• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.91-95
• /
• 2007

[ $YBa_2Cu_3O_{7-{\delta}}$ ] films have been prepared on $LaAlO_3$ (100) single-crystal substrates by the metal organic deposition using dichloroacetate precursors (DCA-MOD). DCA precursor solutions with different composition such as; Yttrium-excess(15 at%), barium-poor(25 at%), and a stoichiometric(Y:Ba:Cu=1:2:3) were prepared in order to investigate the effects of precursor composition on the properties of YBCO films prepared by DCA-MOD method. Coated films were calcined at low temperature up to $500^{\circ}C$ in flowing humid oxygen atmosphere. Conversion heat treatment was performed $800^{\circ}C$ for 2 h in flowing Ar gas containing 1000 ppm oxygen with a humidity of 9.45%. For the film prepared using excess yttrium composition, high critical current density ($J_c$) of $>2MA/cm^2$ was obtained whereas, for the films prepared using barium-poor composition, $J_c$ was lower than $1MA/cm^2$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.12a
• /
• pp.107-108
• /
• 2006

High $J_c$ $YBa_2Cu_3O_x$, superconducting films were fabricated by MOD method using fluorine-free dichloroacetic acid(DCA) as chelating solvent for preparing precursor solution. DCA-MOD precursor solution was coated on a single crystal (001) $LaAlO_3$(LAO) substrate by a dip coating method with a speed of 25 mm/min. Coated films were calcined at lower temperature up to $500^{\circ}C$ and Conversion heat treatment was performed at various temperatures of $780{\sim}810^{\circ}C$. SEM observations showed that films have very dense microstructures for the films prepared at the temperature higher than $800^{\circ}C$ regardless of diluting solvent; methanol or 2-methoxyethanol. A High critical current density ($J_c$) of 1.28 $MA/cm^2$ (@77 K and self-field) was obtained for the YBCO film prepared using 2-methoxyethanol as a solvent.

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.59-64
• /
• 2006

High $J_c\;YBa_2Cu_3O_x$ superconducting films were fabricated by MOD method using fluorine-free dichloroacetic acid(DCA) as chelating solvent for preparing precursor solution. Coating solutions were prepared by dissolving Y-, Ba- and Cu-acetates in DCA solvent followed by drying in rota vapor to obtain the blue gel that is diluted in methanol and 2-methoxyethanol for adjusting the cation concentration. DCA-MOD precursor solution was coated on a single crystal(001) $LaAlO_3(LAO)$ substrate by a dip coating method with a speed of 25 mm/min. Coated films were calcined at lower temperature up to $500^{\circ}C$ in flowing oxygen atmosphere with a 7.2% humidity. Conversion heat treatment was performed at various temperatures of $780{\sim}810^{\circ}C$ for 2 h in flowing Ar gas containing 1000 ppm oxygen with a humidity of 9.45%. SEM observations showed that films have very dense microstructures for the films prepared at the temperature higher than $800^{\circ}C$ regardless of diluting solvent; methanol or 2-methoxyethanol. X-ray diffraction analysis showed that YBCO grains grew with a (001) preferred orientation. A High critical current density($J_c$) of 1.28 $MA/cm^2$(@77 K and self-field) was obtained id. the YBCO film prepared using 2-methoxyethanol as a solvent.

• Progress in Superconductivity
• /
• v.7 no.2
• /
• pp.152-157
• /
• 2006

New precursor solution with dichloroacetic acid (DCA) was developed for fabricating high $J_c$ REBCO film. DCA based-precursor solution was coated on $LaAlO_3$(001) substrate by dip coating method. Processing parameters such as oxygen partial pressure, water vapor, ramping rate and pyrolysis temperature were controlled in order to obtain a good epitaxial film. The film with thickness of 0.5 micrometer was obtained by single coating and no crack was observed at calcined films. Oxygen partial pressure was controlled in the range of $100{\sim}1,000$ ppm and conversion heat treatment was carried out at the temperature range of $705-765^{\circ}C$. A critical transition temperature ($T_c$) of 90 K and a critical transport current density ($J_c$) of $>0.5\;MA/cm^2$ (77 K and self-field) were obtained for the GdBCO film. It is thought that fluorine-free MOD solution using DCA is promising precursor solution for fabricating high quality REBCO films.

• Progress in Superconductivity
• /
• v.8 no.2
• /
• pp.186-192
• /
• 2007

High $J_c\;YBa_2Cu_3O_{7-x}$ superconducting films have been fabricated $LaAlO_3(100)$ substrate by MOD method using dichloroacetic acid(DCA) as chelating solvent for preparing precursor solution. Heating rate was varied in order to optimize the calcination heat treatment condition in DCA-MOD method. Coated films were calcined at lower temperature up to $500^{\circ}C$ in flowing humid oxygen atmosphere. The heating rate was calcined from $13.3^{\circ}C/min\;to\;0.28^{\circ}C/min$. Conversion heat treatment was performed $800^{\circ}C$ for 2 h in flowing Ar gas containing 1000 ppm oxygen with a humidity of 9.45%. Surface and cross sectional SEM microstructures showed that particle sizes were increased with heating rate at a calcination step. The amount of pores was increased with heating rate in the calcined films. Dense microstructure and sharp texture were developed in an YBCO films after conversion heat treatment. A high critical current density (Jc) of $1.26MA/cm^2$ (@77 K and self-field) was obtained for the YBCO film which was prepared with a heating rate of $0.28^{\circ}C/min$.

• 한국초전도학회:학술대회논문집
• /
• v.16
• /
• pp.37-37
• /
• 2006

• 한국초전도학회:학술대회논문집
• /
• 2007.07a
• /
• pp.95-95
• /
• 2007

• 한국초전도학회:학술대회논문집
• /
• 2007.07a
• /
• pp.78-78
• /
• 2007

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.96-101
• /
• 2007

[ $YBa_2Cu_3O_{7-{\delta}}$ ] films have been prepared on $LaAlO_3$ (100) single-crystal substrates by a metalorganic deposition using dichloroacetate precursors (DCA-MOD). Calcination conditions were varied in order to optimize the microstructure and the superconducting properties of YBCO film. Coated films were calcined at various temperatures ranging from $400{\sim}700^{\circ}C$ in flowing humid oxygen atmosphere. Ramping rate to calcination tempertures was $2.22^{\circ}C/min$. Conversion heat treatment was performed at $800^{\circ}C$ for 2 h in flowing Ar gas containing 1000 ppm oxygen with a humidity of 9.45%. Observations of surface and cross sectional SEM microstructure showed that the particle size in the calcined film increased in the range of 100-200 nm with heating rate and the calcination temperature. SEM EDS analysis showed that 13 a/o of chlorine was contained in the calcined film. It was also observed that the porosity increased with the heating rate and temperature. Porous microstructure was developed when YBCO films were prepared using porous calcined film. Dense microstructure and high $J_c$ over $1\;MA/cm^2$ was obtained when calcination was carried out at the temperature of $500^{\circ}C$ with a heating rate of $2.22^{\circ}C/min$.