• The Journal of Advanced Prosthodontics
• /
• 제7권2호
• /
• pp.146-150
• /
• 2015

PURPOSE. This in vitro study aimed to compare the failure load and failure characteristics of two different zirconia framework designs of premolar crowns when subjected to static loading. MATERIALS AND METHODS. Two types of zirconia frameworks, conventional 0.5 mm even thickness framework design (EV) and 0.8 mm cutback of full contour crown anatomy design (CB), were made for 10 samples each. The veneer porcelain was added on under polycarbonate shell crown made by vacuum of full contour crown to obtain the same total thickness of the experiment crowns. The crowns were cemented onto the Cobalt-Chromium die. The dies were tilted 45 degrees from the vertical plane to obtain the shear force to the cusp when loading. All crowns were loaded at the lingual incline of the buccal cusp until fracture using a universal testing machine with cross-head speed 0.5 mm/min. The load to fracture values (N) was recorded and statistically analyzed by independent sample t-test. RESULTS. The mean and standard deviations of the failure load were $1,170.1{\pm}90.9$ N for EV design and $1,450.4{\pm}175.7$ N for CB design. A significant difference in the compressive failure load was found (P<.05). For the failure characteristic, the EV design was found only cohesive failures within veneering porcelain, while the CB design found more failures through the zirconia framework (8 from 10 samples). CONCLUSION. There was a significant difference in the failure load between two designs, and the design of the framework influences failure characteristic of zirconia crown.

• 대한치과의사협회지
• /
• 제23권9호통권196호
• /
• pp.747-751
• /
• 1985

• 대한심미치과학회지
• /
• 제23권2호
• /
• pp.70-76
• /
• 2014

After extraction of tooth, alveolar ridge resorption is inevitable in most cases. Clinicians confront with horizontal and vertical resorption of alveolar bone. Without massive amount of bone and soft tissue graft, dental implant will be placed apically to gain stability. In those cases, not only white esthetic part, but also pink esthetic part should be restored with pink porcelain. The margin of prosthesis should be located apically to reproduce natural look with adjacent teeth. However, when the margin is located apically, it is always hard to remove remaining cement, thus complications may arise. In this report, a novel design of implant prosthesis is introduced to solve those issues. The novel design is consisted of zirconia framework with pink porcelain and separate crowns on top of the framework. It eliminates the possibility of cement remnants by bringing the crown margin coronally. Pink esthetic part is incorporated in abutment part instead of crown part and the screw hole is covered with separate crowns.

• 대한치과보철학회지
• /
• 제62권1호
• /
• pp.20-27
• /
• 2024

고기능성 폴리머 중 하나인 Polyetherketoneketone (PEKK)는 좋은 생체적합성과 우수한 물성을 가져 치과 영역을 포함한 다양한 분야에서 사용되고 있다. 이러한 PEKK를 프레임워크로 하는 임플란트 지지 고정성 보철물에 관한 성공적인 증례들이 많이 보고되어 왔으나, 보고된 증례에 대한 장기간의 관찰과 합병증에 관한 고찰은 부족한 상태이다. 이에 본 증례보고에서는 PEKK 프레임워크를 composite resin, lithium disilicate crown, high-impact polymethyl methacrylate PMMA로 각각 veneering하여 임플란트 지지 고정성 보철 수복을 한 세 가지 증례와 각각의 6년간의 경과관찰 결과를 소개하고 이를 고찰해 보고하고자 한다.

• 대한치과보철학회지
• /
• 제37권4호
• /
• pp.454-464
• /
• 1999

The metal ceramic crown is currently the most popular complete veneer restoration in dentistry, but in many cases, the metal cervical collar at the facial margin is unesthetic and unacceptable. Facial porcelain margin has been used in place of it. But this dose not solve the problems, such as dark gingival discoloration and cervical opaque reflection of porcelain veneer. Recently, metal copings which were designed to terminate its labio-cervical end on the axial walls coronal to the shoulder have been clinically used to solve the esthetic problem of metal ceramic crown. But in this design, porcelain veneer of labio-cervical area which is not supported by metal may not be able to resist the stress during cementation and mastication. The purpose of this study was to evaluate fracture strength and fractured appearance of crowns according to different coping designs. A resin maxillary left central incisor analogue was prepared for a metal ceramic crown, and metal dies were made with duplication mold. Metal copings were made and assigned to one of four groups based on facial framework designs: group 1, coping with 0.5mm metal collar; group 2, metal extended to the shoulder; group 3, metal extended to 1mm coronal tn the shoulder: group 4, metal extended to 2mm coronal to the shoulder. Copings and crowns were adjusted to be same size and thickness, and cemented to metal dies with zinc phosphate cement by finger pressure. Fracture strength was measured with Instron Universal Testing Machine. Metal dies were anchored in Three-way-vice at 3mm below finish line and at $130^{\circ}$ inclined to the long axis of the crown. Load was directed lingually at 2mm below midincisal edge. Load value at initial crack and at catastrophic fracture was recorded. The results obtained were as follows : 1. Fracture strength values at initial crack were higher in groups 1, 2 than in groups 3, 4 but this difference was not statistically significant(P<0.05). 2. Conventional metal collared crown had greater catastrophic fracture strength than any other collarless crowns. 3. The greater the labial metal coping reduction, the lower the catastrophic fracture strength of crowns but when more than 1mm of labial metal reduction was done, the difference in strengths was not statistically significant(p<0.05). 4. The strongest collarless coping design was group 2.

