• Journal of the Korean Society for Heat Treatment
• /
• v.23 no.3
• /
• pp.156-162
• /
• 2010

The modified 9Cr-1Mo steel (P91 steel) is very popular as a boiler tube material of the USC (Ultra-Supercritical) power plants. The steels were tempered in the temperature range of 400 to $650^{\circ}C$ and the mechanical tests, such as impact and hardness tersts were performed at the room temperature for the tempered steels. A drop in the impact value (embrittlement) and the hardeness increase were simultanously observed in the range of temperature between $475^{\circ}C$ and $600^{\circ}C$, particularly at $550^{\circ}C$. TEM observation shows the hardening was caused by $M_2C$, resulting in the embrittlement. And the maximum volume fraction of $M_3C$ was also observed at $550^{\circ}C$, Therefore, the embrittlement seems to be caused by both the $M_2C$ and $M_3C$.

• Journal of Powder Materials
• /
• v.28 no.5
• /
• pp.375-380
• /
• 2021

In this study, we investigate the effect of the duration of mechanical alloying on the microstructures and mechanical properties of ODS ferritic/martensitic steel. The Fe(bal.)-10Cr-1Mo pre-alloyed powder and Y₂O₃ powder are mechanically alloyed for the different mechanical alloying duration (0 to 40 h) and then constantly fabricated using a uniaxial hot pressing process. Upon increasing the mechanical alloying time, the average powder diameter and crystallite size increased dramatically. In the initial stages within 5 h of mechanical alloying, inhomogeneous grain morphology is observed along with coarsened carbide and oxide distributions; thus, precipitate phases are temporarily observed between the two powders because of insufficient collision energy to get fragmented. After 40 h of the MA process, however, fine martensitic grains and uniformly distributed oxide particles are observed. This led to a favorable tensile strength and elongation at room temperature and 650℃.

• Korean Journal of Metals and Materials
• /
• v.47 no.5
• /
• pp.283-289
• /
• 2009

This paper dealt with a statistical analysis for evaluating the creep crack growth rate (CCGR) for Modified 9Cr-1Mo (ASTM Grade 91) steel. The CCGR data was obtained by the creep crack growth (CCG) tests conducted under various applied loads at $600^{\circ}C$. To obtain logically the B and q values used in the CCGR equation, three methods such as the least square fitting method (LSFM), the mean value method (MVM) and the probabilistic distribution method (PDM) were adopted and their CCGR lines were compared, respectively. In addition, a number of random variables were generated by using the Monte Carlo simulation (MCS), and the CCGR lines were predicted probabilistically. It was found that both the B and q coefficients followed a 2-parameter Weibull distribution well. In the case of the ranges of 10-90% for the probability variables, P(B, q), the CCGR lines were predicted. Fractographic study was conducted from the specimen after the CCG tests.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.11
• /
• pp.69-76
• /
• 1997

The rotating bending fatigue tests were performed using the specimens taken from Cr-Mo-V steel, widely sued in thermal power plant turbines, at various temperatures such as room temperature, 300 .deg. C, 425 .deg. C and 550 .deg. C. The characteristics of fatigue crack propagation were examined and analyzed by using fracture mechanics parameter. The plastic replica method was also applied in order to measure the crack length on the basis of serial observation of fatigue crack propagation behavior on the defected specimen surface. The fatigue crack propagation behavior of Cr-Mo-V steel was investigated within the frame work of elastic-plastic fracture mechanics. The propagation law of fatigue crack is obtained uniquely by using the term .sigma. $^{n}$ sub a/where .sigma. $_{a}$ is the service stress, a is the crack length and n is a constant. The values of constant n are nearly equal to 2.48, 2.60 and 8.61 at room temperature, 300 .deg. C and 425 .deg. C.

• Transactions of the KSME C: Technology and Education
• /
• v.4 no.2
• /
• pp.101-109
• /
• 2016

The material properties of heat resistant materials at power plants are affected by thermal aging as operating time is accumulated. In this study, the influence of thermal aging on yield strength, tensile strength and fracture behavior for Mod.9Cr-1Mo (ASME Grade 91) steel which is a material widely adopted for Generation IV nuclear energy system has been investigated and analyzed. Service exposed Gr.91 steel materials sampled from a piping system of an ultra-supercritical (USC) plant in Korea with accumulated operation time of 73,716 hours were used for material testing. The test results of the service exposed material specimens were compared with those of the virgin Gr.91 steel specimens. Those test data were compared with the material properties of ASME code and RCC-MRx code. Conservatisms of the material properties in the design codes have been quantified based on the comparisons of those from virgin and service exposed material specimens.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.17 no.3
• /
• pp.148-154
• /
• 2018

