• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2003.04a
• /
• pp.113-116
• /
• 2003

The investigation of delamination growth behavior in hybrid composite material such as FRMLs should be considered delamination growth rate, dA_D/da$ using the delamination shape factor, $f_S$ instead of traditional fracture mechanics parameters. The main objective of this study is to evaluate the relationship between delamination element (i. e. delamination width, b, delamination contour, c, delamination shape factor, $f_S$ and delamination growth rate, dA_D/da$) and delamination growth in FRMLs under cyclic bending moment. The delamination shape formed along the fatigue crack between aluminum layer and glass fiber/epoxy layer are measured by scanning method. The details of study are as follow : ⅰ) Relationship between crack length, a and delamination width, b. ⅱ) Variation of delamination growth rate, dA_D/da$ was attendant on delamination shape factors, $f_{S1}$, $f_{S2}$, $f_{S3}$. The test result indicated the delamination growth behavior depends in delamination element such as delamination width, b, delamination shape factors, $f_{S1}$, $f_{S2}$, $f_{S3}$.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2003.04a
• /
• pp.398-404
• /
• 2003

Most previous researches for the hybrid composite materials such as FRMLs(Al/AFRP, Al/GFRP) have evaluated the fatigue delamination behavior using the traditional fracture mechanism. However, most previous researches have not generally been firmed yet. Because delamination growth behavior in hybrid composite should be consider delamination growth rate, $dA_D$/da using the delamination shape factors, fs instead of traditional fracture mechanic parameters. The major purpose of this study was to evaluate the relationship between delamination shape factor, fs and delamination growth rate, $dA_D$ . And a propose parameter on the delamination aspect ratio, b/a. The details of the study are as follow : 1) Relationship between crack length, a and delamination width,b. 2) Relationship between delamination aspect ration, b/a and delamination area rate,($(A_D)_{N}(A_D)_{ALL}$. 3) Variation of delamination growth rate, $dA_D/da$ was attendant on delamination shape factors, $fs_1$, $fs_2$, $fs_3$. The test results indicated the delamination growth rate depends on delamination shape factors.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.1
• /
• pp.55-62
• /
• 2004

Although the previous researches evaluated the fatigue behavior of glass fiber/epoxy laminates using the traditional fracture mechanism, their researches were not sufficient to do it: the damage zone of glass fiber/epoxy laminates was occurred at the delamination zone instead of the crack-metallic damages. Thus, previous researches were not applicable to the fatigue behavior of glass fiber/epoxy laminates. The major purpose of this study was to evaluate delamination behavior using the relationship between crack length and delamination width in hybrid composite material such as Al/GFRP laminate. The details of investigation were as follows : 1) Relationship between crack length and delamination width, 2) Relationship between delamination aspect ratio and delamination area rate, 3) Variation of delamination growth rate is attendant on delamination shape factors. The test results indicated that the delamination growth rate depends on delamination width delamination aspect ratio and delamination shape factors.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.1349-1353
• /
• 2003

Previous researches for fiber reinforced composite material(FRCM) have been evaluated the fatigue delamination behavior using the traditional fracture mechanics parameters. Therefore. previous researches for FRCM have not generally been firmed yet. Because delamination growth behavior in FRCM should be consider relationship between delamination area, A$\sub$D/ and crack length, a instead of traditional fracture mechanics parameters. Especially, in case of delamination behavior for FRCM without crack should be considering equivalent crack, i.e., pseudo crack, a$\sub$p/, using the fracture behavior of FRCM with crack. The major purpose of this study was to evaluate the delamination for FRCM without crack. The details of the studies are as follow : 1) Relationship between crack growth rate, da/dN and stress intensity factor, ΔK in FRCM containing a saw-cut and circular hole with crack. 2) Propose of PSEUDO CRACK MODEL for the delamination in FRCM without crack. 3) Analysis of crack propagation energy, E$\sub$crack/ using a total energy, E$\sub$total/ and delamination growth energy, E$\sub$del/.

• Structural Engineering and Mechanics
• /
• v.48 no.1
• /
• pp.41-56
• /
• 2013

Initiation and growth of delamination is a great concern of designers of composite structures. Interface elements with de-cohesive constitutive law in the content of continuum damage mechanics can be used to predict initiation and growth of delamination in single and mixed mode conditions. In this paper, an interface element based on the cohesive zone method has been developed to simulate delaminatoin growth of post-buckled laminate under fatigue loading. The model was programmed as the user element and user material by the "User Programmable Features" in ANSYS finite element software. The interface element is a three-dimensional 20 node brick with small thickness. Because of mixed-mode condition of stress field at the delamination-front of post-buckled laminates, a mixed-mode bilinear constitutive law has been used as user material in this model. The constitutive law of interface element has been verified by modelling of a single element. A composite laminate with initial delamination under quasi-static compressive Loading available from literature has been remodeled with the present approach. Moreover, it will be shown that, the closer the delamination to the free surface of laminate, the slower the delamination growth under compressive fatigue loading. The effects of laminate configuration on delamination growth are also investigated.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.2
• /
• pp.317-326
• /
• 2003

