• 열처리공학회지
• /
• 제14권2호
• /
• pp.110-117
• /
• 2001

Artificial aging was performed to simulate the microstructural degradation in 2.25CrMo steel arising from long time exposure at $540^{\circ}C$. It was found that the carbides became coarser and spheroidized as aging time increased. An attempt was made to evaluate the microstructural degradation in artificially aging heat treated 2.25CrMo steel by the ultrasonic attenuation and velocity measurements. Ultrasonic velocity was found essentially insensitive to the microstructural changes resulting from aging heat treatment. However, the ultrasonic attenuation was observed to increase with increasing aging time. Also, it was noticed that the change of ultrasonic attenuation with aging time was more sensitive at high frequency regions.

• 열처리공학회지
• /
• 제27권2호
• /
• pp.72-78
• /
• 2014

Isothermal transformation behavior of a 10% Cr heat resistant steel fabricated by centrifugal casting process was investigated. Normalized specimen at $1100^{\circ}C$ for 1 hour was isothermally annealed at temperature range between $600^{\circ}C$ and $700^{\circ}C$ with various time. The annealed specimen had eutectoid structure which was generated along austenitic grain boundary during isothermal annealing. Areal fraction of eutectoid structure increased up to 25% after holding at $700^{\circ}C$ for 20 hours. It was observed that austenitic matrix was transformed to ferrite structure and fine $M_{23}C_6$ carbides with increase of annealing time. Time-temperature-transformation diagram of the centrifugally cast 10% Cr steel with 0.18 wt% C was plotted based on the results of isothermal transformation behavior.

• 한국재료학회지
• /
• 제17권5호
• /
• pp.268-272
• /
• 2007

Inconel 617 is a candidate tube material for high temperature gas-cooled reactors(HTGR). The microstructure and mechanical properties of Inconel 617 were studied after exposure at high temperature($1050^{\circ}C$). The dominant oxide layer was Cr-oxide. The internal oxide and Cr-depleted region were observed below the Cr-oxide layer. The depth of Cr-depleted zone and internal oxide increased with exposure time. The major phases of carbides are $M_{23}C_6\;and\;M_6C$. The composition of $M_{23}C_6\;and\;M_6C$ were determined to be Cr-rich and Mo-rich, respectively. $M_6C$ carbide is more stable than $M_{23}C_6$ at high temperature. From the results of high temperature compression test, there were no significant changes in hardness and yield strength upon increasing exposure time.

• 한국안전학회지
• /
• 제17권4호
• /
• pp.71-79
• /
• 2002

It was attempted to evaluate the degree of degradation of thermally aged 2.25-1Mo steek by ultrasonic monlinear parameter(UNP) measurement and X-ray diffraction analysis of extracted carbide. Artificial aging was performed to simulate the microstructural degradation in 2.25Cr-1Mo steel arising from long time exposure at $540{\circ}C$. Microstructural analysis (number of carbides per unit area) and measurements of mechanical properties(Vickers hardness, DBTT) and degradation evaluation parameters(UNP and intensity ration of X-ray diffraction peak of electrolytically extracted carbide) were performed. Both of UNP and intensity ratio of X-ray diffraction peak for M6C carbide to that of M23C6 carbide(IR) increased abruptly in the initial 1000 hour of aging and then changed little. UNP and IR were proposed as potential parameters to evaluate the degree of aging degradation of 2.25Cr-1Mo steel.

• Corrosion Science and Technology
• /
• 제5권4호
• /
• pp.123-128
• /
• 2006

It was analyzed the causes of boiler tube rupture due to a degradation and corrosion on the boiler tubes in fossil power plant. The experiments were carried out among samples taken from the operating facilities. The result were analyzed based on experimental results from mechanical strength, microstructure observation, and hardness measurement in order to determine the cause of local rupture on boiler tubes. In general, 2.25Cr-1Mo steel generates carbides, it is coarsened, its ductility and strength abruptly decreased as degradation is in progress, In order to confirm this phenomenon, we observed changes of the mount of Cr and Mo of carbide by carrying out EDX chemical composition analysis. The amount of Cr and Mo in the degraded material or service exposed material gradually increased the amount of Mo but initially they were almost maintained at the same amount. Furthermore, we observed that the carbide become coarsened both in the grain and at the grain boundary. Tensile test was carried out to measure a material hardness and to recognize a drop-off of hardness. Overall result for tensile strength and hardness turned out to be lower than new material and mechanical strength and hardness was degraded as the material degradation was in progress.

• Advances in materials Research
• /
• 제7권1호
• /
• pp.17-28
• /
• 2018

Niobium is a candidate base for new alloys devoted to applications at especially elevated temperatures. Elaborating and shaping niobium-based alloys by conventional foundry may lead to mechanically interesting microstructures. In this work a series of charges constituted of pure elements were subjected to high frequency induction melting in cold crucible to try obtaining cast highly refractory Nb-xCr and Nb-xCr-0.4 wt.%Calloys(x=27, 34 and 37 wt.%). Melting and solidification were successfully achieved. The as-cast microstructures of the obtained alloys were characterized by electron microscopy and X-ray diffraction and their hardness were specified by Vickers macro-indentation. The obtained as-cast microstructures are composed of a body centered cubic (bcc) niobium dendritic matrix and of an interdendritic eutectic compound involving the bcc Nb phase and a $NbCr_2$ Laves phase. The obtained alloys are hard to cut and particularly brittle at room temperature. Hardness is of a high level (higher than 600Hv) and is directly driven by the chromium content or the amount of {bcc Nb - $NbCr_2$} eutectic compound. Adding 0.4 wt.% of carbon did not lead to carbides but tends to increase hardness.

