• Restorative Dentistry and Endodontics
• /
• v.17 no.1
• /
• pp.36-54
• /
• 1992

The purpose of this study was to compare the shear bond strengths to ground dentin surfaces of four dentinal bonding agents in 193 teeth. Various dentin surfaces treated with four dentin bonding agents were attached with two restorative composite resins. The effectiveness of the bonding were tested by the monitoring the shear bond strength. The shear bond strengths were measured after 2 hours and 24 hours after surface conditioning with four dentin bonding agents. Effects of EDTA, the additive illumination, and sealer treatments without primer on bond strength to dentin surfaces were assessed. In addition the effects of the thickness of specimens ranging from 0.65 mm to 1.95 mm and the ratio of catalyst and base paste on the bond strength of chemical cure composite resin were estimated. The shear bond strength was determined by testing specimens in the Instron universal testing machine (Model No. 1122) at a crosshead speed of 1.0 mm/min. Following condusions were drawn: 1. The highest mean shear bond strengths of chemical cure composite resin to dentin conditioning with dentin bonding agents aged 2 hours were obtained, and then that was decreased with time followed by EDTA treatment. 2. In light cure composite resin, the shear bond strength was increased following dentin conditioning with bonding agents with time, irradiation time and EDTA treatment except in SB group. 3. The thicker the composite resin specimen was, the less the shear bond strength in chemical cure composite resin was. 4. In light cure composite resin, there was a little change in shear bond strength following dentin conditioning with bonding agents. 5. In chemical cure composite resin, the shear bond strength was the highest in the ratio of 1/1 of catalyst and base part. 6. Without a dentin primer, shear bond strength to dentin conditioned only with UB sealer was the highest among four sealers in light cure composite resin.

• Restorative Dentistry and Endodontics
• /
• v.15 no.1
• /
• pp.165-173
• /
• 1990

The purpose of this study was to measure the effect of two commercially available composite resin systems and GC dentin cement on the shear bond strength of the etched porcelain to enamel and dentin. The specimens were divided into six groups, and each group was as follows. Group I : etched enamel-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group II : etched enamel-Scotchbond 2-Silux-unfilled resin-silane-etched porcelain. Group III : dentin-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group IV : dentin-Scotchbond 2-Silux-unfilled resin-silane-etched porcelain Group V : dentin-GC dentin cement-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group VI : dentin-GC dentin cement-Scotchbond 2-Silux- unfilled resin-silane-etched porcelain Following polymerization. the specimens were stored in 100% humidity for 24 hours before testing. Shear bond strength was measured with Instron universal testing machine. The results obtained were as follows; 1. The shear bond strength of the etched porcelain to enamel was greater than that of the etched porcelain to dentin. 2. The shear bond strength of Silux-Scotchbond 2 to dentin was greater than that of CHOICE-dentin/enamel bonding agent. 3. There was no significant difference in shear bond strength to dentin between the groups lined with GC dentin cement. 4. The shear bond strength of Silux-Scotchbond 2 to dentin was greater than that of the groups lined with GC dentin cement. 5. There was no significant difference in shear bond strength to dentin between the groups lined with GC dentin cement and the group directly bonded with CHOICE-dentin/enamel bonding agent.

• The Journal of Advanced Prosthodontics
• /
• v.2 no.2
• /
• pp.39-45
• /
• 2010

PURPOSE. The aim of this study was to determine differences in shear bond strength to human dentin using immediate dentin sealing (IDS) technique compared to delayed dentin sealing (DDS). MATERIALS AND METHODS. Forty extracted human molars were divided into 4 groups with 10 teeth each. The control group was light-cured after application of dentin bonding agent ($Excite^{(R)}$ DSC) and cemented with $Variolink^{(R)}$. II resin cement. IDS/SE (immediate dentin sealing, $Clearfil^{TM}$ SE Bond) and IDS/SB (immediate dentin sealing, $Adapter^{TM}$ Single Bond 2) were light-cured after application of dentin bonding agent ($Clearfil^{TM}$ SE Bond and $Adapter^{TM}$ Sing Bond 2, respectively), whereas DDS specimens were not treated with any dentin bonding agent. Specimens were cemented with $Variolink^{(R)}$. II resin cement. Dentin bonding agent ($Excite^{(R)}$. DSC) was left unpolymerized until the application of porcelain restoration. Shear strength was measured using a universal testing machine at a speed of 5 mm/min and evaluated of fracture using an optical microscope. RESULTS. The mean shear bond strengths of control group and IDS/SE group were not statistically different from another at 14.86 and 11.18 MPa. Bond strength of IDS/SE group had a significantly higher mean than DDS group (3.14 MPa) (P < .05). There were no significance in the mean shear bond strength between IDS/SB (4.11 MPa) and DDS group. Evaluation of failure patterns indicates that most failures in the control group and IDS/SE groups were mixed, whereas failures in the DDS were interfacial. CONCLUSION. When preparing teeth for indirect ceramic restoration, IDS with $Clearfil^{TM}$ SE Bond results in improved shear bond strength compared with DDS.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.1
• /
• pp.57-66
• /
• 2017

