• Journal of Technologic Dentistry
• /
• v.31 no.4
• /
• pp.9-15
• /
• 2009

The purpose of this study was to observe the change of mechanical property and microstructure in porcelain fused to gold alloy by heat treatment. PFG alloys are composed with Au-Pd-Ag alloy of the additional elements with indium, tin and copper. Specimens were tested in hardness using vicker,s micro-hardness tester and the surface micro structural changes were analysed by SEM and EDS. The results were as fellows: 1. The vickers hardness showed highest in Au-Pd-Ag alloy of the additional element with tin. 2. By hardening-oxiding result, the vicker,s hardness increased in additional element with tin but there was no significant difference in additional elements with indium and copper. 3. The surface oxide layer of Au-Pd-Ag alloy with added indium and tin increased but there was small change in additional element with copper. 4. The elements of indium and tin increased with increasing heat treatment in the surface alloy.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.1
• /
• pp.103-117
• /
• 1997

The purpose of this experiment was to determind whether the gold electrodeposit on Pd-Ag and Ni-Cr alloys influences on the shear bond strength between veneering resin and silicoated metal surface. All the metal specimens were sandblasted with $250{\mu}m$ aluminum oxide and followed by silicoating and resin veneering. According to the metal surfaces to be veneered, experimental groups were divided into five. Group Prec : Gold alloy without gold coating Group Semi : Pd-Ag alloy without gold coating Group Base : Ni-Cr alloy without gold coating Group Semi-G : Pd-Ag alloy with gold coating Group Base-G : Ni-Cr alloy with gold coating All specimens were thermocycled 1,000 times at temperature of $5^{\circ}C$ to $55^{\circ}C$. The effects of gold electrodeposit on the shear bond strength between resin and metal interface were measured and fractured surface of the resin veneered metal was examined under the scaning electron microscope. The following results were obtained 1. The shear bond strength between resin and metal was $64.51{\pm}11.11Kg/cm^2$ in Prec group, $62.77{\pm}11.23Kg/cm^2$ in Base group and $58.97{\pm}9.20Kg/cm^2$ in Semi Group. There was no significant difference among the groups. 2. The bond strength in groups Semi-G and Base-G decreased about 17%, compared to the nongold-electrodeposit groups(Semi, Base). 3. In groups of non electrodeposit(Prec, Semi, Base), fracture occurred at the interface between alloy and resin, while fracture interface was observed between gold coating and resin in group Semi-G, and between metal substrate and gold coating in group Base-G respectively.

• The Journal of Korean Academy of Prosthodontics
• /
• v.14 no.1
• /
• pp.31-34
• /
• 1976

The author studied the effects of some dental gold alloys and dental nonprecious metals on muscle. The metal specimens were cast in the size of $1.0mm.{\times}5.0mm.{\times}3.0mm.$ and implanted in the gluteus maximus musculus of the two dogs. The subjects were sacrificed at 3 weeks and 5 weeks respectively after implantation. The tissue was examined his to-pathologically. The findings were as follows. 1. The more the alloy contains gold, the less the tissue response to the alloy and the less the connective tissue layer around the specimens. 2. The recovery of connective tissue layer in gold specimens was markedly observed. 3. There were very thick connective layers around nonprecious specimens.

• The Journal of Korean Academy of Prosthodontics
• /
• v.33 no.3
• /
• pp.584-609
• /
• 1995

