• Journal of Energy Engineering
• /
• v.13 no.4
• /
• pp.281-290
• /
• 2004

Spent refractories from a coal gasifier after 1000 hours of operation were analyzed for crystalline phases, chemical composition and microstructures as a function of slag penetration depth, and the slag corrosion mechanism was determined. The chemical corrosion of chromia refractory occurred via reaction between Cr$_2$O$_3$ of the refractory and FeO and A1$_2$O$_3$ in the slag. The FeO reacted with Cr$_2$O$_3$ at the slare/refractory interface and formed FeCr$_2$O$_4$. After all FeO were consumed, Al in the penetrating slag substituted Cr in Cr$_2$O$_3$, forming (Al, Cr)$_2$O$_3$, at the edges of the particle, which were broken to form fragments rich in Al. The corrosion resistance of Cr$_2$O$_3$ varied with the particle size and the extent of sintering, and the higher resistance was observed in the larger and more sintered particles. There was no chemical change in ZrO$_2$, but showed the effects of physical corrosion: the grain boundaries became more wavy, and ZrO$_2$ grains were split in the corroded area. The slag penetration depth increased in the refractory samples farther down from the feed nozzles.

• Journal of the Korean Vacuum Society
• /
• v.7 no.3
• /
• pp.201-207
• /
• 1998

We have investigated about interface characteristics between ZnO thin films and metal electrodes when ZnO and metal electrodes were fabricated as piezoelectric vibrators. At this, ZnO thin films were deposited by rf reactive magnetron sputtering method. After fabricating piezoelectric vibrator of Cr/ZnO/Cr structure with optimum condition, we analyse interface characteristics between ZnO thin films and metal electrodes by I-V measurement. AES depth profile, SEM and C-V measurement. From these measurements we found that ZnO piezoelectric vibrators showed good property when they fabricated as Cr/$SiO_2$/ZnO/Cr structure. And we could confirm these things by driving, and measuring vibration displacement of piezoelectric vibrator with $SiO_2$diffusion barrier.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.9
• /
• pp.924-929
• /
• 2004

The microstructure, electrical and dielectric characteristics of $ZnO-{Pr}_6{O}_11-{CoO}-{Dy}_2{O}_3$-based varistors were investigated without and with various metal oxide additives(NiO, MgO, Cr$_2$O$_3$). The average grain size decreased in the range of 18.4 $\backsim$ 11.5 $\mu$m, in order of NiO\longrightarrowMgO\longrightarrow{Cr}_2{O}_3$ and the density decreased in the range of 5.62 \backsim 5.33 $g/{cm}^3$ in order of NiO\longrightarrowCr$_2$O$_3$\longrightarrowMgO. While, the nonlinear exponent increased In the range of 19.8$\backsim$67.4 in order of NiO\longrightarrowMgO\longrightarrow${Cr}_2{O}_3$ and the leakage current decreased in the range of 25.6 $\backsim$ 1.2 $\mu$A in order of NiO\longrightarrow${Cr}_2{O}_3$\longrightarrowMgO. Among all varistors, the Cr$_2$O$_3$-added varistor exhibited the highest nonlinearity, with a nonlinear exponent of 67.4 and a leakage current of 1.2 $\mu$A. Furthermore, this varistor exhibited the lowest dielectric dissipation factor of 0.0407.

• Journal of Environmental Science International
• /
• v.23 no.5
• /
• pp.829-837
• /
• 2014

Titania-supported chromium oxides with different loadings have been embarked in catalytic oxidation of trichloroethylene (TCE) to inquire association of the formation of crystalline $Cr_2O_3$ with catalytic performances. A better activity in the oxidative TCE decomposition at chosen temperatures was represented when chromium oxides ($CrO_x$) had been dispersed on pure anatase-type $TiO_2$ (DT51D) rather than on phase-mixed and sulfur-contained ones such as P25 and DT51. The extent of TCE oxidation at temperatures below $350^{\circ}C$ was a strong function of $CrO_x$ content in $CrO_x$/DT51D $TiO_2$, and a noticeable point was that the catalyst has two optimal $CrO_x$ loadings in which the lowest $T_{50}$ and $T_{90}$ values were measured for the TCE oxidation. This behavior in the activity with respect to $CrO_x$ amounts could be associated with the formation of crystalline $Cr_2O_3$ on the support surface, that is less active for the oxidation reaction, and an easier mobility of the surface oxygen existing in noncrystalline $CrO_x$ species with higher oxidation states, such as $Cr_2O_8$ and $CrO_3$.

