• Journal of Powder Materials
• /
• v.4 no.2
• /
• pp.100-105
• /
• 1997

In this study the changes of the hardness and microstructures during aging at 120$^{\cire}C$ of an RS-P/M Al-5.6wt%Zn-2.0wt%Mg-1.3wt%Zr-1.0wt%Mn-0.25wt%Cu alloy were studied using a transmission electron microscopy. The hardness increased rapidly at early stage of aging and reached the maximun when the specimen was aged for 24 hr. The many irregular-shaped $Al_4Mn$ and rod-shaped $Al_6Mn$ dispersoids with 0.1-0.4 $\mu$m in length were observed in the as-extruded alloy. The dark particles with 2-3 nm in size were observed in aged specimen for 5hr and those are thought to be G.P.zones or precursor of $\eta'$ precipitates. In aged specimen for 24 hr, the $\eta'$ phases were distributed homogeneously within the matrix and the PFZ with 30-40 nm in width was observed along the grain boundary. With further aging, the width of PFZ increased and $\eta$ phases were also detected within the matrix.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.123-126
• /
• 2006

In this study, bottom-up type powder processing and top-down type SPD (severe plastic deformation) approaches were combined in order to achieve full density of carbon nanotube (CNT)/metal matrix composites with superior mechanical properties by improved particle bonding and least grain growth, which were considered as a bottle neck of the bottom-up method using the conventional powder metallurgy of compaction and sintering. ECAP (equal channel angular pressing), the most promising method in SPD, was used for the CNT/Cu powder consolidation. The powder ECAP processing with 1, 2, 4 and 8 route C passes was conducted at room temperature.

• Journal of the Korean Mathematical Society
• /
• v.44 no.3
• /
• pp.627-645
• /
• 2007

We investigate the eigenvalues of the semi-circulant preconditioned matrix for the finite difference scheme corresponding to the second-order elliptic operator with the variable coefficients given by $L_vu\;:=-{\Delta}u+a(x,\;y)u_x+b(x,\;y)u_y+d(x,\;y)u$, where a and b are continuously differentiable functions and d is a positive bounded function. The semi-circulant preconditioning operator $L_cu$ is constructed by using the leading term of $L_vu$ plus the constant reaction term such that $L_cu\;:=-{\Delta}u+d_cu$. Using the field of values arguments, we show that the eigenvalues of the preconditioned matrix are clustered at some number. Some numerical evidences are also provided.

• Journal of Korea Foundry Society
• /
• v.22 no.1
• /
• pp.35-41
• /
• 2002

To improve the reliability of solder joints, a composite solder which consists of solder matrix and intermetallic reinforcements was manufactured by a new method. The cast ingot of Sn-6.9Cu-2.9Ag alloy had primary Cu6Sn5 intermetallics in the form of dendrites. After rolling the ingot, the intermetallic dendrites were crushed into fine particles and distributed uniformly throughout the solder matrix. As the rolled strips became thinner, the average size of the crushed particles reached a critical size which did not decrease any more by further rolling. The critical size was nearly the same as the average width of intermetallic dendrite trunk. The crushed intermetallic particles did not melt and remained in solid state during reflow soldering due to their high meltingterm-perature. The coarsening and gravitational segregation of the particles were observed during reflow soldering.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.7 no.1
• /
• pp.47-58
• /
• 2004

Loss factors of A356, Mn-Cu alloy and aluminum matrix composites reinforced with $SiC_p$ and Ni-coated graphite particles at various contents have been investigated using clamped-free cantilever beam method. The loss factors of half-power bandwidth of the specimens were measured over a wide range of frequencies from 50 to 3300Hz. Among the specimens, Al-10%$SiC_p$-10%$C_p$ showed the highest loss factor at the mode I, while Mn-Cu alloy showed the highest loss factors at the modes II and III. Consequently, at the mode I the Al-10%$SiC_p$--10%$C_p$ showed the loss factor of 0.00093, which is 2.64 and 1.58 times higher than those of A356 and Mn-Cu alloy, respectively.

