• 한국기계연구소 소보
• /
• 통권18호
• /
• pp.163-168
• /
• 1988

Impregnation of molten thermoplastic resin into continuous unidirectional fiber bundles was investigated. The degree of impregnation is defined as the ratio between the number of impregnated fibers and the total number of fibers of a bundle. The degree of impregnation was modeled as a function of time, impregnation pressure, temperature and tow size assuming the radial inward flow through the fiber bundle is governed by the Darcy's law. The permeability was assumed to be constant. Experiments were performed to evaluate the validity of the medel. Today's T300 graphite fiber bundles and Polyetheretherketone(PEEK) resin was used. A fiber bundle and resin powder were put into a mold and pressure and temperature were applied. After a predetermined time, the sample was taken out and microphotographs of the cross-section were taken. From the microphotographs, the number of impregnated fibers was counted and then the degree of impregnation was determined. Experiments were also performed for different tow sizes. Good agreements were found between the model and the experiments rendering a confidence in the model.

• 한국가구학회지
• /
• 제14권2호
• /
• pp.21-29
• /
• 2003

This study was carried out to investigate characteristics of plywood overlaid with softwood veneers densified by resin impregnation and compression. The resin impregnability of Korean pine veneer under atmospheric pressure soaking was greater than that of larch, and impregnability of melamine resin was slightly greater than phenolic resin. It was suggested that resin impregnation ratio was affected by density and thickness of veneer. The largest melamine resin impregnation ratio of 50.7% was obtained with 1.26mm thick Korean pine veneer, and the lowest phenolic resin impregnation ratio of 11.7% with 3.41mm thick larch veneer. Therefore, it was suggested that the vacuum-pres sure-soak treatment is required at thick larch veneer. In densifying resin-impregnated veneers, densification ratio from 13.4 to 31.2% was obtained by high pressure from 15.6 to $20.8kgf/cm^2$. Impregnation of melamine resin also showed relatively greater at densification than that of phenolic resin. So it showed the degree of densification of about 20% or greater. It was seemed that adhesive bonding strength of plywood(base panel) which was directly pressed and overlaid with resin-impregnated veneer was affected by resin tackiness after resin impregnation followed by semi-drying. In laboratory scale, melamine resin impregnation was more favorable for the development of adhesive bonding strength owing to moisture control.

• 한국생산제조학회지
• /
• 제22권5호
• /
• pp.806-811
• /
• 2013

In this study, to prevent the nonhomogeneity of fiber orientation during the molding of GFRP composites, GFRP prepreg was fabricated using roving fiber and polypropylene resin. Analyses on the degree of impregnation, tensile strength, and microstructure were conducted on the fabricated prepregs. A lower pulling speed, higher resin temperature, and longer die length showed a greater degree of impregnation of the prepreg. The scanning electron microscope (SEM) micrograph showed, a homogeneous fiber orientation. As a result, fundamental techniques for improved productivity were suggested for the manufacturing field.

• 펄프종이기술
• /
• 제36권4호
• /
• pp.41-48
• /
• 2004

To make a basepaper for multipurposed seed paper, old news print (ONP) and mixed office waste paper (MOW), modified and unmodified with a commercial cellulase, were investigated. Each handsheet was applied with different chemicals such as insecticides, germicides and herbicides. The interactions behaviors of chemicals used with base papers were evaluated by means of the contents of chemicals impregnation and dissolving behaviors in water and soil. The ONP and MOW treated with the cellulase had higher impregnation and dissolving capacities in both water and soil than untreated ONP and MOW. However, the modified ONP showed lower impregnation and dissolving capacities compared to the modified MOW. The content of impregnation of chemicals would be affected with the degree of microfibrils produced by the modification treatment. Otherwise, dissolving capacities of chemicals depend on the affinity of the residual lignin in the paper.

• Design & Manufacturing
• /
• 제16권2호
• /
• pp.60-65
• /
• 2022

In the pultrusion process for the CFRP (Carbon fiber reinforced plastic) rectangular pipe, the drawing device is eseential which can continuously produces products and draws the carbon fiber tow. In addition, since the degree of cure changes depending on the temperature and the temperature ditribution of the curing mold changes depending on the pultrusion speed, the temperature distribution of the curing mold under certain conditions must be studied before processing. In this study, in the pultrusion process using a closed impregnation method, which has several advantages compared to the general pultrusion process using a open bath impregnation method, the drawing force required to pull the carbon fiber tows and the temperature distribution of the curing mold was analyzed to design the drawing device and the curing mold efficiently.

• Composites Research
• /
• 제26권4호
• /
• pp.230-234
• /
• 2013

본 연구에서는 연속 유리섬유 강화 폴리유산 복합재료를 직접함침방법을 이용하여 제조하였고, 이의 기계적 열적 물성이 고찰되었다. 프리프레그의 물성은 기존의 알려진 폴리유산의 물성과 사출 성형으로 제조된 유리섬유 강화 폴리유산 복합소재와 비교 평가되었으며, 섬유체적분율 27.7% 를 갖는 연속 유리섬유 강화 폴리유산 복합재료의 인장응력, 굽힘응력, 굴곡탄성율은 각각 331.1 MPa, 528.6 MPa, 24.0 GPa의 향상된 값을 보였다. 또한 향상된 열변형 온도와 결정화도가 확인되었다. 생산속도에 따른 함침도가 고찰되었고, 그 결과 본 연구에 사용된 공정조건에서는 분당 5 m의 섬유당김속도에서 함침도 90% 이상의 연속 유리섬유 강화 폴리유산 복합재료를 제조가능하였다.

