• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2002년도 추계학술대회 논문집
• /
• pp.359-365
• /
• 2002

The fatigue crack growth behavior of the SA516/60 steel which is used for pressure vessels was examined experimentally at room temperature $25^{\circ}C,\;-30^{\circ}C,\;-60^{\circ}C,\;-80^{\circ}C,\;-100^{\circ}C$ and $-120^{\circ}C$ with stress ratio of R=0.05, 0.1 and 0.3. Fatigue crack propagation rate da/dN related with stress intensity factor range ${\Delta}K$ was influenced by stress ratio in stable of fatigue crack growth (Region II) with an increase in ${\Delta}K$. The resistance of fatigue crack growth at low temperature is higher compared with that at room temperature, which is attributed to tile extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and low temperatures are mainly explained by the crack closure and the strengthening due to the plasticity induced and roughness induced.

• 한국강구조학회 논문집
• /
• 제15권5호통권66호
• /
• pp.475-487
• /
• 2003

본 연구는 선형탄성 파괴역학적 방법을 사용하여 피로 손상을 평가할 수 있는 해석모델을 개발하는데 있다. 트럭 한 대가 교량상부를 통과할 때 부재에 발생하는 응력이력을 블록하중이라 정의하고 하중상호작용효과를 설명하는 균열닫힘 모델 이론을 적용한다. 블록하중에 대해 사하중 응력과 균열개구응력을 고려하여 응력범위빈도해석을 수행하였다. 여기서 구한 응력범위빈도분포에 확률적 방법을 적용하여 응력범위빈도분포의 확률분포 파라미타를 추 정하였다. 확률분포의 확률변수를 발생시키는 Monte Carlo Simulation 실행을 하여 파괴블럭수와 확률분포를 구한다. 이로부터 부재의 파로파괴가 발생하지 않는 피로신뢰성을 계산한다. 또한 파괴블럭수를 일평균 트럭교통량으로 나누면 예상잔존수명을 구할 수 있다. 제안된 피로신뢰성 해석모델을 사용하여 강상자형교 가로보와 수직보강개의 용접부에 피로신뢰성 해석을 수행 한 결과, 피크해석방법 결과와 잔존수명이 3.8% 정도 차이가 있었다. 이는 제안된 모델이 균열닫힘 현상이나 균열지연 형상을 고려하고 있음을 알 수 있었다.

• 한국전산구조공학회논문집
• /
• 제25권4호
• /
• pp.293-300
• /
• 2012

본 논문에서는 직교이방성 적층평판에서의 균열생성 및 전파로 이루어진 층간분리해석을 다룬다. 기존의 p-유한요소가 가지고 있는 요소의 강건성을 균열진전해석에 적용하여, 균열진전시 모델링을 재구성하지 않고, 균열 선단부에 해당되는 꼭지점 모드의 위치만을 이동하도록 하여, 요소망을 단순화시켰다. 이와 같은 층간분리해석에 대해서 이 논문에서의 주요 목적은 다음 두 가지이다. 첫째, 적층복합 재료의 층간분리해석 시, 일반적인 유한요소 모델과 비교하여 매우 간단한 요소망을 가지는 모델을 제안하는 것이다. 모델의 타당성을 평가하기 위해 적층 복합재료로 구성된 이중 외팔보 해석을 통하여, 기존 참고문헌 값과의 비교를 수행하였다. 둘째, 제안된 모델을 내부균열을 갖는 적층평판의 층간분리해석에 적용하여 여러 가지 거동 양상에 대한 평가이다. 이와 같은 목적을 수행하기 위하여 로바토 형상함수를 이용한 완전층별요소가 고려되었으며, 선형탄성파괴역학에 기초한 3차원 가상균열닫힘법을 이용하여 에너지 방출률을 산정하였다.

• Journal of Welding and Joining
• /
• 제18권2호
• /
• pp.86-94
• /
• 2000

This study was performed to investigate types and formation mechanism of cracks in two Al alloy welds, A5083 and A7N01 spot-welded by pulse Nd : YAG laser, using SEM, EPMA and Micro-XRD. In the weld zone, three types of crack were observed : center line crack({TEX}$C_{C}${/TEX}), diagonal crack({TEX}$C_{D}${/TEX}), and U shape crack({TEX}$C_{U}${/TEX}). Also, HAZ crack({TEX}$C_{H}${/TEX}) was observed in the HAZ region, furthermore, mixing crack({TEX}$C_{M}${/TEX}) consisting of diagonal crack and HAZ crack was observed. White film was formed at th hot crack region in the fractured surface after it was immersed to 10% NaOH water. In the case of A5083 alloy, white films in {TEX}$C_{C}${/TEX} crack and {TEX}$C_{D}${/TEX} crack region were composed of low melting phases, {TEX}$Fe_{2}SiAl_{8}${/TEX} and eutectic phases, $Mg_2$Al$_3$ and $Mg_2$Si. Such films observed $CuAl_2$, {TEX}$Mg_{32}(Al,Zn)_{3}${/TEX}, MgZn$_2$, $Al_2$CuMg and $Mg_2$Si were observed in the whitely etched films near {TEX}$C_{C}${/TEX} crack and {TEX}$C_{D}${/TEX} crack regions. The formation of liquid films was due to the segregation of Mg, Si, Fe in the case of A5083 alloy and Zn, Mg, Cu, Sim in the case of A7N01 alloy, respectively. The {TEX}$C_{C}${/TEX} and {TEX}$C_{D}${/TEX} cracks were regarded as a result of the occurrence of tensile strain during the welding process. The formation of {TEX}$C_{M}${/TEX} crack is likely to be due to the presence of liquid film at the grain boundary near the fusion line in the base metal as well as in the weld fusion zone during solidification. The {TEX}$C_{U}${/TEX} crack is considered a result of the collapsed keyhole through incomplete closure during rapid solidification.