When shooting small arms, the inner surface temperature is heated up to about $700{\sim}1,000^{\circ}C$ by the friction of the bullet and the inner wall of the barrel and the combustion of propellant. High-temperature propellant gas and high-speed movement of the bullet cause corrosion of the inner wall, which is noticeable immediately in front of the chamber. In this study, the mechanical properties of Cr-Mo-V steel, which is the base material, were tested using Taguchi experimental design to find the best nitriding treatment conditions. For the nitriding process, the working time, salt bath temperature, and salt concentration were combined as three conditions and placed in the $L_9(3^4)$, orthogonal array table. The thicknesses of the white layer and the nitrogen diffusion layer were measured after nitriding under each condition in a salt bath furnace. Durability was evaluated by measuring the degree of dispersion through actual shooting because it was difficult to evaluate the mechanical properties of the cylinder inner structure. As a result, it was confirmed that the durability was optimal at $565^{\circ}C$, 1 hour, 0.5%. These optimal conditions were selected by the statistical analysis of the Minitab program(ver.17).

• Journal of the Korean Society for Nondestructive Testing
• /
• v.27 no.5
• /
• pp.417-425
• /
• 2007

The ferritic 9Cr-1Mo-V-Nb heat-resisting steel was experimentally studied in order to characterize its microstructural evolution during creep-fatigue by coercivity measurement. The creep-fatigue test was conducted at $550\;^{\circ}C$ with the tensile holding time of 60s and 600s, respectively. The coercivity decreased until the failure and the hardness monotonously decreased for the whole fatigue life. As the life fraction of creep-fatigue increased, the $M_{23}C_6$ carbide coarsened following the Ostwald ripening mechanism. However, the MX carbonitrides did not grow during creep-fatigue due to so stable at $550\;^{\circ}C$. The width of martensite lath increased because of the dislocation recovery at the lath boundaries. The magnetic coercivity has an influence on the microstructural properties such as dislocation, precipitates and martensite lath boundaries, which interpreted in relation to microstructural changes. Consequently, this study proposes a magnetic coercivity to quantify the level of damage and microstructural change during the creep-fatigue of ferritic 9Cr-1Mo-V-Nb steel.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.678-683
• /
• 2003

Ultrasonic method using SH(shear horizontal) wave has been developed to determine the surface damage in fatigued material. Fatigue damages based on propagation energy were analyzed by multiregression analysis and phase measurement in interrupted fatigue test specimen including CrMoV and 12Cr alloy steel. From the test results, as the fatigue damage increased the propagation time of the launched waves increased and amplitude of wavelet decreased. Also, analysis for the waveform modulation showed a reliable estimation, with confidence limit of 97% for 12Cr steel and 95% for CrMoV steel, respectively. Therefore, It is thought that SH ultrasonic wave technique can be applied to determine fatigue damage of in-service component nondestructively.

• Journal of Technologic Dentistry
• /
• v.36 no.3
• /
• pp.149-158
• /
• 2014

Purpose: Dental casting Co-Cr-Mo based alloys of five kinds of ingot type and two kinds of shot type were analyzed the melting processes with heating time of high frequency induction centrifugal casting machine using infrared thermal image analyzer. Methods: When Co-Cr-Mo based alloys were put about 30g/charge in the ceramic crucible of high frequency induction centrifugal casting machine and heat, Infrared thermal image analyzer and IR thermometer indicated these alloys in the crucible were set and operated. Results: The melting temperatures of alloys measuring infrared thermal image analyzer were deviated ${\pm}10^{\circ}C$ compared to those of manufacturing company. On the other hand, the melting time of alloys were differently appeared with the shape of alloys(ingot and shot type). Conclusion: The melting temperatures of dental Co-Cr-Mo based alloys were measured the degree of $1,360{\sim}1410^{\circ}C$ and the heating time with the alloys of ingot and shot type were deviated ${\pm}10sec$.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.3
• /
• pp.251-257
• /
• 2011

This paper deals with the statistical properties of parameters B and q in the creep crack growth rate (CCGR) law, da/dt=B$(C^*)^q$, in Mod. 9Cr-1Mo (ASME Gr.91) steel which is considered a candidate materials for fabricating next generation nuclear reactors. The CCGR data were obtained by creep crack growth (CCG) tests performed on 1/2-inch compact tension (CT) specimens under an applied load of 5000N at a temperature of $600^{\circ}C$. The CCG behavior was analyzed statistically using the empirical equation between CCGR, da/dt and the creep fracture mechanics parameter, $C^*$. The B and q values were determined for each specimen by the least-squares fitting method. The probability distribution functions for B and q were investigated using normal, log-normal, and Weibull distributions. As far as this study is considered, it can be appeared that B and q followed the log-normal and Weibull distributions. Moreover, a strong positive linear correlation was found between B and q.