열처리조건에 따른 Cu-Ni-Si-Sn-Fe-P 석출경화형 동합금계의 물성변화 특성 (Mechanical and Physical Property Changes of Cu-Ni-Si-Sn-Fe-P Copper Alloy System According to the Heat Treatment Conditions)

  • 김승호;염영진
    • 열처리공학회지
    • /
    • 제26권5호
    • /
    • pp.225-232
    • /
    • 2013
  • The influence of aging treatment, addition elements and rolling reduction ratio on the microstructure, mechanical, electrical and bendability properties of Cu-Ni-Si-P-x (x = Fe, Sn, Zn) alloys for connector material application was investigated. SEM/EDS analysis exhibited that Ni2-Si precipitates with a size of 20~100 nm were distributed in grains. Fe, Sn, Zn elemnets in Cu-Ni-Si-P alloy imporved the mechanical strength but it was not favor in increasing of electrical conductivity. As higher final rolling reduction ratio, the strength and electrical conductivity is increased after aging treatment, but it indicated excellent bendability. Especially, Cu-2Ni-0.4Si-0.5Sn-0.1Fe-0.03P alloy show the tensile strength value of 700MPa and the electrical conductivity was observed to reach a maximum of 40%IACS. It is optimal for lead frame and connector.

Investigation of Initiation of Electroless Ni-P and Ni-Cu-P deposition on pure iron

  • Yiyong, W-U;Kim, M.;S.C. Kwon
    • 한국표면공학회:학술대회논문집
    • /
    • 한국표면공학회 2001년도 추계학술발표회 초록집
    • /
    • pp.10-10
    • /
    • 2001
  • In this paper, initial depositing process of electroless Ni-Cu-P alloy was investigated by means of SEM, TEM and AES. The results show that the initial deposition is inhomogeneous and there exist different transition layers between different coatings and substrates, which are decided by the structures and compositions of the bath. For Ni-P binary alloy, its deposition takes place superiorly at grain boundary and on some grains with beneficial texture, the thickness of transition layer composed of Ni-Fe-P reaches 2000 angstrom. But during initiation of Ni-Cu-P trinary alloy, only at grain boundary is prIor to be deposited electrolessly, transited layer contains Ni-Fe-Cu-P and is decreased to about 500 angstrom. The structures of the films of Ni-P and Ni-Cu-P are crystalline at the initial depositing stage. The mechanisms of the process are put forward in this paper.

  • PDF

Cu-Fe계 동합금의 강도 및 전기전도도에미치는 첨가 원소의 영향

  • 김대현;이광학
    • 한국재료학회:학술대회논문집
    • /
    • 한국재료학회 2009년도 추계학술발표대회
    • /
    • pp.44.1-44.1
    • /
    • 2009
  • 본 연구에서는 Sn과 Mg를 Cu-Fe-P 합금계에 첨가 하였을 때 합금의 미세조직과 물리적 특성에 미치는 영향을 조사하였다. Cu-Fe-P 합금에 Sn과 Mg를첨가 함으로써 생성된 석출상과 합금의 미세조직, 기계적 성질 및 전기전도도를 조사하였다. 합금성분은 OES로 분석하였으며 SEM 및 EDX로 미세 석출상이생성됨을 확인하였다. 본연구를 통하여 Cu-Fe-P 합금계에 Sn과 Mg를 적절히 첨가 함으로써 고강도-고전도도의 동합금 제조가 가능함을 확인하였다.

  • PDF

Cu-Fe-P계 합금의 강도 및 전기전도도에 미치는 첨가 원소의 영향 (Effects of Alloying Elements on the Tensile Strength and Electrical Conductivity of Cu-Fe-P Based Alloys)

