• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.6 no.3
• /
• pp.53-62
• /
• 1986

For the research on the fatigue fracture behavior in the welded joints of steel structures, base metal specimens and welded ones were selected, and the direct fatigue tests were carried out. Thereafter, fatigue-life (S-N) curves, plastic strain-number of cycles (${\varepsilon}_p$-N) curve, the extrapolated fatigue-life (${\varepsilon}_p$-$N_c$) curve, and da/dN-${\Delta}K$ curves were plotted. By these results the followings were obtained. It was shown that the ratio of fatigue strength at $2{\times}10^6$ cycles of the welded specimen to that of the base metal one was 0.6, and that 0.72 for the base metal and 0.65 for the welded one were the ratio of fatigue strength at $2{\times}10^6$ cycles to yielding stress. The S-N curve for the welded specimen was separated into two sections, the low gradient section and the steep section. As this result, it was shown that the more stress became to reduce, the more the reduction of fatigue strength became to be great. It was shown that fatigue strength at $2{\times}10^6$ cycles from this case was about 83 % of that from the S-N curve plotted with one section. It was thought that the reason was that weld flaw acted greatly on the fatigue strength within the low stress range. It was shown that at the instart of crack initiation plastic strain increased abrupt1y in the case of the welded specimen more than the case of the base metal specimen, and increased abruptly in the upper stress range in both cases. It was shown that the experimental constant ${\alpha}$, 0.42, in the base metal nearly accorded with Manson-Coffin's result, but this made a great difference with the case in the welded specimen. It was thought that it was due to the abrupt change of plastic strain and the influence of weld flaw.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.26 no.2
• /
• pp.121-143
• /
• 2010

To investigate the effect of implant types and bone resorption on the fracture characteristics. 4 types of Osstem$^{(R)}$Implant were chosen and classified into external parallel, internal parallel, external taper, internal taper groups. Finite elements analysis was conducted with ANSYS Multi Physics software. Fatigue fracture test was performed by connecting the mold to the dynamic load fatigue testing machine with maximum load of 600N and minimum load of 60N. The entire fatigue test was performed with frequency of 14Hz and fractured specimens were observed with Hitachi S-3000 H scanning electron microscope. The results were as follows: 1. In the fatigue test of 2 mm exposed implants group, Tapered type and external connected type had higher fatigue life. 2. In the fatigue test of 4 mm exposed implants group, Parallel type and external connected types had higher fatigue life. 3. The fracture patterns of all 4 mm exposed implant system appeared transversely near the dead space of the fixture. With a exposing level of 2 mm, all internally connected implant systems were fractured transversely at the platform of fixture facing the abutment. but externally connected ones were fractured at the fillet of abutment body and hexa of fixture or near the dead space of the fixture. 4. Many fatigue striations were observed near the crack initiation and propagation sites. The cleavage with facet or dimple fractures appeared at the final fracture sites. 5. Effective stress of buccal site with compressive stress is higher than that of lingual site with tensile stress, and effective stress acting on the fixture is higher than that of the abutment screw. Also, maximum effective stress acting on the parallel type fixtures is higher. It is careful to use the internal type implant system in posterior area.