• Corrosion Science and Technology
• /
• v.14 no.4
• /
• pp.195-199
• /
• 2015

Materials of choice for offshore structures and the marine industry have been increasingly favoring materials that offer high strength-to-weight ratios. One of the most promising families of light-weight materials is titanium alloys, but these do have two potential Achilles' heels: (i) the passive film may not form or may be unstable in low oxygen environments, leading to rapid corrosion; and (ii) titanium is a strong hydride former, making it vulnerable to hydrogen embrittlement (cracking) at high temperatures in low oxygen environments. Unfortunately, such environments exist at deep sea well-heads; temperatures can exceed $120^{\circ}C$, and oxygen levels can drop below 1 ppm. The present study demonstrates the results of investigations into the corrosion behavior of a range of titanium alloys, including newly developed alloys containing rare earth additions for refined microstructure and added strength, in artificial seawater over the temperature range of $25^{\circ}C$ to $200^{\circ}C$. Tests include potentiodynamic polarization, crevice corrosion, and U-bend stress corrosion cracking.

• Transactions on Electrical and Electronic Materials
• /
• v.2 no.3
• /
• pp.28-32
• /
• 2001

It was studied in the present work how the thermal cycling performance of LOC (lead on chip) packages depends on the package construct or leadframe materials. First, package body thickness and Au wire diameter were manipulated for the selection of proper package design. Secondly, two different types of leadframe materials (i.e. copper and 52%Fe-48%Ni alloy) were tested to determine the better material for improved reliability margin of plastically encapsulated microelectronic packages. This work shows that manipulating package body thickness was more effective than an increase of Au wire from 23$\mu\textrm{m}$ to 33$\mu\textrm{m}$ for the prevention of wire debonding failure. Further, this work indicates that the LOC packages including the copper leadframes can be more susceptible to thermal cycling reliability degradation due to chip cracking than those including the alloy leadframes.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.124-124
• /
• 2015

Acoustic microscopy and scanning electron microscopy were applied to non-destructively evaluate the hydrogen-induced cracking of API X-80 steels and to find the initiation time of the crack. The API X-80 steel had the average grain size of about $4-10{\mu}m$. The hardness was reduced from 240 to 202 [Hv] after exposing in HIC environment for 2-days. Friction coefficient and wear loss were 0.745 and 0.392 mm, respectively. Empirical equation of corrosion potential and corrosion rate of the steel with HIC time in $5%NaCl-0.5%CH_3COOH$ at $25^{\circ}C$ were $Eh\;(up)=0.06^*t[day]+0.2951$, $Eh(down)=0.376^*t[day]+0.5938$, respectively. HIC grew with micro-size after 1-day exposure. The HIC tended to propagate on the surface with Al, Si, Ti, and Mn.

• Applied Chemistry for Engineering
• /
• v.20 no.1
• /
• pp.1-8
• /
• 2009

Bio-oil has attracted considerable interest as one of the promising renewable energy resources because it can be used as a feedstock in conventional petroleum refineries for the production of high value chemicals or next-generation hydrocarbon fuels. Currently, catalytic vapor cracking is considered the most potential upgrading method for stabilization of bio-oil, which is a pre-process required prior to feeding bio-oil into refineries. This review introduces the recent research and development trends on bio-oil upgrading via catalytic vapor cracking, focusing on catalysts and upgrading methods used.

• International Journal of Highway Engineering
• /
• v.8 no.3 s.29
• /
• pp.163-172
• /
• 2006

This study evaluated the laboratory properties of asphalt binder and mixture modified with SPC(Sulfur Polymer Cement), which consists of sulfur as a main ingredient that is an industrial by-product made from refining process of crude oil and carbon-black as an additive. Four levels of SPC modifier ratios(0, 10, 30, 50%) were evaluated in the laboratory. Superpave(Superior Performing Asphalt Pavements) system was used to determine the PG(Performance Grade) and evaluate the property of SPC modified binder at the different temperatures. IDT(Indirect Tensile Test) was performed to evaluate the resistance of fatigue and low-temperature cracking at $10^{\circ}C\;and\;-10^{\circ}C$. Wheel-tracking test was also performed to evaluate the rutting-resistance of SPC modified asphalt mixtures. Test results showed that the more SPC modifier ratios, the better rutting-resistance and the more potential of low-temperature cracking resistance. However, SPC modifier did not show the effect on the fatigue cracking resistance.

