• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.5
• /
• pp.243-249
• /
• 2007

The age hardening behavior and mechanical properties of an extruded Al-Zn-Mg-(Cu)-0.1 wt.%Sc alloy were investigated with the Sc addition and ageing temperature. The results showed that the $Al_3Sc$ compounds were formed by Sc addition and distributed preferentially along the extrusion direction. The age hardening of Al-Zn-Mg-Cu-0.1 wt.%Sc alloy which was treated by T6 process was more significant than that of Al-Zn-Mg-0.1 wt.%Sc alloy. The tensile property of Al-Zn-Mg-Cu+0.1 wt.%Sc alloy was also higher than that of Al-Zn-Mg-0.1 wt.%Sc alloy, which is 691 MPa and 584 MPa in strength and 9% and 11% in elongation, respectively.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.5
• /
• pp.257-261
• /
• 2006

Scandium(Sc) in Al-Zn-Mg-Cu based Al alloy on precipitation phenomenon was compared to a 7001(Al-7.2%Zn-3.2%Mg-1.8%Cu) Al alloy. GP zone and ${\eta}^{\prime}$ phases were the main strengthening phases at low aging temperature under $100^{\circ}C$, but ${\eta}^{\prime}$ and $Al_3Sc$ phases were the main strengthening phases at high aging temperature above $1600^{\circ}C$ in Sc added 7000(Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr) Al alloy. With the addition of 0.1%Sc in 7000 Al alloy, the activation energy for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phase decreased compared to the 7001 Al alloy. This result indicates that the Sc accelerated the precipitation for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phases in 7000 Al alloy. Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr-0.1 Sc alloy has higher strength than 7001 Al alloy, which has high strength.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.31 no.1
• /
• pp.32-39
• /
• 2011

The object of this study is to evaluate and discriminate nondestructively the dislocation substructures of Cu and Cu-Zn alloy subjected to the low-cycle-fatigue. The ultrasonic wave velocity, electrical resistivity and positron annhilation lifetime(PAL) were measured to the nondestructive testing. Cyclic fatigue test of Cu and Cu-Zn alloy with much different stacking fault energies was conducted and the correlations between dislocation behavior and nondestructive parameters were studied. Dislocation cell substructure was developed in Cu, while planar array of dislocation structure was developed in Cu-35Zn alloy only increasing dislocation density with fatigue cycles. Decrease in ultrasonic wave velocity, increase in electrical resistivity and PAL were shown because of the development of lattice defects, dislocations and vacancies, by cyclic fatigue at room temperature. In contrast to Cu-Zn alloy of the planar-array dislocation substructure showing continuous changes in the nondestructive parameters, it does not make any noticeable changes in the nondestructive parameters after the evolution of dislocation cell substructure in Cu.

• Journal of Korea Foundry Society
• /
• v.29 no.6
• /
• pp.265-269
• /
• 2009

The optimum RRA heat treating conditions and SCC (stress corrosion cracking) resistance of semi-solid Al-Zn-Mg-Cu alloy fabricated by inclined cooling plate were compared with those of conventional mould cast alloys. The non-stirring method characterized by using a cooling plate can effectively eliminate dendritic structure and form a fine globular semisolid microstructure in as-cast Al-Zn-Mg-Cu alloy and the SCC resistance of semi-solid Al-Zn-Mg-Cu alloy was higher than that of conventional mold cast alloy. Also, after retrogressed treatment at RRA heat treatment of semi-solid Al-Zn-Mg-Cu alloy, retrogressed treatment time has increased more than 10 minutes at $180^{\circ}C$ to recovery the T6 heat treatment strength.

• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.682-689
• /
• 1995

In order to refine the grain size of Mg-Zn alloy 0.5 to 6wt.%Cu or Si elements were added. Alloy ingot was made under vacuum atmosphere of 4 ${\times}$ 10$\^$-4/ Torr in the quartz tube coated by BN. Grain size and hardness were measured after solution treatment for 8 hours at 435$^{\circ}C$. Optimal condition for grain size refining effect was obtained at the minimum composition of 2wt.%Cu or 1.5wt.%Si addition to Mg-6wt%Zn alloy. Age hardening behavior was experimented at the optimal compositions of the Mg-6wt.%Zn, Mg-6wt.% Zn-2wt.%Cu and Mg-6wt.% Zn-1.5wt.%Si. The hardness increment due to fine grain size was higher at the Mg-Zn-Cu alloy system, but that due to age hardening was higher at the Mg-Zn-Si alloy system.

