• Journal of the Korean Ceramic Society
• /
• v.36 no.7
• /
• pp.718-724
• /
• 1999

Densification and grain growth behavior of bimodal size distributed alumina powder mixtures were investigated as a function of amount of coarse alumina powder. The specimens which contained coarse alumina powder for 60to 80wt% showed the highest green density. The amount of shrinkage of sintered specimen lineraly decreased with the increase of coarse alumina powder up to the content that showed the highest green density and then further addition of coarse alumina powder led to drastic decrease of shrinkage of specimen. Especially crack-like void were concurrently revealed in the sintered body with addition of coarse alumina powder above 60wt% When the sintering temperature increased up to 1650$^{\circ}C$ the amount of shrinkage of specimen linearly decreased and the grain growth were also retarded with increase of coarse lauminia powder.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1153-1154
• /
• 2006

Effects of sintering conditions such as sintering temperature and heating rate on oxygen content, density, microstructure and toughness of sintered Mo were investigated. The oxygen content of the sintered Mo significantly depended on the sintering conditions. The oxygen content of the primary sintered(below 1673 K) Mo influenced the densifications. The number of pores at grain boundaries of the secondary sintered(at 2073 K)Mo depended on the oxygen content of the primary sintered Mo. Grain growth of the secondary sintered Mo was inhibited by the existence of pores at the grain boundaries. The secondary sintered Mo having larger number of pore and smaller grain size demonstrated higher strength.

• Journal of Powder Materials
• /
• v.14 no.3 s.62
• /
• pp.208-214
• /
• 2007

The microstructure and hardness of (W,Ti)C cemented carbides with a different metallic binder composition of Ni and Co fabricated by powder technology were investigated. The densifications of the prepared materials were accomplished by using vacuum sintering at $1450^{\circ}C$. Nearly full dense (W,Ti)C cemented carbides were obtained with a relative density of up to 99.7% with 30 wt.% Co and 99.9% with 30 wt.% Ni as a metallic binder. The average grain size of the (W,Ti)C-Co and the (W,Ti)C-Ni was decreased by increasing the metallic binder content. The hardness of the dense (W,Ti)C-15 wt%Co and (W,Ti)C-15 wt%Ni, was greater than that of the other related cemented carbides; in addition, the cobalt-based cemented carbides had greater hardness values than the nickel-based cemented carbides.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.2
• /
• pp.196-205
• /
• 2020

The purpose of this study was to investigate a method for improving the physical and mechanical properties of laminated board made from oil palm trunk (OPT). The effects of pretreating the lamina with heat-pressure and altering the lamina composition of the laminated board were investigated. The outer third of OPT in cross-section had high-density wood, while the underlying third had low to medium density. The hot press was applied to pretreat the lamina that had low to medium density. The lamina were 1.5 cm in thickness, 5 cm in width, and 65 cm in length. The hot press was applied at 2.94 MPa or 4.41 MPa at 150 ℃ for 60 minutes, and the target thickness of the lamina was 1 cm. The three layers of the laminated board samples were bonded with isocyanate adhesive at a glue spread of 300 g/㎡ and cold pressed at 0.98 MPa for 3 h. The laminated board samples were tested according to Japanese Agricultural Standard (JAS) 234-2003. The results showed that the densification of the inner lamina did not significantly affect the physical-mechanical properties of the laminated board produced. However, the laminated board made with high-density laminas for the outer layers fulfilled the JAS 234-2003 standard for the modulus of elasticity and the modulus of rupture.

• Journal of the Mineralogical Society of Korea
• /
• v.30 no.3
• /
• pp.83-91
• /
• 2017

In-situ high-pressure and ex-situ high temperature-pressure experiments of natural beryl ($Be_3Al_2Si_6O_{18}$, P6/mcc) from two different localities (beryl-A and beryl-B) were studied using pure water as pressure transmitting medium. Compared to the previous study using a mixture of methanol:ethanol medium in 4 : 1 by volume, pressure- and temperature-induced chemical and structural changes under water medium are expected to be different. The derived bulk moduli are 111(7) GPa, $K{_0}^{\prime}=73(7)$; 110(9) GPa, $K{_0}^{\prime}=65(8)$ for beryl-A and beryl-B, respectively. We observe densifications in volume compression, which appear to be attributed to the phase transitions of water to ICE VI and ICE VII around 1.0 GPa and 2.5 GPa, respectively.

• Journal of the Korean Ceramic Society
• /
• v.48 no.2
• /
• pp.168-172
• /
• 2011

Alumina powder was added in a general porcelain (Backja) with clay, feldspar and quartz contents to promote the mullite ($3Al_2O_3{\cdot}2SiO_2$) generation in the porcelain. Low melting materials ($B_2O_3(450^{\circ}C)$, $MnO_3(940^{\circ}C)$, CuO($1080^{\circ}C$)) were doped at ~3 wt% to modify the sinterability of porcelain with a high alumina contents and promote the mullite generation. Green body was made by slip casting method with blended slurry and then, they were fired at $1280^{\circ}C$ for 1hr by a $2^{\circ}C/min$. Densifications of samples with high alumina contents (20~30 wt%) were impeded. As the doping contents of low melting materilas increased, the sinterability of samples was improved. The shrinkage rate and bulk density of samples were improved by doping with low melting materials. Mullite phase increased with increasing the low melting contents in the phase analyses. This means lots of alumina and quartz were transformed into mullite phase by low melting contents doping. In the results, high bending strength of samples with high alumina contents was accomplished by improving the densification and mullite generation in the porcelain.