• International Journal of Highway Engineering
• /
• v.18 no.1
• /
• pp.33-41
• /
• 2016

PURPOSES : This study primarily focused on evaluating the performance characteristics of 4.75-mm nominal maximum aggregate size (NMAS) asphalt mixtures for their more effective implementation to a layered flexible pavement system. METHODS : The full-scale pavements in the FDOT's accelerated pavement testing (APT) program, including 4.75-mm mixtures at the top with different thicknesses and asphalt binder types, were considered for the faster and more realistic evaluation of the rutting performance. The results of superpave indirect tensile (IDT) tests and hot-mix asphalt fracture mechanics (HMA-FM) based model predictions were used for cracking performance assessments. RESULTS : The results indicated that the rutting performance of pavement structures with 4.75-mm mixtures may not be as good as to those with the typical 12.5-mm mixtures, and pavement rutting was primarily confined to the top layer of 4.75-mm mixtures. This was likely due to the relatively higher mixture instability and lower shear resistance compared to 12.5-mm mixtures. The energy ratio (ER) and HMA-FM based model performance prediction results showed a potential benefit of 4.75-mm mixtures in enhanced cracking resistance. CONCLUSIONS : In relation to their implementation, the best use of 4.75-mm mixtures seem to be as a surface course for low-traffic-volume applications. These mixtures can also be properly used as a preservation treatment that does not necessarily last as long as 12.5-mm NMAS structural mixes. It is recommended that adequate thicknesses and binder types be considered for the proper application of a 4.75-mm mixture in asphalt pavements to effectively resist both rutting and cracking.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.6
• /
• pp.262-270
• /
• 2007

Recently, there has been a new appreciation of aluminum alloys as materials that are capable of reducing the environment load. This is because aluminum alloys are lightweight, easy to recycle, permit miniaturization, and have environmental friendly properties. In this study, we investigated the mechanical and electrochemical properties of 5083F aluminum alloys using slow strain rate test(SSRT) and potentiostatic tests under various potential conditions. In the potentiostatic tests, the current density in the potential range from -0.7 to -1.4V after 1,200 s was low. After considering the results of the potentiostatic tests, maximum tensile strength, yield strength, elongation, time-to-fracture, observation of fractured specimen and fractography analysis, the optimum protection potential range was between -1.3 and -0.7V(Ag/AgCl).

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.154-159
• /
• 1998

In order to assess the susceptibility of the environmentally assisted cracking(EAC) on SA508 Cl.3 steel in primary water condition, potential step test and slow strain rate test(SSRT) were conducted in a simulated crack tip condition. In this test, anodic dissolution was dominant in the crack tip environments. Proposed simple dissolution model is a modification of Hishida's anodic dissolution model at the plastic zone. One can predict actual crack growth rate with the smooth specimen through this model.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2004.05a
• /
• pp.401-407
• /
• 2004

This study is on the constant-current stress corrosion test related to the load stress in welded zone and non-welded zone of high tensile strength steel for natural gas transmission. The surface corrosion pattern of the welded zone of API 5L-X65 specimens for natural gas transmission showed global corrosion and narrow pitting, and the pitting was increased by increasing the load stress. Initially, the average relative electrode potential and the average relative current of the high tensile strength steel for natural gas transmission specimens was decreased suddenly, and the average relative electrode potential was higher and the average relative current was lower in welded zone than base metal. and the average relative electrode potential was decreased by increasing the load stress, and the average relative current was somewhat increased by increasing the load stress. The corrosion rate was less in welded zone than base metal, and the corrosion rate was decreased by increasing the load stress.

• Journal of Ocean Engineering and Technology
• /
• v.18 no.5
• /
• pp.50-56
• /
• 2004

This study is on the constant-current stress corrosion test, related to the load stress, in both the welded and non-welded zones of high tensile strength steel that is used for natural gas transmission. The surface corrosion pattern of the welded zone of API 5L-X65 specimens for natural gas transmission showed general corrosion and narrow pitting, and the pitting was increased with load stress. Initially, the average relative electrode potential and the average relative current of the high tensile strength steel, used for natural gas transmission specimens, were decreased rapidly, and the average relative electrode potential was higher and the average relative current was lower in welded zone, compared to base metal. The average relative electrode potential was decreased with load stress, and the average relative current was somewhat increased by increasing the load stress. The corrosion rate was less in welded zone, compared to base metal, and the corrosion rate was decreased by increasing the load stress.