pellet could not maintain it's shape at the water content of 10% or over. The strongest extrusion force was needs when the die angle had $90^{\circ}C$ in 6 mm extrusion hole diameter, on the other hand, the weakest extrusion force was need at the die angle of $45^{\circ}{\sim}65^{\circ}$. The compression strength of pellet shows the highest strength of 9.2Mpa when we make the compost pellet after screening the compost and make it with a size of 1.18 mm(No.16) or less.

• Journal of Korea Foundry Society
• /
• v.13 no.3
• /
• pp.259-267
• /
• 1993

The effects of casting processes-direct and indirect squeeze casting, permanent mold casting and die casting on the microstructure and mechanical properties were studied for the hypereutectic B390 aluminium alloy. The effects of T5 and T6 heat treatment were also examined. The direct and indirect squeeze casting showed no casting defects such as porosity and shrinkage were observed in permanent mold castings and die castings. The primary silicon phase was refined and homogeneously distributed in the order of indirect squeeze casting, diecasting, direct squeeze casting and permanent mold casting. Depletion of primary silicon phase in die casting surface was disappeared in indirect squeeze casting. Tensile strength of cast and heat treated specimens were increased in the order of direct squeeze casting, permanent mold casting, indirect squeeze casting and die casting. Hardness of indirect squeeze castings was larger than that of other castings. As indirect squeeze casting of B390 aluminium alloy, the time of T6 heat treatment to achieve high strength can be reduced.

• Design & Manufacturing
• /
• v.10 no.1
• /
• pp.12-18
• /
• 2016

Although magnesium alloy has received much attention to date for its lightweight and high specific strength, their applications are impeded by the low formability which is caused by the hexagonal crystal structure at room temperature. In general, equal-channel angular extrusion(ECAE) is recognized as one of the attractive severe plastic deformation techniques where the processed bulk metals generally achieve ultrafine-grained microstructure leading to improved physical characteristics and mechanical properties. ECAE process has several parameters such as angle of die, process temperature, process route and speed. During ECAE process of Mg alloy, these parameters has great influence on the extrudability and the mechanical properties of alloy. The aim of this study is to estimate the influences of process conditions on the formability of AZ31 and AZ31-CaO alloys. Mg alloys are processed through ECAE at elevated temperatures using three types of die with channel angle of $90^{\circ}$, $110^{\circ}$, $135^{\circ}$ using route $B_c$, respectively. This study discusses the feasibility of using ECAE to improve both formability and strength on magnesium alloys by comparative analyzing the mechanical properties and microstructural evolution in each condition.

• Journal of the Korean Society of Industry Convergence
• /
• v.21 no.6
• /
• pp.419-427
• /
• 2018

In case high strength steels are applied for press-formed automotive parts, it is very difficult to secure forming accuracy due to large springback compared to moderate strength steels. In this study, a repetitive step-wise forming analyses based on secant method was proposed as the die design method for mandrel(bending tool) for the 2-axis bending equipments. A bending die with circular mandrel was designed for the DP780 blow motor case of which diameter and thickness are 70.8mm and 2.0mm respectively. Forming tests were performed to verify the validity of established die design and the results were compared with that of conventional HGI(Hot galvanized iron steel) blow motor case. For additional improvement in forming accuracy, an elliptical mandrel was proposed and its validity was verified using forming analyses based on secant method.

• Design & Manufacturing
• /
• v.17 no.3
• /
• pp.15-20
• /
• 2023

In the fine blanking process, which is a press operation known for producing parts with narrow clearances and high precision through the application of high pressure, die roll often occurs during the shearing process when the punch penetrates the material. This die roll phenomenon can significantly reduce the functional surface of the parts, leading to decreased product performance, strength, and fatigue life. In this research, we conducted an in-depth analysis of the factors influencing die roll in the curvature area of the fine blanking process and identified its root causes. Subsequently, we designed and experimentally verified a die roll reduction process specifically tailored for the door latch manufacturing process. Our findings indicate that die roll tends to increase as the curvature radius decreases, primarily due to the heightened bending moment resulting from reduced shape width-length. Additionally, die roll is triggered by the absorption of initial punch energy by scrap material during the early shearing phase, resulting in lower speed compared to the product area. To mitigate the occurrence of die roll, we strategically selected the Shaving process and carefully determined the shaving direction and clearance area length. Our experiments demonstrated a promising trend of up to 75% reduction in die roll when applying the Shaving process in the opposite direction of pre-cutting, with the minimum die roll observed at a clearance area length of 0.2 mm. Furthermore, we successfully implemented this approach in the production of door latch products, confirming a significant reduction in die roll. This research contributes valuable insights and practical solutions for addressing die roll issues in fine blanking processes.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2002.02a
• /
• pp.136-143
• /
• 2002