• International Journal of Korean Welding Society
• /
• v.1 no.1
• /
• pp.58-62
• /
• 2001

The surface of AC8A Ah alloy was modified by adding the Cu powder using a Plasma Transferred Arc (PTA) welding process. Under the optimum fabricating conditions, the modified surface of AC8A Ah alloy was observed to possess the sound microstructure with a minimum porosity. Hardness and wear resistance properties of the as-fabricated alloy were compared with those of the 76 heat-treated one. In case of the as-fabricated alloy, the hardness of the modified layer was twice that of the matrix region. Although significant increase in the hardness of the matrix region was observed after T6 heat treatment, the hardness of the modified layer was not observed to change. The wear resistance of the modified layer was significantly increased compared to that of the matrix region. The microstructure of a weld zone and the matrix region were investigated using the optical microscope, scanning electron microscope (SEM), electron probe microanalysis (EPMA), and transmission electron microscope (TEM). The primary and eutectic silicon in the weld zone were finer and more curved than in the matrix region, while some precipitates has had been found therein. According to the TEM observation, the predominant precipitate present in the weld zone was the $\theta$'phase, which is precipitated during cooling by rapid solidification in PTA welding process. Improvement of hardness and wear properties in the weld zone in the as-fabricated condition can be explained based on the presence of $\theta$’precipitates and fine primary and eutectic silicon distribution.

• 보존과학연구
• /
• s.14
• /
• pp.45-76
• /
• 1993

Au-Cu alloyed coating layer were found by Hg-amalgam process and it seemed to be used Cu-amalgam process similar to Au-amalgam. Coated layer is dense and unique, Thickness of layer was 1.5 to $18.0\mum$ which had 95.3 to 99.8% purity of gold Matrix metal mostly cosists of forged copper alloy which had high purity and ferrite ($\alpha$) strusture. It showed excellent refining technical level at that time. Aowever, the nail, ferrous matrix used for strength needed, composed of silver foil packed and gold layer for adherence between ferrous matrix and gold layer

• Journal of Powder Materials
• /
• v.10 no.3
• /
• pp.168-171
• /
• 2003

Interpenetrating phase composites of $TiB_2$-Cu system were produced via Spark-Plasma Sintering (SPS) oi nanocomposite powders. Under simultaneous action of pressure, temperature and electric current titanium diboride nanoparticles distributed in copper matrix move, agglomerate and form a fine-grained skeleton. Increasing SPS-temperature and he]ding time promote densification due to local melting of copper matrix When copper melting is avoided the compacts contain 17-20% porosity but titanium diboride skeleton is still formed representing the feature of SPS . High degree of densification and formation of titanium diboride network result in increased hardness of high-temperature SPS-compacts.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.28 no.1
• /
• pp.21-27
• /
• 2018

Synthesis of ferromagnetic composite materials for the $Cu-BaFe_{12}O_{19}$ system by mechanical alloying (MA) has been investigated at room temperature. A mixture of copper and barium ferrite with a weight ratio of $Cu:BaFe_{12}O_{19}=4:1$, 3 : 2, 2 : 3 and 1 : 4 was used. It is found that $Cu-BaFe_{12}O_{19}$ composite powders in which $BaFe_{12}O_{19}$ is dispersed in copper matrix are successfully produced by mechanical alloying of $BaFe_{12}O_{19}$ with Cu for 80 min. in all composition. The change in X-ray diffraction patterns and magnetic properties reflects the details for the formation of ferromagnetic metal matrix composite of pure Cu and $BaFe_{12}O_{19}$ during mechanical alloying. Magnetization of $Cu-BaFe_{12}O_{19}$ composite powders gradually increases with increasing the amounts of barium ferrite, whereas coercive force of MA powders gradually decreases due to the refinement of barium ferrite powders with ball milling. However, it can be seen that the coercivity of $Cu-BaFe_{12}O_{19}$ MA composite powders with a weight ratio of $Cu:BaFe_{12}O_{19}=4:1$ and 3 : 2 ball-milled for 80 min. is still high value of 1400 Oe and 1450 Oe, respectively suggesting that the refinement of barium ferrite powders during ball milling process tend to be suppressed due to the ductile copper.

• Journal of Powder Materials
• /
• v.25 no.1
• /
• pp.30-35
• /
• 2018

The friction characteristics of Al-Fe alloy powders are investigated in order to develop an eco-friendly friction material to replace Cu fiber, a constituent of brake-pad friction materials. Irregularly shaped Al-Fe alloy powders, prepared by gas atomization, are more uniformly dispersed than conventional Cu fiber on the brake pad matrix. The wear rate of the friction material using Al-8Fe alloy powder is lower than that of the Cu fiber material. The change in friction coefficient according to the friction lap times is 7.2% for the Cu fiber, but within 3.8% for the Al-Fe alloy material, which also shows excellent judder characteristics. The Al-Fe alloy powders are uniformly distributed in the brake pad matrix and oxide films of Al and Fe are homogeneously formed at the friction interface between the disc and pad, thus exhibiting excellent friction and lubrication characteristics. The brake pad containing Al-Fe powders avoids contamination by Cu dust, which is generated during braking, by replacing the Cu fiber while maintaining the friction and lubrication performance.