• Journal of the Korean Ceramic Society
• /
• v.29 no.2
• /
• pp.101-106
• /
• 1992

Sintering behavior, distribution of dopant oxides and electrical properties in the ZnO-Bi2O3-CoO-Sb2O3 and ZnO-Bi2O3-CoO-Sb2O3-Cr2O3 systems were studied. The linear shrinkage of ZnO varistors from 850 to 950$^{\circ}C$ was related to the decomposition reaction (py\longrightarrowsp+Bi2O3) of the pyrochlore phase. In the distribution of the dopant oxides (CoO, Sb2O3, Cr2O3), Co distribute uniformly throughout the sample, the distribution of Sb coincided with small particles (spinel phase, Zn7Sb2O12), and Cr distributed very consistently with Sb. The increase in breakdown voltage, due to the addition of Cr2O3, was not only attributed to the decrease in the ZnO grain size but also to the solution of Cr2O3 in the spinel phase. The leakage current (80% V60 ${\mu}\textrm{A}$) was increased by the addition of Cr2O3.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.11a
• /
• pp.69-77
• /
• 2001

Wear and Friction characteristics of plasma-sprayed Cr$_2$O$_3$ coating and Cr$_2$O$_3$ coating included SiO$_2$ and TiO$_2$ against SiC ball have been investigated under different loads. Worn surfaces were observed by SEM and worn surfaces were analyzed by EDS. The Friction coefficient and the Wear resistance of Cr$_2$O$_3$-5SiO$_2$-3TiO$_2$coating was less than that of Cr$_2$O$_3$ coating. The main mechanisms were plastic deformation and brittle fracture. The film on surface were made by plastic deformation and compacted wear debris. This film protect wear of coating

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.11
• /
• pp.875-879
• /
• 2010

In this study, we have characterized the roles of $Cr_2O_3$ on the sintering and electrical properties of ZnO. The densification and grain growth of Cr-doped ZnO (ZCr) system was mainly influenced by Cr contents. In the beginning of sintering, the densification of ZnO was retarded as reducing the Zni concentration in ZnO lattice with Cr doping. And the densification and grain growth of ZnO was more retarded due to a formation of spinel phase with increasing the Cr contents. ZCr system revealed varistor behavior with nonlinear coefficient $\alpha$ of 3~23 depending on the sintering temperature, implying double Schottky barrier formation on the grain boundary of ZnO. Especially the best varistor characteristics should be developed with 0.1~0.5 at% Cr contents and under $1100^{\circ}C$ in ZCr systems.

• Journal of the Korean Chemical Society
• /
• v.34 no.6
• /
• pp.534-538
• /
• 1990

Chromium(Ⅵ) compound, [$C_9H_7$NH]$_2Cr_2O_7$ has been prepared by the reaction of isoquinoline with chromium trioxide under the presence of water. [$C_9H_7$NH]$_2Cr_2O_7$ is nonhydroscopic and dissolved in water very well. Structure of [$C_9H_7$NH]$_2Cr_2O_7$ is identified by FTIR spectra and elemental analysis data. The ability of [$C_9H_7$NH]$_2Cr_2O_7$ for the oxidation of alcohols were examined in methylene chloride. [$C_9H_7$NH]$_2Cr_2O_7$ was found as efficient oxidizing agent for the conversion of allyl, primary and secondary alcohols to the corresponding aldehydes or ketones.

• Journal of the Korean Chemical Society
• /
• v.33 no.1
• /
• pp.11-17
• /
• 1989

Pyrazinium chlorochromate and dipyrazinium trichromate which are pyrazinium salts were prepared by the each reaction of pyrazine with chromium trioxide under the presence of HCl and $CH_2Cl_2$. These compounds wese nonhygroscopic and were solved in water very well. Physical properties such as solubility, pH, electrical conductivity, and melting point were measured. These compounds were considered to be ionic ; $C_4H_4N_2H^+$, $CrO_3Cl^-$, $Cr_3O^{2-}_{10}$ by the measurement of electrical conductivity. It was found that CrO$_3$ was formed in the first decomposition process of salts and it was changed into $Cr_2O_3$ in the second process as its weight is decreased. It was also found that especially under the same condition dipyrazinium salt was in the form of isopoly ($Cr_2O^{2-}_{10}$)anion which has been thought to be in the form of $Cr_2O^{2-}_{7}$ obtained from pyridine.

• Journal of the Korean Chemical Society
• /
• v.18 no.2
• /
• pp.110-116
• /
• 1974

Reduction of chromate ion at the Pt-electrode was investigated in neutral unbuffered solutions, in buffered solutions of pH between 8 and 10, and in strongly alkaline medium. In buffered solutions of pH between 8 and 10, the number of electrons transfered in the reduction of chromate ion increased progressively with increasing pH. When chromate ion was reduced in 0.2 N sodium hydroxide medium the following mechanism was suggested: $CrO_4^=+H_2O+2e{\rightarrow}CrO_3^=+2OH^-,\;CrO_3^=3H_2O+e{\rightarrow}Cr(OH)_3+3OH^-$ When tetramethylammonium hydroxide (pH=13.5) was used as the supporting electrolyte, a second wave indicated strong adsorption. In unbuffered solutions of 0.1 N potassium chloride the linear sweep voltammogram consists of three or four distinct waves depending on the initial voltage and the voltage sweep rates, but the first wave was difficult to explain as a diffusion controlled wave.