• Korean Journal of Dental Materials
• /
• v.44 no.2
• /
• pp.171-178
• /
• 2017

The purpose of this study is to investigate the effect of number of times dipped in coloring liquid and sintering temperature on the flexural strength of zirconia ceramic. In this study, using a zirconia block having improved transparency, specimens with size of $25mm{\times}2mm{\times}1.5mm$ were fabricated. The zirconia ceramic specimens were divided into three groups according to the number of times dipped in coloring liquid by 0, 2 and 4 times, and dyed in the coloring liquid to give color to each specimen. Then, after sintering them at the final temperature of $1,450^{\circ}C$ and $1,600^{\circ}C$, flexural strength was measured using a universal testing machine (total 6 group, n=10 for each group). Also, a scanning electron microscopy (SEM) was performed to observe its microstructure, and the data obtained through the experiment were analyzed with two-way ANOVA. The results of the flexural strength analysis show that the highest value was measured $762.3{\pm}42.3MPa$ in EKL2 group, while the lowest value was $516.4{\pm}77.1MPa$ in EKH4 group. According to the results of the two-way ANOVAs, flexural strength was not related with interaction between sintering temperature and number of times dipped in coloring liquid ($R^2=0.737$). However, there were statistically significant differences in flexural strength depending on sintering temperature (P<0.001). The flexural strength of zirconia ceramics having improved transparency was dependent on sintering temperature. The number of times dipped in the coloring liquid did not affect flexural strength of the zirconia ceramic having improved transparency.

• The Journal of Advanced Prosthodontics
• /
• v.4 no.2
• /
• pp.76-83
• /
• 2012

PURPOSE. Zirconia has been used in clinical dentistry for approximately a decade, and there have been several reports regarding the clinical performance and survival rates of zirconia-based restorations. The aim of this article was to review the literatures published from 2000 to 2010 regarding the clinical performance and the causes of failure of zirconia fixed partial dentures (FPDs). MATERIALS AND METHODS. An electronic search of English peer-reviewed dental literatures was performed through PubMed to obtain all the clinical studies focused on the performance of the zirconia FPDs. The electronic search was supplemented by manual searching through the references of the selected articles for possible inclusion of some articles. Randomized controlled clinical trials, longitudinal prospective and retrospective cohort studies were the focuses of this review. Articles that did not focus on the restoration of teeth using zirconia-based restorations were excluded from this review. RESULTS. There have been three studies for the study of zirconia single crowns. The clinical outcome was satisfactory (acceptable) according to the CDA evaluation. There have been 14 studies for the study of zirconia FPDs. The survival rates of zirconia anterior and posterior FPDs ranged between 73.9% - 100% after 2 - 5 years. The causes of failure were veneer fracture, ceramic core fracture, abutment tooth fracture, secondary caries, and restoration dislodgment. CONCLUSION. The overall performance of zirconia FPDs was satisfactory according to either USPHS criteria or CDA evaluations. Fracture resistance of core and veneering ceramics, bonding between core and veneering materials, and marginal discrepancy of zirconia-based restorations were discussed as the causes of failure. Because of its repeated occurrence in many studies, future researches are essentially required to clarify this problem and to reduce the fracture incident.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.2
• /
• pp.96-102
• /
• 2014

PURPOSE. This study was performed to characterize the effects of zirconia coated with calcium phosphate and hydroxyapatite compared to smooth zirconia after bone marrow-derived osteoblast culture. MATERIALS AND METHODS. Bone marrow-derived osteoblasts were cultured on (1) smooth zirconia, (2) zirconia coated with calcium phosphate (CaP), and (3) zirconia coated with hydroxyapatite (HA). The tetrazolium-based colorimetric assay (MTT test) was used for cell proliferation evaluation. Scanning electron microscopy (SEM) and alkaline phosphatase (ALP) activity was measured to evaluate the cellular morphology and differentiation rate. X-ray photoelectron spectroscopy (XPS) was employed for the analysis of surface chemistry. The genetic expression of the osteoblasts and dissolution behavior of the coatings were observed. Assessment of the significance level of the differences between the groups was done with analysis of variance (ANOVA). RESULTS. From the MTT assay, no significant difference between smooth and surface coated zirconia was found (P>.05). From the SEM image, cells on all three groups of discs were sporadically triangular or spread out in shape with formation of filopodia. From the ALP activity assay, the optical density of osteoblasts on smooth zirconia discs was higher than that on surface treated zirconia discs (P>.05). Most of the genes related to cell adhesion showed similar expression level between smooth and surface treated zirconia. The dissolution rate was higher with CaP than HA coating. CONCLUSION. The attachment and growth behavior of bone-marrow-derived osteoblasts cultured on smooth surface coated zirconia showed comparable results. However, the HA coating showed more time-dependent stability compared to the CaP coating.

