• 한국해양공학회지
• /
• 제2권2호
• /
• pp.122-129
• /
• 1988

Recently with the rapid development in marine and shipbuliding industries such as marine structures, ship and chemical plants, there occurs much interest in the study of corrosion fatigue characteristics which was closed up an important role in mechanical design. In this study, the 5086 Al-alloy was tested by use of rotary bending fatigue tester. The retardation effect of overload on the corrosion fatigue crack propagation in sea environment was quantitatively studied. 1) Retardation effect of corrosion fatigue crack propagation is most eminent when overload ratio is 1.52, overload magnitude corresponds to about 77% and 55% of yield strength and tensile strength respectively. 2) After overload ratio 1.52 was used, retardation of corrosion fatigue crack growth rate is largely retarded and quasi-threshold stress intensity factor range($\Delta\textrm{K}_{th}$) appears. 3) According to m of experimental constant, retardation effect of corrosion fatigue crack propagation corresponds to about 25% of constant stress amplitude when overload ratio is 1.52. 4) When overload ratio 1.52 was used, retardation parameter (RP) decreases to about 0.43 and corrosion sensitivity (S)decreses to about 2.1.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2003년도 춘계학술대회 논문집
• /
• pp.1508-1512
• /
• 2003

In this study, retardation behavior of fatigue crack under single overloading of the mixed mode state was experimentally investigated. To produce single overload in the mixed mode I+II state, the compact tension shear (CTS) specimen and loading device were used. The propagation tests for fatigue crack were performed under mode I and mixed-mode loading overloading afterwards. We examined the observed deformation aspects, the variation of fatigue life and crack propagation rate, and the aspects of retardation behavior from tests. The retardation effect of mixed-mode single overload on fatigue crack propagation behavior was smaller than that of mode I single overload. Also the loading modes of variable and constant amplitude loads have influence on the retardation behavior of fatigue cracks.

• 대한기계학회논문집A
• /
• 제25권3호
• /
• pp.470-477
• /
• 2001

Constant ΔK fatigue crack growth tests were performed by applying an intermediate multiple overload for S45C steel. The purpose of the present study is to investigate effects of specimen thickness at various baseline stress intensity factor range levels (ΔK(sub)b), overload application position (a/W) and overload application frequency (OL(sub)HZ) on fatigue crack growth retardation behavior. The principal results are summarized as follows. The amount of retardation for a given ΔK(sub)b level is increased with increasing the baseline stress intensity factor range level for all specimen thickness. The normalized minimum crack growth rate is increased with increasing the specimen thickness, except for ΔK=45MPa√m. The retardation cycle is decreased with increasing a/W and increased with OL(sub)HZ.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 춘계학술대회논문집A
• /
• pp.55-60
• /
• 2000

Constant ${\Delta}K$ fatigue crack growth tests were performed applying an intermediate multiple overload for SM45C steel. The purpose of the present study is to investigate the effects of specimen thickness at various baseline stress intensity levels$({\Delta}K_b)$, overload application frequency(a/W) and overload application frequency$(OL_{HZ})$ on fatigue crack growth retardation behavior. The principal results are summarized as follows. The amount of retardation for a given ${\Delta}K_b$ level is increased with increasing the baseline stress intensity level in all specimen thickness. The normalized minimum crack growth rate is increased with increasing the specimen thickness, except for ${\Delta}K=45MPa \sqrt m$. The retardation cycle is decreased with increasing the overload application position and increased with the overload application frequency.