Warm draw die technique which is one of the new forming technologies to improve formability of sheet metal is applied to the cylindrical and square cup drawing of stainless-aluminum clad sheets. In experiments the temperature of die and blank holder is varied from room temperature to $180^{\circ}C$, while the punch is cooled by circulation of coolant to increase the fracture strength of workpiece on the punch comer area. Test materials chosen for experiments are STS304-A1050-STS304 clad sheets. Teflon film as a lubricant is used on both sides of a workpiece. The limit drawing ratio and relative drawing depth as well as quality of drawn cups(distribution of thickness)are investigated and validity of warm drawing process is also discussed. No separation between each laminated material after drawing occurred through inspection by microscope as well as application of penetrant remover and bond strength test. Therefore, warm forming technique was confirmed to give better results in deep drawing of stainless clad sheet metal.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.8
• /
• pp.9-15
• /
• 1999

Die-sinking electrical discharge machining(EDM) for conductive ceramic matrix composite(CMC) of Tic/$Al_2O_3$ was experienced with addition of ultrasonic emission, and the results were compared with ones obtained by the EDM only. From this experimental study, the values of material removal rate(MRR) and surface roughness($R_{max}$), scanning electron microscope(SEM) micrographs, and weibull probability distribution of bending strength for the specimens were obtained and compared. The trend of MRR was found to be increased slightly with the current and the duty factor for both EDM only and EDM with ultrasonic emission. The MRR values were found to be increased for EDM with ultrasonic emission. The SEM micrographs of EDMed surface by under various operating conditions showed less micro cracks in various places. Although smaller bending strength value was obtained by EDMed surface with ultrasonic emission by weibull probability distribution analysis of bending strength.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.128-128
• /
• 2010

In this study, we investigated the evolution and reduction of the surface roughness during the high-speed chemical dry thinning process of Si wafers. The direct injection of NO gas into the reactor during the supply of F radicals from NF3 remote plasmas was very effective in increasing the Si thinning rate, due to the NO-induced enhancement of the surface reaction, but resulted in the significant roughening of the thinned Si surface. However, the direct addition of Ar and N2 gas, together with NO gas, decreased the root mean square (RMS) surface roughness of the thinned Si wafer significantly. The process regime for the increasing of the thinning rate and concomitant reduction of the surface roughness was extended at higher Ar gas flow rates. In this way, Si wafer thinning rate as high as $20\;{\mu}m/min$ and very smooth surface roughness was obtained and the mechanical damage of silicon wafer was effectively removed. We also measured die fracture strength of thinned Si wafer in order to understand the effect of chemical dry thinning on removal of mechanical damage generated during mechanical grinding. The die fracture strength of the thinned Si wafers was measured using 3-point bending test and compared. The results indicated that chemical dry thinning with reduced surface roughness and removal of mechanical damage increased the die fracture strength of the thinned Si wafer.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.5 no.6
• /
• pp.64-76
• /
• 1997

This paper deals with development of brackets by using aluminum alloy sheets which is indispensable for weight reduction of autobody. The press formability of aluminum alloy sheet is estimated by means of tensile test, V bending test, sample manufacturing test and photograph of microstructure. The results show that the elongation, strength, work hardening exponent, plastic anisotropy coefficient of Al 6***series are better than those of Al 5***series, but for general press formability, Al 5***series are better than Al 6***series due to lower yield strength. Since most of mechanical properties of aluminum sheet are generally inferior to those of cold-rolled steel sheet, shape fixability and press formability of aluminum sheet are very poor. For making components of autobody by use of die for steel sheet application, it is essential that die should be nodified for least bending and stretching. With the modified die for aluminum, it could be possible to make brackets, the component of autobody. Microstructure of Al 5***series has fine grain and small the 2nd phase and that of Al 6***series has relatively coarse grain. Therefore, it seems that fine grain and small the 2nd phase of Al 5***series is one of the factor of lower yield strength, resistance to stamping work, formation of Luder's line.