PURPOSE. Cementation failures of restorations are frequently observed in clinical practice. The purpose of this study is to compare the effect of initial and repeated bonding on the bond strengths of different resin cements to enamel and dentin. MATERIALS AND METHODS. Ninety human maxillary central incisors were bisected longitudinally. The 180 tooth halves were divided into 2 groups (n = 90) for enamel and dentin bonding. The enamel and dentin groups were further divided into 3 groups (n = 30) for different resin cement types. Composite resin (Filtek Ultimate) cylinders ($3{\times}3\;mm$) were prepared and luted to enamel and dentin using Variolink II (Group V), RelyX ARC (Group R), or Panavia F 2.0 (Group P) resin cement. After 24 hours, initial shear bond strengths of the resin cements to enamel and dentin were measured. Using new cylinders, the specimens were de-bonded and re-bonded twice to measure the first and the second bond strengths to enamel and dentin. Failure modes and bonding interfaces were examined. Data were statistically analyzed. RESULTS. Initial and repeated bond strengths to enamel were similar for all the groups. The first ($15.3{\pm}2.2\;MPa$) and second ($10.4{\pm}2.2\;MPa$) bond strengths to dentin were significantly higher in Group V (P<.0001). Second bond strengths of dentin groups were significantly lower than initial and first bond strengths to dentin (P<.0001). CONCLUSION. All resin cements have similar initial and repeated bond strengths to enamel. Variolink II has the highest first and second bond strength to dentin. Bond strength to dentin decreases after the first re-bonding for all resin cements.

• Restorative Dentistry and Endodontics
• /
• v.16 no.2
• /
• pp.126-142
• /
• 1991

The purpose of this study was to evaluate the effect of various dentin surface treatments on shear bond strength, microhardness and fracture mode before and after thermocycling. Recently extracted 75 human molars were used. The teeth were sagittal sectioned faciolingually to obtain 150 specimens. They were randomly divided into six groups. Mesial and distal dentinal surfaces of specimens were exposed by grinding and treated respectively with GC-DENTIN CONDITIONER. 10-3 solution of 4-Meta, Cleansar and Primer of GLUMA, Scotchprep of Scotchbond 2, DENTIN CONDITIONER and PRIMER A, B of ALL BOND according to the manufacturers directions. Specimens of one group were not treated. Adhesive agent of Scotchbond 2, were applied and cured on the treated dentin surfaces. After P-50 were cured on them, specimens were stored in 31c water for 24 hours before shear bond strength measurement Shear bond strength was measured in 10 specimens of each group. 10 specimens of each group were thermocycled in $20^{\circ}C$, $60^{\circ}C$,$20^{\circ}C$, $4^{\circ}C$, $20^{\circ}C$ water in order, for 30 seconds respectively, 100 times a day for 7 days. After thermocycling shear bond strength was measured. Microhardness was checked on treated dentin surface and fractured dentin surface in 10 specimens respectievly. Francture modes were observed with SEM The following results were obtained. 1. Before thermocycling. shear bond strengths in the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND were significantly higher than those in other specimens(P<0.01). 2. After thermocycling. shear bond strengths in the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2 and DENTIN CONDITIONER and PRIMER A, B of AIL BOND were significantly higher than those in specimens not: treated, treated with GC-DENTIN CONDITIONER and 10-3 solution of 4-Meta(P<0.01). Shear bond strengths in the specimens treated with GC-DENTIN CONDITIONER and PRIMER A, B of ALL BOND were significantly higher than those in other specimens except those treated with Scotchprep of Srotchbond 2(P<0.01). 3. Shear bond strengths after thermocycling were reduced in the specimens not treated, treated with GC-DENTIN CONDITIONER and 10-3 solution of 4-Meta and were increased in the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2, without significance, compared with those before thermocycling. In the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND, shear bond strengths after thermocycling were significantly increased, compared with those before thermocycling(P<0.01). 4. Microhardnesses in the fractured surfaces after shear bond strength measurement were significantly increased in the specimens treated with 10-3 solution of 4-Meta and significantly decreased in the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND, compared with those in the treated dentin surfaces(P<0.01). 5. In the specimens treated with Cleanser and Primer of GLUMA, Scotchprep of Scotchbond 2 and DENTIN CONDITIONER and PRIMER A, B of ALL BOND, cohesive fracture modes were observed more than adhesive fracture modes.

