• 펄프종이기술
• /
• 제40권4호
• /
• pp.66-73
• /
• 2008

When coated paperboard is printed, pressed into a groove with a creasing rule and folded, white line cracking occurs along the crease due to intensive mechanical pressure. The cracking will deteriorates product quality and waste resources. Effects of creasing pressure and ink dosage on the foldability of coated board were investigated. It was shown that applying an optimum pressure is important during creasing. When the pressure was too low, the crease formed was not sufficiently deep enough to enable precise folding. When an excess pressure was applied, fiber bonding was destroyed, resulted in unsatisfactory cracking. When the coated board was folded in machine direction (MD), long cracks were formed along MD. When it folded in cross direction (CD), the cracks were shorter and formed perpendicular to CD. Printing promoted cracking due to the decrease in flexibility of coated board. In addition, uneven ink film layer on the coating layer caused worse cracking.

• 한국레이저가공학회지
• /
• 제4권1호
• /
• pp.39-48
• /
• 2001

This study was performed to evaluate basic characteristics of electron beam weldability for high strength aluminum alloys. The aluminum alloys used were A5083 and A6N01, and A7N01. The principal welding process parameters, such as accelerating voltage, beam current, welding speed and chamber pressure were investigated. The dimension and microstructure of welds were evaluated with OLM, and SEM (EDAX). In addition, weldability variation(cracking) due to process parameters was also evaluated. The degree of cracking in the EB fusion zone appears to be affected mainly by aspect ratio, such that as aspect ratio increases the cracking tendency also increases. The alloying element itself may also affect the hot cracking resistance, but its role is considered to be indirect effect such that the relatively higher vaporization pressure elements of Zn and Mg give deeper weld penetration and thus results in greater cracking tendency.

• Nuclear Engineering and Technology
• /
• 제45권2호
• /
• pp.265-276
• /
• 2013

Pressure tubes made of Zr-2.5 wt% Nb alloy are important components consisting reactor coolant pressure boundary of a pressurized heavy water reactor, in which unanticipated through-wall cracks and rupture may occur due to a delayed hydride cracking (DHC). The Canadian Standards Association has provided deterministic and probabilistic structural integrity evaluation procedures to protect pressure tubes against DHC. However, intuitive understanding and subsequent assessment of flaw behaviors are still insufficient due to complex degradation mechanisms and diverse influential parameters of DHC compared with those of stress corrosion cracking and fatigue crack growth phenomena. In the present study, a deterministic flaw assessment program was developed and applied for systematic integrity assessment of the pressure tubes. Based on the examination results dealing with effects of flaw shapes, pressure tube dimensional changes, hydrogen concentrations of pressure tubes and plant operation scenarios, a simple and rough method for effective cooldown operation was proposed to minimize DHC risks. The developed deterministic assessment program for pressure tubes can be used to derive further technical bases for probabilistic damage frequency assessment.

• Corrosion Science and Technology
• /
• 제7권4호
• /
• pp.237-242
• /
• 2008

Physical properties of water, such as dielectric constant and ionic product, significantly vary with the density of water. In the supercritical conditions, since density of water widely varies with pressure, pressure has a strong influence on physical properties of water. Dielectric constant represents a character of water as a solvent, which determines solubility of an inorganic compound including metal oxides. Dissociation equilibrium of an acid is also strongly dependent on water density. Dissociation constant of acid rises with increased density of water, resulting in drop of pH. Density of water and the density-related physical properties of water, therefore, are the major governing factors of corrosion and environmentally assisted cracking of metals in supercritical aqueous solutions. This paper discusses importance of "physical properties of water" in understanding corrosion and cracking behavior of alloys in supercritical water environments, based on experimental data and estimated solubility of metal oxides. It has been pointed out that the water density can have significant effects on stress corrosion cracking (SCC) susceptibility of metals in supercritical water, when dissolution of metal plays the key role in the cracking phenomena.

• 화약ㆍ발파
• /
• 제35권2호
• /
• pp.1-8
• /
• 2017

본 연구에서는 증기압을 이용한 새로운 파암공법의 특징을 간략하게 소개하였다. 이 파암공법은 지하암반굴착에서 지반진동을 저감시키려는 목적으로 개발된 것이다. 한 터널굴착 현장에서 대상공법에 대한 검증시험을 실시하였다. 지반진동은 시험현장 부근에서 측정하였다. 측정된 진동자료는 일본의 한 기업이 제안한 진동 추정식으로 예측한 결과와 서로 비교하였다. 공법의 경제성을 입증해 보이기 위해 간단한 비용분석 결과도 제시하였다.

• Journal of Welding and Joining
• /
• 제17권5호
• /
• pp.47-54
• /
• 1999

It is well known that solidification cracking often occurs in welds of root pass for one-side welding under the conditions of high welding currents and speeds. In this study, the solidification in 590MPa class steel for pressure vessels SPPV490 was investigated by using flux-cored arc welding(FCAW) with 4 types of welding wires and welding conditions of 200∼280A and 2.8∼ 4.2mm/sec. In order to compared the result of cracking in SPPV490, 0.2%C steel for welded structure of SWS400 and 0.45%C steel for machine structural SM45C were also used as base metals. As the results, all the cracks formed in some welding conditions were observed near the center of weld bead. The solidification cracks were generally initiated near the upper surface of bead and propagated toward the inner part. The solidification cracking generally increased with welding current and welding speed in the same base metal and welding material. In cracking susceptibility, SPPV490 showed higher cracking susceptibility than SWS400 in all welding conditions and welding materials. It was considered that cracking susceptibility could not be evaluated with the hardness of weld metals. The cracking ratio increased with decreasing of a/b(a and b; the width of the upper surface and the back surface of the bead) as shape factor of bead. The cracking tendency with shape factor of bead was extended under the condition of higher welding currents.

