• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.4 no.2
• /
• pp.133-142
• /
• 1984

With the weld-joined compact tension specimens compared with each other, that is, transverse and lengthwise about the crack propagation direction, high and low in the input heat level, same as and lower than the base metal in the strength of weld material, the fatigue test were performed. With these data, the log-log curves between the fatigue crack propagation rate ${\frac{da}{dN}}$ and the transition range of the stress intensity factor ${\Delta}K$ ahead the crack tip were drawed. These curves were compared and estimated among each compared specimens, among each zones, that is, the base metal, the heat-affected metal and the weld-mixed metal, and between this study and the past studies. Basically, Little difference in the slope of the $da/dN-{\Delta}K$ relation was showed in all the welded directions, all the input heat levels and all the zones. But, First, to comparison with in the past studies about the base metals, it was showed that da/dN started in the much later rate, increased faster and stoped in the little faster rate. Second, it was showed that, near the time the crack's going from the heat-affected zone to the weld-mixed metal da/dN decreased a little for a while. Third, in the lengthwise weld compared with the transverse weld, in the high input heat weld compared with the low input heat weld in the case used the weld material of the same strength as the base metal, in the opposite case in the case used the one of the lower strength than the base metal, in the case used the weld material of the same strength as compared with the lower strength than the base metal beside the high input heat and the lengthwise weld, it was showed that the crack occured earlier in lower ${\Delta}K$ and later da/dN, the curves went with the same slope. Forth, in the lengthwise weld compared with the transverse weld in the low input heat weld, in the low input heat weld compared with the high input heat weld, it was showed that da/dN went with the lower level.

• Journal of the Society of Naval Architects of Korea
• /
• v.32 no.1
• /
• pp.118-131
• /
• 1995

The shock fracture analysis for the structures of navy vessels subject to underwater explosions or of high speed vessels frequently subject to impact loads has been carried out in two steps such as the global or macro analysis and the fine or micro analysis. In the macro analysis, Doubly Asymptotic Approximation(DAA) has been applied. The three main failure modes of structure members subject to strong shock loading are late time fracture mode such as plastic large deformation mainly due to dynamic plastic buckling, and the early time fracture mode such as tensile tearing failure or transverse shear failure. In this paper, the tensile tearing failure mode is numerically analyzed for the micro analysis by calculating the dynamic stress intensity factor $K_I(t)$, which shows the relation between stress wave and crack propagation on the longitudinal stiffener of the model. Especially, in calculating this factor, the numerical caustic method developed from shadow optical method of caustic well known as experimental method is used. The fully submerged vessel is adopted for the macro analysis at first, of which the longitudinal stiffener, subject to early shock pressure time history calculated in macro analysis, is adopted for the micro analysis.