• Journal of dental hygiene science
• /
• v.13 no.2
• /
• pp.135-141
• /
• 2013

One factor for successful prognosis of finished dental prosthesis is good marginal fit. The purpose of this study in vitro investigation was to compare the marginal fit of all-ceramic crown before and after porcelain veneering, to evaluate the influence of high temperature of the porcelain firing on the fit. For this experiment, model of abutment tooth of maxillary right central incisor was prepared. Ten working models were produced. Ten zirconia cores were made by dental computer aided design/computer aided manufacturing system. The marginal fit of specimens were examined using silicone replica technique. Silicone replicas were sectioned four times and were measured through a digital microscope (${\times}160$). Marginal fit is a distance connected between edge end part of specimen and abutment margin. Each specimens was measured twice, the first measurement was done prior to veneering porcelain firing, while the second measurement was done after the porcelain firing to evaluate this process. Statistical analyses were performed with paired t-test. $Mean{\pm}SD$ marginal fit was $60.8{\pm}14.2{\mu}m$ for zirconia core and $86.1{\pm}13.3{\mu}m$ for all-ceramic crown. They were statistically significant differences (p<0.001). But all specimens showed a marginal fit where the gap widths ranged within the clinical recommendation ($120{\mu}m$), all-ceramic crown production using the zirconia core was adequate.

• Journal of dental hygiene science
• /
• v.15 no.5
• /
• pp.577-584
• /
• 2015

The purpose of this study was to evaluate the effect of metal chloride infiltration treatment on color and strength changes of the yttria-stabilized tetragonal zirconia polycrystals (Y-TZP). Fifty disc specimens were prepared with a Y-TZP powder (ZPEX; Tosoh, Japan). Thirty different metal chloride solutions containing 0.03~0.08 wt% chromium and 0.03~0.07 wt% terbium ions were prepared. Presintered Y-TZP specimens were soaked in metal chloride coloring liquids for 3 minutes and sintered in air at $1,450^{\circ}C$ for 2 hours. The color of the specimens was measured with spectrophotometer and color difference (${\Delta}E^*$) was obtained based on the CIE $L^*$, $a^*$, $b^*$ color coordinate values. To evaluate the effect of metal chloride infiltration strength changes, the biaxial flexural test was performed at crosshead speed 0.5 mm/min. Colors of the sintered Y-TZP showed the colors of Vita shade guide A1, A2 and A3 with the infiltration of chromium and terbium chloride solutions. Density of the sintered Y-TZP increased by the infiltration of chromium and terbium chloride solutions. Bi-axial flexural strength of the sintered Y-TZP did not show statistically significant differences by the infiltration of chromium and terbium chloride solutions (p>0.05). Chromium and terbium chloride did not affect the crystal phase of zirconia, and all specimens showed tetragonal phase. Accordingly, this study suggests that chromium and terbium chlorides can make colored zirconia while adding in a liquid form. The color of colored zirconia differ from that of vita shade guide but it can use all ceramic restoration as substructure in dental clinic.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.1
• /
• pp.1-7
• /
• 2015

PURPOSE. This study was performed to evaluate shear bond strength (SBS) between three dual-cured resin cements and silica coated zirconia, before and after thermocycling treatment. MATERIALS AND METHODS. Sixty specimens were cut in $15{\times}2.75mm$ discs using zirconia. After air blasting of $50{\mu}m$ alumina, samples were prepared by tribochemical silica coating with $Rocatec^{TM}$ plus. The specimens were divided into three groups according to the dual-cure resin cement used: (1) Calibra silane+$Calibra^{(R)}$, (2) Monobond S+$Multilink^{(R)}$ N and (3) ESPN sil+$RelyX^{TM}$ Unicem Clicker. After the resin cement was bonded to the zirconia using a Teflon mold, photopolymerization was carried out. Only 10 specimens in each group were thermocycled 6,000 times. Depending on thermocycling treatment, each group was divided into two subgroups (n=10) and SBS was measured by applying force at the speed of 1 mm/min using a universal testing machine. To find out the differences in SBS according to the types of cements and thermocycling using the SPSS, two-way ANOVA was conducted and post-hoc analysis was performed by Turkey's test. RESULTS. In non-thermal aged groups, SBS of Multilink group (M1) was higher than that of Calibra (C1) and Unicem (U1) group (P<.05). Moreover, even after thermocycling treatment, SBS of Multilink group (M2) was higher than the other groups (C2 and U2). All three cements showed lower SBS after the thermocycling than before the treatments. But Multilink and Unicem had a significant difference (P<.05). CONCLUSION. In this experiment, Multilink showed the highest SBS before and after thermocycling. Also, bond strengths of all three cements decreased after thermocycling.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.8
• /
• pp.176-182
• /
• 2018

