• 한국안전학회지
• /
• 제30권3호
• /
• pp.1-6
• /
• 2015

Self-piercing riveting (SPR) is receiving more recognition as a possible and effective solution for joining automotive body panels and structures, particularly for aluminum parts and dissimilar parts. In this study, static strength and fatigue tests were conducted using coach-peel and cross-tension specimens with Al-5052 plates for evaluation of fatigue strength of the SPR joints. For the static experiment results, the fracture modes are classified into pull-out fracture due to influence of plastic deformation of joining area. During the fatigue tests for the coach-peel and cross-tension specimens with Al-5052, interface failure mode occurred on the top substrate close to the rivet head in the most cycle region. There were relationship between applied load amplitude $P_{amp}$ and life time of cycle N, $P_{amp}=715.5{\times}N^{-0.166}$ and $P_{amp}=1967.3{\times}N^{-0.162}$ were for the coach-peel and cross- tension specimens, respectively. The finite element analysis results for specimens were adopted for the parameters of fatigue lifetime prediction. The relation between SWT fatigue parameter and number of cycles was found to be $SWT=192.8N_f^{-0.44}$.

• 한국안전학회지
• /
• 제29권3호
• /
• pp.1-7
• /
• 2014

In this study, for the evaluation of the static and fatigue joining strength of the joint, the geometry of the cross-tension specimen was adopted. The specimens were produced with optimal joining force and fatigue life of the clinch joint specimens was evaluated. The material selected for use in this study was cold rolled mild steel (SPCC) with a thickness of 0.8 mm. The maximum tensile load was 708 N for the specimen with single point. The fatigue endurance limit (=42.6 N) per point approached to 6% of the maximum tensile strength at a load ratio of 0.1, suggesting that the joints are vulnerable to cross-tension loading during fatigue. Compared to equivalent stress and maximum principal stress, the SWT fatigue parameter and equivalent strain can properly predict the current experimental fatigue life. The SWT parameter can be expressed as $SWT=2497.5N^{-0.552)_f$.

• 한국안전학회지
• /
• 제21권5호
• /
• pp.17-21
• /
• 2006

In this study, SPCC cross-tension type specimens produced under various spot welding conditions were tensile and fatigue tested. Decrease of 2 kA in normal current condition of 10 kA caused a large amount of reduction in both static joining strength and fatigue life. And 2 kA increase resulted in increase of static joining strength and an increase in low cycle regime but a decrease in high cycle regime, revealing the fact that fatigue strength rather than static joining strength would be a major factor during design process in view of the body endurance. As a results of estimating the fatigue lifetimes of various types of spot weld specimens. equivalent stress intensity factor is the proper parameter for predicting the lifetimes of various types of specimens. which can be expressed as ${\Delta}K_{eq}(N/nm^{1.5})=11550N^{-0.36}_{f}$.

• Computers and Concrete
• /
• 제18권1호
• /
• pp.39-51
• /
• 2016

This paper considers the tensile strength of concrete samples in direct, CTT, modified tension, splitting and ring tests using both of the experimental tests and numerical simulation (particle flow code 2D). It determined that which one of indirect tensile strength is close to direct tensile strength. Initially calibration of PFC was undertaken with respect to the data obtained from Brazilian laboratory tests to ensure the conformity of the simulated numerical models response. Furthermore, validation of the simulated models in four introduced tests was also cross checked with the results from experimental tests. By using numerical testing, the failure process was visually observed and failure patterns were watched to be reasonable in accordance with experimental results. Discrete element simulations demonstrated that the macro fractures in models are caused by microscopic tensile breakages on large numbers of bonded discs. Tensile strength of concrete in direct test was less than other tests results. Tensile strength resulted from modified tension test was close to direct test results. So modified tension test can be a proper test for determination of tensile strength of concrete in absence of direct test. Other advantages shown by modified tension tests are: (1) sample preparation is easy and (2) the use of a simple conventional compression press controlled by displacement compared with complicate device in other tests.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 봄 학술발표회 논문집(I)
• /
• pp.774-780
• /
• 1999

The study of bond behavior between concrete and rebar has been performed for a long time. On this study, we tried to analysed variation of bond behaviors quantitatively with varying the strength of concrete. Bond stress which observed below the neutral surface of beam and at connecting part of beam and column is affected by various bond parameters. Resistance of deformed bars which embedded in concrete to the pullout force is divided 1) chemical adhesive force 2) frictional force 3) mechanical resistance of ribs to the concrete and these horizontal components of resistance is being bond strength. We selected the most common and typical variable which is concrete strength among various variables. So we used two kinds of concrete strength like as 25MPa(NSC) and 65MPa(HSC). Tension Test was performed to verify how bond behavior varied with two kinds of concrete strength. Concentration of bond stress was observed at load-end commonly in Tension Test of the initial load stage. At this stage stress distribution was almost coincident at each strength. As tension load added, this stress distribution had difference gradually and movement of pick point of bond stress to free-end and central section was observed. This tendency was observed at first and moving speed was more fast in NSC. At the preceeding result the reason of this phenomenon is considered to discretion of chemical adhesion and local failure of concrete around rebar in load-end direction. Especially, when concrete strength was increased 2.6 times in tension test, ultimate bond strength was increased 1.45 times. In most recent used building codes, bond strength is proportioned to sqare root of concrete compressive strength but comparison of normalized ultimate bond strength was considered that the higher concrete strength is, the lower safety factor of bond strength is in each strength if we use existing building codes. In Tension Test, in case of initial tensile force state, steel tensile stress of central cross section is not different greatly at each strength but tensile force increasing, that of central cross section in NSC was increased remarkably. Namely, tensile force which was shared in concrete in HSC was far greater than that of concrete in NSC at central section.