• Journal of Welding and Joining
• /
• 제20권2호
• /
• pp.82-89
• /
• 2002

In order to clarify hot cracking phenomena occurred in Inconel 690 welds and it's prevention, in this study, the cracking behavior and the influence of welding variables on cracking in Inconel 690 overlay welds on Mn-Ni-Cr-Mo steel(SA 508 cl.3) for pressure vessel were investigated by using mock-up test. The main results are as follows: The cracks in Inconel 690 overlay welds were mainly generated near the start and the end part of welding beads adjacent to STS 309L welded outside of Inconel 690 welds. Most of the cracks showed typical solidification crack, and also it was assumed that there was possibility of liquation cracking in HAZ. The existence of Nb constituents or concentration of Nb was recognized on the fracture facets of the solidification cracks in the welds by SMAW. Therefore Nb was considered to be the main factor of the solidification cracking. As the weld heat input was more increased and the weld bead length was longer, the extent of cracking was more increased. Moreover the extent of cracking was considerably decreased by changing of welding sequence to the start and the end part of welds. Hot cracking in welds by GTAW was considerably decreased as compared with that of SMAW. And cracks were well generated in the Inconel 690 overlay welds adjacent to 575 309L welds. This means that the hot cracking susceptibility of Inconel 690 welds was largely varied by chemical components and/or compositions of filter metals, base metals and neighboring welds.

• 한국압력기기공학회 논문집
• /
• 제11권1호
• /
• pp.20-24
• /
• 2015

Steam generator(S/G) tubes in pressurized water reactor (PWR's) are subject to several types of degradation. This degradation includes denting, pitting, intergranular attack(IGA), intergranular stress corrosion cracking(IGSCC), fatigue, fretting and wear. Degradation can be derived from either the primary side(inside) or the secondary side(outside) of the tube. Recent issue for tube degradation in domestic steam generator is the tube end cracking on seal weld region. The seal weld region at the tube end and tube itself is regarded as a pressure boundary between the primary side and the secondary side. One of the Westinghouse Model-F S/G has experienced tube end cracking and its number of plugging approximately becomes to the operating limit up to 5% due to tube end cracking which was reported as SAI/MAI(single/multiple axial indication) or SCI/MCI(Single/multiple circumferential indication) from the results of eddy current testing. Eddy current mock-up test was carried out to determine the origin of cracking whether it is from weld zone area or parent tube. This result was helpful to analyze crack location on ECT data. Correct action on this problem was the installation of tube-end sleeve. Last year, after removing 340 installed plugs from tubes, selected 269 tubes took tube-end sleeve installation. Tube-end sleeve brought pressure boundary from parent tube to installed sleeve tube. Tube-end sleeve has the benefit of reducing outage period and increasing more revenue than replacing S/G. This paper is provided to assist interest parties in effectively understanding this issue.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.675-680
• /
• 2002

Cracking and bulging in welded and internally lined pressure vessels that work in thermal-mechanical cycling service have been well known problems in the petrochemical, power and nuclear industries. However, published literature and industry surveys show that similar problems have been occurring during the last 50 years. A better understanding of the causes of cracking and bulging causes is needed to improve the reliability of these pressure vessels. This study attempts to add information required for increasing the knowledge and fundamental understanding required. Typical examples of this problem are the coke drums in the delayed coking units refinery process. This case was selected for experimental work, field study and results comparison. Delayed coking units are among the refinery units that have higher economical yields. To shut down these units represents a high negative economical impact in refinery operations. Also, the maintenance costs associated with repairs are commonly very high. Cracking and bulging occurrences in the coke drums, most often at the weld areas, characterize the history of the operation of delayed coking units. To design and operate more robust coke drums with fewer problems, an improved metallurgical understanding of the cracking and bulging mechanisms is required. A methodology that is based field experience revision and metallurgical analyses for the screening of the most important variables, and subsequent finite element analyses to verify hypotheses and to rank the variables according to their impact on the coke drum lives has been developed. This indicated approach provides useful information for increasing coke drum reliability. The results of this work not only order the most important variables according to their impact in the life of the vessels, but also permit estimation of the life spans of coke drums. In conclusion, the current work shows that coke drums may fail as a combination of thermal fatigue and other degradation mechanisms such as: corrosion at high and low temperatures, detrimental metallurgical transformations and plastic deformation. It was also found that FEA is a very valuable tool for understanding cracking and bulging mechanisms in these services and for ranking the design, fabrication, operation and maintenance variables that affect coke drum reliability.

• 한국압력기기공학회 논문집
• /
• 제7권1호
• /
• pp.27-34
• /
• 2011

The objective of this study is to classify the geometry of wall-thinning defect that causes a circumferential crack in the pipe elbows subjected to internal pressure. For this objective, first of all a criterion to determine the occurrence of circumferential cracking at wall-thinned area was developed based on finite element simulation for burst tests of pipe elbow specimens that showed axial and circumferential cracking at wall-thinned area. In addition, parametric finite element analysis including various wall-thinning geometries, locations, and pipe geometries was conducted and the wall-thinning geometries that initiate circumferential crack were determined by applying the criterion to the results of parametric analysis. It showed that the circumferential crack occurs at wall-thinning defect, which has a deep, wide, and short geometry. Also, it is indicated that the pipe elbows with larger radius to thickness ratio are more susceptible to circumferential cracking at wall-thinned area.