• Proceedings of the KWS Conference
• /
• 1995.04a
• /
• pp.130-132
• /
• 1995

• Proceedings of the KWS Conference
• /
• 1993.05a
• /
• pp.111-112
• /
• 1993

• Proceedings of the KWS Conference
• /
• 1999.10a
• /
• pp.259-262
• /
• 1999

• Proceedings of the KWS Conference
• /
• v.43
• /
• pp.94-96
• /
• 2004

• Proceedings of the KWS Conference
• /
• 1999.10a
• /
• pp.220-224
• /
• 1999

• Proceedings of the KWS Conference
• /
• 2000.04a
• /
• pp.151-154
• /
• 2000

• Proceedings of the KWS Conference
• /
• 1994.10a
• /
• pp.161-162
• /
• 1994

No Abstract, See Full Text

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.110-113
• /
• 2003

여러가지 Sn-Ag-Cu 솔더조성과 솔더링 후의 냉각속도에 따라 솔더링 접합부에서의 계면 미세조직의 다양한 변화를 관찰해 보았다. 현재까지 Sn-Ag-Cu 3원계 공정점에 대한 정확한 연구가 미흡하고, 상용으로 제품화되고 있는 Sn-Ag-Cu 합금계는 3원계 공정조성에서 약간 벗어난 조성들을 선택하고 있다고 할 수 있다. 따라서, 본 연구에서 사용한 Sn-Ag-Cu 합금 조성은 Sn-3.5Ag, Sn-3Ag-0.7Cu, Sn-3Ag-1.5Cu, Sn-3.7Ag-0.9Cu, Sn-6Ag-0.5Cu로 선택하였으며, 각 조성에서 Lap Shear Joint를 제조하였다. 사용한 Solder pad는 Cu pad와 Cu pad 위에 Au/Ni를 plating한 것을 이용하였다. 리플로우 솔더링 조건은 $250^{\circ}C$ 이상의 온도에서 60초 실시하였으며, 리플로우 솔더링 후의 냉각속도를 달리하여 냉각시켰다. 솔더링 후의 냉각속도가 느려질수록 계면 금속간화합물(IMC)의 두께가 더욱 증가하며, 조대화되었다. 또한 솔더 조성의 영향에서 Cu와 Ag의 함량이 높을수록 계면 IMC의 두께가 증가되었으며, 이는 솔더내부에 형성된 IMC 입자들이 조대화되어 계면 IMC층에 결합되어 나타났기 때문이다.

• Journal of the Microelectronics and Packaging Society
• /
• v.30 no.1
• /
• pp.55-62
• /
• 2023

In this study, Sn-3.0Ag-0.5Cu (wt.%, SAC305) solder dipping process was performed between Ni-foam skeleton with different pore per inch (PPI) to fabricate Ni-foam/SAC305 composite solder, and then applied to the transient liquid phase (TLP) bonding process to evaluate the microstructure and mechanical properties of the bonded joint. The Ni-foam/SAC305 composite solder preform consisted of Ni-foam and SAC305, and an intermetallic compound (IMC) having a (Ni,Cu)₃Sn₄ composition was formed at the Ni-foam interface. During TLP bonding process, the IMC at the Ni-foam interface was converted to (Ni,Cu)₃Sn₄+Au, and as the bonding time increased, the Ni-foam and SAC305 continuously reacted, and the bonded joint was converted into an IMC. And it was confirmed that the 130 PPI Ni-foam/SAC305 composite solder joint was converted into an IMC at the fastest rate. As a result of performing a shear test to confirm the effect of Ni-foam on mechanical properties, solder joints under all conditions exhibited excellent mechanical properties of 50 MPa or more in the early stages of the TLP bonding process, and the shear strength tends to increase as the bonding time increases.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.211-214
• /
• 2007

Sn-0.3Ag-0.7Cu 조성의 젖음 특성과 반응 특성을 Sn-1.0Ag-0.5Cu 및 Sn-3.0Ag-0.5Cu 합금의 결과와 비교, 분석하였다. 또한 Sn-0.3Ag-0.7Cu 조성의 용융 및 응고 특성을 DSC로 측정하고, 인장시험을 통한 stress-strain curve를 관찰하였다. 아울러 할로겐 함유량이 많은 플럭스를 사용하여 Sn-0.3Ag-0.7Cu 조성의 젖음 특성을 향상 시킬 수 있는지를 조사하였으며, Sn-0.3Ag-0.7Cu 조성에 미량의 In을 첨가하여 젖음 특성의 개선 정도를 분석하였다. 그 결과 할로겐 함유량이 높은 플럭스를 사용한 경우보다 미량의 In을 첨가한 경우에서 wettability의 향상을 보다 효과적으로 유도할 수 있음을 관찰할 수 있었다.