• Journal of Welding and Joining
• /
• 제33권6호
• /
• pp.21-26
• /
• 2015

Recently, application of UHSS(Ultra High Strength Steels) whose tensile strength is over 1000MPa to car body structure are growing due to great needs for light weighting and improved crash worthiness. However, their poor weldability is one of obstacles to expand selecting to car body. In this study, effect of Phosphorus contents on resistance spot weldability of high elongation DP980 steel whose Si content is over 1% was investigated. The cross tension strength (CTS) was decreased showing partial interface fracture as Phosphorus content increase because of solidification segregation of Phosphorus. In order to improve resistance spot weldability by modification of welding condition, in-situ post-weld heating pulse was introduced after main pulse. The optimum cooling time between main and post pulse and post-pulse current condtion were determined through FEM welding simulation and DOE tests. The CTS was increased about 1.5 time showing plug fracture. The decrease of Phosphorus segregation was found to be a major reason for weld ductility and CTS improvement.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(I)
• /
• pp.391-394
• /
• 2005

A theoretical model was developed to predict the shear strength of slender reinforced concrete beams. The shear force applied to a cross-section of the beam was assumed to be resisted primarily by the compressive zone of intact concrete rather than by the tensile zone. The shear capacity of the cross section was defined based on the material failure criteria of concrete: failure controlled by compression and failure controlled by tension. In the evaluation of the shear capacity, interaction with the normal stresses developed by the flexural moment in the cross section was considered. In the proposed strength model, the shear strength of the beam and the location of the critical section were determined at the intersection between the shear capacity and shear demand curves. The proposed strength model was verified by the comparisons to prior experimental results.

• 대한토목학회논문집
• /
• 제31권1A호
• /
• pp.35-41
• /
• 2011

콘크리트구조설계기준에서는 일반적으로 처짐을 제어하기 위해 직접처짐제어법과 간접처짐제어법을 제시하고 있다. 이 때 처짐/깊이-비는 허용 처짐량을 초과하지 않도록 제한된다는 점에서 간접처짐제어법이 더 효과적이다. 실제 처짐량은 많은 요소에 의해 영향을 받기 때문에 실제 처짐량을 정확하게 산정하는 것은 어렵다. 이 연구에서는 철근콘크리트 부재의 사용한 계상태에서 처짐량을 직접 계산함으로써 한계 지간/깊이-비를 산정하였다. 이 때 처짐은 재료 모델로부터 산정된 휨곡률을 통해 산정하였다. 해석의 주요 변수는 인장증강효과 모델, 콘크리트 강도, 단면 크기 및 압축 철근의 유무이다. 해석 결과 2차식 형태의 인장증강효과 모델을 사용함으로써 해석의 일관성을 도모할 수 있는 것으로 나타났다. 또한 한계 지간/깊이-비는 단면 크기와 관계없이 재료 강도와 인장 및 압축 철근비에 따라 변화하는 것으로 나타났다.

• Computers and Concrete
• /
• 제18권1호
• /
• pp.139-154
• /
• 2016

Since the concrete strength around the reinforcement rebar affects the tension stiffening, the tension stiffening effect of ultra high performance concrete on the concrete members reinforced by steel rebar is examined by testing the specimens with circular cross section with the length 850 mm reinforced by a steel rebar at the center of a specimen's cross section in this research. Conducting a tensile test on the specimens, the cracking behavior is evaluated and a curve with an exponential descending branch is obtained to explain the post-cracking zone. In addition, this paper proposes an equation for this branch and parameters of equation is obtained based on the ratio of cover thickness to rebar diameter (c/d) and reinforcement percentage (${\rho}$).

• Structural Engineering and Mechanics
• /
• 제10권2호
• /
• pp.165-180
• /
• 2000

An analytical model with tension softening for the prediction of the capacity of prestressed concrete beams under pure torsion and under torsion combined with shear and flexure is introduced. The proposed approach employs bilinear stress-strain relationship with post cracking tension softening branch for the concrete in tension and special failure criteria for biaxial stress states. Further, for the solution of the governing equations a special numerical scheme is adopted which can be applied to elements with practically any cross-section since it utilizes a numerical mapping. The proposed method is mainly applied to plain prestressed concrete elements, but is also applicable to prestressed concrete beams with light transverse reinforcement. The aim of the present work is twofold; first, the validation of the approach by comparison between experimental results and analytical predictions and second, a parametrical study of the influence of concentric and eccentric prestressing on the torsional capacity of concrete elements and the interaction between torsion and shear for various levels of prestressing. The results of this investigation presented in the form of interaction curves, are compared to experimental results and code provisions.