The purpose of this study was to evaluate the difference of the galvanic corrosion behaviour of the titanium in contact with gold alloy, silva-palladium alloy, and nickel-chromium alloy using the immersion and electrochemical method. And the effects of galvallit couples between titanium and the dental alloys were assessed for their usefulness as materials for superstructure. The immersion method was performed by measuring the amount of metal elementsreleased by Inductivey coupled plasma emission spectroscopy(ICPES) The specimen of fifteen titanium plates, the five gold alloy, five silver-palladium, five nickel-chromium plates, and twenty acrylic resin plates ware fabricated, and also the specimen of sixty titanium plugs, the thirty gold alloy, thirty silver-palladium, and nickelc-hromium plugs were made. Thereafter, each plug of gold alloy, silver-palladium, and nickel-chromium inserted into the the titanium and acrylic resin plate, and also titanium plug inserted into the acrylic resin plate. The combination specimens uf galvanic couples immersed in 70m1 artificial saliva solution, and also specimens of four type alloy(that is, titanium, gold, silver-palladium and nickel-chromium alloy) plugs were immersed solely in 70m1 artificial sativa solution. The amount of metal elements released was observed during 21 weeks in the interval of each seven week. The electrochemical method was performed using computer-controlled potentiosta(Autostat 251. Sycopel Sicentific Ltd., U.K). The wax patterns(diameter 11.0mm, thickness,in 1.5mm) of four dental casting alloys were casted by centrifugal method and embedded in self-curing acrylic resin to be about $1.0cm^2$ of exposed surface area. Embedded specimens were polished with silicone carbide paper to #2,000, and ultrasonically cleaned. The working electrode is the specimen of four dental casting alloys, the reference electrode is a saturated calmel electrode(SCE) and the ounter electrode is made of platinum plate. In the artificial saliva solution, the potential scanning was carried out starting from-700mV(SCE) TO +1,000mV(SCE) and the scan rate was 75mV/min. Each polarization curve of alloy was recorded automatically on a logrithmic graphic paper by XY recorder. From the polarization curves of each galvanic couple, corrosion potential and corrosion rates, that is, corrosion density were compared and order of corrosion tendency was determined. From the experiments, the following results were obtained : 1. In the case of immersing titanium, gold alloy, silver-palladium alloy, and nickel-chromium alloysolely in the artificial saliva solution(group 1, 2, 3, and 4), the total amount of metal elements released was that group 4 was greater about 2, 3 times than group 3, and about 7.8 times than group 2. In the case of group 1, the amount of titanium released was not found after 8 week(p<0.001). 2. In the case of galvanic couples of titanium in contact with alloy(group 5, 6), the total amount of metal elements released of group 5 and 6 was less than that of group 7, 8, 9, and 10(p<0.05). 3. In the case of galvanic couples of titanium in contact with silver-palladium alloy(group 7, 8), the total amount of metal elements released of group 7 was greater about twice than that of group 5, and that of group 8 was about 14 times than that of group 6(p<0.05). 4. In the case of galvanic couples of titanium in contact with nickel-chromium alloy(group 9, 10), the total amount of metal elements released of group 9 and 10 was greater about 1.8-3.2 times than that of group 7 and 8, and was greater about 4.3~25 times than that of group 5 and 6(p<0.05). 5. In the effect of galvanic corrosion according to the difference of the area ratio of cathode and anode, the total amount of metal elements released was that group 5 was greater about 4 times than group 6, group 8 was greater about twice than group 7, and group 10 was greater about 1.5 times than group 9(p<0.05). 6. In the effect of galvanic corrosion according to the elasped time during 21 week in the interval of each 7 week, the amount of metal elements released was decreased markedly in the case of galvanic couples of the titanium in contact with gold alloy and silver-palladium alloy but the total amount of nickel and beryllium released was not decreased markedly in the case of galvanic couples of the titanium in contact with nickel-chromium alloy(p<0.05). 7. In the case of galvanic couples of titanium in contact with gold alloy, galvanic current was lower than any other galvanic couple. 8. In the case of galvanic couples of titanium in contact with nickel-chromium alloy, galvanic current was highest among other galvanic couples.

• Journal of Technologic Dentistry
• /
• v.29 no.2
• /
• pp.79-85
• /
• 2007

In this study, We tried to find out the fracture strength of zirconia coping all ceramic crown and collarless porcelain fused gold alloy crown as the compared group. Each of the collarless porcelain fused gold crown and zirconia all ceramic crown has been produced specimen 10 each. And after pasting them on the steel jig, it had load given at porcelain incisal edge by 130$^{\circ}$ and measured fracture strength by Universal Testing Machine and then We have results from that. 1. The average value of fracture strength suggested 950.49 N at collarless porcelain fused gold alloy crown, 656.81 N at zirconia coping all ceramic crown. 2. Fractured pattern showed that the whole of labial part was exposed in collarless porcelain fused gold crown, but porcelain of margin part did not show fracture in advance. In the practice, the concern that collarless might cause fracture strength to be weaken does not matter, we concluded zirconia all ceramic crown made fracture that only a part of labial porcelain was fractured. The combination of zirconia all ceramic crown and turned out to be excellent.

