• Journal of Technologic Dentistry
• /
• v.31 no.3
• /
• pp.15-20
• /
• 2009

The success of the porcelain fused to gold alloy restoration depends not only on the choice of materials but to a larger degree on the technical skills. The porcelain fused to metal(PFM) alloys containing gold are commonly use for dental purposes in dental laboratory. The gold-colored alloys contain primarily gold, platinum, palladium, and silver, with minimum amounts of such metals as tin, iridium, or titanium. The purpose of this study is on the metal-porcelain fusing layer in porcelain fused to high gold alloy Principal results are as follows. The hardness number(Hv) of PFG is respectively $140.2{\pm}12.6$ in as-casted, $164.3{\pm}14.3$ in heat-treated, $186.6{\pm}20.4$ in fired-treated. The formation of the fusing(intermediate) layer caused by components fusing the interface of porcelain and gold alloy. The main components of the fusing(intermediate) layer are Na, Al, Si, K, Zn, Zr and Ce. The intermediate layer formed by the 2nd firing is more larger than the intermediate layer formed by the 1st firing.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.79-80
• /
• 2013

The purpose of this study was to investigate $2^{nd} $nanotube formed surface observation of the Ti-25Ta-xZr alloys using ATO(anodic titanium oxide) technique. Ti-25Ta-xZr alloy was anodized in 1M $H_3PO_4$ electrolytes containing 0.8 Wt. % NaF at room temperature. After formation of nanotube was achieved out, nanotube was eliminated, and then anodization was carried out repeatedly. The microstructures, phase transformation, and morphology of nanotubular Ti-25Ta-xZr alloys and process of nanotube growth by using ATO method was examined by optical microscopy (OM), X-ray diffraction (XRD), and field emission scanning electron microscopy (FE-SEM). The ${\alpha}$ phase and ${\beta}$ phases were affected to form the second nanotube morphology of Ti-25Ta-xZr alloys.

• Journal of Technologic Dentistry
• /
• v.27 no.1
• /
• pp.19-25
• /
• 2005

Ti6Al4V alloy have been mainly used as implant materials. Ti-6Al-4V alloy instead of pure Ti is being widely used as biomaterials has some characteristics such as high fatigue strength, tensile strength. But it has been reported recently that vanadium component expresses cytotoxicity and carcinogenicity and aluminium component is related with dementia of Alzheimer type. In order to overcome their detrimental effects, $\beta$-phase stabilizer Nb was chosen in the present study, in addition Ta and Hf were added to Ti-40wt.%Nb alloy to improve its mechanical properties. This paper was described the influence of heat treatment of Ti-40Nb alloys with 2wt%Ta, 2wt%Hf on the mechanical properties. Specimens of Ti alloys were melted in vacuum arc furnace and homogenized at 1050$^{\circ}C$ for 24 hr. and then were aged after solution heat treat at $\alpha+\beta$ and $\beta$ regions. The mechanical properties of Ti alloys were analysed by hardness test, tensile test, elongation test and SEM test. The results can be summarized as follows: 1. The mechanical properties Ti-40wt.%Nb were improved when 2wt.% Ta and 2wt.%Hf were added. 2. The higher tensile strength value and elongation at solution heat treat was higher than solution heat treat and then were aged.

• Korean Journal of Materials Research
• /
• v.14 no.6
• /
• pp.432-435
• /
• 2004

Ti and Ti alloys are important materials for medical and dental applications. The effect of equal channel angular process(ECAP) and addition of Fe in Ti were studied with optical microstructure and corrosion behavior. Fine grains in Ti was obtained after ECAP. Corrosion behavior of commercial pure(CP)-Ti and Ti alloys was studied by open circuit test and polarization curve test(PCT) at $36.5^{\circ}C$ with SBF in biological environment. The corrosion behavior of ECAP-Ti was similar to that of CP-Ti in PCT, but Ti-Fe alloys were observed to become more corrosive with increasing Fe content.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.112-112
• /
• 2015