• Restorative Dentistry and Endodontics
• /
• v.21 no.2
• /
• pp.569-584
• /
• 1996

The purpose of this study was to elucidate the effect of benzalkonium chloride on tensile bond strength of BPDM/HEMA dentin bonding. One hundred sixty dentin specimens from freshly extracted bovine mandibular incisors were used, and 0, 0.02, 0.1 or 0.5% benzalkonium chloride solution was applied to the dentin specimen with/after phosphoric acid. 32% phosphoric acid was used when the specimens were bonded with One-Step$^{TM}$, a BPDM/HEMA system and 10% was used when bonded with All-Bond$^{(R)}$ 2, a NTG-GMA/BPDM system. Aelitefil$^{TM}$ composite resin was bonded to the pretreated dentin specimen with the use of All-Bond$^{(R)}$ 2 or One-Step$^{TM}$ dentin bonding agent. After the bonded specimens were stored in $37^{\circ}C$ distilled water for 24 hours, tensile bond strength was measured. The fractured dentin specimens were examined under the scanning electron microscope. The results were as follows : Benzalkonium chloride application after acid-treatment resulted in decrease of dentin bond strength of One-Step$^{TM}$, a BPDM/HEMA system (p>0.05). Benzalkonium chloride application did not exert any influence on dentin bond strength of All-Bond$^{(R)}$ 2, a NTG-GMA/BPDM system (p>0.05). There was no relationship between the concentration or application method of benzalkonium chloride and the dentin bond strength of One-Step$^{TM}$ or All-Bon$^{(R)}$ 2 (p<0.05). On SEM examination of the fractured dentin-resin interface, while mixed failure was prominent in dentin bonding with One-Step$^{TM}$, adhesive and mixed failures were seen together in dentin bonding with All-Bond$^{(R)}$ 2 regardless of the concentration and application method of benzalkonium chloride.

• Restorative Dentistry and Endodontics
• /
• v.40 no.1
• /
• pp.68-74
• /
• 2015

Objectives: This study examined the effects of additional acid etching on the dentin bond strength of one-step self-etch adhesives with different compositions and pH. The effect of ethanol wetting on etched dentin bond strength of self-etch adhesives was also evaluated. Materials and Methods: Forty-two human permanent molars were classified into 21 groups according to the adhesive types (Clearfil SE Bond [SE, control]; G-aenial Bond [GB]; Xeno V [XV]; Beauti Bond [BB]; Adper Easy Bond [AE]; Single Bond Universal [SU]; All Bond Universal [AU]), and the dentin conditioning methods. Composite resins were placed on the dentin surfaces, and the teeth were sectioned. The microtensile bond strength was measured, and the failure mode of the fractured specimens was examined. The data were analyzed statistically using two-way ANOVA and Duncan's post hoc test. Results: In GB, XV and SE ($pH{\leq}2$), the bond strength was decreased significantly when the dentin was etched (p < 0.05). In BB, AE and SU (pH 2.4 - 2.7), additional etching did not affect the bond strength (p > 0.05). In AU (pH = 3.2), additional etching increased the bond strength significantly (p < 0.05). When adhesives were applied to the acid etched dentin with ethanol-wet bonding, the bond strength was significantly higher than that of the no ethanol-wet bonding groups, and the incidence of cohesive failure was increased. Conclusions: The effect of additional acid etching on the dentin bond strength was influenced by the pH of one-step self-etch adhesives. Ethanol wetting on etched dentin could create a stronger bonding performance of one-step self-etch adhesives for acid etched dentin.