• 한국표면공학회지
• /
• 제23권1호
• /
• pp.16-26
• /
• 1990

The standrd electrolyte for the electrodeposition of chromium were preparwith reagent grade chromic acid(200g/L), sulfuric acid(pH=1.8)and oxalic acalic acid(640g/L)as additive. Carbon content in chromium plating varied about2.0-3.8 wt% with current density and temperatures of the bath. The hardeness of chromium platings incresed with increasing the annealing temperatures and showed maximum value of about Hv 1700 after annealing at$ 700^{\circ}C$for 60min. But, decreased it as annealing at above $700^{\circ}C$. The reason for varing thee hardness of chromium codeposited with carbon gradually foumed chromium carbide(Cr7C3), but that changed to Cr23C6 as annealing temperature at above $^700{\circ}C$. The X-ray diffraction pattern indicated that chromium carbides, such as Cr7C3 or Cr3C2, formed at formed at above $300^{\circ}C$. titanium coating sputtered on the on surface of chromium plating had performed and determined the hardness after annealing at 500, 600, $700^{\circ}C$ for 60min. the maximum hardeness was about Hv 2400 as annealing at $700^{\circ}C$. The titanium carbide formed in layer was identified by X-ray diffraction. It was confirmed that chromium and titanium carbide has effect of increasing the hardness.

• Journal of Welding and Joining
• /
• 제18권2호
• /
• pp.232-232
• /
• 2000

The hydrogen attack characteristics of 3Cr-1Mo-V steel as simulated weld heat affected state were studied in this paper. The hydrogen attack susceptibility was evaluated by the ratios of Charpy impact absorbed energy at 0℃($vE_{0HA}$/$vE_{0}$) and reduction of area by tensile test ($RA_{HA}$/RA) before and after exposure to hydrogen at 600℃ under 450kgf/㎠ for 300hr. The values of $vE_{0HA}$/$vE_{0}$ and $RA_{HA}$/RA were aggravated as the peak temperature of the simulated heat affected zone(HAZ) raised. These results were due to the increase of the possession of bubbles along the grain boundaries, which were resulted in the reduction of grain boundary area to be precipitated carbides due to grain coarsening and the carbon dissolved in the martensite-austenite constituent near by the prior austenite grain boundary. The possession ratio of methane bubbles formed along prior austenite grain boundaries were increased with raising the peak temperature. (Received February 22, 2000)

• Journal of Welding and Joining
• /
• 제18권2호
• /
• pp.105-111
• /
• 2000

The hydrogen attack characteristics of 3Cr-1Mo-V steel as simulated weld heat affected state were studied in this paper. The hydrogen attack susceptibility was evaluated by the ratios of Charpy impact absorbed energy at 0℃({TEX}$vE_{0} {HA}_/vE_{0}${/TEX}) and reduction of area by tensile test({TEX}$RA_{HA}/RA${/TEX}) before and after exposure to hydrogen at 600℃ under 450kgf/㎠ for 300hr. The values of {TEX}$vE_{0} {HA}_/vE_{0}${/TEX} and {TEX}$RA_{HA}/RA${/TEX} were aggravated as the peak temperature of the simulated heat affected zone(HAZ) raised. These results were due to the increase of the possession of bubbles along the grain boundaries, which were resulted in the reduction of grain boundary area to be precipitated carbides due to grain coarsening and the carbon dissolved in the martensite-austenite constituent near by the prior austenite grain boundary. The possession ratio of methane bubbles formed along prior austenite grain boundaries were increased with raising the peak temperature.

• 한국재료학회지
• /
• 제32권11호
• /
• pp.466-473
• /
• 2022

The effect of Cr and Mo contents on the hydrogen embrittlement of tempered martensitic steels was investigated in this study. After the steels with different Cr and Mo contents were austenitized at 820 ℃ for 90 min, they were tempered at 630 ℃ for 120 min. The steels were composed of fully tempered martensite with a lath-type microstructure, but the characteristics of the carbides were dependent on the Cr and Mo contents. As the Cr and Mo contents increased, the volume fraction of film-like cementite and prior austenite grain size decreased. After hydrogen was introduced into tensile specimens by electrochemical charging, a slow strain-rate test (SSRT) was conducted to investigate hydrogen embrittlement behavior. The SSRT results revealed that the steel with lower Cr or lower Mo content showed relatively poor hydrogen embrittlement resistance. The hydrogen embrittlement resistance of the tempered martensitic steels increased with increasing Mo content, because the reduction in the film-like cementite and prior austenite grain size plays an important role in improving hydrogen embrittlement resistance. The results indicate that controlling the Cr and Mo contents is essential to achieving a tempered martensitic steel with a combination of high strength and excellent hydrogen embrittlement resistance.