• Journal of Technologic Dentistry
• /
• v.31 no.1
• /
• pp.63-74
• /
• 2009

Partial or complete prosthesis is needed when teeth are lost due to various kinds of reason. Artificial teeth recover occlusion instead of natural teeth. Artificial teeth are required of esthetics, fragile resistance and abrasive resistance. Artificial tooth is made of acrylic resin or porcelain. Nowadays, acrylic resin artificial teeth are mainly used. Acrylic resin teeth are occluded with natural teeth, gold alloy, Ni-Cr alloy or porcelain etc. Acrylic resin teeth have similar translucency, gloss of natural teeth. And it has good chemical bond with denture base material, but it has low wear resistance. The aim of this study is to compare wear resistance among several denture teeth(Endura, SR-orthosit-PE, Planustar) and between artificial resin denture teeth and opposing 3 restorative materials(gold, Ni-Cr alloy, porcelain). Wear tests were conducted with a rotating wear testing apparatus(pin-on-disk type wear tester) under conditions of rpm 180, 75 minutes and constant loading of 50N. The upper part was the cusp of maxillary first molar and the lower part was a disk type restorative materials. To make similar oral environment, water was supplied continually. The acrylic resin teeth wear was determined by weighing the cusp each 5 minutes during 75 minutes test. Vicker's hardness tester was used to evaluate the surface hardness of test specimens. The SEM was used to evaluate the wear surfaces. The results were as follows: 1. Wear rates of acrylic resin teeth opposing to the restorative materials were high in order of Porcelain, Gold, Ni-Cr alloy (p<.05). 2. Wear resistance rate opposing to the Porcelain disk, was shown in order of Endura, SR-orthosit-PE, Planustar. The wear rate of opposing to porcelain disk was above two times more than that of other groups (p<.05). 3. Wear resistance rates opposing to the Gold, Ni-Cr alloy disk, was shown in order of Endura, SR-orthosit-PE, Planustar (p<.05). 4. A degree of the surface hardness is directly proportional to the degree of wear resistance. There are statistically significant differences between each groups (p<.05).

• Restorative Dentistry and Endodontics
• /
• v.18 no.2
• /
• pp.469-481
• /
• 1993

The purpose of this study was to achieve the reduction of the galvanic current between the dental amalgam alloy and gold alloy. In order to measure the galvanic current between these two metals a prep in the size of $4{\times}13mm$ which was filled with amalgam and another prep of $4{\times}2mm$ was filled with gold alloy was made in the acrylic resin. These two preps were then connected to a 2mm diameter copper wire. Using an ammeter to measure the galvanic current, six different kinds of amalgam and gold alloy were immersed in saline solution with approximately 10mm distance between the two alloys. Chemical agents that are thought to reduce the galvanic current such as hydrazine. silver nitrate, potassium chromate, and bonding agents such as Scotch bond 2(3M) and All bond 2(Bisco) were applied to the alloy surface. Cathodic inhibitor such as hydrazine was applied to gold alloy where as anodic inhibitor such as silver nitrate and potassium chromate were applied to amalgam. Both bonding agents, Scotch bond 2(3M) and All bond 2 (Bisco), were applied to amalgam. The following results were obtained when the currency on the coated alloy surface was compared to the uncoated surface. 1. The galvanic currency went down as the time elapsed and after 30 minutes no change was detected. 2. Initial currency was higher in low copper amalgam compared to high copper amalgam. Intitial currency was the highest in low copper lathe-cut amalgam. 3. Group of gold coated with hydrazine had the most reduction in galvanic currency. 4. Group of amalgam coated with silver nitrate or potassium chromate also showed significant reduction in galvanic currency. 5. The bonding agents also helped reduce galvanic currency. 6. Of all the agents used to reduce galvanic currency, silver nitrate showed the best result.

• Journal of dental hygiene science
• /
• v.9 no.2
• /
• pp.153-160
• /
• 2009

The purposed of this study was to investigate the effect of Gold bonding agent as intermediate layer between metal substrate and ceramic coating. Gold bonding agent used to seal off any surface porosity, to mask the greyish color of the metal, and to provide an underlying bright golden hue to the ceramic coverage. The adhesion between metal substrate and ceramic is related to diffusion of oxygen during ceramic firing. The oxide layer produced on non-precious alloy anti titanium was considered to have a potentially adverse effect on metal-ceramic bonding. The oxidation characteristics of titanium and non-precious alloys are the main problem. Every group were divided into test and control groups. Control groups are carried out process of degassing for product oxide layer. Au coating was applied on each Ni-Cr, Co-Cr alloys and cp-Ti specimens with difference surface condition or degassing. Specimens surfaces and cutting plane was characterized by SEM/EDS. Results suggested that Au coating is effective barriers to protect metal oxidation during ceramic firing.