The purposed of this work was to determine nanotube shape variation on the Ti-xNb alloys with alloying elements and applied potentials. Samples were prepared by arc melting, followed by followed by homogenization for 12 hr at $1000^{\circ}C$ in argon atmosphere. This study was evaluated the phase and microstructure of Ti-xNb alloys using an X-ray diffraction (XRD) and optical microscopy (OM). The morphology of the samples was investigated with a field-emission scanning electron microscope (FE-SEM) and energy dispersive X-ray spectroscopy (EDS). The nanotube on the alloy surface was formed in 1 M $H_3PO_4$ with small additions of NaF 0.8 wt.%. All anodization treatments were carried out using a scanning potentiostat (Model 362, EG&G, USA) at constant voltage 30 V for 120 min, respectively. The morphology of the samples was investigated with a field-emission scanning electron microscope (FE-SEM) and energy dispersive X-ray spectroscopy (EDS). Surface characteristics of nanotbue formed on Ti-xNb alloys was investigated by potentiodynamic test and potentiostatic in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. It was observed that the changed ${\alpha}$ phase to ${\beta}$ phase with Nb content.

• Journal of Technologic Dentistry
• /
• v.32 no.3
• /
• pp.195-207
• /
• 2010

Purpose: The purpose of this study was to observe the microstructural changes of surface in the specimens, performing the shear bond strength testing. The currently most used non-precious alloys are nickel-chromium based alloys with or without beryllium. However, their biocompatibility has been questioned concerning possible damages to the health of the patient and professionals involved in the fabrication of prosthesis caused by long exposure to Ni and Be. An option to nickel-chromium alloys is the cobalt-chromium alloy, an alternative that does not sacrifice the physical properties of the metal porcelain systems. Studies in the animals substantially show that the cobalt-chromium alloys are relatively well tolerated, being therefore more biocompatible than the nickel-chromium alloys. Methods: Non-addition Be to nickel-chromium based alloy(Bellabond plus) and cobalt-chromium alloy which has been widely used(Wirobond C) fused with ZEO light porcelain classified control group and cobalt-chromium alloy which is developing alloy of Alphadent company in Korea(Alphadent alloy) fused with ZEO light porcelain classified experimental group. The specimens of $4mm{\times}4mm{\times}0.5mm$ were prepared as-cast and as-opaque to cast body to analyze the mechanical characteristic change, the microstructure of alloy surface. The phase change was used to observe through XRD analysis and OM/SEM was used to observe the surface of specimens as-cast and as-opaque to cast body. Chemical formation of their elements was measured with EDS. Then hardness was measured with Micro Vicker's hardness tester. Shear bond strength test thirty specimens of $10mm{\times}10mm{\times}2mm$ was prepared, veneered, 3mm high and 3mm in diameter, over the alloy specimens. The shear bond strength test was performed in a universal testing machine(UTM) with a cross head speed of 0.5mm/min. Ultimate shear bond strength data were analyzed with one-way ANOVA and the Scheffe's test (P<0.05). Within the limits of this study, the following conclusions were drawn: The X-ray diffraction analysis results for the as-cast and as-opaque specimens showed that the major relative intensity of Bellabond plus alloy were changed smaller than Wirobond C and Alphadent Co-Cr based alloys. Results: Microstructural analysis results for the opaque specimens showed all the alloys increased carbides and precipitation(PPT). Alphadent Co-Cr based alloy showed the carbides of lamellar type. The Vickers hardness results for the opaque specimens showed Wirobond C and Alphadent Co-Cr based alloys were increaser than before ascast, but Bellabond plus alloy relatively decreased. The mean shear bond strengths (MPa) were: 33.11 for Wirobond C/ZEO light; 25.00 for Alphadent Co-Cr alloy/ZEO light; 18.02 for Bellabond plus/ZEO light. Conclusion: The mean shear bond strengths for Co-Cr and Ni-Cr based alloy were significantly different. But the all groups showed metal-metal oxide modes in shear bond strengths test at the interface.