• Carbon letters
• /
• 제15권2호
• /
• pp.142-145
• /
• 2014

Isotropic synthetic graphite scrap and phenolic resin were mixed, and the mixed powder was formed at 300 MPa to produce a green body. New bulk graphite was produced by carbonizing the green body at $700^{\circ}C$, and the bulk graphite thus produced was impregnated with resin and re-carbonized at $700^{\circ}C$. The bulk density of the bulk graphite was $1.29g/cm^3$, and the porosity of the open pores was 29.8%. After one impregnation, the density increased to $1.44g/cm^3$ while the porosity decreased to 25.2%. Differences in the pore distribution before and after impregnation were easily confirmed by observing the microstructure. In addition, by using an X-ray diffractometer, the degrees-of-alignment (Da) were obtained for one side perpendicular to the direction of compression molding of the bulk graphite (the "top-face"), and one side parallel to the direction of compression molding (the "side-face"). The anisotropy ratio calculated from the Da-values obtained was 1.13, which indicates comparatively good isotropy.

• Journal of the Korean Wood Science and Technology
• /
• 제48권1호
• /
• pp.41-49
• /
• 2020

Jabon (Anthocephalus cadamba) is a fast-growing wood species that is widely utilized for light construction and other purposes in Indonesia. The objectives of the current study were to determine the effects of monoethylene glycol (MEG) and SiO₂ nanoparticles (nano SiO₂) impregnation treatment on the dimensional stability and density of jabon wood and to identify the characteristics of impregnated jabon wood. Wood samples were immersed in water (as untreated), MEG, 0.5% MEGSiO₂, then impregnated by applying 0.5 bar of vacuum for 60 min, and then applying 2.5 bar of pressure for 120 min. The results showed that impregnation with MEG and Nano SiO₂ had a significant effect on the dimensional stability of jabon wood. Polymers can fill cell walls in wood indicated by increasing weight percentgain, antiswelling efficiency, bulking effect, and density, then decreasing in water uptake value. Jabon wood morphology by using SEM showed that MEGSiO₂ polymers can cover part of the pitsin the wood vessel wall of jabon. This finding was reinforced by EDX results showing that the silicon content was increased due to the addition of SiO₂ nano. The XRD diffraction pattern indicated that MEGSiO₂ treatment increased the degree of crystallinity in wood samples. Overall, treatment with 0.5% MEGSiO₂ led to the most improvement in the dimensional stability of 5-year-old jabon wood in this study.

• 대한기계학회논문집A
• /
• 제38권8호
• /
• pp.849-855
• /
• 2014

유리섬유강화 플라스틱 복합재료의 압축성형 시, 모재와 유리섬유의 분리 없이 유동성이 우수하고, 불균질한 섬유배향이 없는 GFRP 복합재료 개발에 관한 체계적인 연구결과는 미흡한 실정이다. GFRP 복합재료를 사용하여, 자동차 부품 성형 시 발생하는 불균질도와 섬유배향 발생을 억제하는 많은 연구를 해왔으나 아직 해결되고 있지 않다. 본 연구에서는 위의 문제점들을 해결하기 위해 섬유유동성이 뛰어나고, 섬유배향이 발생하지 않고, 불균질성이 없으며, 구조안정성, 함침도, 기계적 특성 및 재활용성 등이 우수한 유리섬유강화 플라스틱 프리프레그를 제조하여, 수직교차형 평직직조방법을 적용하여, GFRP(Glass Fiber Reinforced Plastic) Sheet 를 제조한다.

• Restorative Dentistry and Endodontics
• /
• 제15권1호
• /
• pp.201-216
• /
• 1990

A variety of surface pre-treatments have been advocated to prepare the dentin prior to placement of a bonding agent. The purpose of this study was to evaluate the effect of various dentin conditioners upon the degree of resin impregnation to the dentinal tubules and the shear bond strength of a new dentinal bonding agent (Scotchbond 2) used in conjunction with a visible light cured composite (Silux). The healthy eighty human molars extracted due to periodontal or orthodontic reasons were used and randomly divided into five groups. All the grinded dentin surfaces were conditioned with 3% $H_2O_2$, Cavity Cleanser (Columbus/Bayer), Dentin Conditioner (GC Inter. Corp.), Scotchprep (3M Co.) according to the manufacturer's directions. The specimens were then demineralized in 10% HCl for 20 sec. and 24 hrs. in order to observe the resin tags in Hitachi X-450 scanning electron microscope at 25KV. Also, shear strengths were obtained using an Instron Testing Machine with a cross head speed of 1 mm/min. The following results were obtained ; 1. In group treating with Dentin Conditioner and Scotchprep, the resin strings were formed on most of the surfaces and penetrated more than $50{\mu}m$ into the tubules. 2. The inner surface of resin treated with Cavity Cleanser, indicating the resin strings formed partly and penetrated about in depth of $30{\mu}m$. 3. In control and experimental group treated with 3% $H_2O_2$, the resin tags were not formed, if any, penetrated shortly. 4. Shear bond strengths in groups treating with Dentin Conditioner and Scotchprep were statistically significant increase than with 3% $H_2O_2$. (P<0.01). 5. The Scotchprep treatment group was significantly higher in shear strength than groups treated with no conditioning and Cavity Cleanser.(P<0.01) 6. Shear bond strengths evaluated were gradually increase in proportion to the tag length of resin impregnation.