• Journal of dental hygiene science
• /
• v.4 no.3
• /
• pp.103-109
• /
• 2004

The present study prepared 72 test samples - 24 made of amalgam alloy, 24 of Verabond (Ni-Cr alloy) for crown and 24 of Talladium $^{TM}alloy$ for denture - according to the manufacturers' manuals and general method in consideration of the width of the mesial-distal dental crown of the lower $1^{st}$ molar and MOD cavity in clinics, put them in a 200 ml beaker containing 80 ml of artificial saliva, and measured their galvanic corrosion at distances of 0 mm, 7 mm and 40 mm after 7 days. Isolated metals in the electrolyte such as Cu, Ag, Ni, Cr, Sn, Zn and Hg were quantitatively analyzed with Inductively Coupled Plasma - Atomic Emission Spectrometer (ICP-AES, JY-50P, VG Elemental Co. France), and from the results were drawn conclusions as follows. First, Cu, Sn, Ag, Hg and Zn were highly advantageous when amalgam contacted gold alloy compared to Ni-Cr alloy for crown and Talladium alloy for denture. In addition, although gold alloy was finest in terms of oral tissue and biocompatibility, it was most disadvantageous when it was with amalgam. Second, when amalgam contacted gold alloy, heavy metals such as Ni and Cr were not isolated at all because gold alloy did not contain such elements but Sn was isolated as much as $227.1{\pm}18.0035{\mu}g/cm^2$ although it was not included in the composition either. Hg was also isolated. These elements are assumed to have been isolated from amalgam itself. Third, when amalgam alloy was apart from gold alloy 0 mm, 7 mm and 40 mm, Cu and Ag showed significance but Hg did not. This suggests that gold alloy must not be used together with amalgam, and must not be used between dissimilar prostheses regardless of distance. Fourth, when amalgam alloy contacted Ni-Cr alloy for crown, Ag was not isolated from the amalgam, but Zn, Ni, Sn, Hg and Cu were isolated in order of quantity. Significance was observed according to distance - 0 mm, 7 mm and 40 mm. Hg was not isolated but heavy metals Ni and Cr were isolated. If amalgam alloy was in the opposite arch or it was apart from Ni-Cr alloy for crown, the isolation Hg was less than that when amalgam alloy contacted Ni-Cr alloy for crown. Fifth, when amalgam alloy contacted Talladium alloy for denture, significance was observed at distances of 0mm, 7 mm and 40 mm. Hg was not isolated but heavy metals Ni and Cr were isolated. If amalgam alloy was in the opposite arch or it was apart from Talladium alloy for denture, the isolation Hg was less than that when amalgam alloy contacted Talladium alloy for denture. Sixth, according to the result of ICPES test on Cu, Sn, Ag, Hg, Zn, Ni and Cr of amalgam alloy, gold ally, Verabond and Talladium alloy when these alloys contacted artificial saliva, significance was observed in Cu and Hg. Seventh, when amalgam alloy contracted two non-precious metals Ni-Cr alloy for crown and Talladium alloy for denture in artificial saliva, significance was observed in the isolated by-products of Hg, Ni and Cr according to distance.

• Journal of Technologic Dentistry
• /
• v.24 no.1
• /
• pp.65-71
• /
• 2002

This study was performed to observe the microhardness change of the surface and the bonding strength between the porcelain and alloy specimens in order to investigate the effects of appended indium, tin and copper on interfacial properties of Au-Pd-Ag alloys. The hardness of castings was measured with a micro-Vicker's hardness tester. The interfacial shear bonding strength between alloy specimen and fused porcelain was measured with a mechanical testing system(MTS 858.20). The microhardness of Au-Pd-Ag alloy was increased by adding indium and tin, but not increased by adding copper. The shear bonding strength of Au-Pd-Ag-Sn alloy and Au-Pd-Ag-Cu alloy showed 87MPa, 57MPa. The higher concentration of adding elements showed the higher shear bonding strength.