• Korean Journal of Metals and Materials
• /
• v.48 no.1
• /
• pp.28-38
• /
• 2010

High temperature high cycle and low cycle fatigue deformation behavior of automotive heat resistant aluminum alloys (A356 and A319 based) were investigated in this study. The microstructures of both alloys were composed of primary Al-Si dendrite and eutectic Si phase. However, the size and distribution for eutectic Si phase varied: a coarse and inhomogeneous distributed was observed in alloy B (A319 based). A brittle intermethallic phase of ${\alpha}-Fe\;Al_{12}(Fe,Mn)_3Si_2$ was detected only in B alloy. Alloy B exhibited high fatigue life only under a high stress amplitued condition in the high cycle fatigue results, whereas alloy A showed high fatigue life when stress was lowered. With regard to the low-cycle fatigue result ($250^{\circ}C$) showing higher fatigue life as ductility increased, alloy A demonstrated higher fatigue life under all of the strain amplitude conditions. Fractographic observations showed that large porosities and pores near the outside surface could be the main factor in the formation of fatigue cracks. In alloy B. micro-cracks were formed in both the brittle intermetallic and coarse Si phasese. These micro-cracks then coalesced together and provided a path for fatigue crack propagation. From the observation of the differences in microstructure and fractography of these two automotive alloys, the authors attempt to explain the high-temperature fatigue deformation behavior of heat resistant aluminum alloys.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.17 no.2
• /
• pp.145-156
• /
• 2021

Ultrasonic Nanocrystal Surface Modification (UNSM) is a peening technology that generates elastic-plastic deformation on the material surface to which a static load of a air compressor and a dynamic load of ultrasonic vibration energy are applied by striking the material surface with a strike pin. In the UNSM-treated material, the structure of the surface layer is modified into a nano-crystal structure and compressive residual stress occurs. When UNSM is applied to welds in a reactor coolant system where PWSCC can occur, it has the effect of relieving tensile residual stress in the weld and thus suppressing crack initiation and propagation. In order to quantitatively evaluate the compressive residual stress generated by UNSM, many finite element studies have been conducted. In existing studies, single-path UNSM or UNSM in a limited area has been simulated due to excessive computing time and analysis convergence problems. However, it is difficult to accurately calculate the compressive residual stress generated by the actual UNSM under these limited conditions. Therefore, in this study, a minimum finite element peening analysis area that can reliably calculate the compressive residual stress is proposed. To confirm the validity of the proposed analysis area, the compressive residual stress obtained from the experiment are compared with finite element analysis results.