• 한국해양공학회지
• /
• 제13권3호통권33호
• /
• pp.36-48
• /
• 1999

Fatigue life and crack retardation behavior after penetration were experimentally examined using surface pre-cracked specimens of aluminium alloy 5083. The Wheeler model retardation parameter was used successfully to predict crack growth behavior after penetration. By using a crack propagation rule, the change in crack shape after penetration can be evaluated quantitatively. Advanced, waveform-based acoustic emission (AE) techniques have been successfully used to evaluate signal characteristics obtained form fatigue crack propagation and penetratin behavior in 6061 aluminum plate with surface crack under fatigue stress. Surface defects in the structural members are apt to be origins of fatigue crack growth, which may cause serious failure of the whole structure. The nondestructive analysis on the crack growth and penetration from these defects may, therefore, be one of the most important subjects on the reliability of the leak before break (LBB) design. The goal of the present study is to determine if different sources of the AE could be identified by characteristics of the waveforms produced from the crack growth and penetration. AE signals detected in four stages were found to have different signal per stage. With analysis of waveform and power spectrum in 6061 aluminum alloys with a surface crack, it is found to be capabilities on real-time monitoring for the crack propagation and penetration behavior of various damages and defects in structural members.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1997년도 추계학술대회 논문집
• /
• pp.829-832
• /
• 1997

It is difficult to explain the effects of complex variable loading experienced by the machine and the structure only with the studies of the single-overload itself. Hence, it is thought that the variation of overload-holding time are required to explain the effects more clearly. The effects of the overload were analyzed by means of the crack retardation, and the fractography on retardation zone. A characteristic of the fractography on retardation zone was that striation distribution did not appear due to decreased crack driving force. Rotary bending fatigue tests were performed with the circular shaft which has two hole defects.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.597-602
• /
• 2001

A method for the retardation of fatigue crack growth using ring indentation at the vicinity of a crack is examined. Residual stresses near crack tip are evaluated using fracture mechanics approach. The motivation is to develop a simple and effective method for obtaining an increase in fatigue lives to total failure of materials with crack. Fatigue testing of aluminum specimen showed that the retardation effects are observed after the application of the method.

• 한국항공우주학회지
• /
• 제31권10호
• /
• pp.27-33
• /
• 2003

균열주위에 링압인을 부가함으로서 피로균열을 지연하는 수법을 제시하였다. 균열주위의 잔류응력분포는 Bueckner가중함수를 이용한 파괴역학적 수법으로 평가하였다. 본 연구는 균열을 가진 재료에 대한 파단시까지의 피로수명을 향상시키기 위한 단순하면서도 표과적인 수법을 개발하는데 있다. 알루미늄재료에 대한 피로실험결과 본 수법이 피로지연효과를 효율적으로 얻을 수 있는 것으로 나타났다.

• 한국재료학회지
• /
• 제28권7호
• /
• pp.398-404
• /
• 2018

Fatigue crack growth retardation of 304 L stainless steel is studied using a neutron diffraction method. Three orthogonal strain components(crack growth, crack opening, and through-thickness direction) are measured in the vicinity of the crack tip along the crack propagation direction. The residual strain profiles (1) at the mid-thickness and (2) at the 1.5 mm away from the mid-thickness of the compact tension(CT) specimen are compared. Residual lattice strains at the 1.5 mm location are slightly higher than at the mid-thickness. The CT specimen is deformed in situ under applied loads, thereby providing evolution of the internal stress fields around the crack tip. A tensile overload results in an increased magnitude of the compressive residual stress field. In the crack growth retardation, it is found that the stresses are dispersed in the crack-wake region, where the highest compressive residual stresses are measured. Our neutron diffraction mapping results reveal that the dominant mechanism is by interrupting the transfer of stress concentration at the crack tip.

• 한국항공우주학회지
• /
• 제31권3호
• /
• pp.15-22
• /
• 2003

피로균열성장모델을 유도하고 지연모델을 제안하였다. 피로균열성장모델은 피로균열선단의 소성변형으로 인하여 균열표면에 발생하는 잔류소성스트레치를 고려하고 있다. 균열 성장률은 균열선단 재료요소의 소성변형에너지와 누적피로손상으로부터 계산된다. 유도한 균열성장모델로부터 계산한 균열성장률은 AL6061-T651과 17-4PH 주강의 시험결과와 잘 일치하고 있다. 피로균열성장지연모델은 인장과대하중으로부터 생성된 잔류소성스트레치를 근거로 하고 있으며, 인장과대하중은 다음 하중 사이클의 소성변형률을 감소시킨다. Strip-yield모델을 이용하여 균열선단의 소성역을 계산하였다. 새로 제안된 지연모델은 인장과대하중하의 피로균열선장특성 및 지체지연 현상을 잘 기술하고 있다.