  • 김대현;이광학
    • 한국재료학회지
    • /
    • 제20권2호
    • /
    • pp.65-71
    • /
    • 2010
  • In this study, the effect of Sn and Mg on microstructure and mechanical properties of Cu-Fe-P alloy were investigated by using scanning electron microscope, transmission electron microscope, tensile strength, electrical conductivity, thermal softening, size and distribution of the precipitation phases in order to satisfy characteristic for lead frame material. It was observed that Cu-0.14wt%Fe-0.03wt%P-0.05wt%Si-0.1wt%Zn with Sn and Mg indicates increasing tensile strength compare with PMC90 since Sn restrained the growth of the Fe-P precipitation phase on the matrix. However, the electrical conductivity was decreased by adding addition of Sn and Mg because Sn was dispersed on the matrix and restrained the growth of the Fe-P precipitation. The size of 100 nm $Mg_3P_2$ precipitation phase was observed having lattice parameter $a:12.01{\AA}$ such that [111] zone axis. According to the results of the study, the tensile strength and the electrical conductivity satisfied the requirements of lead frame; so, there is the possibility of application as a substitution material for lead frame of Cu alloy.

친환경 유기화합물(NaDDC)에 의한 90Cu10NiFe합금의 부식억제 연구 (Studies on Corrosion inhibition of 90Cu10NiFe Alloy by Eco-Friendly Organic Compound ; Sodium Diethyl Dithio Carbamate(NaDDC))

  • 정길봉;김두한;이성도
    • 한국군사과학기술학회지
    • /
    • 제14권6호
    • /
    • pp.1018-1025
    • /
    • 2011
  • The improved properties of corrosion for 90Cu10NiFe alloy in natural seawater were explained by sodium diethyl dithio carbamate(NaDDC), namely organic compound, which is reagent for heavy metal extractions of waste water. The efficiency of NaDDC as corrosion inhibitor for 90Cu10NiFe alloy has been investigated in seawater after immersion in various concentrations of NaDDC solutions for 12~36hrs at pH 8.2 by weight loss test and electrochemical techniques including potentiodynamic polarization and SEM-EDS measurements. The results showed that the corrosion resistance of 90Cu10NiFe alloy improves with the increasing concentration of NaDDC but it did not improves with increasing time any more, so the highest inhibition efficiency was 93% at 100mg/L, 36hrs. The results obtained from weight losses and corrosion rates in polarization curve measurements were in good agreement. Therefore, it showed that NaDDC is a good inhibitor for copper corrosion of 90Cu10NiFe alloy.

ARB법에 의한 Cu-Fe-P합금의 초미세결정립 형성 (Formation of Ultrafine Grains in Cu-Fe-P Alloy by Accumulative Roll-Bonding Process)

  • 이성희;한승전;김형욱;임차용
    • 한국재료학회지
    • /
    • 제19권8호
    • /
    • pp.432-436
    • /
    • 2009
  • A Cu-Fe-P copper alloy was processed by accumulative roll-bonding (ARB) for ultra grain refinement and high strengthening. Two 1mm thick copper sheets, 30 mm wide and 300 mm long, were first degreased and wire-brushed for sound bonding. The sheets were then stacked on top of each other and roll-bonded by about 50% reduction rolling without lubrication at ambient temperature. The bonded sheet was then cut into two pieces of the same dimensions and the same procedure was repeated for the sheets up to eight cycles. Microstructural evolution of the copper alloy with the number of the ARB cycles was investigated by optical microscopy (OM), transmission electron microscopy(TEM), and electron back scatter diffraction(EBSD). The grain size decreased gradually with the number of ARB cycles, and was reduced to 290 nm after eight cycles. The boundaries above 60% of ultrafine grains formed exhibited high angle boundaries above 15 degrees. In addition, the average misorientation angle of ultrafine grains was 30 degrees.

Fe-Al-Nb-B-(Cu)계 초미세결정합금의 자기적 특성 (Magnetic Properties of Ultrafine grained Fe-Al-Nb-B-(Cu) Alloys.)