• Journal of Korea Foundry Society
• /
• v.35 no.4
• /
• pp.67-74
• /
• 2015

In this study, Mg-Zn alloys are investigated in terms of their thermal properties after an addition of Cu. Al element is added to improve the mechanical properties and castability in general case. However, it was excluded here because it significantly decreases the thermal conductivity. On the other hand, Zn was added as a major element, which had less influence on reducing the conductivity and can complement the mechanical properties as well. Cu was also added, and it improved the heat transfer characteristics as the amount was increased. The composition ranges of Zn and Cu are 6 wt.% and 0~1.5 wt.%, respectively. Mg-6Zn-xCu alloy was prepared by a gravity casting method using a steel mold and then the thermal conductivity and the microstructure of the as-cast material were investigated. By measuring the density_(${\rho}$), specific heat_(Cp) and thermal diffusivity_(${\alpha}$), the thermal conductivity_(${\lambda}$) was calculated by the equation ${\lambda}={\rho}{\cdot}Cp{\cdot}{\alpha}$. As the amount of Cu increased in the Mg-6Zn-xCu alloy, the heat transfer characteristics were improved, resulting in a synergistic effect which is slow when the added Cu exceeds 1 wt.%. In order to investigate the relative thermal conductivity/emission of the Mg-6Zn-xCu alloy, AZ91 and AZ31 were experimentally evaluated and compared using a separate test equipment. As a result, the Mg-6Zn-1.5Cu alloy when compared to AZ91 showed improvements in the thermal conductivity ranging from 30 to 60% with a nearly 20% improvement in the thermal emission.

• Journal of Korea Foundry Society
• /
• v.30 no.4
• /
• pp.137-141
• /
• 2010

The effects of Zn amounts on the castability and tensile properties of Al-Zn-Mg-Cu alloys were investigated for development of high strength die casting aluminium alloys. Al-Zn-Mg-Cu alloys with 3.5% Zn showed high cast cracking tendency and poor mold filling behaviour. Al-Zn-Mg-Cu alloys with 5wt% Zn and 7wt% Zn had the tensile strengths of 300~400MPa and the elongations of 2~18%. The effect of Zn on the tensile strength of Al-Zn-Mg-Cu alloys was insignificant, but Al-Zn-Mg-Cu alloy with high Zn amount had lower elongation.

• Journal of the Korean Society of Mechanical Technology
• /
• v.20 no.6
• /
• pp.818-823
• /
• 2018

In this study, the effect of pre-aging treatment for inhibition of natural aging of Al-4.8Zn-1.3Mg alloy by extrusion process was investigated. Firstly, the as-cast microstructure of Al-4.8Zn-1.3Mg alloy billet and its evolution during homogenization($460^{\circ}C$, $4h+510^{\circ}C$, 5h) were investigated by means of optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), hardness analysis. The as-cast microstructures of Al-4.8Zn-1.3Mg alloy reveal $Mg_2Zn$, $Al_5Cu$, $Al_{13}Cu$ formed between dendrities. After homogenization, MgZn, $Al_4Cu$, $Al_{13}Cu$ phases precipitated into the matrix. In addition, standard deviation of homogenized billet was improved than as-cast billet from 2.62 to 0.99. According to pre-aging($100^{\circ}C$, 1h) Al-4.8Zn-1.3Mg alloy by extrusion process, yield strength and tensile strength deviation improved more than condition by natural aging.

• Journal of Korea Foundry Society
• /
• v.22 no.2
• /
• pp.82-88
• /
• 2002

Al-5.5Zn-2.5Mg-l.5Cu semi-solid slurry was prepared by cooling the liquid metal with a low superheat to a solid and liquid co-existing temperature. Relatively round solid particles could be obtained in the slurry through the simple process. The prepared slurry was deformed into the metallic mold by a press and the mechanical properties of obtained specimens were investigated. Mold filling ability of the alloy slurry was also investigated and compared with that of A356 alloy. Al-Zn-Mg-Cu alloy showed lower mold filling ability than A356 alloy probably because small amount of eutectic phase is present and the heat of fusion generated during solidification is smaller than that of A356 alloy.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.313-316
• /
• 2008

This work sought to examine the suitability of twin roll strip casting for Ag-27%Cu-25%Zn-3%Sn brazing alloy (BAg-7A) and to investigate the mechanical properties and microstructure of the strip. The effect of aging heat treatment on the properties was also studied,. This new manufacturing process has applications in the production of the brazing alloy. XRD and microstructural analysis of the Ag-27%Cu-25%Zn-3%Sn strip represented eutectic microstructure of a Cu-rich phase and a Ag-rich matrix regardless of heat treatment. The results of mechanical tests showed tensile strength of 470MPa, a significant enhancement, and an 18% elongation of the twin roll casted strip, due mainly to the solid solution strengthening of Zn atoms (${\sim}20%$) in the Cu-rich phases. Tensile results showed gradually decreasing strengths and increasing elongation with aging heat treatment. Microstructural evolution and fractography were also investigated and related to the mechanical properties.