• Corrosion Science and Technology
• /
• v.8 no.4
• /
• pp.162-169
• /
• 2009

Pure titanium and its alloys are drastically used in implant materials due to their excellent mechanical properties, high corrosion resistance and good biocompatibility. However, the widely used Ti-6Al-4V is found to release toxic ions (Al and V) into the body, leading to undesirable long-term effects. Ti-6Al-4V has much higher elastic modulus than cortical bone. Therefore, titanium alloys with low elastic modulus have been developed as biomaterials to minimize stress shielding. For this reason, Ti-30Ta-xZr alloy systems have been studied in this study. The Ti-30Ta containing Zr(5, 10 and 15 wt%) were 10 times melted to improve chemical homogeneity by using a vacuum furnace and then homogenized for 24 hrs at $1000^{\circ}C$. The specimens were cut and polished for corrosion test and Ti coating and then coated with TiN, respectively, by using DC magnetron sputtering method. The analyses of coated surface were carried out by field emission scanning electron microscope(FE-SEM). The electrochemical characteristics were examined using potentiodynamic (- 1500 mV~+ 2000 mV) and AC impedance spectroscopy(100 kHz~10 mHz) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The equiaxed structure was changed to needle-like structure with increasing Zr content. The surface defects and structures were covered with TiN/Ti coated layer. From the polarization behavior in 0.9% NaCl solution, The corrosion current density of Ti-30Ta-xZr alloys decreased as Zr content increased, whereas, the corrosion potential of Ti-30Ta-xZr alloys increased as Zr content increased. The corrosion resistance of TiN/Ti-coated Ti-30Ta-xZr alloys were higher than that of the TiN-coated Ti-30Ta-xZr alloys. From the AC impedance in 0.9% NaCl solution, polarization resistance($R_p$) value of TiN/Ti coated Ti-30Ta-xZr alloys showed higher than that of TiN-coated Ti-30Ta-xZr alloys.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.12
• /
• pp.434-439
• /
• 2020

Selective laser melting (SLM) manufactures an alloy using laser as a heat source, and has recently been introduced in the dental industry. However, there is a lack of analytical research on metal-ceramic restorations achieved by SLM. This study evaluates and compares the metal-ceramic bond strength of Co-Cr alloys produced by selective laser melting and casting methods. Co-Cr samples required for this study were produced through the sintering process of ceramics, by applying the SLM and CAST methods. The metal-ceramic bond strength was measured by applying the shear bond strength test. In order to determine the area fraction of adherent ceramic, Si content of the specimen was measured using scanning electron microscopy SEM/ EDS. Results of the metal-ceramic bond strength and AFAC were analyzed by t-test (α = 0.05). No significant difference was observed comparing the bond strength of SLM and CAST Co-Cr alloys (P> 0.05). However, the SLM group had much better ceramic adherence than the CAST group (P < 0.001). Moreover, oxidation characteristics were similar for both SLM and CAST Co-Cr alloys, but metal structures were different. These results imply that although the bond of ceramic and Co-Cr alloy is not related to the manufacturing method, SLM alloys impart better ceramic adherence. This indicates that alloys made with SLM can be used to fabricate upper implant prostheses in the future. In particular, it is expected to overcome the shortcomings of the CAST method, and save time and cost.

• The Journal of Korean Academy of Prosthodontics
• /
• v.14 no.1
• /
• pp.31-34
• /
• 1976

The author studied the effects of some dental gold alloys and dental nonprecious metals on muscle. The metal specimens were cast in the size of $1.0mm.{\times}5.0mm.{\times}3.0mm.$ and implanted in the gluteus maximus musculus of the two dogs. The subjects were sacrificed at 3 weeks and 5 weeks respectively after implantation. The tissue was examined his to-pathologically. The findings were as follows. 1. The more the alloy contains gold, the less the tissue response to the alloy and the less the connective tissue layer around the specimens. 2. The recovery of connective tissue layer in gold specimens was markedly observed. 3. There were very thick connective layers around nonprecious specimens.

• Journal of Technologic Dentistry
• /
• v.13 no.1
• /
• pp.9-13
• /
• 1991

The purpose of this study was to determine the marginal fit of recasting by used nickel-chromium metal alloys, Hi-Crown, New-Crown and CB-80. Ninety crown prosthetics were divided into eighteen groups according to new to old metal ratios. Each crown was seated on its master die and then the marginal gaps were measured under optical microscope($\times$50). All groups were showed good marginal fit, except group 3 of Hi-Crown(156$\mu$m). The results suggest that the marginal fit of Ni-Cr metal alloy casting bodies were good as without concerned to mixed ratios and metals.