• 동력기계공학회지
• /
• 제4권4호
• /
• pp.41-47
• /
• 2000

Fatigue crack propagation rate and threshold characteristics of the SA516/70 steel which is used for the low temperature pressure vessels, were studied in the room temperature of $25^{\circ}C$ and low temperature ranges of $-10^{\circ}C,\;-30^{\circ}C,\;-60^{\circ}C\;and\;-80^{\circ}C$ with stress ratio of R=0.1. In the logarithmic relationship between the fatigue crack propagation rate($d{\alpha}/dN$) and stress intensity factor range ${\Delta}K$, the linear relationship was obtained up to $d{\alpha}/dN=4.425{\times}10^4mm/cycle$ in the same of room temperature, but in low temperature case, the relationship was extended to the range of low crack propagation rate. The fractured specimens were examined by SEM. Tested results showed that specimen failed at low temperature exhibit the quasi-cleavage fracture formation however considerable ductility proceed final fracture.

• Geomechanics and Engineering
• /
• 제35권4호
• /
• pp.333-366
• /
• 2023

Rock as a mass generally exhibits discontinuities, commonly witnessed in rock slopes and underground structures like tunnels, rock pillars etc. When these discontinuities experiences loading, a new crack emerges from them which later propagates to a macro scale level of failure. The failure pattern is often influenced by the nature of discontinuity, geometry and loading conditions. The study of crack growth in rocks, namely its initiation and propagation, plays an important role in defining the true strength of rock and corresponding failure patterns. Many researchers have considered the length of the discontinuity to be fully persistent on rock or rock-like specimens by both experimental and numerical methods. However, only during recent decades, there has been a substantial growth in research interest with non-persistent discontinuities where the crack growth and its propagation phenomenon were found to be much more complex than persistent ones. The non-persistence fractures surface is generally considered to be open and closed. Compared to open flaws, there is a difference in crack growth behaviour in closed or narrow flaws due to the effect of surface closure between them. The present paper reviews the literature that has contributed towards studying the crack growth behaviour and its failure characteristics on both open and narrow flaws subjected to uniaxial and biaxial compression loading conditions.

• 대한기계학회논문집
• /
• 제17권2호
• /
• pp.331-341
• /
• 1993

The propagating crack problems under dynamic antiplane mode in orthotropic material is studied in this paper. To analyze the dynamic fracture problems by theoretical method or experimental method in orthotropic material, it is important to know the dynamic stress intensity factor in the vicinity of crack tip. Therefore the dynamic stress field and dynamic displacement field with dynamic stress intensity factor of orthotropic material in mode III were derived. When the crack propagation speed approachs to zero, the dynamic stress components and dynamic displacement components derived in this paper are identical to the those of static state. In addition, the relationships between dynamic stress intensity factor and dynamic energy release rate are determined by using the concept of crack closure energy with the dynamic stresses and dynamic displacements derived in this paper. Finally, the characteristics of crack propagation are studied with the properties of orthotropic material and crack speed. The variation of angle .alpha. between fiber direction and crack propagating direction and crack propagation speed fairly effect on stress component and displacement component in crack tip. The influence of crack propagation speed on the speed on the stress and displacement is greater in the case of .alpha.=90.deg. than in the case of .alpha.=0.deg. and the faster the crack propagation speed, the greater the stress value and displacement value.

• 대한기계학회논문집A
• /
• 제26권2호
• /
• pp.374-379
• /
• 2002

Corrosion fatigue tests were carried out to clarify the influence of acid fog as environmental factor on the fatigue strength of SM55C using rotary bending fatigue tester. The fatigue strength of acid fog specimen extremely decreased about 80% compared to that of distilled water specimen. In acid fog environment, a number of cracks commenced at corrosion pit and coalesced with the adjacent cracks during they propagate, and they formed a single non-propagating circumferential crack under the endurance stress of N=5$\times$10$\^$7/ cycles. Also, the depth of the crack is smaller than that of normal fatigue crack, so the crack has a veil small aspect ratio. The reason of this peculiar crack growth characteristics is that the crack opening-closure behaviors are hindered by corrosion products on the surface crack faces, and hence it is thinkable that the strong corrosion action like anodic dissolution for crack growth in depth direction is weaker compared with surface, resulting from faint pumping action of crack during loading-shedding processes.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1999년도 제29회 춘계학술대회
• /
• pp.38-46
• /
• 1999

Numerical methods are procured for evaluating the contact stresses, the dissipation of friction energy density and the fatigue cracking emanated from the contact surface under the partial slip condition. A rounded punch is used for the indenter pressing and slipping on the elastic half plane. Plane strain condition is assumed for the present analysis. Several sample calculations are carried out to investigate the effect of the punch roundness, the shear load path, and the crack obliquity and closure on the failure. It is found that the present methods can be a useful tool for studying the physical failure of the of the contacting materials such as fretting wear and fretting fatigue cracking.

• 한국산업융합학회 논문집
• /
• 제7권4호
• /
• pp.399-405
• /
• 2004

Currently, the use of carbon steel in a high temperature environment, such atomic reactor, increases. Test piece was heated in electric furnace and the prescribed temperature was controlled within ${\pm}1^{\circ}C$. Debris that falls apart from cracked section due to friction is accumulated inside. Then, as it causes fretting corrosion (formation of oxide layer), it contributes to crack closure.