The influence of cyclic bending moment on the delamination and the fatigue crack propagation behavior in Al/GFRP laminate such as the wing section was investigated. The main objective of this study was to evaluate the relationship between crack profile and delamination behavior. And a propose parameter on the delamination growth rate(d $A_{D}$/da) of Al/GFRP laminates with a saw-cut using relationship between delamination area( $A_{D}$) and cycles(N), crack length(a), stress intensity factor range($\Delta$K). Also, the fiber bridging effect factor( $F_{BE}$ ) was propose that the fiber bridging modification factor($\beta$$_{fb}$ ) to evaluate using the delamination growth rate(d $A_{D}$/da). The shape and size of the delamination zone formed along the fatigue crack between aluminum alloy sheet. Class fiber-adhesive layer were measured by an ultrasonic C-scan image. The shape of delamination zone turns out to be semi-elliptic with the contour decreased non-linearly toward the crack tip. It represents that relationship between crack length and delamination growth rate(d $A_{D}$/da) were interdependent by reciprocal action, therefore it's applicable present a model for the delamination growth rate(dA/sib D//da) in Al/GFRP laminates.minates.s.

• Journal of Ocean Engineering and Technology
• /
• v.16 no.6
• /
• pp.55-59
• /
• 2002

Delamination means that cracking occurs on the interface layer between composite laminates. In this paper, to predict the delamination growth in composite laminates subjected to low-velocity impact, the unit load method was introduced, and an eighteen-node 3-D finite element analysis, based on assumed strain mixed formulation, was conducted. Strain energy release rate, necessary to determine the delamination growth, was calculated by using the virtual crack closure technique. The unit load method saves the computation time more than the re-meshing method. The virtual crack closure technique enables the strain energy release rate to be easily calculated, because information of the singular stress field near the crack tip is not required. Hence, the delamination growth in composite laminates that are subjected to low-velocity impact can be efficiently predicted using the above-mentioned methods.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.8
• /
• pp.2491-2500
• /
• 1996

An experimental and analytical investigation is performed to study the buckling behavior of composite laminates with an embedded delamination. It is of particular interest to veryfy whether delamination growth cddurs with continuming deformation after buckling of composite laminates with an embedded delamination. Experiments are conducted for [0/sub 4///90/sub 8//0/sub 4/]/sub r/ laminates with delamination size in which local buckling mode governs buckling. Results show that delamination growth occurs in hgigher load after buckling and is accompanid by other damage mechanisms such as splitting. Also, it is found that transverse deformation before difurcation buckling is due to initial imperfection and structure such as plate with small bending stiffness is sensitive to that.

• Journal of Mechanical Science and Technology
• /
• v.17 no.3
• /
• pp.343-349
• /
• 2003

The fuselage-wing intersection suffers from the cyclic bending moment of variable amplitude. Therefore, the influence of cyclic bending moment on the delamination and the fatigue crack propagation behavior in AFRP/Al laminate of fuselage-wing was investigated in this study. The cyclic bending moment fatigue test in AFRP/Al laminate was performed with five levels of bending moment. The shape and size of the delamination Lone formed along the fatigue crack between aluminum sheet and aramid fiber-adhesive layer were measured by an ultrasonic C-scan. The relationships between da/dN and ΔK, between the cyclic bending moment and the delamination zone size, and between the fiber bridging behavior and the delamination zone were studied. As results, fiber failures were not observed in the delamination zone in this study, the fiber bridging modification factor increases and the fatigue crack growth rate decrease and the shape of delamination zone is semi-elliptic with the contour decreasing non-linearly toward the crack tip.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.1402-1405
• /
• 2003

The main object of this study was evaluated by the delamination damage for fiber stacking angle. Therefore, this work need to compare the shape of delamination for a different fiber stacking angie. So this study uses a method of fatigue test which was created [0]$_2$,[+45]$_2$[90]$_2$. The extension of the delamination zone formed between aluminium alloy and glass fiber-adhesive layer were measured by an ultrasonic C-scan image. As a result, the shapes of delamination zone don't depend upon the crack propagation. We could know that the delamination zone grew interaction between stress flow of fiber layer and crack driving force. Hence, the existing study were applied to the stress transfer, fiber bridging effect, delaminantion growth rate should need to the develop useful factor because of change of fiber stacking angle.