• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.3
• /
• pp.353-358
• /
• 2013

The ultrasonic characteristics of 2.25Cr-1Mo steel were investigated in relation to the isothermal heat treatment temperature and time. Charpy impact tests and hardness tests were conducted on individual specimens with three different heat treatment conditions. A pulse-echo method with longitudinal waves was used to measure the attenuation and velocity of ultrasonic waves. The FATT (fracture appearance transition temperature) increased with an increase in the isothermal heat treatment time, which implies that the toughness decreased. As the isothermal heat treatment time and temperature increased, the longitudinal wave velocity and ultrasonic attenuation coefficient were raised.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.445-450
• /
• 2000

The integrity of the turbine rotors can be assessed by measuring reversible permeability and Vickers hardness of the aged rotors at service temperature. The measurement system of reversible permeability, which measured by applied alternating perturbing magnetic field, was constructed in order to evaluate material degradation, nondestructively. The test specimen was 1Cr-1Mo-0.25V steel used widely for turbine rotor material, and the specimens were prepared by the isothermal heat treatment at $630\;^{\circ}C$. The reversible permeability of the test materials were measured at room temperature. The peak interval of reversible permeability and Vickers hardness decreased with the increase of degradation. The degradation of test material may be determined nondestructively by the lineality of Vickers hardness and the peak interval of reversible permeability.

• Journal of the Korean Society for Heat Treatment
• /
• v.35 no.3
• /
• pp.121-129
• /
• 2022

Recently the growth of the renewable energy production has caused the flexible operation in LNG combined cycle power plant. Due to the rapid start and stop operations, large CrMoV castings used for turbine casings and valve bodies could be distorted and lead to replacement or welding repair. This study was performed to find out the characteristics of the repair welding for a damaged CrMoV casting steel. A typical field repair method (arc & TIG welding) was applied to making specimens. The degraded N2 packing head sample from the steam turbine was used. The evaluations of weldments were carried out in terms of microstructural characterization, microhardness measurements, tensile, creep-rupture and fatigue tests. Color etching was also applied for better understanding of welding microstructures. As the boundary between HAZ and base material was deteriorated by welding, it caused microstructural changes formed during PWHT and the shortening of the remaining residual life. By comparing the properties according to repair welding method, it was possible to derive what important welding factors were. As a result, arc welding method is more suitable for repair welding on CrMoV castings.

• Journal of the Korean Society of Safety
• /
• v.25 no.1
• /
• pp.22-26
• /
• 2010

Material degradation should be considered to assess integrity and residual life of high temperature equipments. However, the property data reflecting degradation are not sufficient for practical use. In this study, mechanical properties of 1Cr-1Mo-0.25V casting steel generally used for turbine casing were measured and variation of microstructure was observed. Degradation was simulated by isothermal heat treatment.

• Journal of Welding and Joining
• /
• v.13 no.4
• /
• pp.103-112
• /
• 1995

This study was performed to optimize friction welding conditions of Cr-Mo steel bars used for hydraulic of pneumatic valve spools and to realize the real-time evaluation of weld quality by acoustic emission method. SNCM220, SCM435, SCAM645, and SCM415 steel bars were tested to find optimum conditions of friction welding. Auantitative equations which exhibit the relations of tensile strength, elongation, reduction of area and energy absorption with friction heating time were obtained by the experiment. Acoustic emission was also performed in the friction weldig process, and the real-time evaluation was enabled to find the optimum range of weld strength. Finally, the strength and toughness of welded joints were interpreted by the sem analysis of tensile fracture surfaces.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.210-215
• /
• 2001

The ferritic 2.25CrMo steel has been used for high temperature structure applications such as turbine rotors, boilers and pressure vessels in fossil plant and petroleum chemical facilities. However, this steel is known to result in aging degradation due to temper embrittlement, carbide induced brittleness and softening of matrix after long time exposure to high temperature. This research investigated the microstructural and mechanical changes after artificial degradation treatment and evaluated the degree of degradation by several nondestructive methods. The decrease of electrical resistivity and increase of magnetic Barkhausen noise(RMS voltage) with increasing aging time were observed. The change of electrical resistivity and Barkhausen noise showed a good correlation with the ductile-brittle transition temperature.

• Journal of Magnetics
• /
• v.6 no.1
• /
• pp.27-30
• /
• 2001

We present a new procedure to evaluate the residual life of 1Cr-1Mo-0.25V steel from reversible magnetic permeability. The method is based on the existence of first harmonics in the differential magnetization around the coercive force. The apparatus is based on the detection of the voltage induced in a coil using a lock-in amplifier tuned to the frequency of the exciting coil. Results obtained for the first harmonics and Vickers hardness on aged samples show that the peak interval of reversible permeability and Vickers hardness decrease as aging time increases. The correlation between Vickers hardness and the peak interval of the reversible permeability may be used to evaluate the residual life of 1Cr-lMo-0.25V steel, nondestructively.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.4
• /
• pp.49-60
• /
• 1997

This paper deals with the effect of coating layer on the fatigue strength of TiN coated 1Cr-1Mo-0.25V steel prepared by using the arc ion plating (AIP) process, in which it was characterized by the presence of extractor grid (ion filter). The rotary bending fatigue tests were carried out under room air conditions, and the fatigue crack initiation and growth bwhavior were observed by using plastic replica method. As experimental results, it was found that the obvious improvement of fatigue life at lower stress region was confirmed in TiN coated specimen processed with ion filter. It was also exlained that the increase of fatigue life in the case of an improved AIP process with ion filter was attributed to the retardation of crack initiation of the substrate surface due to hard coating layer, more densly formed with the reduced size and density of droplets.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2000.10a
• /
• pp.369-374
• /
• 2000

This study has been achieved on the characteristics of ultrasonic wave in 2.25Cr-1Mo steel to evaluate the feasibility of ultrasonic nondestructive technique on the assessment of aging degradation. The measured values were used find a relationship between the ultrasonic propagation properties and degradation such as coarsening of carbides and precipitates. The ultrasonic attenuation coefficient was mainly affected by the grain size of prior austenitic phase as well as degradation. In this results, degradation and grain size in 2.25Cr-1Mo steel was able to cope with the changes in ultrasonic wave properties by applying the nondestructive evaluation method

• Journal of Surface Science and Engineering
• /
• v.50 no.2
• /
• pp.91-97
• /
• 2017

The aim of this paper is to investigate the characteristics of electrochemical corrosion with the plasma ion nitriding temperature for 16Cr-10Ni-2Mo stainless steel. The corrosion behavior was analyzed by means of galvanostatic experiment in natural seawater that applied various current density with plasma ion nitriding temperature parameters. In result of galvanostatic experiment, relatively less surface damage morphology and the less damage depth was observed at a nitrided temperature of $450^{\circ}C$ that measured the thickest nitrided layer(S-phase). On the other hand, the most damage depth and unified corrosion behavior presented at a temperature of $500^{\circ}C$.