• Restorative Dentistry and Endodontics
• /
• v.45 no.3
• /
• pp.36.1-36.10
• /
• 2020

Objectives: This study aims to assess the effect of universal adhesives pretreatment on the bond strength of resin-modified glass ionomer cement to dentin. Materials and Methods: Fifty caries-free human third molars were employed. The teeth were randomly assigned into five groups (n = 10) based on dentin surface pretreatments: Single Bond Universal (3M Oral Care), Gluma Bond Universal (Heraeus Kulzer), Prime&Bond Elect (Dentsply), Cavity Conditioner (GC) and control (no surface treatment). After Fuji II LC (GC) was bonded to the dentin surfaces, the specimens were stored for 7 days at 37℃. The specimens were segmented into microspecimens, and the microspecimens were subjugated to microtensile bond strength testing (1.0 mm/min). The modes of failure analyzed using a stereomicroscope and scanning electron microscopy. Data were statistically analyzed with one-way analysis of variance and Duncan tests (p = 0.05). Results: The surface pretreatments with the universal adhesives and conditioner increased the bond strength of Fuji II LC to dentin (p < 0.05). Single Bond Universal and Gluma Bond Universal provided higher bond strength to Fuji II LC than Cavity Conditioner (p < 0.05). The bond strengths obtained from Prime&Bond Elect and Cavity Conditioner were not statistically different (p > 0.05). Conclusions: The universal adhesives and polyacrylic acid conditioner could increase the bond strength of resin-modified glass ionomer cement (RMGIC) to dentin. The use of universal adhesives before the application of RMGIC may be more beneficial in improving bond strength.

• Restorative Dentistry and Endodontics
• /
• v.25 no.2
• /
• pp.180-192
• /
• 2000

One bottle system was recently developed in order to simplify the clinical skills and save chair time after continuous improvements on dentin bonding agents. There has been many studies to measure the bond strength of one bottle systems but no actual work has been done on micromorphologic study of resin-dentin interdiffusion zone after one bottle system application. To evaluate the bonding patterns of various commercially available one bottle systems to dentin, observation of resin-dentin interdiffusion zone under TEM was performed. Caries-free human third molars within one month of extractions were chosen for the experiments. The molars were sectioned 1mm above the cementoenamel junction and got rid of the root portions. Crown portions of the teeth were sectioned parallel to occlusal surface so that dentin discs of 1mm in thickness were remained. 7 one bottle systems and 1 two bottle system were applied according to manufacturer's instructions and followings were the results. 1. In every experimental groups, cross bandings of collagen fiber were distinguishable and tight bon dings between the bonding agents and dentin were observed. 2. Hybrid layer was clearly observed in ONE-STEP$^{(R)}$, Prime & Bond$^{(R)}$ 2.1, Syntac$^{(R)}$ SC, MAC-BOND II groups but it was not clear in Single Bond, D-Liner Dual PLUS, ONE COAT BOND groups. 3. Electron-density of hybrid layer was uniform in pattern in MAC-BOND II, Prime & Bond$^{(R)}$ 2.1 groups but not so uniform in ONE-STEP$^{(R)}$ group. 4. Electron-dense amorphous phase in most superior layer of the resin-dentin interdiffusion zone was characteristically observed in Single Bond, Syntac$^{(R)}$ SC, ONE COAT BOND groups. It can be concluded that bondings between the dentin bonding agents and dentin can be various in pattern according to their chemical compositions and the condition during applications.

• The Journal of the Korean dental association
• /
• v.53 no.12
• /
• pp.958-966
• /
• 2015

Objective: Sodium hypochlorite (NaOCl) decreases the bond strength of resin composite. The purpose of this study was to compare the effect of antioxidant and superficial dentin surface removal on the microtensile bond strength of NaOCl-treated dentin. Materials and Methods: Twenty non-carious human third molars were used in this study. The dentin surfaces were treated with 5.25% NaOCl for 10 min, followed either by treatment with 10% ascorbic acid or superficial dentin surface removal. Two-step self-etch adhesive and resin composite were used for restoration. The bonded specimens were subjected to the microtensile bond strength test. Statistical analysis was performed using one-way analysis of variance (ANOVA) and Tukey's test (p < 0.05). Results: The bond strength after removal of the superficial dentin surface following NaOCl irrigation was similar to that in the control group. The group treated with 10% ascorbic acid demonstrated significantly higher bond strength than the other groups. Conclusion: NaOCl irrigation-induced reduction in dentin bond strength could be recovered by either treatment with 10% ascorbic acid or simple removal of the superficial dentin surface.