One of the most important factor of esthetic prosthesis is the color of the teeth. Zirconia is produced in the process of design, milling, coloring, drying, and sintering. The effect of the drying degree of zirconia colorant on the color tone is examined. For the experiment, a total of 45 zirconia specimens(15 for each) were fabricated by using cad/cam system. The zirconia specimens(L block(LAZOR), Z block(Zircos-E block posterior), A block(AlphaZ)) were then subjected to zirconia sintering in accordance with the manufacturer's instructions, using a chemical coloring agent to Non-drying(0sec), intermediate (10sec), and completely dried (10min) temperature holding times. The color tone was measured using a spectrophotometer. The results were analyzed with a One-way analysis of variance and the Tukey post-hoc test (${\alpha}=.05$) The $L^*$ values of L, A specimens, $a^*$ values of A specimens, and $b^*$ values of Z specimens were not statistically different according to the degree of drying (p>0.05), While the $L^*$ value of Z specimen, $a^*$ value of L, Z specimen, $b^*$ values of L, A specimens were statistically different according to the degree of drying(p <0.05). In conclusion, the drying of zirconia colourants improves zirconia brightness and increases the optical properties of the enamel.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.3
• /
• pp.248-255
• /
• 2013

PURPOSE. This study compared the effect of three intraoral repair systems on the bond strength between composite resin and zirconia core. MATERIALS AND METHODS. Thirty zirconia specimens were divided into three groups according to the repair method: Group I-CoJet$^{TM}$ Repair System (3M ESPE) [chairside silica coating with $30{\mu}m$ $SiO_2$ + silanization + adhesive]; Group II-Ceramic Repair System (Ivoclar Vivadent) [etching with 37% phosphoric acid + Zirconia primer + adhesive]; Group III-Signum Zirconia Bond (Heraus) [Signum Zirconia Bond I + Signum Zirconia Bond II]. Composite resin was polymerized on each conditioned specimen. The shear bond strength was tested using a universal testing machine, and fracture sites were examined with FE-SEM. Surface morphology and wettability after surface treatments were examined additionally. The data of bond strengths were statistically analyzed with one-way ANOVA and Tamhane post hoc test (${\alpha}$=.05). RESULTS. Increased surface roughness and the highest wettability value were observed in the CoJet sand treated specimens. The specimens treated with 37% phosphoric acid and Signum Zirconia Bond I did not show any improvement of surface irregularity, and the lowest wettability value were found in 37% phosphoric acid treated specimens. There was no significant difference in the bond strengths between Group I ($7.80{\pm}0.76$ MPa) and III ($8.98{\pm}1.39$ MPa). Group II ($3.21{\pm}0.78$ MPa) showed a significant difference from other groups (P<.05). CONCLUSION. The use of Intraoral silica coating system and the application of Signum Zirconia Bond are effective for increasing the bond strength of composite resin to zirconia.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.23 no.2
• /
• pp.119-130
• /
• 2007

Purpose: This investigation was designed to estimate the flexure strength, density, and microstructure of the colored and uncolored zirconia oxide ceramics for fixed partial denture. Material and Methods: LAVATM All Ceramic(3M-ESPE, USA), Cercon Smart Ceramic(Dentsply, USA), and Z-match Ceramic(DentAim, Korea) were used for this study. All specimen was fabricated by ASTM C1161. After preparing $25{\times}2{\times}1.5mm$ of rectangular column and sitting rectangular column on universal test machine (UTM), external supporting point distance is 20.0 mm, internal supporting point distance is 10.0 mm. Specimen was loaded with 0.2 mm/min of cross head speed until fracture and at the time of broken of specimen, measuring loading value with PC software. Results: The results were obtained as follows: 1. Flexure strength of uncolored zirconia was higher than that of colored zirconia. 2. In uncolored zirconia, flexure strength of LAVATM Ceramic was more higher than the other ceramics, and it showed statistical difference between LAVATM Ceramic and Cercon Smart Ceramic (P<0.05). 3. In colored zirconia, flexure strength of LAVATM Ceramic was more higher than the other ceramics too, but they did not show statistical difference (p>0.05). 4. In Weibull analysis, Characterastic strength was showed highest value to uncolored LAVATM Ceramic and lowest value to Z-match ceramic, and Weibull modulus(m) of uncolored zirconia was higher than that of colored zirconia. 5. In XRD analysis, all group except Z-match showed high peak of t-ZrO2 but they did not show m-ZrO2. Colored zirconia group showed lower peak of t-ZrO2 than that of uncolored zirconia group.

• Journal of the Korean Ceramic Society
• /
• v.37 no.3
• /
• pp.288-293
• /
• 2000

Effects of contact damage and residual stress for two kinds of dental restorative layered ceramics, porcelain/alumina and porcelain/zirconia bilayers, were observed with Hertzian and Vickers indentation methods. Indentation stress-strain behavior of each material, strength degradation of the coating material, and crack propagation behavior in the coating layer after Vickers indentation were examined by an optical microscope. As a result, porcelain as coating materials showed the classical brittleness. It was inferred that damage and strength in two bilayer system were dependent on thermal expansion mismatch between the coating material and the substrate, which affected the strength degradation. Residual stress resulting from thermal expansion mismtch was formed in the coating layer, and specially in the case of porcelain/zirconia, residual stress was eliminated as coating thickness decreased.