• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.3
• /
• pp.295-302
• /
• 2007

Statement of problem. Fracture of the tooth-colored superstructure material is one of the main prosthetic complications in implant-supported prostheses. Purpose. The purpose of this in vitro study was to compare the fracture strength between the cement-retained implant-supported metal-ceramic crowns and the indirect composite resinveneered metal crowns under the vertical compressive load. Material and methods. Standard implants of external type (AVANA IFR 415 Pre-mount; Osstem Co., Busan, Korea) were embedded in stainless steel blocks perpendicular to their long axis. Customized abutments were fabricated using plastic UCLA abutments (Esthetic plastic cylinder; Osstem Co., Busan, Korea). Thirty standardized copings were cast with non-precious metal (Rexillium III, Pentron, Walling ford, Conn., USA). Copings were divided into two groups of 15 specimens each (n = 15). For Group I specimens, metal-ceramic crowns were fabricated. For Group II specimens, composite resin-veneered (Sinfony, 3M-ESPE, St. Paul, MN, USA) metal crowns (Sinfony-veneered crowns) were fabricated according to manufacturer's instructions. All crowns were temporary cemented and vertically loaded with an Instron universal testing machine (Instron 3366, Instron Corp., Norwood, MA, USA). The maximum load value (N) at the moment of complete failure was recorded and all data were statistically analyzed by independent sample t-test at the significance level of 0.05. The modes of failure were also investigated with visual analysis. Results. The fracture strength of Sinfony-veneered crowns ($2292.7{\pm}576.0N$) was significantly greater than that of metal-ceramic crowns ($1150.6{\pm}268.2N$) (P < 0.05). With regard to the failure mode, Sinfony-veneered crowns exhibited adhesive failure, while metal-ceramic crowns tended to fracture in a manner that resulted in combined failure. Conclusion. Sinfony-veneered crowns demonstrated a significantly higher fracture strength than that of metal-ceramic crowns in cement-retained implant-supported prostheses.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.26 no.3
• /
• pp.311-322
• /
• 2010

The purpose of this study was to evaluate the bond strengths between IPS e.max Press and four different types of resin cements that often used for esthetic restoration. Disc shaped IPS e.max Press blocks(N=40, diameter: 12mm, thickness: 3mm) were fabricated according to the manufacture's instruction and cleaned with ultrasonic cleaner. They were embedded into an autopolymerizing acrylic resin. Fourty cylinder shaped resin block(Filtek Z350, diameter: 4.5mm, thickness: 3mm) were fabricated using a plastic tube. Each specimens were randomly divided into 4 experimental group and bonded each other using 4 different resin cements(Variolink II(light-cure), Variolink II(dual-cure), Calibra, Super-Bond C&B) according to the manufactures' recommendations. All the specimens were stored in normal saline at $37^{\circ}C$ for 24 hours before test. Universal testing machine at a crosshead speed of 1mm/min was used to evaluate the shear bond strength. The data were statistically analyzed using one-way ANOVA(P<.01). Multiple comparison was done by the Tukey HSD test. The shear bond strength of Super-Bond C&B to e.max was significantly lower than those of Calibra, Variolink II(light-cure), Variolink II(dual-cure) (P<.01). The shear bond strength of Calibra, Variolink II(light-cure), Variolink II(dual-cure) to e.max were not significantly different. The shear bond strengths of light-cure/dual-cure cement were higher than that of self-cure cement.