• Journal of the Korean Society for Precision Engineering
• /
• v.6 no.3
• /
• pp.78-89
• /
• 1989

Applicability of tearing modulus based on J-integral proposed by Paris et al is investigated using compact tension specimens of strutural alloy steel (SCM4). Both general fracture test and instability fracture test are performed. The applied tearing modulus, ( $T_{j}$)app estimated from the real load vs. crack growth curve measured from experiments are compared with that estimated from the limit load vs. crack growth curve. The results are : (1) the $T_{j}$parameter could be applied to predict crack growth instability : (2) The use of ( $T_{j}$)app estimated from the load vs. crack growth curve, proposed in this study could be well predicted crack growth instability instead of that estimated form the limit load vs. crack growth curve.e.

• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.203-213
• /
• 1996

In this study the subcritical crack growth behavior in an Al2O3-SiCw composite has been investigated using in situ fracture technique of applied moment double cantilever beam (AMDCB) specimens indside an SEM. This technique allows the detailed observation of whisker and grain bridging in the crack wake region. The experimental results indicated that the KI-a curve was deviated from the conventional powder law form and that the existed a region where the rate of microcrack growth was decreased with increasing the externally applied stress intensity factor. This behavior could be explained by arising crack growth resistance i.e. R-curve behavior which was associated with crack shielding due to whisker and grain bridging. The R-curve was also analyzed from the KI-a curve data in order to quantify the bridging effect in the Al2O3-SiCw composite.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.5
• /
• pp.797-804
• /
• 2001

To obtain representative fatigue crack growth characteristic curve in residual stress field, fatigue crack growth test was carried out at various stress ratio and fatigue crack growth characteristic curve was represented using crack closure concept. Obtained results are as follows;K(sub)op/K(sub)max was independent of K(sub)max when R was lower than 0.5 and crack closure phenomenon was not observed when R is higher than 0.5. therefore neglecting crack closure behaviour, actual fatigue crack growth rate can be underestimated. Thus, considering crack closure phenomenon, fatigue crack growth characteristics curve of A 106 Gr B Steel weldment can be effectively estimated.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.5
• /
• pp.928-937
• /
• 1989

Applicability of $T_{\delta}$ proposed by Shin et al as an instability parameter for ductile material is investigated, Both general fracture test and instability fracture test are performed using compact tension specimens of structural alloy steel(SCM4), The values of ( $T_{\delta}$)$_{app}$(applied tearing modules) estimated from the real load vs. crack growth curve measured from experiments are compared with those estimated from the limit load vs. crack growth curve. The results are:(1) the $T_{\delta}$ parameter may be used as a crack instability parameter:(2) the use of ( $T_{\delta}$)$_{app}$ estimated from the load-crack growth curve, proposed in this study is reasonably justified.ified.d.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.5
• /
• pp.1097-1103
• /
• 1988

This paper deals with surface crack behavior and the fatigue life prediction of notched specimens using the relation between surface crack length, a, and the cycle ratio, $N/N_{f}$. From the $a-N\;/\;N_{f}$ curves, UC(the upper limit curve), LC(the lower limit curve) and MC(the middle limit curve) were assumed and utilized to predict the fatigue life and crack growth rate. The data computed from the three assumed curves were compared with the experimental data. It has been found that in the stable crack growth region ($N/N_{f}=0.3-0.8$) fatigue life can be predicted within 20% errors. Using the characteristics of $a-N\;/\;N_{f}$ curve, it is possible to predict the $da/dN-K_{max}$ curve, the $da/dN-{\Delta}K_{{\varepsilon}_t}$ curve, and the $S-N_{f}$ curve.

• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1095-1100
• /
• 1996

• Journal of Advanced Marine Engineering and Technology
• /
• v.29 no.8
• /
• pp.855-861
• /
• 2005

Fracture toughness defined near the initiation of stable crack growth is investigated by R-curve and Direct Current electric Potential Determination(DCPD) under mode I plane strain conditions for CT specimen with 25.4mm thickness of SS400 steel. Fracture toughness. $J_{IC}$lit near crack tip of CT specimen by R-curve is 17.14 $kg_{f}/mm$ and however. its value by DCPD is 22.82 $Rg_{f} mm$ The value of fracture toughness by DCPD is larger than that by R-curve. Therefore, it is suggested that the evaluation of fracture toughness by R-curve is optimum than by DCPD, when considering amount of crack growth about each of fracture toughness.

• Journal of Advanced Marine Engineering and Technology
• /
• v.23 no.4
• /
• pp.488-503
• /
• 1999

The present paper considers the constraint effect on J-R curves under the two-parameter $J-A_2$ controlled crack growth within a certain amount of crack extension. Since the parameter $A_2$ in $J-A_2$ three-term solution is independent of applied loading under fully plasticity or large-scale defor-mation $A_2$ is a proper constraint parameter uring crack extension. Both J and $A_2$ are used to char-acterize the resistance curves of ductile crack growth using J as the loading level and $A_2$ are used to char-acterize the resistance curves of ductile crack growth using J as the loading level and A2 as a con-straint parameter. Approach of the constraint-corrected J-R curve is proposed and a procedure of transferring the J-R curves determined from standard ASTM procedure to non-standard speci-mens or real cracked structures is outlined. The test data(e.g. initiation toughness JIC and tearing modulus $T_R$) of Joyce and Link(Engineer-ing Fracture Mechanics 1997, 57(4) : 431-446) for single-edge notched bend[SENB] specimen with from shallow to deep cracks is employed to demonstrate the efficiency of the present approach. The variation of $J_{IC}$ and $T_R$ with the constraint parameter $A_2$ is obtained and a con-straint-corrected J-R curves is constructed for the test material of HY80 steel. Comparisons show that the predicted J-R curves can very well match with the experimental data for both deep and shallow cracked specimens over a reasonably large amount of crack extension. Finally the present constraint-corrected J-R curve is used to predict the crack growth resistance curves for different fracture specimens. over a reasonably large amount of crack extension. Finally the present constraint-corrected J-R curve is used to predict the crack growth resistance curves for different fracture specimens. The constraint effects of specimen types and specimen sizes on the J-R curves can be easily obtained from the constrain-corrected J-R curves.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.3
• /
• pp.472-478
• /
• 1989

Using the SMC(sheet moulding compound) composite material consisting of E-glass chopped strand mat and unsaturated polyester resin, three-point bending tests are carried out to evaluate the elasto-plastic fracture toughness by means of R curve. The crack extension is experimentally observed with the ink staining method. The point of stable crack growth is discussed in consideration of the load-load point displacement curve, the damage behavior of the notch vicinity, and the R-curves. The damage zone of the notch vicinity was composed of the initiation and growth of subcracks as well as those of the main crack. The point of stable crack growth can be defined as the inflection point in the R curves and its point also concurrs with the proportional limit on the load-load point displacement curve.

• Journal of Ocean Engineering and Technology
• /
• v.9 no.2
• /
• pp.112-122
• /
• 1995

In this work, prediction of fatigue life and fatigue crack growth are studied. 4th order polynominal function is presented to describe the crack growth behaviors from artifical pit of SM45C steel. Crack growth curves obtained from 4th order polyminal growth equations are in good agreement with experimental data The crack growth behaviors at arbitrary stress levels and investigated by the concept of elastic-plastic fracture mechanics using ${\Delta}J$. Fatigue life prediction are carried out by numerical integral method. Prediction lives obtained by proposed method in this study, is in good agreement with the experimental ones. Life prediction results calculated by using of ${\Delta}J$ better than those of ${\Delta}K$.