  • 박진영;서수정;김규진;김광윤;노태환
    • 한국자기학회지
    • /
    • 제6권4호
    • /
    • pp.218-224
    • /
    • 1996
  • 새로운 고성능 자심용 연자성 합금을 개발하기 위해, 급냉응고 방식에 의해 제조된 $Fe_{83-x}Al_{x}Nb_{5}B_{12}(X=1~5at%)$ 합금의 결정화거동 및 자기적 특성을 조사하였다. 3at% Al의 $Fe_{80}Al_{3}Nb_{5}B_{12}$ 합금이 조사된 Fe-Al-Nb-B계 합금중에서 가장 우수한 연자기 특성을 가지며, 이때 미세한 $\alpha-Fe$상 결정립 조직을 가지는 것으로 판명되었다. 또, 이 조성의 합금에 1 at%의 Cu를 첨가하면, 약 6~7 nm정도의 크기를 가지는 극히 미세한 결정립의 $\alpha-Fe$ 상조직이 얻어졌으며 이에 따라 대단히 현저한 연자기 특성의 향상이 실현되었다. 이때 초미세 결정구조 $Fe_{79}Al_{3}Nb_{5}B_{12}Cu_{1}$ 합금의 자기적 특성은 다음과 같다 : ${\mu}_{eff}(1\;kHz)=26,000,\;B_{10}=1.45\;T,\;H_{c}=25\;mOe,\;P_{c}(100\;kHz,\;0.2\;T)=55\;W/kg$.

  • PDF

Fe83.2Si5.33-0.33xB10.67-0.67xPxCu0.8 나노결정질 연자성 합금의 P함량에 따른 미세구조 및 자기적 특성 변화 관찰에 관한 연구 (A Study on the Microstructure and Magnetic Properties of Fe83.2Si5.33-0.33xB10.67-0.67xPxCu0.8 Nanocrystalline Soft Magnetic Alloys with varying P Content)

  • 임현아;배경훈;남영균;안수봉;양상선;김용진;이정우;정재원
    • 한국분말재료학회지
    • /
    • 제28권4호
    • /
    • pp.293-300
    • /
    • 2021
  • We investigate the effect of phosphorous content on the microstructure and magnetic properties of Fe83.2Si5.33-0.33xB10.67-0.67xPxCu0.8 (x = 1-4 at.%) nanocrystalline soft magnetic alloys. The simultaneous addition of Cu and P to nanocrystalline alloys reportedly decreases the nanocrystalline size significantly, to 10-20 nm. In the P-containing nanocrystalline alloy, P atoms are distributed in an amorphous residual matrix, which suppresses grain growth, increases permeability, and decreases coercivity. In this study, nanocrystalline ribbons with a composition of Fe83.2Si5.33-0.33xB10.67-0.67xPxCu0.8 (x = 1-4 at.%) are fabricated by rapid quenching melt-spinning and thermal annealing. It is demonstrated that the addition of a small amount of P to the alloy improves the glass-forming ability and increases the resistance to undesirable Fex(B,P) crystallization. Among the alloys investigated in this work, an Fe83.2Si5B10P1Cu0.8 nanocrystalline ribbon annealed at 460℃ exhibits excellent soft-magnetic properties including low coercivity, low core loss, and high saturation magnetization. The uniform nanocrystallization of the Fe83.2Si5B10P1Cu0.8 alloy is confirmed by high-resolution transmission electron microscopy analysis.

NOVEL TECHNIQUE TO PRODUCE HYBRID P/M COMPONENTS USING DISSIMILAR FERROUS ALLOYS

  • MIN CHUL OH;HYUNJOO SEOK;YEONGCHEOL JO;BYUNGMIN AHN
    • Archives of Metallurgy and Materials
    • /
    • 제64권2호
    • /
    • pp.613-616
    • /
    • 2019
  • The objective of the present research is to develop the novel multi-compaction technology to produce hybrid structure in powder metallurgy (P/M) components using dissimilar Fe-based alloys. Two distinct powder alloys with different compositions were are used in this study: Fe-Cr-Mo-C pre-alloyed powder for high strength and Fe-Cu-C mixed powder for enhanced machinability and lower material cost. Initially, Fe-Cu-C was pre-compacted using a bar-shaped die with lower compaction pressure. The green compact of Fe-Cu-C alloy was inserted into a die residing a half of the die, and another half of the die was filled with the Fe-Cr-Mo-C powder. Then they subsequently underwent re-compaction with higher pressure. The final compact was sintered at 1120℃ for 60 min. In order to determine the mechanical behavior, transverse rupture strength (TRS) and Vickers hardness of sintered materials were measured and correlated with density variations. The microstructure was characterized using optical microscope and scanning electron microscope to investigate the interfacial characteristics between dissimilar P/M alloys.