• 한국태양에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.51-55
• /
• 2011

In this paper, the optimized doping condition of crystalline silicon solar cells with 156 ${\times}$ 156 mm2 area was studied. To optimize the drive-in condition in the doping process, the other conditions except drive-in temperature and time were fixed. After etching 7 ${\mu}m$ of the surface to form the pyramidal structure, the silicon nitride deposited by the PECVD had 75~80 nm thickness and 2 to 2.1 for a refractive index. The silver and aluminium electrodes for front and back sheet, respectively, were formed by screen-printing method, followed by firing in $400-425-450-550-850^{\circ}C$ five-zone temperature conditions to make the ohmic contact. Drive-in temperature was changed in range of $828^{\circ}C$ to $860^{\circ}C$ and time was from 3 min to 40 min. The sheet resistance of wafer was fixed to avoid its effect on solar cell. The solar cell fabricated with various conditions showed the similar conversion efficiency of 17.4%. This experimental result showed the drive-in temperatures and times little influence on solar cell characteristics.

• 한국태양에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.246-250
• /
• 2009

String & tabbing step in the crystalline PV module manufacturing process for the temperature directly affects solar cells. In fact, in the manufacture of PV modules tend to be temperature factor and the corresponding changes n the output shows the same characteristics. In this journal, it will be considered about thermal characteristics, especially changes of characteristic in high temperature of the solar cell through experiment that we measure electric output characteristics of solar cells after those are applied with high temperature changes for two seconds. And we can think about the possibility of efficiency improvements over looks in PV module manufacturing processes.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.72-72
• /
• 2010

The PV module company use variable process step and type. Especially soldering process is important, because crystalline cell can be bow by beating temperature. Most PV module company use hot air soldering type in the tabbing & string process. Although hot air type is used widely but this type is bound to influence on cell damage. So recently new way is introducing like a high current way. In this paper, we compare with characteristics of each soldering type and then conform a method to minimize solar cell deformation. Actually solar cell deformation show many difference by fix position and cooling time after soldering step.

• Solar Energy
• /
• v.8 no.2
• /
• pp.73-76
• /
• 1988

Thick films based on the mature crystalline silicon technology are expected to exhibit eversmaller cost reduction. The thin-film-based technology is, however, expected to exhibit a much sharper drop in cost as it develops. In this report, technology and recent R & D of thin film solar cell, such as amorphous silicon, cadnium telluride, copper indium diselenide and gallium arsenide, are described. Perspectives of world photovoltaic market and solar cell price are also described.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.77-79
• /
• 2009

Amorphous/crystalline silicon heterojunction solar cells, TCO/a-Si:H (p)/c-Si(n)/a-Si:H(n)/Al, are investigated. The influence of various parameters for the front structures was studied. We used thin (10 nm) a-Si:H(p) layers of amorphous hydrogenated silicon are deposited on top of a thick ($500{\mu}m$) crystalline c-Si wafer. This work deals with the influence of the a-Si:H(p) doping concentration on the solar cell performance is studied.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2007.02a
• /
• pp.44-44
• /
• 2007

• 한국태양에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.40-44
• /
• 2011

Recent studies in crystalline silicon solar cell fabrication have been focused on high efficiency and low cost. However, the rising of the cost results in additional processes to approach high efficiency. The fabrication process also becomes complicated with additional technologies. In this paper, we studied the selective emitter formation with phosphorous paste to improve the conversion efficiency. Selective emitter formations like two-step diffusion or etch-back method require at least one more step compared in the conventional line since heavily and lightly doped area was needed to form separately.However,one-step diffusion process is the method diffusing heavily and lightly doped area at the same time only with additional screen-printing step. This study lays the foundation for the simple way to form the selective emitter.

• Journal of the Semiconductor & Display Technology
• /
• v.11 no.2
• /
• pp.7-11
• /
• 2012

SiNx films have been wildly used as anti-reflection coatings and passivation for crystalline silicon solar cells. In this study, the SiNx films were deposited by using high frequency (13.56MHz) PECVD and optical & passivation properties were investigated. The RF power was changed in a certain range for the film deposition. Then, the refractive index, etch rate, minority carrier lifetime and cell efficiency were measured to study the properties of the film respectively. The optimal deposition conditions for application to crystalline silicon solar cells were proposed as results of the study. Finally, the best cell efficiency of 16.98% was obtained from the solar cell with the SiNx films deposited by RF power of 550W.

• Current Photovoltaic Research
• /
• v.11 no.3
• /
• pp.75-78
• /
• 2023

Recently, the installation of photovoltaic modules in urban areas has been increasing. In particular, the demand for solar modules installed in a limited space is increasing. However, since the crystalline silicon solar module's size is proportional to the solar cell's size, it is difficult to manufacture a module that can be installed in a limited area. In this study, we fabricated a solar module with a shingled design that can control horizontal and vertical width using a bi-directional laser scribing method. We fabricated a string cell with a width of 1/5 compared to the existing shingled design string cells using a bi-directional laser scribing method, and we fabricated a solar module by connecting three strings in parallel. Finally, we achieved a conversion power of 5.521 W at a 103 mm × 320 mm area.

• Korean Journal of Materials Research
• /
• v.22 no.9
• /
• pp.450-453
• /
• 2012

In crystalline solar cells, the substrate itself constitutes a large portion of the fabrication cost as it is derived from semiconductor ingots grown in costly high temperature processes. Thinner wafer substrates allow some cost saving as more wafers can be sliced from a given ingot, although technological limitations in slicing or sawing of wafers off an ingot, as well as the physical strength of the sliced wafers, put a lower limit on the substrate thickness. Complementary to these economical and techno-physical points of view, a device operation point of view of the substrate thickness would be useful. With this in mind, BC-BJ Si and GaAs solar cells are compared one to one by means of the Medici device simulation, with a particular emphasis on the substrate thickness. Under ideal conditions of 0.6 ${\mu}m$ photons entering the 10 ${\mu}m$-wide BC-BJ solar cells at the normal incident angle (${\theta}=90^{\circ}$), GaAs is about 2.3 times more efficient than Si in terms of peak cell power output: 42.3 $mW{\cdot}cm^{-2}$ vs. 18.2 $mW{\cdot}cm^{-2}$. This strong performance of GaAs, though only under ideal conditions, gives a strong indication that this material could stand competitively against Si, despite its known high material and process costs. Within the limitation of the minority carrier recombination lifetime value of $5{\times}10^{-5}$ sec used in the device simulation, the solar cell power is known to be only weakly dependent on the substrate thickness, particularly under about 100 ${\mu}m$, for both Si and GaAs. Though the optimum substrate thickness is about 100 ${\mu}m$ or less, the reduction in the power output is less than 10% from the peak values even when the substrate thickness is increased to 190 ${\mu}m$. Thus, for crystalline Si and GaAs with a relatively long recombination lifetime, extra efforts to be spent on thinning the substrate should be weighed against the expected actual gain in the solar cell output power.