• 한국세라믹학회지
• /
• 제36권7호
• /
• pp.718-724
• /
• 1999

Densification and grain growth behavior of bimodal size distributed alumina powder mixtures were investigated as a function of amount of coarse alumina powder. The specimens which contained coarse alumina powder for 60to 80wt% showed the highest green density. The amount of shrinkage of sintered specimen lineraly decreased with the increase of coarse alumina powder up to the content that showed the highest green density and then further addition of coarse alumina powder led to drastic decrease of shrinkage of specimen. Especially crack-like void were concurrently revealed in the sintered body with addition of coarse alumina powder above 60wt% When the sintering temperature increased up to 1650$^{\circ}C$ the amount of shrinkage of specimen linearly decreased and the grain growth were also retarded with increase of coarse lauminia powder.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1153-1154
• /
• 2006

Effects of sintering conditions such as sintering temperature and heating rate on oxygen content, density, microstructure and toughness of sintered Mo were investigated. The oxygen content of the sintered Mo significantly depended on the sintering conditions. The oxygen content of the primary sintered(below 1673 K) Mo influenced the densifications. The number of pores at grain boundaries of the secondary sintered(at 2073 K)Mo depended on the oxygen content of the primary sintered Mo. Grain growth of the secondary sintered Mo was inhibited by the existence of pores at the grain boundaries. The secondary sintered Mo having larger number of pore and smaller grain size demonstrated higher strength.

• 한국분말재료학회지
• /
• 제14권3호
• /
• pp.208-214
• /
• 2007

The microstructure and hardness of (W,Ti)C cemented carbides with a different metallic binder composition of Ni and Co fabricated by powder technology were investigated. The densifications of the prepared materials were accomplished by using vacuum sintering at $1450^{\circ}C$. Nearly full dense (W,Ti)C cemented carbides were obtained with a relative density of up to 99.7% with 30 wt.% Co and 99.9% with 30 wt.% Ni as a metallic binder. The average grain size of the (W,Ti)C-Co and the (W,Ti)C-Ni was decreased by increasing the metallic binder content. The hardness of the dense (W,Ti)C-15 wt%Co and (W,Ti)C-15 wt%Ni, was greater than that of the other related cemented carbides; in addition, the cobalt-based cemented carbides had greater hardness values than the nickel-based cemented carbides.

• Journal of the Korean Wood Science and Technology
• /
• 제48권2호
• /
• pp.196-205
• /
• 2020

The purpose of this study was to investigate a method for improving the physical and mechanical properties of laminated board made from oil palm trunk (OPT). The effects of pretreating the lamina with heat-pressure and altering the lamina composition of the laminated board were investigated. The outer third of OPT in cross-section had high-density wood, while the underlying third had low to medium density. The hot press was applied to pretreat the lamina that had low to medium density. The lamina were 1.5 cm in thickness, 5 cm in width, and 65 cm in length. The hot press was applied at 2.94 MPa or 4.41 MPa at 150 ℃ for 60 minutes, and the target thickness of the lamina was 1 cm. The three layers of the laminated board samples were bonded with isocyanate adhesive at a glue spread of 300 g/㎡ and cold pressed at 0.98 MPa for 3 h. The laminated board samples were tested according to Japanese Agricultural Standard (JAS) 234-2003. The results showed that the densification of the inner lamina did not significantly affect the physical-mechanical properties of the laminated board produced. However, the laminated board made with high-density laminas for the outer layers fulfilled the JAS 234-2003 standard for the modulus of elasticity and the modulus of rupture.

• 한국광물학회지
• /
• 제30권3호
• /
• pp.83-91
• /
• 2017

천연산 녹주석($Be_3Al_2Si_6O_{18}$, P6/mcc) 중 산출지가 각각 다른 아쿠아마린 시료인 녹주석-A, 녹주석-B를 물을 압력전달 매개체로 사용하여 고압실험 및 고온-고압실험을 실시하였다. 기존 문헌과 다르게 압력전달 매개체로 물을 이용했을 때 고압 및 고온-고압 상태에서 녹주석의 조성과 구조에 어떠한 영향을 주며 탄성 특성이 어떻게 변하는지를 확인하기 위함이다. 그 결과 녹주석-A, B의 체적탄성률은 각각 111(7) GPa, $K{_0}^{\prime}=73(7)$; 110(9) GPa, $K{_0}^{\prime}=65(8)$로 확인되었다. 이는 기존 연구에서 메탄올 에탄올 4 : 1 체적비로 혼합하여 관찰한 것과 다른 값 및 경향성을 보여주는 것으로 확인하였으며 관찰된 녹주석의 치밀화는 ICE VI, ICE VII 상변이 구간인 약 1.0 GPa, 약 2.5 GPa 구간과 일치하였다.

• 한국세라믹학회지
• /
• 제48권2호
• /
• pp.168-172
• /
• 2011

Alumina powder was added in a general porcelain (Backja) with clay, feldspar and quartz contents to promote the mullite ($3Al_2O_3{\cdot}2SiO_2$) generation in the porcelain. Low melting materials ($B_2O_3(450^{\circ}C)$, $MnO_3(940^{\circ}C)$, CuO($1080^{\circ}C$)) were doped at ~3 wt% to modify the sinterability of porcelain with a high alumina contents and promote the mullite generation. Green body was made by slip casting method with blended slurry and then, they were fired at $1280^{\circ}C$ for 1hr by a $2^{\circ}C/min$. Densifications of samples with high alumina contents (20~30 wt%) were impeded. As the doping contents of low melting materilas increased, the sinterability of samples was improved. The shrinkage rate and bulk density of samples were improved by doping with low melting materials. Mullite phase increased with increasing the low melting contents in the phase analyses. This means lots of alumina and quartz were transformed into mullite phase by low melting contents doping. In the results, high bending strength of samples with high alumina contents was accomplished by improving the densification and mullite generation in the porcelain.