• 구강회복응용과학지
• /
• 제26권1호
• /
• pp.33-38
• /
• 2010

상악의 악성 종양에 대한 치료로서 상악골 절제술이 시행되며 필연적으로 이것은 환자 구개부에 결손부를 생성한다. 이로 인해 안모의 변형, 연하, 저작, 발음 등 다양한 문제가 발생할 수 있다. 상악골 절제술 후 이런 문제들을 극복하기 위해 외과적 재건 또는 보철적 치료가 치료 방법으로 선택될 수 있으나 대부분의 상악골 절제술 환자에서 구강악안면 재건의 방법으로 구개폐쇄장치가 더 선호된다. 본 증례는 Aramany 분류 II급에 해당하는 상악골 부분 절제술을 시행한 환자에게 구개폐쇄장치의 유지와 안정을 얻고 모든 기존의 금관수복물을 유지할 수 있는 swing-lock attachment를 사용하여 수복한 임상과정 및 결과에 관하여 보고하고자 한다.

• 대한치과보철학회지
• /
• 제56권1호
• /
• pp.17-24
• /
• 2018

가철성 국소의치의 금속구조물을 제작하는 방법은 왁스 패턴을 제작하여 주조하는 lost wax technique이 주로 사용되어 왔으나, 디지털 기술의 발달로 서베잉과 금속구조물을 CAD (Computer aided design)로 디자인하여 제작할 수 있게 되었다. 여러 증례에서 CAD를 이용한 pattern의 프린팅 방식으로 얻은 레진 패턴이 구강 내에 정확하게 적합 되었고 최종 금속구조물 또한 좋은 적합도를 보였다고 보고되었다. 본 원저는 치조골 소실이 심한 상, 하악부분 무치악 환자에서 가철성 국소의치의 금속구조물을 두 가지 방식으로 각각 제작하였다. 첫 번째는 일반적인 lost wax technique과 두 번째는 CAD를 통해 pattern을 프린팅하여 금속구조물을 주조하는 방식으로 제작하여, CAD data와 fit checker를 이용해 금속구조물과 서베이드 크라운과의 유격을 측정함으로써 금속구조물의 적합도를 비교하였다. 두 가지 방식 모두 임상적으로 사용 가능한 금속구조물의 적합도를 얻었기에 이를 보고하고자 한다.

• The Journal of Advanced Prosthodontics
• /
• 제5권2호
• /
• pp.92-97
• /
• 2013

PURPOSE. All-ceramic crowns are subject to fracture during function. To minimize this common clinical complication, zirconium oxide has been used as the framework for all-ceramic crowns. The aim of this study was to compare the fracture strengths of two computer-aided design/computer-aided manufacturing (CAD/CAM) zirconia crown systems: Lava and Digident. MATERIALS AND METHODS. Twenty Lava CAD/CAM zirconia crowns and twenty Digident CAD/CAM zirconia crowns were fabricated. A metal die was also duplicated from the original prepared tooth for fracture testing. A universal testing machine was used to determine the fracture strength of the crowns. RESULTS. The mean fracture strengths were as follows: $54.9{\pm}15.6$ N for the Lava CAD/CAM zirconia crowns and $87.0{\pm}16.0$ N for the Digident CAD/CAM zirconia crowns. The difference between the mean fracture strengths of the Lava and Digident crowns was statistically significant (P<.001). Lava CAD/CAM zirconia crowns showed a complete fracture of both the veneering porcelain and the core whereas the Digident CAD/CAM zirconia crowns showed fracture only of the veneering porcelain. CONCLUSION. The fracture strengths of CAD/CAM zirconia crowns differ depending on the compatibility of the core material and the veneering porcelain.

• 대한치과보철학회지
• /
• 제61권4호
• /
• pp.367-378
• /
• 2023

최근 CAD-CAM (computer-aided design-computer-aided manufacturing) 기술 및 3D 프린팅 기술의 발전과 함께 다양한 디지털 기법들의 도입으로 top-down 방식의 최종 보철 수복의 정확성과 효율성이 증대되고 있다. 본 증례는 전후 엇갈린 교합을 가진 환자에서 총 9개의 상하악 구치부 임플란트 식립을 통해 안정적인 교합 지지를 얻으면서 잔존 치조골의 고도 흡수 경향을 보인 상악 전치부 무치악 부위는 케네디 4급 임플란트 보조 국소의치로 수복함으로써 연조직의 심미성을 회복하였다. 전산화단층촬영 가이드 수술로 계획된 위치에 임플란트를 식립하고, 이중 스캔 기법으로 임시 수복 단계에서 안정화된 교합을 최종 보철물에 반영하며, 코핑과 프레임워크를 금속 3D 프린팅으로 제작하여 효율적이며 예측 가능한 top-down 방식의 전악 구강 수복을 달성하였기에 이를 보고하고자 한다.

• 대한치과보철학회지
• /
• 제49권4호
• /
• pp.354-361
• /
• 2011

구강 스캐너와 CAD/CAM 기술로 인해 컴퓨터로 제작하는 방식이 활발히 보급된 고정식 보철 증례와는 달리, 의치를 디지털 방식으로 제작하는 데에는 아직 한계가 많다. 촉각을 느낄 수 있는 입력 장비와 전자 서베잉의 개념, 그리고 쾌속 조형법의 적용으로 인해 국소의치를 디지털로 제작할 수 있는 솔루션이 최근 소개되고 있다. 본 증례보고에서는 이러한 국소의치의 디지털 솔루션을 이용하여 총 다섯 명의 환자에서 서베이드 금관 및 국소의치를 제작하였다. 인상 과정상의 문제로 모형과 실제 치아 사이의 형태적 차이가 있었던 경우를 제외하고는 국소의치의 적합도는 우수했으며, 장착 후 안정성과 착탈 시의 유지력 또한 임상에서 적용하는 데에 문제가 없었다.